Abstract
Mechanical milling of a mixture of pure iron and chromium powders with a nominal composition of 28 at. % of Fe and 72 at. % of Cr was performed using two kinds of tools. The alloying process was followed by X ray diffraction and57Fe Mössbauer spectroscopy. The room temperature Mössbauer spectra revealed the formation of a broad single line at the expense of the area of α-Fe sextet. At 4.2 °K most of the singlet still remains unsplit. This behavior may be due to some metastable structure induced by the preparation method.
Similar content being viewed by others
References
E. Hellstern and L. Schultz, Appl. Phys. Lett. 49 (1986) 1163.
G. Wang, D. Zhang, H. Chen, B. Lin, W. Wang and Y. Dong, Physics Letters A, 155 (1991) 57.
B. Fultz, G. Le Caer and P. Matteazzi, J. Mater. Res., 4 (1989) 1451.
E. Hellstern and L. Schultz, Proc. LAM6 Conf., Garmisch-Partenkirchen 1986, Vol. 2 (Oldenburg, Munchen, 1987), p215.
R.A. brand, Duisburg University (version of 1988).
K. Sumiyama, N. Ohshima and Y. Nakamura, Trans. JIM 28 (1987) 699.
S. K. Xia, E. Baggio-Saitovitch and C. Larica, to be published.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Peña Rodriguez, V.A., Baggio-Saitovitch, E., Xia, S.K. et al. Mechanical alloying of Fe and Cr: Structural and magnetic studies. Hyperfine Interact 69, 721–724 (1992). https://doi.org/10.1007/BF02401928
Issue Date:
DOI: https://doi.org/10.1007/BF02401928