Abstract
An electrolytic copper rod was drawn in 24 passes to a 90 pct reduction in area and subsequently annealed under various conditions. The global texture of the drawn wire, as measured by X-ray methods, showed a fiber texture approximated by a strong 〈111〉 and a weak 〈100〉 component. However, its microtexture, as measured by electron backscattered diffraction (EBSD), indicated that the major 〈111〉+minor 〈100〉 duplex fiber texture was dominant only in the center region, while a relatively diffuse texture developed with a somewhat higher density of orientations having a 〈11w〉//wire axis in the middle and surface regions. The inhomogeneous texture in the as-deformed wire gave rise to an inhomogeneous microstructure and texture after annealing. When annealed at 300 °C or 600 °C for 3 hours, the wire developed a duplex fiber texture consisting of major 〈100〉+minor 〈111〉 components in the center region, a strong 〈100〉 fiber texture in the middle region, and a weak texture consisting of 〈111〉 and 〈100〉 components with the 〈111〉 component being slightly stronger in the surface region. When the drawn wire was annealed at the high temperature of 700 °C, the texture at short annealing times was similar to that of the wire annealed at the lower temperatures of 300 °C and 600 °C for 3 hours, but prolonged annealing gave rise to a texture ranging from the 〈111〉 to 〈112〉 components due to abnormal grain-growth that started in the surface region. The recrystallization texture consisting of the major 〈100〉+minor 〈111〉 components was explained by the strain-energy-release maximization (SERM) model, in which the recrystallization texture is determined such that the absolute maximum principal stress direction due to dislocations in the deformed state is along the minimum elastic-modulus direction in recrystallized grains. On the other hand, the abnormal grain-growth texture was attributed to grain-boundary mobility differences between differently oriented grain.
Similar content being viewed by others
References
H. Mecking: in Preferred Orientation in Deformed Metals and Rocks: An Introduction to Modern Texture Analysis, H.-R. Wenk, eds., Academic Press, Orlando, FL, 1985, p. 277.
A.D. Rollett and S.I. Wright: in Texture and Anisotropy, U.F. Kocks, C.N. Tomé, and H.R. Wenk, eds., Cambridge University Press, Cambridge, United Kingdom, 1998, p. 227.
G. Linsen, H.D. Mengelberg, and H.P. Stüwe: Z. Metallkd., 1964, vol. 55, p. 600.
N. Inakazu, Y. Kaneno, and H. Inoue: Mater. Sci. Forum, 1994, vols. 157–162, p. 715.
F.J. Humphreys and M. Hatherly: Recrystallization and Related Annealing Phenomena, Pergamon Press, Oxford, United Kingdom, 1995.
F.F. Kraft, U. Chakkingal, G. Baker, and R.N. Wright: J. Mater. Process. Technol., 1996, vol. 60, p. 171.
E. Grant, D. Juul Jensen, B. Ralph, and N. Hansen: 7th Int. Conf. on Texture of Materials, C.M. Brakman, P. Jongenburger, and E.J. Mittenmeijer, eds., Netherlands Society for Materials Science, Noordwijkerhout, The Netherlands, 1984, p. 239.
I.L. Dillamore and W.T. Roberts: Metall. Rev., 1965, vol. 10, pp. 271–380.
C.S. Barrett and T.B. Massalski: Structure of Metals, 3rd ed., McGraw-Hill, New York, NY, 1966, pp. 569–70.
H.J. Shin, H.-T. Jeong, and D.N. Lee: Mater. Sci. Eng., 2000, vol. A279, p. 244.
K. Rajan and R. Petkie: Mater. Sci. Eng., 1998, vol. A257, p. 185.
H. Inoue, N. Nakazu, and H. Yamamoto: 6th Int. Conf. on Texture of Materials, S. Nagashima, ed., The Iron and Steel Institute of Japan, Tokyo, 1981, p. 591.
P.A. Beck and P.R. Sperry: J. Appl. Phys., 1950, vol. 21 p. 150.
S.P. Bellier and R.D. Doherty: Acta Metall., 1977, vol. 25, p. 521.
D.N. Lee: Scripta Metall. Mater., 1995, vol. 32, p. 1689.
D.N. Lee: Met. Mater., 1999, vol. 5, p. 401.
D.N. Lee: Int. J. Mech. Sci., 2000, vol. 42, p. 1645.
H. Park and D.N. Lee: Mater. Sci. Forum, 2002, vol. 408–412, p. 637.
S. Matthies: Phys. Status Solidi, 1980, vol. 101, p. 111.
Y.B. Park, D.N. Lee, and G. Gottstein: Acta Mater., 1998, vol. 46, p. 3371.
D.N. Lee: J. Mater. Process. Technol., 2001, vol. 117, p. 307.
S.-H. Hong and D.N. Lee: J. Eng. Mater. Technol. (ASME JEMT), 2002, vol. 124, p. 13.
J.-H. Choi, S. Kang, and D.N. Lee: J. Mater. Sci., 2000, vol. 35, p. 4055.
I. Kim and S.K. Lee: Textr. Microstr., 2000, vol. 34, p. 159.
M. Hillert: Acta Metall., 1965, vol. 13, p. 227.
L.S. Shvindlerman, G. Gottstein, D.A. Molodov, and V.G. Suraeva: 1st Joint Int. Conf. on Recrystallization and Grain Growth, G. Gottstein and D.A. Molodov, eds., Springer-Verlag, New York, NY, 2001, p. 177.
D.A. Porter and K.E. Eastering: Phase Transformations in Metals and Alloys, Chapman & Hall, London, 1992, p. 130.
J. Harase, R. Shimizu, and D.J. Dingley: Acta Metall. Mater., 1991, vol. 39, p. 763.
R.D. Doherty et al.: Mater. Sci. Eng., 1997, vol. A238, p. 219.
Y. Hayakawa, M. Muraki, and J.A. Szpunar: Acta Mater., 1998, vol. 46, p. 1063.
G. Gottstein and L.S. Shvindlerman: Grain Boundary Migration in Metals, CRC Press, Boca Raton, FL, 1999, p. 203.
D.A. Molodov: 1st Joint Int. Conf. on Recrystallization and Grain Growth, G. Gottstein and D.A. Molodov, eds., Springer-Verlag, New York, NY, 2001, p. 21.
A.N. Aleshin, V.Y. Aristov, B.S. Bokstein, and L.S. Shvindlerman: Phys. Status Solidi, 1978, vol. A45, p. 359.
F. Czerwinski, H. Li, M. Megret, and J.A. Szpunar: Scripta Metall. Mater., 1997, vol. 37, p. 1967.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Park, H., Lee, D.N. The evolution of annealing textures in 90 Pct drawn copper wire. Metall Mater Trans A 34, 531–541 (2003). https://doi.org/10.1007/s11661-003-0089-x
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-003-0089-x