Electrochemical oxide film formation at noble metals as a surface-chemical process

https://doi.org/10.1016/0079-6816(95)00040-6Get rights and content

Abstract

The mechanisms of electrochemical oxide film formation at noble metals are described and exemplified by the cases of Pt and Au, especially in the light of recent experimentation by means of cyclic voltammetry, ellipsometry and vacuum surface-science studies using LEED and AES.

Unlike the mechanisms of base-metal oxidation, e.g., in corrosion processes, anodic oxide film formation at noble metals proceeds by surface chemical processes involving, initially, sub-monolayer, through monolayer, formation of 2-dimensional OHO arrays. During such 2-d processes, place-exchange between electrosorbed OH or O species on the surface, and Pt or Au atoms within the surface lattice, takes place leading to a quasi-2-d compact film which then grows ultimately to a multilayer hydrous oxide film, probably by continuing injection of ions of the substrate metal and their migration through the growing film under the influence of the field.

The initial, sub-monolayer stage of electrosorption of OH involves competitive chemisorption by anions, e.g. HSO4, ClO4, Cl, which inhibits onset of the first stage of surface oxidation. These processes are demonstrable in experiments on single-crystal surfaces. The combination of such anion effects with place-exchange during the extension of the film, leads to a general mechanism of noble metal oxide film formation.

The formation of the oxide films can be examined in detail by recording the distinguishable stages in the film's electrochemical reduction in linear-sweep voltammetry which is sensitive down to OHO fractional coverages as low as 0.5% and over time-scales down to 50μs in experiments on time-evolution and transformation of the states of the oxide films.

By means of LEED, AES and STM or AFM experiments, the reconstructions and perturbations (e.g. generation of stepped terraces) which oxide films cause on singlecrystal surfaces can be followed.

References (252)

  • M.W. Breiter et al.

    J. Electrochem. Soc.

    (1962)
  • W. Böld et al.

    Electrochim. Acta

    (1961)
    W. Bold et al.

    Electrochim. Acta

    (1961)
  • J.O'M. Bockris et al.

    J. Chem. Phys.

    (1968)
  • A.K. Vijh et al.

    Chem. Rev.

    (1967)
  • H. Angerstein-Kozlowska et al.

    J. Electroanal. Chem.

    (1973)
  • J.W. Schultze et al.

    Electrochim. Acta

    (1976)
    J.W. Schultze et al.

    Electrochim. Acta

    (1976)
  • B.E. Conway et al.

    J. Vac. Sci. Technol.

    (1977)
  • B. Tafel

    Zeit. Phys. Chem.

    (1905)
  • A. Bewick et al.

    J. Electroanal. Chem.

    (1975)
  • H. Angerstein-Kozlowska et al.

    J. Electroanal. Chem.

    (1979)
  • B.V. Erschler et al.

    Acta Physiocochim. U.R.S.S.

    (1938)
  • J.F. Armstrong et al.J.F. Armstrong et al.
  • H. Angerstein-Kozlowska et al.

    J. Electroanal. Chem.

    (1964)
  • A.L. Hodgkin et al.

    Nature

    (1939)
    A.L. Hodgkin et al.

    J. Physiol.

    (1952)
  • A. Hickling

    Trans. Faraday Soc.

    (1942)
  • B.E. Conway et al.

    Disc. Faraday Soc.

    (1973)
  • V. Gutmann

    Chemistry in Britain

    (1971)
  • A.N. Frumkin, Zeit, Phys. Chem. 103, 55...A.N. Frumkin

    Zeit. Physik

    (1926)
  • A.N. Frumkin

    Couche Double

    Act. Scient.

    (1936)
  • D.C. Grahame

    Chem. Rev.

    (1947)
  • A.N. Frumkin et al.

    Acta Physicochim. U.R.S.S.

    (1935)
    A.N. Frumkin et al.

    Acta Physicochim. U.R.S.S.

    (1936)
    A.N. Frumkin et al.

    Acta Physicochim. U.R.S.S.

    (1936)
  • A.N. Frumkin et al.

    Acta Physicochim. U.R.S.S.

    (1940)
    A.N. Frumkin et al.

    Acta Physicochim. U.R.S.S.

    (1940)
  • J.A.V. Butler et al.

    Trans. Faraday Soc.

    (1936)
  • J.A.V. Butler et al.

    Trans. Faraday Soc.

    (1938)
  • F.P. Bowden et al.F.P. Bowden et al.F.P. Bowden et al.F.P. Bowden et al.F.P. Bowden et al.
  • F.P. Bowden et al.F.P. Bowden et al.
  • F.P. BowdenF.P. Bowden
  • M. Proskurnin et al.

    Trans. Faraday Soc.

    (1935)
  • M. Barclay et al.

    Trans. Faraday Soc.

    (1940)
  • S. Levina et al.

    Acta Physicochim. U.R.S.S.

    (1936)
  • S. Gilman

    J. Phys. Chem.

    (1962)
    S. Gilman

    J. Phys. Chem.

    (1963)
  • B.E. Conway
  • Y.M. Tyurin et al.

    Elektrokhimiya

    (1972)
    Y.M. Tyurin et al.

    Elektrokhimiya

    (1973)
  • B.E. Conway
  • M.A.H. Lanyon et al.
  • N. Sato et al.

    J. Electrochem. Soc.

    (1964)
    N. Sato et al.

    J. Electrochem. Soc.

    (1964)
  • B. Cabrera et al.

    Rep. Prog. Phys.

    (1949)
  • R. Ghez

    J. Chem. Phys.

    (1973)
  • M. Fleischmann et al.

    J. Electrochem. Soc.

    (1963)
  • R. Woods
  • M.J. Dignam
  • B.E. Conway

    Prog. in Surface Science

    (1984)
  • L.D. Burke
  • B.E. Conway et al.

    Adv. Catalysis

    (1992)
  • G.P. Sakelleropoulos

    Adv. Catalysis

    (1981)
  • H.A. Laitinen et al.

    J. Electrochem. Soc.

    (1960)
  • F.G. Will et al.

    Zeit Elektrochem.

    (1960)
  • B.E. Conway et al.

    Anal. Chem.

    (1973)
  • S.W. Feldberg et al.

    J. Electrochem. Soc.

    (1963)
  • F.C. Anson et al.

    J. Amer. Chem. Soc.

    (1957)
  • Cited by (564)

    View all citing articles on Scopus
    View full text