Abstract
Ag2O-doped (1.2% wt.) nitrate freeze-dried powders (Bi : Pb : Sr : Ca : Cu = 1.7 : 0.3 : 2 : 2.5 : 3.5) were processed under an external electrical field and 17.5 MPa pressure at 800°C, for 4 min in vacuum. Final heat treatments (HT) were applied at 835–850°C for 70 h. in air (Bi, Pb)2Sr2CaCu2O x (2212-phase) was formed by electrical field processing in just 4 min. Electrical field application enhanced (Bi, Pb)2Sr2Ca2Cu3O y (2223-phase) formation during final HT. Ag2O additions to field sintered BSCCO ceramics increased the amount of 2223-phase and the zero resistance critical temperature (T e(R=0)) by ∼ 4 k.
Similar content being viewed by others
References
P. Badica, G. Aldica, J. R. Groza, M. C. Bunescu, and S. Mandache, Supercond. Sci. Technol. 15, 32(2002).
J. R. Groza,ASM Handbook,Vol.7:Powder Metal Technologies and Applications, ASM International Handbook Committee, Ohio, 1998,eds.P. W. Lee,W. B. Eisen,andR. M. German,p.583.
T. T. M. Palstra, B. Batlogg, L. F. Schneemeyer, and J. V. Waszezak, Phys. Rev. B 38, 5102(1988).
T. Hasegawa, H. Kobayashi, H. Kumakura, H. Kitaguchi, and K. Togano, Physica C 222, 111(1994).
G. Aldica, A. F. Alexeev, P. Badica, T. Y. Gridasova, and V. V. Morozov Electronne Stroenie I Svoistava Tugoplavkih Metalov I Soedinenii (in Russian).(Institut Problem Materialovedeniya ‘I N Franztzevitch’, Kiev, 1995),p.95.
T. Hatano, K. Aota, S. Ikeda, K. Nakamura, and K. Ogawa, Jpn. J. Appl. Phys. 27, L2055(1988).
B. J. Reardon and C. R. Hubbard, Powder Diffrac. 7, 142(1992)
Y. T. Huang, C. Y. Shei. W. N. Wang, C. K. Chiang, and W. H. Lee, Physica C 169, 76(1990).
B.HeebL.J.GaucklerT.LangD.BuhlNASAConferencePublication132901994;InProceedingsofthe4thWorldCongressonSuperconductivityJune27-July1K.KristenandBurnhameds.OrlandoFlorida1994p.382eds.K.KrishenandC.Burnham,Vol.2,p.753
C.-H. Shan, S. K. Risbud, K. Yamazaki, and K. Shoda, Mater. Sci. Eng. B 26, 55(1994).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Aldica, G., Groza, J.R., Badica, P. et al. BPSCCO Superconductor with Addition of Ag2O Synthesized Under Electrical Field. Journal of Superconductivity 16, 1001–1005 (2003). https://doi.org/10.1023/A:1026295408106
Issue Date:
DOI: https://doi.org/10.1023/A:1026295408106