Characterization of Ferritin Adsorption onto Gold

doi:10.1006/jcis.1996.4625

Journal of Colloid and Interface Science

Volume 186, Issue 1, 1 February 1997, Pages 129-140

https://doi.org/10.1006/jcis.1996.4625 Get rights and content

Abstract

The adsorption of ferritin from phosphate-buffered saline (PBS) onto gold has been examined using a quartz crystal microbalance (QCM), surface plasmon resonance (SPR), X-ray photoelectron spectroscopy (XPS), and atomic force microscopy (AFM). Application of these techniques allows elucidation of the surface coverage and layer thickness of ferritin on gold. The kinetics of ferritin adsorption onto gold were investigated by monitoring the resonant frequency shift of a QCM. Adsorption isotherms for ferritin in PBS and in air have been measured by QCM. These isotherms suggest less than monolayer coverage of ferritin on gold. A layer thickness of 4.8 ± 0.2 nm was calculated for the dry ferritin film from QCM data. Measurements of the shift in the reflectivity of light at a fixed angle close to the SPR plasmon resonance were also used to follow the kinetics of ferritin adsorption. Full SPR curves were measured in PBS solution and air and were used to determine the effective thickness of the ferritin layer in both environments. The ferritin layer on gold from SPR data was found to be twice as thick when measured in PBS as it was for a dry film. This difference in thickness is attributed to shrinkage of ferritin with drying. Angle-resolved XPS measurements on a dry ferritin film (preadsorbed on gold) yield a ferritin thickness of 4.7 ± 0.5 nm, a value in good agreement with those determined from QCM and SPR. QCM, SPR, and XPS all yield a surface coverage of 6.3 ± 0.7 mg m⁻²for dry ferritin layers on gold. AFM enabled examination of the topography of ferritin adsorbed on gold on the nanometer scale and confirmed that ferritin forms an incomplete monolayer. In all cases, ferritin was found to be irreversibly adsorbed to gold and to form a stable protein layer, thus making it well suited as a biological receptor layer for immunosensing applications.

References (0)

Cited by (151)

A photonic resonator interferometric scattering microscope for label-free detection of nanometer-scale objects with digital precision in point-of-use environments
2023, Biosensors and Bioelectronics
Label-free detection and digital counting of nanometer-scaled objects such as nanoparticles, viruses, extracellular vesicles, and protein molecules enable a wide range of applications in cancer diagnostics, pathogen detection, and life science research. Here, we report the design, implementation, and characterization of a compact Photonic Resonator Interferometric Scattering Microscope (PRISM) designed for point-of-use environments and applications. The contrast of interferometric scattering microscopy is amplified through a photonic crystal surface, upon which scattered light from an object combines with illumination from a monochromatic source. The use of a photonic crystal substrate for interferemetric scattering microscopy results in reduced requirements for high-intensity lasers or oil-immersion objectives, thus opening a pathway toward instruments that are more suitable for environments outside the optics laboratory. The instrument incorporates two innovative elements that facilitate operation on a desktop in ordinary laboratory environments by users that do not have optics expertise. First, because scattering microscopes are extremely sensitive to vibration, we incorporated an inexpensive but effective solution of suspending the instrument’s main components from a rigid metal framework using elastic bands, resulting in an average of 28.7 dBV reduction in vibration amplitude compared to an office desk. Second, an automated focusing module based on the principle of total internal reflection maintains the stability of image contrast over time and spatial position. In this work, we characterize the system's performance by measuring the contrast from gold nanoparticles with diameters in the 10–40 nm range and by observing various biological analytes, including HIV virus, SARS-CoV-2 virus, exosome, and ferritin protein.
Non-eluting, surface-bound enzymes disrupt surface attachment of bacteria by continuous biofilm polysaccharide degradation
2018, Biomaterials
Citation Excerpt :
A quantitative study of the Psl degradation due to enzyme activity at the surface was performed with in situ quartz crystal microbalance (QCM) experiments. QCM is a highly sensitive, quantitative measure of surface adsorption rates as changes in the resonant frequency (ΔF) of a piezoelectric quartz crystal are directly proportional to any adsorbed mass [54,55]. The surface adsorption rate of Psl was measured for covalently-bound PslGh sensors (SiO2 surface), compared to clean (untreated) sensors.
Bacterial colonization and biofilm formation on surfaces are typically mediated by the deposition of exopolysaccharides and conditioning protein layers. Pseudomonas aeruginosa is a nosocomial opportunistic pathogen that utilizes strain-specific exopolysaccharides such as Psl, Pel or alginate for both initial surface attachment and biofilm formation. To generate surfaces that resist P. aeruginosa colonization, we covalently bound a Psl-specific glycoside hydrolase (PslG_h) to several, chemically-distinct surfaces using amine functionalization (APTMS) and glutaraldehyde (GDA) linking. In situ quartz crystal microbalance (QCM) experiments and fluorescence microscopy demonstrated a complete lack of Psl adsorption on the PslG_h-bound surfaces. Covalently-bound PslG_h was also found to significantly reduce P. aeruginosa surface attachment and biofilm formation over extended growth periods (8 days). The PslG_h surfaces showed a ∼99.9% (∼3-log) reduction in surface associated bacteria compared to control (untreated) surfaces, or those treated with inactive enzyme. This work demonstrates a non-eluting ‘bioactive’ surface that specifically targets a mechanism of cell adhesion, and that surface-bound glycoside hydrolase can significantly reduce surface colonization of bacteria through local, continuous enzymatic degradation of exopolysaccharide (Psl). These results have significant implications for the surface design of medical devices to keep bacteria in a planktonic state, and therefore susceptible to antibiotics and antimicrobials.
Virus-Like Particles (VLPs) in Supramolecular Chemistry
2017, Comprehensive Supramolecular Chemistry II
Virus capsids, and other related protein cages, are remarkable examples of natural supramolecular assemblies. These systems self-assemble from a distinct number of subunits to form well-regulated and often highly symmetrical quaternary structures. They exhibit sophisticated functionalities such as protection of cargo molecules (e.g., their genome), targeting host cells and triggered release of their cargo. Scientists have drawn inspiration from protein cages and utilize them as platforms to explore this new area of materials science. The interior cavities of protein cages can be used as size-constrained reaction volumes to encapsulate cargo molecules. The exterior surfaces can be engineered to direct the interaction of the cage to the external environment such as for cell-targeting and programmed stimulation of immunological responses. Individual protein cages are also viewed as ideal building blocks for higher-order assembly of ordered arrays.
Evaluation of ferritin and transferrin binding to tau protein
2016, Journal of Inorganic Biochemistry
Tau protein is a neurodegeneration biomarker. Due to the high concentration of metal ions in the brain, the metallation of tau proteins and their catalytic role in reactive oxygen formation have been identified as a major biochemical pathway of neurodegeneration. High levels of iron ions have been detected in Alzheimer's disease brains. One of biological sources of iron ions are iron-rich proteins, such as transferrin or ferritin. However, the interactions between tau and these metallo-proteins have not been fully characterized. Here, the interactions between the longest form of full-length tau protein (tau441) with iron-rich proteins were detected using electrochemical impedance spectroscopy. Tau441 was immobilized on Au surface, via N-terminal (N-tau-Au film) or Cys-residues (Cys-tau-Au film), and the charge-transfer resistance, R_ct, was monitored prior and post ferritin or transferrin binding. Significant increase in R_ct was observed post transferrin binding above 50 μg mL^− 1, but not ferritin regardless of concentration with N-tau-Au film. Additionally, the electrochemical trend was linear with respect to transferrin concentration. Electrochemical data indicated low binding by ferritin to N-tau-Au or Cys-tau-Au films. The interaction of apotransferrin or apoferritin with tau films was also evaluated. Electrochemical data may be pointing to the differences in protein binding modes by transferrin compared to ferritin as well as to importance of metal ions in protein-protein interactions.
Potential dependence of ferritin monomer, dimer and oligomer adsorption on a polycrystalline Au surface
2013, Electrochimica Acta
An electrochemical quartz crystal microbalance (EQCM) was used to measure the effects of in situ potential changes on the adsorption and desorption of ferritin on polycrystalline Au. As-received horse-spleen ferritin, and purified ferritin monomer, dimer and higher oligomer fractions separated by gel chromatography were compared. Experiments were carried out at pH 5 where the ferritin is expected to have a net negative charge. Despite electrostatic repulsion, significant adsorption was observed on Au even at the most negative potentials studied, though it could be suppressed by using a low ionic strength electrolyte. This adsorption was attributed to hydrophobic interactions caused by partial denaturation of the protein, and it was greater for as-received ferritin containing higher oligomers than for monomeric ferritin. The reversibility of the adsorption was also lower when higher oligomers were present. Potential dependent adsorption/desorption could be useful as a diagnostic method for protein solutions.
A GFET Nitrile Sensor Using a Graphene-Binding Fusion Protein
2022, Advanced Functional Materials

View all citing articles on Scopus

¹: To whom correspondence should be addressed.

View full text

Regular ArticleCharacterization of Ferritin Adsorption onto Gold

Abstract

Regular Article
Characterization of Ferritin Adsorption onto Gold