Thermal analysis, microstructure and impurity phases evolution in Fe14Cr ferritic steel powders ball-milled in air and under an argon atmosphere

  • Published:
Journal of Thermal Analysis and Calorimetry Aims and scope Submit manuscript

Abstract

Refined structure of the ferritic phase induced by mechanical milling (under reducing atmosphere) and its thermal stability are required in various applications of nanostructured ferritic alloys. The impurification with nitrogen and oxygen uptaken from the air is very probable during ball-milling, especially at the long-time high-energy milling conditions. As a rule, these interstitial impurities in as-milled powders are in quantities under the sensibility limit of conventional measurement techniques, such as XRD and SEM/EDS. To evidence the tendency for microstructure modification by impurities introduced during milling, the Fe–14Cr–3W–0.4Ti–0.25Y2O3 (Fe14Cr) ferritic steel powders (re)loaded in air and milled up to 170 h with interruption of the milling process, and heated up to 1373 K were investigated by thermal analysis in correlation with X-ray diffraction and scanning electron microscopy. XRD failed to detect the impurities in powders milled up to 38 h in air although a consistent mass loss related to the degassing of N2 was registered in thermogravimetric, TG, curves. (Fe,Cr)4N, fcc-γ, (Fe,Cr)2O3 impurity phases in powders milled over 38 h in air and (Fe,Cr)2O4 formed upon heating were readily detected by XRD. The analysis of these results allowed to better understand the impurification process and to generalise it for any as-milled Fe–Cr-based alloy powder processed in any milling conditions irrespective of the milling atmosphere, duration and thus, of amounts of contaminants. The quality of three powders milled for 170 h in three different conditions was compared: in air, under an argon atmosphere with interruptions of the milling process and under an argon atmosphere without interruption of the milling process. The contamination of powder milled for 170 h under an argon atmosphere without interruption of the milling process is insignificant (corresponding to less than 0.5 mass% mass loss in TG) as compared to powders obtained in the other two milling conditions. New approaches for minimising the contamination from air are suggested.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9

Similar content being viewed by others

References

  1. Odette GR. Recent progress in developing and qualifying nanostructured ferritic alloys for advanced fission and fusion applications. JOM. 2014;66:2427–41.

    Article  CAS  Google Scholar 

  2. Stork D, Agostini P, Boutard JL, Buckthorpe D, Diegele E, Dudarev SL, English C, Federici G, Gilbert MR, Gonzalez S, Ibarra A, Linsmeier Ch, Puma Li A, Marbach G, Morris PF, Packer LW, Raj B, Rieth M, Tran MQ, Ward DJ, Zinkle SJ. Developing structural, high-heat flux and plasma facing materials for a near-term DEMO fusion power plant: the EU assessment. J Nucl Mater. 2014;455:277–91.

    Article  CAS  Google Scholar 

  3. Suryanarayana C. Mechanical alloying and milling. New York: Marcel Dekker; 2004.

    Book  Google Scholar 

  4. Aufrecht J, Leineweber A, Foct J, Mittemeijer EJ. The structure of nitrogen-supersaturated ferrite produced by ball milling. Philos Mag. 2008;88:1835.

    Article  CAS  Google Scholar 

  5. Hryha E, Nyborg L. Thermogravimetry study of the effectiveness of different reducing agents during sintering of Cr-prealloyed PM steels. J Therm Anal Calorim. 2014;118:825–34.

    Article  CAS  Google Scholar 

  6. HrubovIa´kova´ M, Dudrova´ E, Hryha E, Kaba´tova´ M, Harvanova´J. Parameters controlling the oxide reduction during sintering of chromium prealloyed steel. Hindawi Publishing Corporation Advances in Materials Science and Engineering; 2013, p. 16. Article ID 789373.

  7. Danninger H, Gierl C, Kremel S, Leitner G, Jaenicke-Roessler K, Yu Y. Degassing and deoxidation processes during sintering of unalloyed and alloyed PM steels. Powder Metall Prog. 2002;2(3):125–40.

    CAS  Google Scholar 

  8. Rawers JC, Krabbe R, Cook DC, Kim TH. Differences in the microstructure of iron mechanically processed powder alloyed with interstitial and substitutional elements. Nanostruct Mater. 1997;9:145.

    Article  CAS  Google Scholar 

  9. Rawers JC, Cook DC. Influence of attrition milling on nano-grain boundaries. Nanostruct Mater. 1999;11:331.

    Article  CAS  Google Scholar 

  10. Teus SM, Mazanko VF, Olive JM, Gavriljuk VG. Grain boundary migration of substitutional and interstitial atoms in α-iron. Acta Mater. 2014;69:105.

    Article  CAS  Google Scholar 

  11. Mihalache V. Thermal analysis of ball-milled Fe–14Cr–3W–0.4Ti–0.25Y2O3 ferritic steel powder. Evidence for contamination from the air. J Therm Anal Calorim. 2016;124:1179.

    Article  CAS  Google Scholar 

  12. Lemoine C, Fnidiki A, Lemarchand D, Teillet J. Grain core study of Fe1-xCrx nanograins obtained by mechanical alloying. J Phys Condens Matter. 1999;11:8341.

    Article  CAS  Google Scholar 

  13. Fnidiki A, Lemoine C, Teillet JJ. Structural and magnetic properties of grain boundaries in Fe60Cr40 alloy synthesized by mechanical alloying. J Phys Condens Matter. 2002;14:7221.

    Article  CAS  Google Scholar 

  14. Alleg S, Souilah S, Suñol JJ. Thermal stability of the nanostructured powder mixtures prepared by mechanical alloying. In: Elkordy AA, editor. Applications of calorimetry in a wide context—differential scanning calorimetry, isothermal titration calorimetry and icrocalorimetry. Vienna: InTech Publisher; 2013. p. 21–48.

    Google Scholar 

  15. Azzaza S, Alleg S, Sunol JJ. Microstructure characterization and thermal stability of the ball milled iron powders. J Therm Anal Calorim. 2015;119(2):1037–46.

    Article  CAS  Google Scholar 

  16. Salahinejad E, Amini R, Hadianfard MJ. Structural evolution during mechanical alloying of stainless steels under nitrogen. Powder Technol. 2012;215:247.

    Article  CAS  Google Scholar 

  17. Rawers JC, Maurice D. Understanding mechanical infusion of nitrogen into iron powders. Acta Metall Mater. 1995;43(11):4101–7.

    Article  CAS  Google Scholar 

  18. Hebda M, Gądek S, Skałon M, Kazior J. Effect of mechanical alloying and annealing on the sintering behaviour of AstaloyCrL powders with SiC and carbon addition. J Therm Anal Calorim. 2013;113:395–403.

    Article  CAS  Google Scholar 

  19. Tavares SSM, Fruchart D, Miraglia S, Laborie D. Magnetic properties of an AISI 420 martensitic stainless steel. J Alloys Compd. 2000;312:307.

    Article  CAS  Google Scholar 

  20. Chasoglou D, Hryha E, Nyborg L. Effect of process parameters on surface oxides on chromium-alloyed steel powder during sintering. Mater Chem Phys. 2013;138(138):405–15.

    Article  CAS  Google Scholar 

  21. Hryha E, Nyborg L. Oxide transformation in Cr–Mn-prealloyed sintered steels: thermodynamic and kinetic aspects. Metall Mater Trans A. 2014;45:1736–47.

    Article  CAS  Google Scholar 

  22. Brust S. Transformation of surface oxides during vacuum heat treatment of a powder metallurgical hot work tool steel. Diploma work; 2013.

  23. Calderon RO, Gierl-Mayer C, Danninger H. Application of thermal analysis techniques to study the oxidation/reduction phenomena during sintering of steels containing oxygen sensitive alloying elements. J Therm Anal Calorim. 2017;127:91–105.

    Article  CAS  Google Scholar 

  24. Kirakosyan H, MinasyanT Niazyan O, Aydinyan S, Kharatyan S. DTA/TG study of CuO and MoO3 co-reduction by combined Mg/C reducers. J Therm Anal Calorim. 2016;123:35.

    Article  CAS  Google Scholar 

Download references

Acknowledgements

This work was supported by the European Community in the framework of the European Fusion Development Agreement (EFDA) under Project WP13-MAT-01-ODSFS-01. The views and opinions expressed in this paper do not necessarily reflect those of the European Commission. The Romanian Ministry of Research is acknowledged for the use of their National Institute of Materials Physics facility under the Core Program: Project PN16480103.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Valentina Mihalache.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Mihalache, V., Mercioniu, I., Aldica, G. et al. Thermal analysis, microstructure and impurity phases evolution in Fe14Cr ferritic steel powders ball-milled in air and under an argon atmosphere. J Therm Anal Calorim 134, 463–474 (2018). https://doi.org/10.1007/s10973-018-7274-z

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10973-018-7274-z

Keywords

Navigation