Abstract
Oat (Avena sativa) biomass was studied as an alternative to recover Au(III) ions from aqueous solutions and for its capacity to reduce Au(III) to Au(0) forming Au nanoparticles. To study the binding trend of Au(III) to oat and the possible formation of Au nanoparticles, the biomass and a solution of Au(III) were reacted for a period of 1 h at pH values ranging from 2 to 6. The results demonstrated that Au(III) ions were bound to oat biomass in a pH-dependent manner, with the highest adsorption (about 80%) at pH 3. HRTEM studies showed that oat biomass reacted with Au(III) ions formed Au nanoparticles of fcc tetrahedral, decahedral, hexagonal, icosahedral multitwinned, irregular, and rod shape. To our knowledge, this is the second report about the production of nanorods as a product of the reaction of a Au(III) solution with a biological material. These studies also showed that the pH of the reaction influenced the nanoparticle size. The smaller nanoparticles and the higher occurrence of these were observed at pH values of 3 and 4, whereas the larger nanoparticles were observed at pH 2.
Similar content being viewed by others
References
Armendariz V., M. Jose-Yacaman, A. Duarte-Moller, J.R. peralta-Videa, H. Troiani, I. Herrera & J.L. Gardea-Torresdey, 2004. HRTEM characterization of gold nanoparticles produced by wheat biomass. Rev. Mex. Fis. (in press).
Brust M., D. Bethell, C.J. Kiely & D.J. Schiffrin, 1998. Selfassembled gold nanoparticle thin films with nonmetallic optical and electronic properties. Langmuir 14, 5425–5429.
Gardea-Torresdey J.L., K.J. Tiemann, G. Gamez, K. Dokken, S. Tehuacamanero & M. Jose-Yacaman, 1999. Gold nanoparticles obtained by bio-precipitation from gold(III) solutions. J. Nanopart. Res. 1, 397–404.
Gardea-Torresdey J.L., J.G. Parsons, E. Gomez, J.R. Peralta-Videa, H.E. Troiani, P. Santiago & M. Jose Yacaman, 2002a. Formation of Au nanoparticle inside live alfalfa plants. Nano Lett. 2, 397–401.
Gardea-Torresdey J.L., K.J. Tiemann, J.G. Parsons, G. Gamez & M. Jose Yaccaman, 2002b. Characterization of trace level Au(III) binding to alfalfa biomass. Adv. Environ. Res. 6, 313–323.
Gardea-Torresdey J.L., E. Gomez, J.R. Peralta-Videa, J.G. Parsons, H. Troiani & M. Jose-Yacaman, 2003. Alfalfa sprouts: A natural source for the synthesis of silver nanoparticles. Langumir. 4, 1357–1361.
Goia D.V. & E. Matijevic, 1999. Tailoring the particle size of monodispersed colloidal gold. Colloids Surf. A. 146, 139–152.
Greene B., M. Hosea, R. McPherson, M. Henzi, M.D. Alexander & D.W. Darnall, 1986. Interaction of gold(I) and gold(III) complexes with algal biomass. Environ. Sci. Technol. 20, 627–632.
Hosea M.,B. Greene, R. McPherson, M. Henzl, M.D. Alexander & D.W. Darnall, 1986. Accumulation of elemental gold on the alga chlorella vulgaris. Inorg. Chem. Acta 123, 161–165.
Kohler J.M., A. Csaki, J. Reichert, R. Moller, W. Straube & W. Fritzche, 2001. Selective labeling of oligonucleotide monolayers by metallic nanobeads for fast optical readout of DNA-chips. Sensor Actuators Chem B 76, 166–172.
Kuyucak N. & B. Volesky, 1989. Accumulation of gold by algal biosorbent. Biorecovery 1, 189–204.
Lopez M.L., J.L. Gardea-Torresdey, J.R. Peralta-Videa, G. de la Rosa, V. Armendariz, I. Herrera & H. Troiani, 2004. Gold binding by native and chemically modified hop biomasses. Bioinorg. Chem. Appl. (accepted for publication).
Mafune F., J. Kohono, Y. Takeda & T. Kondow, 2002. Full physical preparation of size-selected gold nanoparticles in solutions: Laser ablation and laser induced size control. J. Phys. Chem. B 106, 7575–7577.
Magnusson M.H., K. Deppert, J. Malm, J. Bovin & L. Samuelson, 1999. Size-selected gold nanoparticles by aerosol technology. Nanostruct. Mater. 12, 45–48.
Martin C.R. & D.T. Mitchell, 1998. Nanomaterials on analytical chemistry. Anal. Chem. 9, 322A–327A.
McConnell W.P, J.P. Novak, L.C. Brousseau III, R.R. Fuiere, R.C. Tenent & D.L Feldheim, 2000. Electronic and optical properties of chemically modified nanoparticles and molecularly bridged nanoparticle arrays. J. Phys. Chem. B 104, 8925–8930.
Mukherjee P., A. Ahmad, D, Mandal, S. Senapati, S.R. Sainkar, S. Mohammad, I. Khan, R. Ramani, R. Parischa, P.V. Ajayakumar, M. Alam, M. Sastry & R. Kumar, 2001. Bioreduction of AuCl4 ) ions by fungus, Verticillium sp. and surface trapping of the gold nanoparticles formed. Angew. Chem. Int. Ed. 40, 3585–3588.
Mukherjee P., S. Senapati, D. Mandal, A. Ahmad, M.I. Khan, R. Kumar & M. Sastry, 2002. Extracellular synthesis of gold nanoparticles by using Fusarium oxysporum. Chem. Biochem. 5, 461–463.
Okitsu K., A. Yue, S. Tanabe, H. Matsumoto & Y. Yobiko, 2001. Formation of colloidal nanoparticles in a ultrasonic field: control of rate of gold(III) reduction and size formed nanoparticles. Langmuir 17, 7717–7720.
Sau T.K., Pal, A., Jana, N.R., Wang, Z.L. & T. Pal, 2001. Size controlled synthesis of gold nanoparticles using photochemically prepared seed particles. J. Nanopart. Res. 3, 257–261.
Tanaka K., 1999. Nanotechnology towards the 21st century. Thin Solid Films 341, 120–125.
Tolles W.M., 1996. Nanoscience and nanotechnology in Europe. Nanotechnology 7, 59–105.
Troiani H.E., A. Camacho-Bragado, V. Armendariz, J.L. Gardea-Torresday & M. Jose Yacaman, 2003. Synthesis of carbon onions by gold nanoparticles and electron irradiation. Chem. Mater. 15, 1029–1031.
Turkevich J.,1985a. Colloidal gold part I: Historical and preparative aspects, morphology and properties. Gold Bull. 18, 86–91.
Turkevich J.,1985b. Colloidal gold part II: Color, coagulation, adhesion, alloying and catalytic properties. Gold Bull. 18, 125–131.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Armendariz, V., Herrera, I., peralta-videa, J.R. et al. Size controlled gold nanoparticle formation by Avena sativa biomass: use of plants in nanobiotechnology. Journal of Nanoparticle Research 6, 377–382 (2004). https://doi.org/10.1007/s11051-004-0741-4
Issue Date:
DOI: https://doi.org/10.1007/s11051-004-0741-4