Abstract
The deformation, fracture and toughening mechanisms of nacre from a kind of fresh-water bivalve mollusc (Cristaria plicata) were studied by SEM, TEM and microindentation tests. Experimental results revealed a strong anisotropy of the damage behaviour reflecting the microstructural character of nacre. The fractured surface parallel to the cross-sectional surface of nacre was much more tortuous than that parallel to the platelet surface. The crack line on the cross-sectional surface was step-like, while that on the platelet surface was polygonal. Sliding of aragonite layer combined with the plastic deformation of organic matrix is the main plastic deformation mechanism of nacre. Three main toughening mechanisms have been found acting in concert: crack deflection, fibre pull-out and organic matrix bridging.
Similar content being viewed by others
References
A. H. Heuer, D. J. Fink, V. J. Laraia, J. L. Arias, P. D. Calvert, K. Kendall, G. L. Messing, J. Blackwell, P. C. Rieke, D. H. Thompson, A. P. Wheeler, A. Veis andA. I. Caplan,Science 255 (1992) 1098.
J. F. V. Vincent, “Structural Biomaterial” (MacMillan Press, London, 1982) p. 171.
P. Calvert,MRS Bull. 10 (1992) 37.
S. Mann, in “Biomineralization: Chemical and Biological Perspectives”, edited by S. Mann, J. Webb and R. J. P. Williams (VCH Verlagsgesellschaft, Weiheim, 1989) p. 35.
K. Simkiss andK. M. Wilbur, in “Biomineralization: Cell Biology and Mineral Deposition” (Academic Press, New York, 1989) p. 231.
M. A. Crenshaw,Mater. Res. Soc. Symp. Proc. 218 (1989) 185.
J. D. Currey, in “The Mechanical Properties of Biological Materials”, edited by J. F. V. Vincent and J. D. Currey (Cambridge University Press, London, 1980) p. 75.
L. J. Huang andH. D. Li,Mater. Res. Soc. Sym. Proc. 174 (1990) 101.
A. P. Jackson,J. Mater. Sci. Lett. 5 (1986) 975.
J. D. Currey,Proc. R. Soc. Lond. B196 (1977) 443.
A. P. Jackson, J. F. V. Vincent andR. M. Turner,ibid. B234 (1988) 415.
P. Calvert,Mater. Res. Soc. Symp. Proc. 180 (1990) 619.
M. Yasrebi, G. H. Kim, K. E. Gunnison, D. J. Milius, M. Sarikaya andI. A. Aksay,ibid. 180 (1990) 625.
M. Sarikaya, K. E. Gunnison, M. Yasrebi andI. A. Aksay,ibid. 174 (1990) 109.
V. J. Laraia andA. H. Heuer,ibid. 174 (1990) 125.
R. Z. Wang, H. B. Wen, F. Z. Cui andH. D. Li, to be published.
F. Z. Cui, H. B. Wen, H. B. Zhang, H. D. Li andD. C. liu,Mater. Sci. Eng. C (1994) in press.
K. T. Faber andA. G. Evans,Acta Metall. 31 (1983) 565.
P. F. Becher, T. N. Tiegs, J. C. Ogle andW. H. Warwick, in “Fracture Mechanisms of Ceramics”, Vol. 7, edited by R. C. Bradt (Plenum Press, New York, 1986) p. 61.
J. -S. Ha andK. K. Chawla,J. Mater. Sci. Lett. 12 (1993) 84.
L. M. Sheppard,Ceram. Bull. 71 (1992) 617.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Wang, R.Z., Wen, H.B., Cui, F.Z. et al. Observations of damage morphologies in nacre during deformation and fracture. J Mater Sci 30, 2299–2304 (1995). https://doi.org/10.1007/BF01184577
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01184577