Setting solution concentration effect on properties of a TTCP/DCPA-derived calcium phosphate cement

  • Published:
Journal of Materials Science: Materials in Medicine Aims and scope Submit manuscript

Abstract

The present work was to investigate the effects of concentration of (NH4)2HPO4 (diammonium hydrogen phosphate) setting solution on properties of a tetracalcium phosphate (TTCP)/dicalcium phosphate anhydrous (DCPA)—derived calcium phosphate cement. Experimental results indicated that working/setting time of the cement paste decreased with increasing (NH4)2HPO4 concentration of the setting solution. After being immersed in Hanks’ solution for 1 day or longer, the XRD intensities of initial TTCP and DCPA phases largely decreased, while apatite phase became dominant. More residual TTCP phase was observed in the 1 day-immersed cement prepared from higher concentration setting solutions. Compressive strength of the cement immersed for 1 day was consistently higher than that immersed for 30 min or 7 days. After being immersed for 1 day, the average CS value reached a maximal value (59 MPa) as (NH4)2HPO4 concentration was increased to 0.6 M, beyond that the cement strength decreased and maintained in a relatively high range of 47–54 MPa. Cells incubated with conditioned medium of Al2O3 powder and with blank medium exhibited similar average viability values (0.80 and 0.78, respectively). The OD value with extractions of cement decreased with increasing (NH4)2HPO4 concentration of the setting solution. The average 0.25, 0.5 and 0.6 M—OD values were 0.78, 0.67 and 0.66, respectively. When setting solution concentration was greater than 0.6 M, the OD value sharply declined to 0.47.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6

Similar content being viewed by others

References

  1. Driskell TD, Heller AL, Koenigs J. Dental treatments. US patent no 3,913,229, 1975.

  2. Brown WE, Chow LC. A new calcium phosphate setting cement. J Dent Res. 1983;207:662–72.

    Google Scholar 

  3. Bohner M. Calcium orthophosphates in medicine: from ceramics to calcium phosphate cements. Injury. 2000;31:S37–47.

    Article  Google Scholar 

  4. Schliephake H, Gruber R, Dard M, Wenz R, Scholz S. Repair of calvarial defects in rats by prefabricated hydroxyapatite cement implants. J Biomed Mater Res. 2004;69A:382–90.

    Article  CAS  Google Scholar 

  5. Heini PF, Berlemann U. Bone substitutes in vertebroplasty. Eur Spine J. 2001;10:S205–13.

    Article  Google Scholar 

  6. Constantz BR, Barr BM, Ison IC, Fulmer MT, Baker J, McKinney L, Goodman SB, Gunasekaren S, Delaney DC, Ross J, Poser RD. Histological, chemical, and crystallographic analysis of four calcium phosphate cements in different rabbit osseous sites. J Biomed Mater Res. 1998;43:451–61.

    Article  CAS  Google Scholar 

  7. Wang JL, Zin YT, Tzeng CC, Lin CI, Lin SW, Chang GL. The assay of bone reaction after implantation of calcium sulfate and a composite of calcium sulfate and calcium phosphate. J Med Biol Eng. 2003;4:205–12.

    Google Scholar 

  8. Kurashina K, Kurita H, Kotani A, Kobayashi S, Kyoshima K, Hirano M. Experimental cranioplasty and skeletal augmentation using an alpha-tricalcium phosphate/dicalcium phosphate dibasic/tetracalcium phosphate monoxide cement: a preliminary short-term experiment in rabbits. Biomaterials. 1998;19:701–6.

    Article  CAS  Google Scholar 

  9. Daculsi G, Weiss P, Bouler JM, Gauthier O, Aguado E. Biphasic calcium phosphate/hydrosoluble polymer composites: a new concept for bone and dental substitution biomaterials. Bone. 1999;25:59S–61S.

    Article  CAS  Google Scholar 

  10. Yoshikawa M, Toda T. In vivo estimation of periapical bone reconstruction by chondroitin sulfate in calcium phosphate cement. J Eur Ceram Soc. 2004;24:521–31.

    Article  CAS  Google Scholar 

  11. Frankenburg EP, Goldstein SA, Bauer TW, Harris SA, Poser RD. Biomechanical and histological evaluation of a calcium phosphate cement. J Bone Joint Surg Am. 1998;80:1112–24.

    CAS  Google Scholar 

  12. Khairoun I, Boltong MG, Driessens FCM, Planell JA. Effect of calcium carbonate on clinical compliance of apatitic calcium phosphate bone cement. Biomaterials. 1997;18:1535–9.

    CAS  Google Scholar 

  13. Panda AK, Mishra S, Bisaria VS. Alkaloid production by cell suspension cultures of Holarrhena antidysenterica— I. Effect of major nutrients. Biotechnol Bioeng. 1992;39:1043–51.

    Article  CAS  Google Scholar 

  14. dos Santosa LA, Carrodeguas RG, Rogero SO, Higa OZ, Boschi AO, de Arruda ACF. α-Tricalcium phosphate cement: “in vitro” cytotoxicity. Biomaterials. 2002;23:2035–42.

    Article  Google Scholar 

  15. Tsai CH, Lin JHC, Ju CP. Gamma-radiation-induced changes in structure and properties of tetracalcium phosphate and its derived calcium phosphate cement. J Biomed Mater Res B Appl Biomater. 2007;80:244–52.

    Google Scholar 

  16. Mears DC. Metals in medicine and surgery. Int Met Rev. 1977;22:119–53.

    Google Scholar 

  17. Ishikawa K, Takagi S, Chow LC, Ishikawa Y. Properties and mechanisms of fast-setting calcium phosphate cements. J Mater Sci Mater Med. 1995;6:528–33.

    Article  CAS  Google Scholar 

  18. Brown PW, Constantz B. Hydroxyapatite and related materials. 1st ed. Boca Raton, Fl: CRC Press; 1994.

    Google Scholar 

  19. Takagi S, Chow LC, Ishikawa K. Formation of hydroxyapatite in new calcium phosphate cements. Biomaterials. 1998;19:1593–9.

    Article  CAS  Google Scholar 

  20. Chen WC, Chern Lin JH, Ju CP. Transmission electron microscopic study on setting mechanism of tetracalcium phosphate/dicalcium phosphate anhydrous-based calcium phosphate cement. J Biomed Mater Res. 2003;64A:664–71.

    Article  CAS  Google Scholar 

  21. Chen WC, Ju CP, Chern Lin JH. Effect of heat treatment on compressive strength and setting behavior of TTCP/DCPA-derived calcium phosphate cement. J Mater Sci Lett. 2002;21:1583–5.

    Article  CAS  Google Scholar 

  22. Miyamoto Y, Ishikawa K, Fukao H, Sawada M, Nagayama M, Kon M, Asaoka K. In vivo setting behaviour of fast-setting calcium phosphate cement. Biomaterials. 1995;16:855–60.

    Article  CAS  Google Scholar 

  23. Chen WC, Ju CP, Chern Lin JH. Variation in structure and properties of a non-dispersive TTCP-DCPA-derived CPC immersed in Hank’ solution. J Oral Rehabil. 2007;34:541–51.

    Article  Google Scholar 

  24. Wang IC, Ju CP, Chern Lin JH. Gamma-radiation effect on morphology and properties of TTCP/DCPA-derived calcium phosphate cement. Mater Trans. 2005; 46:1701–5.

    Google Scholar 

  25. Schneider M, Marison IW, Stockar UV. The importance of ammonia in mammalian cell cultures. J Biotechnol. 1996;46:161–85.

    Article  CAS  Google Scholar 

  26. Chen PF, Harcum SW. Effects of amino acid additions on ammonium stressed CHO cells. J Biotechnol. 2005;117:277–86.

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Jiin-Huey Chern Lin.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Chen, CK., Ju, CP. & Lin, JH.C. Setting solution concentration effect on properties of a TTCP/DCPA-derived calcium phosphate cement. J Mater Sci: Mater Med 23, 2109–2114 (2012). https://doi.org/10.1007/s10856-012-4700-9

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10856-012-4700-9

Keywords

Navigation