Abstract
The metallurgical behavior during shielded metal arc welding (SMAW) and the slag detachability of the CaO-CaF2-SiO2 type ENiCrFe-7-covered electrodes was investigated. The results indicated that the slag detachability could be improved as the SiO2 in the flux coatings decreased. When the SiO2 in the flux coating was 10.9 pct, about 28.3 pct CaF2 resulted in the best slag detachability. The CaF2 and SiO2 in the flux coating interacted during SMAW to form gaseous SiF4 to be evacuated. In the reactions, one SiO2 consumed two CaF2, leading to the reduction of the ratio of CaF2/SiO2. After comparing the slag compositions, the best slag detachability was obtained at CaO:CaF2:SiO2 = 1.7:1.8:1, but the worst slag detachability appeared at CaO:CaF2:SiO2 = 1.3:0.9:1. The XRD analysis revealed that the oxides and fluorides in the slags preferred to gather together to form cuspidine and other complex phases. If the CaF2 was dominant in the slags, they intended to form homogenous porous microstructures that were relatively strong and would most likely detach from the weld metal in blocks, exhibiting good slag detachability. If the cuspidine phase was dominant, the slags exhibited a ‘rock strata’-like microstructure in the intergranular area. Such microstructure was very fragile and could be broken into fine powders that were easily embedded in the weld ripples, leading to slag adhesions. This work provides the researcher with a wealth of information and data, which will also be beneficial to the welding material producers and users.
Similar content being viewed by others
References
J.N. DuPont, J.C. Lippold, and S.D. Kiser: Welding Metallurgy and Weldability of Nickel-Base Alloys, 1st ed., John Wiley & Sons Inc., Hoboken, NJ, 2009, pp. 1–5.
AWS A5.11/A5.11M: Nickel and Nickel-Alloy Welding Electrodes for Shielded Metal Arc Welding, American Welding Society, Miami, FL, 2005.
S.D. Strauss: Power, 1996, vol. 140, pp. 29–30.
D.L. Olson, S. Liu, R.H. Frost, G.R. Edwards, and D.A. Fleming: Nature and Behavior of Fluxes Used for Welding, Brazing, and Soldering, ASM Handbook, Materials Park, OH, 1993, vol. 6, pp. 43–54.
C.A. Natalie, D.L. Olson, and M. Blander: Ann. Rev. Mater. Sci., 1986, vol. 16, pp. 389–413.
S.I. Moravetsky: Paton. Weld. J., 2011, vol. 1, pp. 28–31.
S.I. Moravetsky: Paton. Weld. J., 2011, vol. 2, pp. 20–23.
K. Sham and S. Liu: Welding Journal, 2014, vol. 8, pp. 271s–81s.
D.L. Olson, G.R. Edwards, and S.K. Marya: Ferr. Alloy Weldments, 1992, vol. 67–70, pp. 253–68.
B. Singh, Z.A. Khan, and A.N. Siddiquee: J. Mech. Eng. Res., 2013, vol. 5, pp. 123–27.
R. Qin and G. He: Metall. Mater. Trans. A, 2013, vol .44A, pp. 1475–84.
E. Baune, C. Bonnet, and S. Liu: Weld. J., 2000, vol. 79, no. 3, pp. 57s–65s.
H. Nanto, R. Nakagawa, T. Yanagida, Y. Fujimoto, K. Fukuda, Y. Miyamoto, K. Hirasawa and Y. Takei: Sens. Mater., 2015, vol. 27, pp. 277–82.
T. Watanabe, H. Fukuyama, M. Susa, and K. Nagata: Metall. Mater. Trans. B, 2000, vol. 31B, pp. 1273–82.
B.K. Das, U.S. Yadav, and D.N. Jena: Recycling of steel plant waste through sinter. In: Proceedings of the national seminar on recent techniques in mineral processing waste and environment management. by G.V. Rao ed., Indian Institute of Mineral Engineers. Allied Publishers LTD, New Delhi, 2000, pp.187–92
Y. Nakajima and M. Mukai: ISIJ Int., 1993, vol. 33, pp. 109–15.
S. Nakamura, F. Tsukihashi, and N. Sano: ISIJ Int., 1993, vol. 33, pp. 53–58.
Z. Duan, R. Qin, and G. He: Metall. Mater. Trans. A, 2014, vol. 45A, pp. 843–53.
J.R. Davis: ASM Specialty Handbook: Nickel, Cobalt, and Their Alloys, ASM International, Materials Park, OH 2000, p. 33.
M.D. Almeida, R.J. Brook, and T.G. Carruthers: J. Mater. Sci., 1979, vol. 14, pp. 2191–94.
G. Fiquet, P. Richet, and G. Montagnac: Phys. Chem. Minerals, 1999, vol. 27, pp. 103–11.
B. Schumann, and H. Neumann: Crystal Res. Technol., 1984, vol.19, pp. K13–K14.
M. Amri, G.J. Clarkson, and R.I. Walton: J. Phys. Chem. C, 2010, vol. 114, pp. 6726–33.
T. Watanabe, H. Fukuyama, and K. Nagata: ISIJ Int., 2002, vol. 42, pp. 489–97.
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted November 23, 2014.
Rights and permissions
About this article
Cite this article
Wang, H., Qin, R. & He, G. SiO2 and CaF2 Behavior During Shielded Metal Arc Welding and Their Effect on Slag Detachability of the CaO-CaF2-SiO2 Type ENiCrFe-7-Covered Electrode. Metall Mater Trans A 47, 4530–4542 (2016). https://doi.org/10.1007/s11661-016-3629-x
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-016-3629-x