Abstract
The present investigation was carried out to assess the localized corrosion resistance of materials proposed for the construction of the safety-grade sodium-to-air decay-heat removal system for fast breeder reactors. The materials, such as Alloy 800,9Cr-lMo steel, and type 316LN stainless steel, in different microstructural conditions were assessed for pitting and stress-corrosion cracking resistances in a chloride medium. The results indicated that 9Cr-lMo steel in the normalized and tempered condition can be considered for the above application from the standpoint of corrosion resistance.
Similar content being viewed by others
References
A.K. Agrawal and J.G. Guppy, Ed.,Decay Heat Removal and Natural Convection in Fast Breeder Reactors, Hemisphere Publishing, 1981
S. Athmalingam, S.C. Chetal, and S.B. Bhoje, “Design Specifications for Safety Grade Decay Heat Removal Circuit,” Report PFBR/32900/SP/1004/R-A, 1988
A.S. Khanna, M.A.R. Iyengar, and J.B. Gnanamoorthy,Ind. J. Environ. Protect., Vol 6, 1986, p 47–51
J.B. Gnanamoorthy,Mater. Perform., Vol 29, 1990, p 63–65
U. Kamachi Mudali, R.K. Dayal, T.P.S. Gill, and J.B. Gnanamoorthy,Werk. Rorros., Vol 37, 1986, p 637–643
U. Kamachi Mudali, A.K. Bhaduri, and J.B. Gnanamoorthy,Mater. Sci. Technol., Vol 6, 1990, p 475–481
“Recommended Practices for Making and Using U-bend Stress Corrosion Test Specimens,” ASTM G 30-90,Annual Book of ASTM Standards, Vol 03.02, ASTM, 1990, p 100-105
G.J. Bignold, inFerritic Steels for Fast Reactor Steam Generators, BNES, London, 1978, p 342–345
J. Congleton and T.P. Wilks,Fatigue Fract. Eng. Mater. Struct., Vol 11, 1988, p 139–148
S. Kawai and K. Kasai,Fatigue Fract. Eng. Mater. Struct., Vol 8, 1985, p 115–127
H.S. Khatak, V. Seetharaman, and J.B. Gnanamoorthy,Pract. Metallography, Vol 20, 1983, p 570
J.W. Oldfield and B. Todd,Mater. Perform., Vol 29, 1990, p 57–58
P. Muraleedharan, H.S. Khatak, and J.B. Gnanamoorthy, “Failure Analysis of a Stainless Steel Sheathed Heating Coil,” Internal Report, Reactor Research Centre, Kalpakkam, 1984
J.J. Eckenrod and C.W. Kovach, inProperties of Austenitic Stainless Steels and Their Weld Metals (Influence of Slight Chemistry Variations), ASTM STP 679, C.R. Brinkman and H.W. Garvin, Ed., ASTM, 1979, p 17-41
U. Kamachi Mudali, “Studies on Pitting, Intergranular Corrosion and Passive Film in Nitrogen-Bearing Austenitic Stainless Steels,” Ph.D. thesis, University of Madras, 1993
D. McIntyre, inCorrosion of Metals Under Insulation, W.I. Pollack and J.B. Barnhart, Ed., ASTM STP 880, ASTM, 1985, p 27
M.O. Speidel, inCorrosion in Power Generating Equipments, M.O. Speidel and A. Atrens, Ed., Plenum Press, 1984, p 85
W.P. Gillbreath and M.J. Adamson, inStress Corrosion—New Approaches, ASTM STP 610, ASTM, 1976, p 176
B.F. Brown, inThe Theory of Stress Corrosion Cracking in Alloys, J.C. Scully, Ed., NATO Scientific Affairs Division, Brussels, 1971, p 186
A.Gallaccio and M.A. Pelensky, inStress Corrosion Testing, ASTM STP 425, ASTM, 1967, p 99
M.O. Speidel, inCorrosion Problems in Energy Conservations and Generations, C.S. Tedmon, Ed., The Electrochemical Society, 1974, p 359
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kamachi Mudali, U., Khatak, H.S., Dayal, R.K. et al. Localized corrosion studies on materials proposed for a safety-grade sodium-to- air decay-heat removal system for fast breeder reactors. JMEP 2, 135–140 (1993). https://doi.org/10.1007/BF02649686
Issue Date:
DOI: https://doi.org/10.1007/BF02649686