Abstract
A series of CoFeNi2V0.5Nbx (x = 0–1) high-entropy alloys (HEAs) were synthesized to investigate the alloying effect of the Nb element on the microstructures and properties. It was found that the microstructures change from initial single-phase FCC solid solutions (x = 0), to a hypoeutectic microstructure (0 < x < 0.75), then to a fully eutectic microstructure (x = 0.75), and finally to a hypereutectic microstructure (0.75 < x < 1). The eutectic microstructure consists of the FCC solid solution phase and the Fe2Nb-type Laves phase. Nb0 (x = 0) and Nb02 (x = 0.2) alloys exhibit excellent ductility, the compressive plastic elongation of which can reach up to 80 % without fracture. With increasing Nb content, increased brittle Laves phase leads to the decrease of the plastic strain and the increase of the yield strength, and the Vickers hardness shows an approximately linear increase from HV 133.4 to HV 687.7. Besides, the CoFeNi2V0.5Nbx HEAs exhibit excellent soft magnetic behavior, in which the Nb0 alloy shows the maximum saturation magnetization (M s) of 70.33 emu/g, and minimum coercivity (H c) of 1.62 Oe.
Similar content being viewed by others
References
B. Cantor, I.T.H. Chang, P. Knight, A.J.B. Vincent, Mater. Sci. Eng. A 375–377, 213–218 (2004)
J.W. Yeh, S.K. Chen, S.J. Lin, J.Y. Gan, T.S. Chin, T.T. Shun, C.H. Tsau, S.Y. Chang, Adv. Eng. Mater. 6, 299–303 (2004)
Y. Zhang, T.T. Zuo, Z. Tang, M.C. Gao, K.A. Dahmen, P.K. Liaw, Z.P. Lu, Prog. Mater Sci. 61, 1–93 (2014)
B. Gludovatz, A. Hohenwarter, D. Catoor, E.H. Chang, E.P. George, R.O. Ritchie, Science 345, 1153–1158 (2014)
P. Koželj, S. Vrtnik, A. Jelen, S. Jazbec, Z. Jagličić, S. Maiti, M. Feuerbacher, W. Steurer, J. Dolinšek, Phys. Rev. Lett. 113, 107001-1–107001-5 (2014)
Y.P. Lu, Y. Dong, S. Guo, L. Jiang, H.J. Kang, T.M. Wang, B. Wen, Z.J. Wang, J.C. Jie, Z.Q. Cao, H. Ruan, T.J. Li, Sci. Rep. 4, 6200-1–6200-5 (2014)
M. Tsai, J. Yeh, Mater. Res. Lett. 2, 107–123 (2014)
C. Juan, C. Hsu, C. Tsai, W. Wang, T. Sheu, J. Yeh, S. Chen, Intermetallics 32, 401–407 (2013)
C. Hsu, C. Juan, W. Wang, T. Sheu, J.W. Yeh, S. Chen, Mater. Sci. Eng. A 528, 3581–3588 (2011)
H. Zhang, Y. He, Y. Pan, S. Guo, J. Alloy Compd. 600, 210–214 (2014)
W. Wang, W. Wang, J.W. Yeh, J. Alloy Compd. 589, 143–152 (2014)
O.N. Senkov, S.V. Senkova, D.M. Dimiduk, C. Woodward, D.B. Miracle, J. Mater. Sci. 47, 6522–6534 (2012)
O.N. Senkov, J.M. Scott, S.V. Senkova, F. Meisenkothen, D.B. Miracle, C.F. Woodward, J. Mater. Sci. 47, 4062–4074 (2012)
O.N. Senkov, J.M. Scott, S.V. Senkova, D.B. Miracle, C.F. Woodward, J. Alloy Compd. 509, 6043–6048 (2011)
O.N. Senkov, G.B. Wilks, J.M. Scott, D.B. Miracle, Intermetallics 19, 698–706 (2011)
O.N. Senkov, S.V. Senkova, C. Woodward, D.B. Miracle, Acta Mater. 61, 1545–1557 (2013)
O.N. Senkov, C.F. Woodward, Mater. Sci. Eng. A 529, 311–320 (2011)
O.N. Senkov, S.V. Senkova, D.B. Miracle, C. Woodward, Mater. Sci. Eng. A 565, 51–62 (2013)
J.Y. He, C. Zhu, D.Q. Zhou, W.H. Liu, T.G. Nieh, Z.P. Lu, Intermetallics 55, 9–14 (2014)
A.J. Zaddach, C. Niu, C.C. Koch, D.L. Irving, JOM 65, 1780–1789 (2013)
S. Guo, C. Ng, J. Lu, C.T. Liu, J. Appl. Phys. 109, 103505 (2011)
F. Tian, L.K. Varga, N. Chen, J. Shen, L. Vitos, J. Alloy Compd. 599, 19–25 (2014)
C. Li, X. Mi, W. Ye, S. Hui, Y. Yu, W. Wang, Mater. Sci. Eng. A 578, 103–109 (2013)
R. Saha, V. Srinivas, T.V. Chandrasekhar, Rao, A. Banerjee. J. Magn. Magn. Mater. 324, 1071–1079 (2012)
C.F. Yao, Q.C. Jin, X.C. Huang, D.X. Wu, J.X. Ren, D.H. Zhang, Int. J. Adv. Manuf. Technol. 65, 1019–1030 (2013)
J. Wang, Z. Zheng, J. Xu, Y. Wang, J. Magn. Magn. Mater. 355, 58–64 (2014)
L.H. Kong, Y.L. Gao, T.T. Song, Q.J. Zhai, J. Magn. Magn. Mater. 323, 2165–2169 (2011)
S.G. Ma, Y. Zhang, Mater. Sci. Eng. A 532, 480–486 (2012)
Acknowledgments
This work was supported by the National Natural Science Foundation of China Nos (51134013, 51075070, 51104029 and 313011), respectively, the natural science foundation of Liaoning Province (2014028013) and the fundamental research funds for the central universities.
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Jiang, L., Lu, Y., Dong, Y. et al. Effects of Nb addition on structural evolution and properties of the CoFeNi2V0.5 high-entropy alloy. Appl. Phys. A 119, 291–297 (2015). https://doi.org/10.1007/s00339-014-8964-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-014-8964-4