Abstract
The oxygen reduction reaction (ORR) at cobalt tetraazaanulene (CoTAA) modified electrodes was investigated. As a first approach, modified electrodes were prepared by electrodeposition of CoTAA on glassy carbon (GC). The modification of the GC surface was monitored by u.v.–vis. differential reflectance spectroscopy (UVDRS). The recorded spectra (i.e., absorbance as a function of wavelength and time) showed that the electrodeposition of CoTAA at 0.8 V vs Ag|AgCl, that is, at a potential where the TAA ligand is oxidized to TAA+•, seems to produce a thin polymer film. Starting from these preliminary results, porous rotating disc electrodes (RDEs) were prepared by electrodeposition of CoTAA (0.8 V vs Ag|AgCl, 1 min) on graphite powder embedded in a recast Nafion® film. The use of a porous RDE allowed comparison of the activity and selectivity of Pt nanoparticles and CoTAA for the ORR under experimental conditions close to those of a fuel cell cathode, that is, at the catalyst|Nafion® interface. The activity towards the ORR of a porous electrode modified by electrodeposition of CoTAA is not affected when methanol is present in the electrolyte phase, whereas a noticeable decrease in the activity of Pt-based oxygen cathodes was observed under the same conditions. Half-cell life tests showed that CoTAA-modified electrodes and Pt-based electrodes have a comparable stability over a period of 90 min.
Similar content being viewed by others
References
B. Bittins Cattaneo, S. Wasmus, B. Lopez-Mishima and W. Vielstich, J. Appl. Electrochem. 23 (1993) 625.
D. Chu and S. Gilman, J. Electrochem. Soc. 141 (1994) 1770.
P.S. Kauranen and E. Skou, J. Electroanal. Chem. 408 (1996) 189.
H. Alt, H. Binder and G. Sandstete, J. Catal. 28 (1973) 8.
F. Beck, J. Appl. Electrochem. 7 (1977) 239.
K. Wiesner, Electrochim. Acta 31 (1986) 1073.
P. Gouerec, M. Savy and J. Riga, Electrochim. Acta 43 (1998) 743.
Y-H. Tse, P. Janda, H. Lam, J. Zhang, W.J. Pietro and A.B.P. Lever, J. Porphyrins Phtalocyanines 1 (1997) 3.
C.L. Bailey, R.D. Bereman, D.P. Rillema and R. Nowak, Inorg. Chem. 7 (1986) 137.
B. Keita, Y.W. Lu and L. Nadjo, J. Electroanal. Chem. 367 (1994) 285.
C. Miry, D. Le Brun, J-M. Kerboal and M. L'Her, J. Electroanal. Chem., to be published.
F. Gloaguen, P. Convert, S. Gamburzev, O.A. Velev and S. Srinivasan, Electrochim. Acta 43 (1998) 3767.
H. Hiller, P. Dimroth and H. Pfitzner, Liebigs Ann. Chem. 717 (1968) 137.
J.C. Sauer, Organic Synthesis 36 (1956) 66.
A. Rakotondrainibe, A. Spinelli, B. Beden and C. Lamy, Spectrosc. Eur. 5–6 (1993) 20.
I. Bhugun and F.C. Anson, J. Electroanal. Chem. 430 (1997) 155.
P.J. Lukes, A.C. McGregor, T. Clifford and J.A. Crayston, Inorg. Chem. 31 (1992) 4697.
A. El Hourch, A. Rakotondrainibe, B. Beden, P. Crouïgneau, J-M. Léger, C. Lamy, A.A. Tanaka and E.R. Gonzalez, Electrochim. Acta 39 (1994) 889.
P. Ocon, C. Sieiro, J-M. Léger, B. Beden and C. Lamy, Synth. Met. 62 (1994) 9.
E. Yeager, Electrochim. Acta 11 (1984) 1527.
A. Kabbabi, F. Gloaguen, F. Andolfatto and R. Durand, J. Electroanal. Chem. 373 (1994) 251.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Convert, P., Coutanceau, C., Crouïgneau, P. et al. Electrodes modified by electrodeposition of CoTAA complexes as selective oxygen cathodes in a direct methanol fuel cell. Journal of Applied Electrochemistry 31, 945–952 (2001). https://doi.org/10.1023/A:1017596408165
Issue Date:
DOI: https://doi.org/10.1023/A:1017596408165