Size distribution and optical properties of self-assembled Ge on Si

  • Published:
Applied Physics A Aims and scope Submit manuscript

Abstract.

The distribution of Ge islands is analysed in order to understand their optical behaviour. The Ge islands described in this paper were deposited by low-pressure chemical vapour deposition at relatively high temperature (700 °C), therefore the diffusion length of adatoms is high (∼100 μm) and thus, not the limiting factor for nucleation. By changing the deposition time and the coverage, square-based pyramids, domes and relaxed domes are nucleated. Mainly domes emit light, the emission being in the wavelength range 1.38–1.55 μm. When pyramids or relaxed domes are present, the photoluminescence broadens and decreases in intensity. The electroluminescence of vertically correlated islands increases with the number of layers, i.e. with the number of islands. The nucleation of islands on patterned (001) Si is changed when the deposition is performed on Si mesas with high index facets. The size distribution becomes narrower when the mesa size is decreased. An intermixing of up to 40% Si in the 2D layer was determined from photoluminescence data. PIN diodes fabricated on patterned wafers show an area-dependent electroluminecence related to a different microstructure of islands on large and small mesas. Finally, the lateral ordering on {hkl} facets is discussed.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

Author information

Authors and Affiliations

Authors

Additional information

Received: 14 April 2000 / Accepted: 17 April 2000 / Published online: 6 September 2000

Rights and permissions

Reprints and permissions

About this article

Cite this article

Vescan, L., Goryll, M., Stoica, T. et al. Size distribution and optical properties of self-assembled Ge on Si. Appl Phys A 71, 423–432 (2000). https://doi.org/10.1007/s003390000555

Download citation

  • Issue Date:

  • DOI: https://doi.org/10.1007/s003390000555

Navigation