Summary
Ortho substituted poly(4,4'-diphenylene pyromellitimide)s were prepared from pyromellitic dianhydride and 3,3′-dihydroxybenzidine or 3,3′-dimethoxybenzidine. Thermal cyclodehydration of the corresponding poly(amic acid)s, PAA, led to the formation of ortho-hydroxy- or o-methoxy-polyimides, while catalytic imidization in the presence of aliphatic anhydrides was accompanied by acylation of the OH groups resulting in the formation of lateral acetoxy substituents. The direction of the latter reaction was controlled by the acidity of dehydration agents and the use of a catalyst. Imidization in the presence of acetic anhydride and pyridine led to poly[(3,3'-diacetoxy-4,4'-diphenylene)pyromellitimide] and the use of trifluoroacetic anhydride resulted in the formation of the corresponding polyisoimide with ortho-trifluoroacetoxy groups. This polyisoimide was completely soluble in amide solvents above 60°C. The polymers were studied by FTIR spectroscopy, TGA, and WAXS. It was found that ortho substituents such as OH and methoxy groups could react with the imide cycle above 350°C causing its rearrangement to benzoxazole. The formation of notable amounts of benzoxazole was also observed for o-acetoxy polyimides.
Similar content being viewed by others
Author information
Authors and Affiliations
Additional information
Received: 20 November 2001/Revised version: 19 March 2002/ Accepted: 19 March 2002
Rights and permissions
About this article
Cite this article
Guzmán-Lucero, D., Likhatchev, D. Imide-to-benzoxazole rearrangement in ortho substituted poly(4-4'-diphenylene pyromellitimide)s. Polymer Bulletin 48, 261–269 (2002). https://doi.org/10.1007/s00289-002-0038-7
Issue Date:
DOI: https://doi.org/10.1007/s00289-002-0038-7