Abstract
A qualitative investigation of CaO single crystal and hot-pressed polycrystal behaviour in high K2O melts is presented. Under carefully controlled anhydrous conditions, no intermediate crystalline compound was detected at temperatures up to 800° C. Calcium oxide dissolves preferentially along grain boundaries and/or along 〈1 0 0〉 directions on {1 0 0} faces. The melt viscosity gradually increases with its CaO content. The single crystal corrosion rate, therefore, decreases with time and a protective glassy layer may eventually develop on its surface.
Similar content being viewed by others
References
M. Cassou, Gaz de France, upublished results.
R. W. Rice, J. Amer. Ceram. Soc. 52 (1969) 420; Proc. Brit. Ceram. Soc. 12 (1968) 99.
M. W. Benecke, N. E. Olson and J. A. Pask, J. Amer. Ceram. Soc. 50 (1967) 365.
E. Rengade, Ann. Chim. Phys. 11 (1907) 425.
J. C. Bardin, M. Avallet. and M. Cassou, Compt. Rend. Acad. Sci. Paris C278 (1974) 709.
M. G. Barker and A. P. Dawson, J. Less Common Metals 45 (1976) 323.
Y. Oishi, A. R. Cooper and W. D. Kingery, J. Amer. Ceram. Soc. 48 (1965) 88.
S. Chatterji and J. W. Jeffery, Nature 209 (1966) 1233.
F. Natola and Ph. Touzain, Canad. J. Chem. 48 (1970) 1955.
Author information
Authors and Affiliations
Additional information
Supplied by Cristal-Tec, Grenoble, France.
Prepared by calcination of CaCO3, Prolabo, Paris, France.
Rights and permissions
About this article
Cite this article
Cassou, M., Mocellin, A. Observation of CaO corrosion by K2O melts. J Mater Sci 12, 909–914 (1977). https://doi.org/10.1007/BF00540972
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00540972