Abstract
Pure Mo was incorporated in TiAl matrixvia two different routes: (1) hot pressing of alternately sandwiched Ti-Al sheets and Mo foils; and (2) coextrusion and heat treatment of Ti-Al green compact and Mo rod. The reaction zone between TiAl and Mo is found to contain two intermetallic phases: β-(Mo,Ti)Al andp-(Mo,Ti)3Al. The β-p boundary is incoherent, whereas the TiAl-β andp-Mo boundaries are semicoherent. The reaction zone grows with increasing heat-treatment time in a parabolic form. The incorporated Mo exhibits lower hardness than the TiAl matrix, implying that ductilizing and toughening of TiAl by introducing Mo as a ductile reinforcement are possible.
Similar content being viewed by others
References
M. Dahms:Mater. Sci. Eng., 1989, vol. A110, pp. L5-L8.
G.-X. Wang and M. Dahms:Powder Metall. Int., 1992, vol. 24, pp. 219–25.
G.-X. Wang and M. Dahms: JOM, 1993, May, pp. 52–56.
G.-X. Wang and M. Dahms:Metall. Trans. A, 1993, vol. 24A, pp. 1517–26.
B. Dogan, G.-X. Wang, and M. Dahms:Scripta Metall., 1993, vol. 29, pp. 943–48.
G.-X. Wang, B. Dogan, F.-Y. Hsu, H.-J. Klaar, and M. Dahms: Metall. Mater. Trans. A, 1996, vol. 28A, in press.
P.R. Subramanian, M.G. Mendiratta, D.B. Miracle, and D.M. Dimiduk:Intermetallic Matrix Composites,
M.G. Mendiratta, J.J. Lewandowski, and D.M. Dimiduk:Metall. Trans. A, 1991, vol. 22A, pp. 1573–83.
H.E. Deve, A.E. Evans, G.R. Odette, R. Mehrabian, M.L. Emiliani, and R.J. Hecht:Acta Metall., 1990, vol. 38, pp. 1491–1502.
E. Angeltinger, C. Elliot, N. Glumac, G. Lucas, R. Odette, and W. Sheckherd:Proc. High Temperature Intermetallics Symp., Los Angeles, CA, 1989, p. 658.
H.C. Cao, B.J. Dalgleish, H.E. Deve, C. Elliott, A.G. Evans, R. Mehrabian, and G.R. Odette:Acta Metall., 1989, vol. 37, pp. 2969–77.
K..T. Venkateswara Rao, G.R. Odette, and R.O. Ritchie:Acta Metall., 1994, vol. 42, pp. 893–911.
K..T. Venkateswara Rao and R.O. Ritchie: Paper presented at the1994 TMS Fall Meeting, Rosemont, IL, Oct. 2–6, 1994.
F. Pirwitz, M. Dahms, G.-X. Wang, S.W. Hülsmann, and D. Nerger: inHot Isostatic Pressing 93, Proc. Int. Conf., Antwerp, Apr. 21–23, 1993, L. Delaey and H. Tas, eds., 1993, pp. 91–98.
S.-C. Huang and E.L. Hall:Metall. Trans. A, 1992, vol. 22A, pp. 427–39.
P. Budberg and R. Schmidt-Fetzer: inTernary Alloys: A Comprehensive Compendium of Evaluated Constitutional Data and Phase Diagrams, G. Petzow and G. Effenberg, eds., VCH Verlagsgesellschaft, Weinheim, Germany, 1993, vol. 7, pp. 229–38.
M.-X. Zhang, K.-C. Hsieh, and Y.A. Chang:Mater. Res. Soc. Proc., 1992, vol. 273, pp. 103–13.
M.-X. Zhang, K.-C. Hsieh, Y.A. Chang, J.P. Neumann, and A.D. Romig, Jr.: Paper presented at the1994 TMS Fall Meeting, Rosemont, IL, Oct. 2–6, 1994.
M.-X. Zhang, K.-C. Hsieh, Y.A. Chang, J.P. Neumann, and A.D. Romig, Jr.:Intermetallics, 1995, vol. 3, pp. 47–56.
J.B. Davis, H.C. Cao, G. Bao, and A.G. Evans:Acta Metall., 1991, vol. 39, pp. 1019–24.
W.B. Pearson:A Handbook of Lattice Spacings and Structures of Metals and Alloys, Pergamon Press, Elmsford, NY, 1967.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hsu, F.Y., Wang, G.X., Klaar, H.J. et al. Investigation of the reaction zone between TiAl and Mo. Metall Mater Trans A 27, 2285–2292 (1996). https://doi.org/10.1007/BF02651882
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02651882