Zinkblende- und Wurtzitüberstrukturen bei ternären Chalkogeniden der Zusammensetzung 1₂46₃

Abstract

Earlier literature data on the structure of Cu₂GeSe₃ and the low temperature modification of Cu₂GeS₃ could not be corroborated. Both compounds crystallize in an orthorhombic superstructure of zincblende with 2 formula units per cell (space group Imm2). The point positions for Cu₂GeSe₃ were obtained from single crystal intensity data collected on an automatic diffractometer. An orthorhombic superstructure of wurtzite was found with the high temperature modification of Cu₂SiS₃ (space group Cmc2₁ with 4 formula units per cell). The two new structures belong to the normal tetrahedral structures. According to the tetrahedral structure rules these structures might occur not only with 1₂46₃ but with 14₂5₃ compounds as well.

Zusammenfassung

Frühere Literaturangaben über die Struktur von Cu₂GeSe₃ und der Tieftemperaturmodifikation von Cu₂GeS₃ wurden als unrichtig befunden. Beide Verbindungen kristallisieren in einer orthorhombischen Zinkblendeüberstruktur mit 2 Formeleinheiten pro Zelle (Raumgruppe Imm2). Die Punktpositionen für Cu₂GeSe₃ wurden erhalten unter Verwendung von Einkristallintensitäten, die auf einem automatischen Diffraktometer gemessen wurden. Eine orthorhombische Wurtzitüberstruktur wurde bei der Hochtemperaturmodifikation von Cu₂SiS₃ aufgefunden (Raumgruppe Cmc2₁ mit 4 Formeleinheiten pro Zelle). Die beiden neuen Strukturen gehören zu den normal tetraedrischen Strukturen und könnten entsprechend den Tetraederstrukturregeln nicht nur bei 1₂46₃₋, sondern auch bei 14₂5₃₋ Verbindungen auftreten.