Abstract
Strontium-modified lead titanate (PST) thin films with composition Pb1-xSrxTiO3 (0.10<x≤0.60) were grown on Pt/Ti/SiO2/Si substrates using a soft chemical process. The crystallization of the PST thin films was achieved by heat treatment at 600 °C. The structural and microstructural modifications in the films were studied using X-ray diffraction (XRD) and atomic force microscopy, respectively. The XRD study shows that the lattice parameters of polycrystalline PST thin films calculated from X-ray data indicate a decrease in lattice tetragonality with the increase in strontium content in these films. This indicates a gradual change from tetragonal to cubic structure. By atomic force microscopy analysis, the average grain size of the thin films was systematically reduced with the increase in Sr content. The dielectric property of the thin films was found to be strongly dependent on the Sr concentration. With 60 at. % Sr content, a ferroelectric to paraelectric phase transition was observed at room temperature.
Similar content being viewed by others
References
A. Roelofs, T. Schneller, K. Szot, R. Waser: Nanotechnology 14, 250 (2003)
A. Sheikholeslami, P.G. Gulak: Proc. IEEE 86, 667 (2000)
M. Klee, U. Mackens, R. Kiewitt, G. Greuel, C. Metzmacher: Philips J. Res. 51, 363 (1998)
S. Liu, M. Liu, Y. Zeng, C. Li, S. Chen, Y. Huang, D. Xia: Mater. Sci. Eng. C 22, 73 (2002)
F.M. Pontes, D.S.L. Pontes, E.R. Leite, E. Longo, E.M.S. Santos, S. Mergulh ao, A. Chiquito, P.S. Pizani, F. Lanciotti, Jr., T.M. Boschi, J.A. Varela: J. Appl. Phys. 91, 6650 (2002)
H. Yang, K. Tao, B. Chen, X. Qiu, B. Xu, B. Zhao: Appl. Phys. Lett. 81, 4817 (2002)
N.V. Giridharanm, R. Jayavel: Mater. Lett. 52, 57 (2002)
X.G. Tang, A.L. Ding, H.Q. Li, D. Mo: J. Non-Cryst. Solids 297, 67 (2002)
P. Venkateswarlu, S.S.N. Bharadwaja, S.B. Krupanidhi: Thin Solid Films 389, 84 (2001)
V. Bouquet, M.I.B. Bernardi, S.M. Zanetti, E.R. Leite, E. Longo, J.A. Varela, V.M. Guilloux, A. Perrin: J. Mater. Res. 15, 2446 (2000)
E.R. Camargo, J. Frantti, M. Kakihana: J. Mater. Chem. 11, 1875 (2001); C. Huber, M.T. Delapierre, C. Elissalde, F. Weill, M. Maglione: J. Mater. Chem. 13, 650 (2003)
P. Duran, F. Capel, D. Gutierrez, J. Tarjat, M.A. Bañares, C. Moure: J. Mater. Chem. 11, 1828 (2001)
E.R. Leite, F.M. Pontes, E.J.H. Lee, R. Aguiar, E. Longo, D.S.L. Pontes, M.S.J. Nunes, H.R. Macedo, P.S. Pizani, F. Lanciotti, Jr., T.M. Boschi, J.A. Varela, C.A. Paskocimas: Appl. Phys. A 74, 529 (2002)
F.M. Pontes, S.H. Leal, P.S. Pizani, M.R.M.C. Santos, E.R. Leite, E. Longo, F. Lanciotti, Jr., T.M. Boschi, J.A. Varela: J. Mater. Res. 18, 659 (2003)
K.-T. Kim, C.-I. Kim: Thin Solid Films 420–421, 544 (2002)
M. Jain, S.B. Majumder, R. Guo, A.S. Bhalla, R.S. Katiyar: Mater. Lett. 56, 692 (2002)
D.H. Kang, J.H. Kim, J.H. Park, K.H. Yoon: Mater. Res. Bull. 36, 265 (2001)
S.J. Kang, D.H. Chang, Y.S. Yoon: Thin Solid Films 373, 53 (2000)
H.-M. Chen, J.Y.-M. Lee: Appl. Phys. Lett. 73, 309 (1998)
F.M. Pontes, E.R. Leite, E. Longo, J.A. Varela, E.B. Araújo, J.A. Eiras: Appl. Phys. Lett. 76, 2433 (2000)
S.G. Lu, X.H. Zhu, C.L. Mak, K.H. Wong, H.L.W. Chan, C.L. Choy: Appl. Phys. Lett. 82, 2877 (2003)
H.-Y. Tian, W.-G. Luo, X.-H. Pu, X.-Y. He, P.-S. Qiu, A.-L. Ding: Mater. Chem. Phys. 69, 166 (2001)
Author information
Authors and Affiliations
Corresponding author
Additional information
PACS
61.10.Nz; 68.37.Ps; 77.55.+f; 77.84.-s; 81.15.-z
Rights and permissions
About this article
Cite this article
Pontes, F., Leal, S., Santos, M. et al. Structural and ferroelectric properties of Pb1-xSrxTiO3 thin films. Appl. Phys. A 80, 875–880 (2005). https://doi.org/10.1007/s00339-003-2335-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-003-2335-x