Abstract
The objective of this study was to investigate the effect of accelerated aging on compression strength, modulus of rupture, modulus of elasticity, color change, volumetric swelling, and volumetric shrinkage of bamboo specimens with and without node sections. In the study, these properties were compared with those of Scots pine and beech wood specimens. Depending on bamboo sections, the aging procedure reduced modulus of rupture, modulus of elasticity, and compression strength. Bamboo specimens showed relatively high strength properties compared to wood specimens due to having high density. Strength properties increased from bottom to top of bamboo culms. The presence of nodes in the specimens reduced compression strength and modulus of rupture but affected modulus of elasticity slightly. Remarkable color changes in specimens were observed after aging. Volumetric swelling and shrinkage of bamboo specimens exposed to aging decreased probably due to heat effect of aging procedure.
Similar content being viewed by others
References
Ahmad M (2000) Analysis of Calcutta bamboo for structural composite materials. Dissertation, Faculty of Virginia Polytechnic Institute and State University
Ahmad A, Kamke FA (2005) Analysis of Calcutta bamboo for structural composite materials: Physical and mechanical properties. Wood Sci Technol 39:448–459
American Society for Testing and Materials (1989) Standard test method for evaluating the properties of wood-base fiber and particle panel materials. ASTM Stand D 1037–89, West Conshohocken, PA
Bhargava RL (1987) Bamboo. In: Hamilton F, Leopold B (eds) Pulp and paper manufacture, vol 3 Secondary fibers and non-wood pulping, 3rd ed. The Joint Textbook Committee of the Paper Industry (TAPPI–CPPA), Atlanta
Boonstra MJ (2008) A two-stage thermal modification of wood. Dissertation, Ghent University
Genc M (2009) Basic principles of Sylviculture. 2nd Chapter (in Turkish) http://ormanweb.sdu.edu.tr/dersler/mgenc/ste/ste2.pdf. Assessed 27 February 2011
Hamdam H, Anwar UMK, Zaidon A, Tamizi MM (2009) Mechanical properties and failure behavior of Gigantochloa scortechinii. J Trop Forest Sci 21:336–344
Kajita H, Mukudai J, Yano H (1991) Durability evaluation of particleboards by accelerated aging tests. Wood Sci Technol 25:239–249
Kartal SN, Green F III (2003) Decay and termite resistance of medium density fiberboard (MDF) made from different wood species. Int Biodeter Biodeg 5:29–35
Kim JS, Lee KH, Cha MY, Kim YS (2008) Anatomical, physical and chemical changes of Bamboo (Phyllostachys puberscence) during weathering processes. The International Research Group on Wood Protection, Stockholm. IRG/WP 08-10650
Kocaefe D, Poncsak S, Boluk Y (2008) Effect of thermal treatment on the chemical composition and mechanical properties of birch and aspen. BioResources 3:517–537
Kojima Y, Suzuki S (2011) Evaluation of wood-based panel durability using bending properties after accelerated aging treatments. J Wood Sci 57:126–133
Lee AWC, Xuesong B, Peralta PN (1994) Selected physical and mechanical properties of giant timber bamboo grown in South Carolina. Forest Prod J 44:40–46
Leithoff H, Peek RD (2001) Heat treatment of bamboo. The International Research Group on Wood Protection, Stockholm. IRG/WP 01-40216
Li X (2004) Physical, chemical, and mechanical properties of bamboo and its utilization potential for fiberboard manufacturing. Dissertation, Louisiana State University
Liese W (1992) The structure of bamboo in relation to its properties and utilization. In: Zhu S, Li W, Zhang X, Wang Z (eds) Bamboo and its use. Proceedings of the International Symposium on Industrial Use of Bamboo, 7–11 December. Beijing, China
Liese W (1998) The anatomy of bamboo culms. International Network for Bamboo and Rattan, Beijing
Lima HC, Willrich FL, Barbosa NP, Rosa MA, Cunha BS (2008) Durability analysis of bamboo as concrete reinforcement. Mater Struct 41:981–989
Lin CJ, Tsai MJ, Wang SY (2006) Nondestructive evaluation techniques for assessing dynamic modulus of elasticity of moso bamboo (Phyllosachys edulis) lamina. J Wood Sci 5:342–347
Lo TY, Cui HZ, Leung HC (2004) The effect of fiber density on strength capacity of bamboo. Mater Lett 58:2595–2598
Naik NK (2010) Mechanical and physico-chemical properties of bamboos. http://www.bambootech.org/files/mechanicaltesting%20report.pdf. Accessed 9 June 2010
Ohmae Y, Nakano T (2009) Water adsorption properties of bamboo in the longitudinal direction. Wood Sci Technol 43:415–422
Ohmae Y, Saito Y, Inoue M, Nakano T (2009a) Mechanism of water adsorption capacity change of bamboo by heating. Eur J Wood Prod 67:13–18
Ohmae Y, Saito Y, Inoue M, Nakano T (2009b) Water adsorption process of bamboo heated at low temperature. J Wood Sci 55:13–17
Okkonen EA, River BH (1996) Outdoor aging of wood-based panels and correlation with laboratory aging: Part 2. Forest Prod J 46:68–74
Poblete H, Cuevas H, Diaz-Vaz JE (2009) Property characterization of Chusquea culeou, a bamboo growing in Chile. Maderas Cienc tecnol 11:129–138
Qin L, Yu WJ (2009) Research on surface color, properties of thermo-treated reconstituted bamboo lumber after artificial weathering test. Advanced Materials Research 79–82:1395–1398
Sahin HI (2006) The determination of kraft pulping conditions of Bamboo (Phyllostachys bambusoides). Dissertation, Karadeniz Technical University
Shao S, Wen G, Jin Z (2008) Changes in chemical characteristics of bamboo (Phyllostachys pubescens) components during steam explosion. Wood Sci Technol 42:439–451
Shao ZP, Zhou L, Liu YM, Wu ZM, Arnaud C (2010) Differences in structure and strength between internode and node sections of moso bamboo. J Trop Forest Sci 22:133–138
Tjeerdsma BF, Boonstra M, Militz H (1998) Thermal modification of non-durable wood species. 2. Improved wood properties of thermally treated wood. The International Research Group on Wood Preservation IRG/WP 98-40124
Tran VH (2010) Growth and quality of indigenous bamboo species in the mountainous regions of Northern Vietnam. Dissertation, Georg-August-Universität
Turkish Standard Institution (1976a) Wood-determination of moisture content for physical and mechanical tests. TS 2471, Ankara
Turkish Standard Institution (1976b) Wood-determination of density for physical and mechanical tests. TS 2472, Ankara
Turkish Standard Institution (1977) Wood-determination of ultimate stress in compression parallel to grain. TS 2595, Ankara
Turkish Standard Institution (1984a) Wood-determination of volumetric shrinkage. TS 4085, Ankara
Turkish Standard Institution (1984b) Wood-determination of volumetric swelling. TS 4086, Ankara
Wahab R, Mohamad A, Samsi HW, Yunus AAM, Moktar J (2006) Physical characteristics, anatomy and properties of managed Gigantochloa scortechinii natural bamboo stands. J Plant Sci 1:144–153
Yildiz S (2002) Physical, mechanical, technologic and chemical properties of Fagus orientalis and Picea orientalis wood treated by heating. Dissertation, Karadeniz Technical University
Yildiz S, Yildiz UC, Tomak ED (2011) The effects of natural weathering on the properties of heat treated alder wood. BioResources 6:2504–2521
Yu H, Fei B, Ren H, Jiang Z, Liu X (2008a) Variation in tensile properties and relationship between tensile properties and air-dried density for moso bamboo. Front For China 3:127–130
Yu HQ, Jiang ZH, Hse CY, Shupe TF (2008b) Selected physical and mechanical properties of moso bamboo (Phyllostachys pubescens). J Trop Forest Sci 20:258–263
Acknowledgments
The authors would like to thank Prof. Dr. Mustafa Var for providing the bamboos in the Department of Landscape Architecture, KTU and Asst. Prof. Dr. Derya Ustaomer for color measurements in the Department of Forest Industry Engineering, KTU, Turkey.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Tomak, E.D., Topaloglu, E., Ay, N. et al. Effect of accelerated aging on some physical and mechanical properties of bamboo. Wood Sci Technol 46, 905–918 (2012). https://doi.org/10.1007/s00226-011-0454-7
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00226-011-0454-7