Abstract
Due to the poor solubility of aromatic polyesters in common organic solvents, trifluoroacetic acid is usually used as a co-solvent to increase their solubility for characterizations. However, only few studies have reported the side reactions induced by it. We present here the application of in situ1H-NMR techniques to explore its effect on the hydroxyl end-groups, which are usually used for the molecular weight determination of polyesters by end-group estimation method. Using bis(2-hydroxyethyl) terephthalate (BHET) as model compound, 1H quantitative NMR results show the peak integration of hydroxyethyl end-groups decreased with time via a pseudo-first-order kinetics in dtrifluoroacetic acid/d-chloroform mixture solvent (1:10, V:V). This is due to the esterification of hydroxyethyl groups with trifluoroacetic acid, revealed by the 1H-13C gradient-enhanced heteronuclear multiple bond correlation (gHMBC) spectrum. The mixtures of dimethyl terephthalate and BHET with different molar ratios were used to represent poly(ethylene terephthalate) (PET) with different degrees of polymerization, and the effect of trifluoroacetic acid on the estimation of hydroxyethyl groups and subsequent molecular weight determination of polyesters was studied. Our results show that if a relative error of 5% is allowed, the NMR measurements must be finished within 1.3 h of solution preparation at 25 °C in the mixture solvent. The results were confirmed in PET sample, while in poly(ethylene adipate), the obtained esterifaction constant is faster that those in aromatic system. The results can be applied to other polymer systems with alcohol functionalized groups, and used as a guideline for the characterization of polyesters and polyethers by end-group estimation method.
Similar content being viewed by others
References
Scheirs, J.; Long, T. E. in Modern polyesters: chemistry and technology of polyesters and copolyesters. John Wiley and Sons, Chichester, 2003.
Kalakkunnath, S.; Kalika, D. S. Dynamic mechanical and dielectric relaxtion characteristics of poly(trimethylene terephthalate). Polymer 2006, 47, 7085–7094.
Lotti, N.; Colonna, M.; Fiorini, M.; Finelli, L.; Berti, C. Poly(butylene terephthalate) modified with ethoxylated bisphenol S with increased glass transition temperature and improved thermal stability. Polymer 2011, 52, 904–911.
Gubbels, E.; Jasinska-Walc, L.; Merino, D. H.; Goossens, H.; Koning, C. Solid-state modification of poly(butylene terephthalate) with a bio-based fatty acid dimer diol furnishing copolyesters with unique morphologies. Macromolecules 2013, 46, 3975–3984.
Zhang, W.; Li, J.; Li, H.; Jiang, S.; An, L. Temperature dependence of deformation behavior of poly(butylene terephthalate). Polymer 2018, 143, 309–315.
Zekriardehani, S.; Joshi, A. S.; Jabarin, S. A.; Gidley, D. W.; Coleman, M. R. Effect of dimethyl terephthalate and dimethyl isophthalate on the free volume and barrier properties of poly(ethylene terephthalate) (PET): amorphous PET. Macromolecules 2018, 51, 456–467.
Schyns, Z. O. G.; Shaver, M. P. Mechanical recycling of packaging plastics: a review. Macromol. Rapid Commun. 2021, 42, 2000415.
Qiu, J.; Ma, S.; Wang, S.; Tang, Z.; Li, Q.; Tian, A.; Xu, X.; Wang, B.; Lu, N.; Zhu, J. Upcycling of polyethylene terephthalate to continuously reprocessable vitrimers through reactive extrusion. Macromolecules 2021, 54, 703–712.
Fagnani, D. E.; Tami, J. L.; Copley, G.; Clemons, M. N.; Getzler, Y. D. Y. L.; McNeil, A. J. 100th Anniversary of macromolecular science viewpoint: Redefining sustainable polymers. ACS Macro Lett. 2021, 10, 41–53.
Li, Y.; Makita, Y.; Zhang, G.; Rui, G.; Li, Z.; Zhong, G.; Miyoshi, T.; Huang, H.; Zhu, L. Effects of rigid amorphous fraction and lamellar crystal orientation on electrical insulation of poly(ethylene terephthalate) films. Macromolecules 2020, 53–3977.
Chou, C.; Liu, Y.; Zhang, Y.; Hsueh, C.; Yang, F.; Lee, S. Thermomechanical deformation of polyethylene-terephthalate artifcial muscles. Polymer 2020, 210, 123013.
Narimisa, M.; Onyshchenko, Y.; Morent, R.; De Geyter, N. Improvement of PET surface modifcation using an atmospheric pressure plasma jet with different shielding gases. Polymer 2021, 215, 123421.
Mori, S. Size exclusion chromatography of poly(ethylene terephthalate) using hexafluoro-2-propanol as the mobile phase. Anal. Chem. 1989, 61, 1321–1325.
Sanches, N. B.; Dias, M. L.; Pacheco, E. B. A. V. Comparative techniques for molecular weight evaluation of poly(ethylene terephthalate) (PET). Polym. Test. 2005, 24, 688–693.
Liu, F.; Zhang, J.; Wang, J.; Na, H.; Zhu, J. Incorporation of 1,4-cyclohexanedicarboxylic acid into poly(butylene terephthalate)-b-poly(tetramethylene glycol) to alter thermal properties without compromising tensile and elastic properties. RSC Adv. 2015, 5, 94091–94098.
Tanaka, K.; Oouchi, M.; Hayashi, F.; Maeda, H.; Waki, H. Structural analysis of the end groups and substructures of commercial poly(ethylene terephthalate) by multiple-WET 1H/13C NMR. Macromolecules 2016, 49, 5750–5754.
Chen, J.; Chen, D.; Huang, W.; Yang, X.; Li, X.; Tu, Y.; Zhu, X. A one pot facile synthesis of poly(butylene terephthalate)-block-poly(tetramethylene oxide) alternative multiblock copolymers via PROP method. Polymer 2016, 107, 29–36.
Zhu, X.; Gu, J.; Li, X.; Yang, X.; Wang, L.; Li, Y.; Li, H.; Tu, Y. PROP: an in situ cascade polymerization method for the facile synthesis of polyesters. Polym. Chem. 2017, 8, 1953–1962.
Paszkiewicz, S.; Szymczyk, A.; Pawlikowska, D.; Irska, I.; Taraghi, I.; Pilawka, R.; Gu, J.; Li, X.; Tu, Y.; Piesowicz, E. Synthesis and characterization of poly(ethylene terephthalate-co-1,4-cyclohe-xanedimethylene terephtlatate)-block(-poly(tetramethylene oxide) copolymers. RSC Adv. 2017, 7, 41745–41754.
Wang, G.; Jiang, M.; Zhang, Q.; Wang, R.; Liang, Q.; Zhou, G. New bio-based copolyesters poly(trimethylene 2,5-thiophenedicar-boxylate-co-trimethylene terephthalate): synthesis, crystallization behavior, thermal and mechanical properties. Polymer 2019, 173, 27–33.
Xie, H.; Lu, H.; Zhang, Z.; Li, X.; Yang, X.; Tu, Y. Effect of block number and weight fraction on the structure and properties of poly(butylene terephthalate)-block-poly(tetramethylene oxide) multiblock copolymers. Macromolecules 2021, 54, 2703–2710.
Zhao, Y.; Li, Y.; Xie, D.; Chen, J. Effect of chain extrender on the compatibility, mechanical and gas barrier properties of poly(butylene adipate-co-terephthalate)/poly(propylene carbonate) bio-composites. J. Appl. Polym. Sci. 2021, 138, 50487.
Cheng, H. N.; English, A. D. in NMR spectroscopy of polymers in solution and in the solid state. American Chemical Society, Washington DC, 2002.
Shit, S. C.; Maiti, S. Application of NMR spectroscopy in molecular weight determination of polymers. Eur. Polym. J. 1986, 22, 1001–1008.
Hariharan, R.; Pinkus, A. Useful NMR solvent mixture for polyesters: trifluoroacetic acid-d/chloroform-d. Polym. Bull. 1993, 30, 91–95.
Päch, M.; Zehm, D.; Lange, M.; Dambowsky, I.; Weiss, J.; Laschewsky, A. Universal polymer analysis by 1H NMR using complementary trimethylsilyl end groups. J. Am. Chem. Soc. 2010, 132, 8757–8765.
Li, X.; McCord, E. F.; Baiagern, S.; Fox, P.; Howell, J. L.; Sahooc, S. K.; Rinaldi, P. L. 2D-NMR studies of a model for Krytox® fluoropolymers. Magn. Reson. Chem. 2011, 49, 413–424.
Chen, D.; Gao, L.; Li, X.; Tu, Y. Precise molecular weight determination and structure characterization of end-functionalized polymers: an NMR approach via combination of one-dimensional and two-dimensional techniques. Chinese J. Polym. Sci. 2017, 35, 681–692.
Wang, W.; Wu, F.; Lu, H.; Li, X.; Yang, X.; Tu, Y. A cascade polymerization method for the property modification of poly(butylene terephthalate) by the incorporation of isosorbide. ACS Appl. Polym. Mater. 2019, 1, 2313–2321.
Xu, S.; Wu, F.; Li, Z.; Zhu, X.; Li, X.; Wang, L.; Li, Y.; Tu, Y. A green cascade polymerization method for the facile synthesis of sustainable poly(butylene-co-decylene terephthalate) copolymers. Polymer 2019, 178, 121591.
Li, Z.; Li, Y.; Zhao, Y.; Wang, H.; Zhang, Y.; Song, B.; Li, X.; Lu, S.; Hao, X.; Hla, S.; Tu, Y.; Li, X. Synthesis of metallopolymers and direct visualization of the single polymer chain. J. Am. Chem. Soc. 2020, 142, 6196–6205.
Li, H.; Xu, S.; Li, J.; Tu, Y.; Li, X.; Tu, Y.; Li, J.; Wang, Y.; Li, Z. Biodegradable all polyester-based multiblock copolymer elastomers with controlled properties. Polym. Chem. 2021, 12, 1837–1845.
Zhao, Y.; Gao, L.; Lu, H.; Li, X.; Tu, Y.; Chang, T. The non-free draining effect for small cyclics in solution. Polymer 2021, 213, 123202.
Youk, J. H.; Kambour, R. P.; MacKnight, W. J. Polymerization of ethylene terephthalate cyclic oligomers with antimony trioxide. Macromolecules 2000, 33, 3594–3599.
Jadhav, A. L.; Malkar, R. S.; Yadav, G. D. Zn- and Ti-modified hydrotalcites for transesterification of dimethyl terephthalate with ethylene glycol: effect of the metal oxide and catalyst synthesis method. ACS Omega 2020, 5, 2088–2096.
Kavanagh, P.; Knipe, A. C.; Watts, W. E. Kinetic study of the esterification of arylmethanols in trifluoroacetic acid: mechanistic change consequent upon aryl substituent effects. J. Chem. Soc., Chem. Commun. 1979, 905–906.
Gillen, C. J.; Knipe, A. C.; Watts, W. E. A kinetic study of the mechanism of esterification of 1-arylethanols in trifluoroacetic acid. Tetrahedron Lett. 1981, 22, 597–600. https://doi.org/10.1007/s10118-021-2605-0
Acknowledgments
This work was financially supported by the National Natural Science Foundation of China (No. 21774090), National Key R&D Program of China (No. 2018YFB1105700), and the Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD).
Author information
Authors and Affiliations
Corresponding authors
Electronic Supplementary Information
Rights and permissions
About this article
Cite this article
Tu, YY., Wan, XT., Huan, J. et al. The Effect of Trifluoroacetic Acid on Molecular Weight Determination of Polyesters: An in Situ NMR Investigation. Chin J Polym Sci 39, 1590–1596 (2021). https://doi.org/10.1007/s10118-021-2605-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10118-021-2605-0