Two aluminium alloys with nominal compositions of Al-8Fe-4Ce and Al-8Fe-1V-2Si (all compositions in wt %) were rapidly solidified by ultrasonic gas atomization. The atomized powders with an average particle size (d50) of 30 μm were vacuum hot pressed and subsequently hot extruded. The P/M extrusion exhibited similar microstructure and elevated temperature tensile properties. The tensile and stress rupture samples of both the alloys exhibited ductile dimple failure. However, the Al-Fe-V-Si extrusion samples exhibited significantly better creep and stress rupture properties. The Al-Fe-Ce alloy was found to be more susceptible to cavitation at elevated temperatures which resulted in poor stress rupture properties.
Similar content being viewed by others
References
S. K. Das and L. A. Davis, Mater. Sci. and Eng. A 98 (1988) 1.
“Dispersion Strengthened Aluminium Alloys,” edited by Y. W. Kim and W. M. Griffith (AIME, Warrendale, PA, USA, 1988).
E. J. Lavernia, J. D. Ayers and T. S. Srivatsan, Internat. Met. Rev. 37 (1992) 1.
Y. W. Kim in “Dispersion Strengthened Aluminium Alloys,” edited by Y. W. Kim and W. M. Griffith (AIME, Warrendale, PA, USA, 1988) p. 157.
D. J. Skinner in “Dispersion Strengthened Aluminium Alloys,” edited by Y. W. Kim and W. M. Griffith (AIME, Warrendale, PA, USA, 1988) p. 181.
E. Bouchaud, L. Kubin and H. Octor, Metall. Trans. A, 22A (1991) 1021.
I. G. Palmer, M. P. Thomas and G. J. Marshall in “Dispersion Strengthened Aluminium Alloys,” edited by Y. W. Kim and W. M. Griffith (AIME, Warrendale, PA, USA, 1988) p. 217.
D. Legdzina and T. A. Parthasarathy, Metall. Trans. A 21A (1990) 2155.
F. Carreno, G. Gonzalez-Doncel and O. A. Ruano, Mater. Sci. and Engg. A A164 (1993) 216.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Prakash, U., Raghu, T., Gokhale, A.A. et al. Microstructure and mechanical properties of RSP/M Al-Fe-V-Si and Al-Fe-Ce alloys. Journal of Materials Science 34, 5061–5065 (1999). https://doi.org/10.1023/A:1004700830936
Issue Date:
DOI: https://doi.org/10.1023/A:1004700830936