Abstract
Thermal decomposition processes in mixtures of Ca : Cu = 1 : 1 nitrate powders produced by a conventional technique and by freeze drying method have been investigated by thermal analysis and X-ray diffraction. Results have been compared with literature values and data obtained by our investigations of individual calcium and copper nitrates. Temperatures at which decomposition processes occur change with by ±30°C and depend also on the level of mixing of the nitrates. An exemption is the temperature for CuO phase formation, which was determined for the Cu-nitrate and for both 1 : 1-nitrate powders to be at 266°C. The domains of stability for different phases are shown to be variable. Also, for 1 : 1-powders, α-type and β-type Ca(NO3)2 · 2H2O phases coexist, while in Ca-nitrate only the α-type phase was observed.
Similar content being viewed by others
References
S. E. DORRIS, B. C. PROROK, M. T. LANAGAN, S. SINHA and R. B. POEPPEL, Physica C 212 (1993) 66.
M. G. SMITH, J. O WILLIS, D. E. PETERSON, J. F. BINGERT, D. S. PHILLIPS, J. Y. COULTER, K. V. SALAZAR and W. L. HULTS, ibid. 231 (1994) 409.
G. BALESTRINO, R. DESFEUX, S. MARTELLUCCI, A. PAOLETTI, G. PETROCELLI, A. TEBANO, B. MERCEY and M. ERVIEU, J. Mater. Chem. 5 (1995) 1879.
C. ARUTA, G. BALESTRINO, S. MARTELLUCCI, A. PAOLETTI and G. PETROCELLI, J. Appl. Phys. 81 (1997) 220.
A. JEREMIE, G. GRASSO and R. FLUKINGER, Physica C 255 (1995) 53.
A. CRISAN, G. BALESTRINO, S. LAVANGA, P. G. MEDAGLIA and E. MILANI, ibid. 313 (1999) 70.
H. IHARA, K. TOKIWA, H. OZAWA, M. HIRABAYASHI, H. MATUHATA and Y. S. SONG, Jpn. J. Appl. Phys. 33 (1994) L503.
G. BALESTRINO, A. CRISAN, S. LAVANGA, P. G. MEDAGLIA, G. PETROCELLI and A. A. VARLAMOV, Phys. Rev. B 60 (1999) 10 504.
G. ALDICA, P. BADICA, A. F. ALEXEEV and I FRADINA, Analele Univ. Buc. 46 (1997) 173.
B. M. NIRSHA, YU. V. OBOZENKO and A. A. FAKEEV, Neorganitcheskie Mat. 1 (1981) 305.
P. KRISHNARAJ, M. LELOVIC and N. G. EROR, Physica C 215 (1993) 305.
W. WENDAND, J. Texas Sci. 10 (1958) 392.
G. REMN, “Kurs neorganitcheskoi chimii,” edited Mir. Vol. 1 (1972) p. 824.
J. GHOSE and A. KANUNGO, J. Thermal Analysis 20 (1981) 459.
L. ILCHEVA, M. MANEVA and P. BOZADZIEV, ibid. 16 (1979) 205.
P. BADICA, G. ALDICA, G. ALEXE and A. CRISAN, Mater. Lett. 43 (2000) 180.
T. SIEGRIST, R. S. ROTH, C. J. RAWN and J. J. RITTER, Chem Mater. 2 (1990) 192.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Badica, P., Aldica, G. & Crisan, A. Decomposition of Ca : Cu = 1 : 1 nitrate powder: thermal analysis and structural studies. Journal of Materials Science 37, 585–594 (2002). https://doi.org/10.1023/A:1013777826319
Issue Date:
DOI: https://doi.org/10.1023/A:1013777826319