Abstract
During laser processing to create an Al–SiCp surface metal matrix composite (MMC) layer on AA6061 Al alloy, needle-shaped particles were formed when a high laser energy input was used. Optical microscopy showed this phase to be similar to Al4C3 and Al4SiC4. Previous work was unable to identify the compound as one of those already known in the Al–Si–C system that included Al4C3, Al4SiC4, Al8SiC7, Al4Si2C5 and Al4Si3C6. Therefore, in the present work a phase identification was undertaken on the unknown, using transmission electron microscope (TEM) and the associated energy dispersion analytical X-ray (EDAX) system, together with X-ray diffractometry (XRD). This suggested that the phase was an aluminium silicon carbide having an hexagonal structure with a = 0.3316 and c = 2.1330 nm, which could be a metastable phase formed under the particular laser processing conditions used.
Similar content being viewed by others
References
C. W. DRAPER and J. M. PROATE, Int. Met. Rev. 30 (1995) 85.
A. M. WALKER, W. M. STEEN and D. R. F. WEST, in “Aluminium technology”, edited by T. Sheppard (Institute Metals, London, 1986) p. 712.
H. WOLLMER and E. HORNBOGEN, in “Treatment of materials”, edited by B. L. Mordike (D. G. M. Information, Institute for Metals, London, 1987) p. 163.
N. B. DAHOTRE, T. D. MCCAY and M. H. MCCAY, J. Appl. Phys. 65 (1989) 5072.
A. G. CROOKS and E. HORNBOGEN, Metall. 43 (1989) 957.
T. N. BAKER, H. XIN, C. HU and S. MRIDHA, Mater. Sci. Technol. 10 (1994) 536.
C. HU and T. N. BAKER, J. Mater. Sci. 30 (1995) 891.
C. HU, L. BARNARD, S. MRIDHA and T. N. BAKER, J. Mater. Pro. Technol. 58 (1996) 87.
C. HU, H. XIN and T. N. BAKER, Mater. Sci. Technol. 12 (1996) 227.
X. B. ZHOU and J. T. M. DE HOSSON, Scripta Metall. Mater. 28 (1993) 219.
J. D. AYERS, R. J. SCHAEFER and W. P. ROBEY, J. Met. 33 (1981) 19.
P. SALLAMAND and J. M. PELLETIER, Mater. Sci. Eng. A171 (1993) 263.
C. HU, H. XIN and T. N. BAKER, J. Mater. Sci. 30 (1995) 5985.
V. J. BARCZAK, J. Amer. Ceram. Soc. 44 (1961) 299.
J. SCHOENNAHL, B. MILLER and M. DAIRE, J. Mater. Sci. 4 (1979) 338.
G. SCHNEIDER, L. J. GAUCKLEV, G. PETZOW and A. ZANGVIL, ibid. 62 (1979) 574.
L. L. ODEN and R. A. MCCUNE, Metall. Trans. A 18 (1987) 2005.
J. C. VIALA, P. FORTIER and J. BOUIX, J. Mater. Sci. 25 (1990) 1842.
B. L. KIDWELL, L. L. ODEN and R. A. MCCUNE, J. Appl. Crystallog. 17 (1984) 481.
Z. INOUE, Y. INOMATA, H. TANAKA and H. KAWABATA, J. Mater. Sci. 15 (1980) 575.
R. OSCROFT, P. KORGUL and D. THOMPSON, Brit. Ceram. Proc. 42 (1992) 33.
M. F. ASHBY and K. E. EASTERLING, Acta. Metall. 32 (1984) 1935.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
HU, C., BAKER, T.N. A new aluminium silicon carbide formed in laser processing. Journal of Materials Science 32, 5047–5051 (1997). https://doi.org/10.1023/A:1018653030270
Issue Date:
DOI: https://doi.org/10.1023/A:1018653030270