Abstract
Xerogels were prepared from zirconium, barium, aluminum, lanthanum and lithium acetates, corresponding to a Li containing ZBLA composition. The study of their thermal properties (DSC, TG/DTG, FT-IR) showed that they might be used as chemically stable precursors in the preparation of fluoride glasses. Hydrofluoric acid in solution was chosen as a mild fluorinating agent. This newly proposed technique of fluorinating allowed to obtain high quality ZBLALi glass which presents the advantage of higher thermal stability and homogeneity in comparison with the glass obtained using individual commercial fluorides.
Similar content being viewed by others
References
M. Poulain, SPIE, 3416 (1998) 2.
J. Ballato, M. Dejneka, R. E. Riman, E. Snitzer and W. M. Zhou, J. Mater. Res., 11 (1996) 841.
K. Miazato, D. F. de Souza, A. Delben, J. R. Delben, S. L. Oliveira and L. A. O. Nunes, J. Non-Cryst. Sol., 273 (2000) 246.
C. J. Brinker and J. W. Scherer, ‘Sol-Gel Science. The Physics and Chemistry of Sol-Gel Processing’, Academic Press, Boston 1990.
M. Zaharescu, A. Jitaianu, A. Braileanu, J. Madarász, Cs. Novák and G. Pokol, J. Therm, Anal. Cal., 71 (2003) 191.
M. Saad and M. Poulain, J. Non-Cryst. Sol., 184 (1995) 352.
R. E. Riman, M. Dejneka, J. Ballato and E. Snitzer, European J. Solid State Inorg. Chem., 32 (1995) 873.
M. Tada, S. Fujihara and T. Kimura, J. Mater. Res., 14 (1999) 1610.
M. Poulain and R. Lebullenger, J. Non-Cryst. Sol., 184 (1995) 166.
M. Odlyha, R. P. W. Scott and C. F. Simpson, J. Thermal Anal., 40 (1993) 1197.
V. Musat Bujoreanu and E. Segal, J. Therm. Anal. Cal., 68 (2002) 191.
K. Nakamoto, Infrared and Raman Spectra of Inorganic and Coordination Compounds, 4th Edition, Wiley Interscience Publication 1985.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Melnikov, P., Rolim, R., Delben, A. et al. Thermal properties of fluoride glasses and their gel precursors. Journal of Thermal Analysis and Calorimetry 75, 87–93 (2004). https://doi.org/10.1023/B:JTAN.0000017331.26326.54
Issue Date:
DOI: https://doi.org/10.1023/B:JTAN.0000017331.26326.54