Abstract
Plane-strain compression tests were made on age-hardened Al-4 pct Cu single crystals of various orientations. The resulting stress-strain curves showed much less anisotropy than would be expected from single-phase crystals under the same conditions of testing. The data are explained by a model in which compatibility is maintained between the matrix and the precipitate platelets, the platelets both deforming and rotating. This model predicts that normally weak orientations are strengthened more by precipitation than normally hard orientations.
Similar content being viewed by others
References
W. A. Backofen, W. F. Hosford, and J. J. Burke:ASM Trans. Quart., 1962, vol. 55, p. 264.
W. F. Hosford and W. A. Backofen: inFundamentals of Deformation Processing, Syracuse Univ. Press, p. 259, 1964.
W. F. Hosford:Met. Eng. Quart., 1966, vol. 6, p. 13.
G. I. Taylor:J. Inst. Metals, 1938, vol. 62, p. 307.
J. F. W. Bishop and R. Hill:Phil. Mag., 1951, vol. 42, pp. 414, 1307.
W. F. Hosford:Acta Met., 1966, vol. 14, p. 1085.
G. Y. Chin, E. A. Nesbitt and A. J. Williams:Acta Met, 1966, vol. 14, p. 467.
B. C. Wonsiewicz and G. Y. Chin:Met. Trans., 1970, vol. 1, p. 2715.
E. W. Kelley and W. F. Hosford,Trans TMS-AIME, 1968, vol. 242, p. 5.
C. S. Barrett and B. Massalski:Structure of Metals, McGraw-Hill, p. 500, New York, 1966.
F. A. McClintock and A. S. Argon:Mechanical Behavior of Materials, p. 279, Addison-Wesley, Reading, Mass., 1966.
J. Althoff, K. Drefahl, and P. Wincierz: Metallgesellschaft, Frankfurt, West Germany, 1970, private communication.
M. Toralba and G. Wasserman:Z. Metallic., 1968, vol. 59, p. 467.
C. J. Beevers and R. W. K. Honeycombe: inFracture, p. 279, Technology Press of M.I.T., 1959.
Author information
Authors and Affiliations
Additional information
Formerly Graduate Student, Department Materials and Metallurgical Engineering, the University of Michigan
Rights and permissions
About this article
Cite this article
Hosford, W.F., Zeisloft, R.H. The anisotropy of age-hardened Al-4 pct Cu single crystals during plane-strain compression. Metall Trans 3, 113–121 (1972). https://doi.org/10.1007/BF02680590
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF02680590