Abstract
Visible-light-active Fe-POMs was fabricated via precipitating Fe3+ with Keggin type polyoxometalates (H3PW12O40, H4SiW12O40 or H3PMo12O40) under solvothermal condition. The as-prepared Fe-POMs were denoted as FePW, FeSiW and FePMo, respectively. Among the three kinds of Fe-POMs, FePMo displayed the highest visible light absorption, the largest specific surface area, the most sensitive photocurrent response and the smallest charge transfer resistance, which were all beneficial for heterogeneous photocatalysis. The efficiency for Cr(VI) reduction was ca. 88% by FePMo after 50 min visible light irradiation. The estimated rate constant(0.042 min−1) was ca. 2.5 and 1.8 times that by FePW and FeSiW, respectively. FTIR spectra indicated that the Keggin structure of PMo12O403− was maintained in FePMo. Mechanism study indicated that the photogenerated electrons in LUMO and the holes in HOMO were thermodynamically feasible for Cr(VI) reduction and H2O oxidation, respectively. Using FePMo as an optimized photocatalyst, good stability was also observed after 5 cyclic runs in both photocatalytic performance and XRD structure.
Similar content being viewed by others
References
Carlos E. B., Violeta L., Bryan B., J. Hazard. Mater., 2012, 223/224, 1
Wang C., Du X., Li J., Guo X., Wang P., Zhang J., Appl. Catal. B: Environ., 2016, 193, 198
Zou Y., Wang X., Khan A., Wang P., Liu Y., Alsaedi A., Hayat T., Wang X., Environ. Sci. Technol., 2016, 50, 7290
Al-Shannag M., Al-Qodah Z., Bani-Melhem K., Qtaishat M. R., Alkasrawi M., Chem. Eng. J., 2015, 260, 749
Fu F., Wang Q., J. Environ. Manage., 2011, 92, 407
Chen C., Ma W., Zhao J., Chem. Soc. Rev., 2010, 39, 4206
An X., Tang Q., Lan H., Liu H., Qu J., Appl. Catal. B: Environ., 2019, 244, 407
Zhang G., Yang W., Wu W., Wu X., Zhang L., Kuang X., Wang S., Lu C., J. Catal., 2019, 369, 54
Zhao X., Zhang Y., Zhao Y., Tan H., Zhao Z., Shi H., Wang E., Li Y., Dalton Trans., 2019, 48, 6484
Tang Q., An X., Lan H., Liu H., Qu J., Appl. Catal. B: Environ., 2020, 268, 118394
Huang Y., Wang R., J. Mater. Chem. A, 2019, 7, 12105
Liu W., Dong L., Li R., Chen Y., Sun S., Li S., Lan Y., ACS Appl. Mater. Interf., 2019, 11, 7030
Tangestaninejad S., Mirkhani V., Moghadam M., Mohammadpoor-Baltork I., Shams E., Salavati H., Ultrason. Sonochem., 2008, 15, 438
Koutsouroubi E. D., Xylouri A. K., Armatas G. S., Chem. Commun., 2015, 51, 4481
Wang Q., Liu E., Zhang C., Huang S., Cong Y., Zhang Y., J. Colloid. Interf Sci., 2018, 516, 304
Shi H., Yan G., Zhang Y., Tan H., Zhou W., Ma Y., Li Y., Chen W., Wang E., ACS Appl. Mater. Interfaces, 2017, 9, 422
Cen Q., Gao Q., Zhang C., Liu Y., Wang Q., Wang Q., J. Colloid Interf. Sci., 2020, 562, 12
Gao Q., Lin D., Fan Y., He Q., Wang Q., Chem. Eng. J., 2019, 374, 10
Fournier M., Feumi-Jantou C., Rabia C., Hervé G., Launay S., J. Mater. Chem., 1992, 2, 971
Al-Garni T., Al-Jallal N., Aouissi A., J. Chem., 2017, 2017, 5641604
Yin D., Zhang L., Zhao X., Chen H., Zhai Q., Chin. J. Catal., 2015, 36, 2203
Silva M. J., Liberto N. A., De Andrade Leles L C, Pereira U. A., J. Mol. Catal A: Chem., 2016, 422, 69
Spojakina A., Kraleva E., Jiratova K., Petrov L., Appl. Catal. A: Gen., 2005, 288, 10
Grosvenor A. P., Kobe B. A., Biesinger M. C., McIntyre N. S., Surf. Interface Anal., 2004, 36, 1564
Phillips D. C., Sawhill S. J., Self R., Bussell M. E., J. Catal., 2002, 207, 266
Wang Q., Shi X., Xu J., Crittenden J. C., Liu E., Zhang Y., Cong Y., J. Hazard. Mater., 2016, 307, 213
Cong Y., Ji Y., Ge Y., Jin H., Zhang Y., Wang Q., Chem. Eng. J., 2017, 307, 72
Wang Q., Zhu N., Liu E., Fu L., Zhou T., Cong Y., Electrochim. Acta, 2016, 216, 266
Tian H., Araya T., Li R., Fang Y., Huang Y., Appl. Catal. B: Environ., 2019, 254, 371
Dong G., Zhang Y., Pan Q., Qiu J., J. Photoch. Photobio. C, 2014, 20, 33
Wu Q., Zhao J., Qin G., Wang C., Tong X., Song X., Appl. Catal. B: Environ., 2013, 142, 142
Zhao Z., Zhang W., Sun Y., Yu J., Zhang Y., Wang H., Dong F., Wu Z., J. Phys. Chem. C, 2016, 120, 11889
Liu B., Liu X., Liu J., Feng C., Li Z., Li C., Gong Y., Pan L., Xu S., Sun C. Q., Appl. Catal. B: Environ., 2018, 226, 234
Author information
Authors and Affiliations
Corresponding authors
Additional information
Supported by the National Natural Science Foundation of China(No.21876154), the Zhejiang Provincial Natural Science Foundation, China(No.LR18B070001), and partially supported by the Robert A. Welch Foundation(No.B-0027)(SM) and the Researchers Supporting Project(No.RSP-2020/7a) at King Saud University(AN).
Electronic Supplementary Information
Rights and permissions
About this article
Cite this article
Cen, Q., Xiao, W., Liu, Y. et al. Fabrication of Fe-POMs as Visible-light-active Heterogeneous Photocatalyst. Chem. Res. Chin. Univ. 36, 1128–1135 (2020). https://doi.org/10.1007/s40242-020-0320-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40242-020-0320-y