Abstract
Functionalization of atomically thin nanomaterials enables the tailoring of their chemical, optical and electronic properties. Exfoliated black phosphorus (BP)—a layered two-dimensional semiconductor—exhibits favourable charge-carrier mobility, tunable bandgap and highly anisotropic properties, but it is chemically reactive and degrades rapidly in ambient conditions. Here we show that covalent aryl diazonium functionalization suppresses the chemical degradation of exfoliated BP even after three weeks of ambient exposure. This chemical modification scheme spontaneously forms phosphorus–carbon bonds, has a reaction rate sensitive to the aryl diazonium substituent and alters the electronic properties of exfoliated BP, ultimately yielding a strong, tunable p-type doping that simultaneously improves the field-effect transistor mobility and on/off current ratio. This chemical functionalization pathway controllably modifies the properties of exfoliated BP, and thus improves its prospects for nanoelectronic applications.
This is a preview of subscription content, access via your institution
Access options
Subscribe to this journal
Receive 12 print issues and online access
$259.00 per year
only $21.58 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1038%2Fnchem.2505/MediaObjects/41557_2016_Article_BFnchem2505_Fig1_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1038%2Fnchem.2505/MediaObjects/41557_2016_Article_BFnchem2505_Fig2_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1038%2Fnchem.2505/MediaObjects/41557_2016_Article_BFnchem2505_Fig3_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1038%2Fnchem.2505/MediaObjects/41557_2016_Article_BFnchem2505_Fig4_HTML.jpg)
Similar content being viewed by others
References
Morita, A. Semiconducting black phosphorus. Appl. Phys. A 39, 227–242 (1986).
Tran, V., Soklaski, R., Liang, Y. & Yang, L. Layer-controlled band gap and anisotropic excitons in few-layer black phosphorus. Phys. Rev. B 89, 235319 (2014).
Ling, X., Wang, H., Huang, S., Xia, F. & Dresselhaus, M. S. The renaissance of black phosphorus. Proc. Natl Acad. Sci. USA 112, 4523–4530 (2015).
Kou, L., Chen, C. & Smith, S. C. Phosphorene: fabrication, properties, and applications. J. Phys. Chem. Lett. 6, 2794–2805 (2015).
Das, S. et al. Tunable transport gap in phosphorene. Nano Lett. 14, 5733–5739 (2014).
Liu, H. et al. Phosphorene: an unexplored 2D semiconductor with a high hole mobility. ACS Nano 8, 4033–4041 (2014).
Li, L. et al. Black phosphorus field-effect transistors. Nature Nanotech. 9, 372–377 (2014).
Wang, H. et al. Black phosphorus radio-frequency transistors. Nano Lett. 14, 6424–6429 (2014).
Koenig, S. P., Doganov, R. A., Schmidt, H., Neto, A. C. & Oezyilmaz, B. Electric field effect in ultrathin black phosphorus. Appl. Phys. Lett. 104, 103106 (2014).
Wang, Q. H., Kalantar-Zadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nature Nanotech. 7, 699–712 (2012).
Jariwala, D., Sangwan, V. K., Lauhon, L. J., Marks, T. J. & Hersam, M. C. Emerging device applications for semiconducting two-dimensional transition metal dichalcogenides. ACS Nano 8, 1102–1120 (2014).
Xia, F., Wang, H. & Jia, Y. Rediscovering black phosphorus as an anisotropic layered material for optoelectronics and electronics. Nature Commun. 5, 4458 (2014).
Buscema, M. et al. Fast and broadband photoresponse of few-layer black phosphorus field-effect transistors. Nano Lett. 14, 3347–3352 (2014).
Low, T., Engel, M., Steiner, M. & Avouris, P. Origin of photoresponse in black phosphorus phototransistors. Phys. Rev. B 90, 081408 (2014).
Sun, J. et al. Formation of stable phosphorus–carbon bond for enhanced performance in black phosphorus nanoparticle–graphite composite battery anodes. Nano Lett. 14, 4573–4580 (2014).
Kou, L., Frauenheim, T. & Chen, C. Phosphorene as a superior gas sensor: selective adsorption and distinct I–V response. J. Phys. Chem. Lett. 5, 2675–2681 (2014).
Wood, J. D. et al. Effective passivation of exfoliated black phosphorus transistors against ambient degradation. Nano Lett. 14, 6964–6970 (2014).
Favron, A. et al. Photooxidation and quantum confinement effects in exfoliated black phosphorus. Nature Mater. 14, 826–832 (2015).
Goldwhite, H. Introduction to Phosphorus Chemistry (Cambridge Univ. Press, 1981).
Dreyer, D. R., Park, S., Bielawski, C. W. & Ruoff, R. S. The chemistry of graphene oxide. Chem. Soc. Rev. 39, 228–240 (2010).
Johns, J. E. et al. Metal oxide nanoparticle growth on graphene via chemical activation with atomic oxygen. J. Am. Chem. Soc. 135, 18121–18125 (2013).
Loh, K. P., Bao, Q., Eda, G. & Chhowalla, M. Graphene oxide as a chemically tunable platform for optical applications. Nature Chem. 2, 1015–1024 (2010).
Johns, J. E. & Hersam, M. C. Atomic covalent functionalization of graphene. Accounts Chem. Res. 46, 77–86 (2012).
Voiry, D. et al. Covalent functionalization of monolayered transition metal dichalcogenides by phase engineering. Nature Chem. 45– 49 (2014).
Delamar, M., Hitmi, R., Pinson, J. & Saveant, J. M. Covalent modification of carbon surfaces by grafting of functionalized aryl radicals produced from electrochemical reduction of diazonium salts. J. Am. Chem. Soc. 114, 5883–5884 (1992).
Kariuki, J. K. & McDermott, M. T. Nucleation and growth of functionalized aryl films on graphite electrodes. Langmuir 15, 6534–6540 (1999).
Piao, Y. et al. Brightening of carbon nanotube photoluminescence through the incorporation of sp3 defects. Nature Chem. 5, 840–845 (2013).
Niyogi, S. et al. Spectroscopy of covalently functionalized graphene. Nano Lett. 10, 4061–4066 (2010).
Englert, J. M. et al. Covalent bulk functionalization of graphene. Nature Chem. 3, 279–286 (2011).
Bahr, J. L. et al. Functionalization of carbon nanotubes by electrochemical reduction of aryl diazonium salts: a bucky paper electrode. J. Am. Chem. Soc. 123, 6536–6542 (2001).
Wang, Q. H. et al. Understanding and controlling the substrate effect on graphene electron-transfer chemistry via reactivity imprint lithography. Nature Chem. 4, 724–732 (2012).
Bekyarova, E. et al. Chemical modification of epitaxial graphene: spontaneous grafting of aryl groups. J. Am. Chem. Soc. 131, 1336–1337 (2009).
Koehler, F. M., Jacobsen, A., Ensslin, K., Stampfer, C. & Stark, W. J. Selective chemical modification of graphene surfaces: distinction between single- and bilayer graphene. Small 6, 1125–1130 (2010).
Pelavin, M., Hendrickson, D., Hollander, J. & Jolly, W. Phosphorus 2p electron binding energies. Correlation with extended Hueckel charges. J. Phys. Chem. 74, 1116–1121 (1970).
Blackburn, J. R., Nordberg, R., Stevie, F., Albridge, R. G. & Jones, M. M. Photoelectron spectroscopy of coordination compounds. Triphenylphosphine and its complexes. Inorg. Chem. 9, 2374–2376 (1970).
Sugai, S. & Shirotani, I. Raman and infrared reflection spectroscopy in black phosphorus. Solid State Commun. 53, 753–755 (1985).
Zhang, S. et al. Extraordinary photoluminescence and strong temperature/angle-dependent Raman responses in few-layer phosphorene. ACS Nano 8, 9590–9596 (2014).
Allongue, P. et al. Covalent modification of carbon surfaces by aryl radicals generated from the electrochemical reduction of diazonium salts. J. Am. Chem. Soc. 119, 201–207 (1997).
Paulus, G. L., Wang, Q. H. & Strano, M. S. Covalent electron transfer chemistry of graphene with diazonium salts. Acc. Chem. Res. 46, 160–170 (2012).
Hansch, C., Leo, A. & Taft, R. A survey of Hammett substituent constants and resonance and field parameters. Chem. Rev. 91, 165–195 (1991).
Elofson, R. M. & Gadallah, F. Substituent effects in the polarography of aromatic diazonium salts. J. Org. Chem. 34, 854–857 (1969).
Farmer, D. B. et al. Chemical doping and electron−hole conduction asymmetry in graphene devices. Nano Lett. 9, 388–392 (2008).
Coletti, C. et al. Charge neutrality and band-gap tuning of epitaxial graphene on SiC by molecular doping. Phys. Rev. B 81, 235401 (2010).
Sinitskii, A. et al. Kinetics of diazonium functionalization of chemically converted graphene nanoribbons. ACS Nano 4, 1949–1954 (2010).
Xiang, D. et al. Surface transfer doping induced effective modulation on ambipolar characteristics of few-layer black phosphorus. Nature Commun. 6, 6485 (2015).
Acknowledgements
We acknowledge useful discussions with J. Kang and X. Liu. This research was supported by the Office of Naval Research (N00014-14-1-0669), the Materials Research Science and Engineering Center (MRSEC) of Northwestern University (NSF DMR-1121262), the National Institute of Standards and Technology (NIST CHiMaD 70NANB14H012) and the Department of Energy (DE-FG02-09ER16109). The work made use of the NUANCE Center, which has received support from the MRSEC (NSF DMR-1121262), State of Illinois and Northwestern University. Raman spectroscopy measurements were conducted at Argonne National Laboratory's Center for Nanoscale Materials, a US Department of Energy, Office of Science, Office of Basic Energy Sciences User Facility, under Contract No. DE-AC02-06CH11357.
Author information
Authors and Affiliations
Contributions
C.R.R. conceived the experiments with the assistance of J.D.W. and S.A.W., executed the aryl diazonium chemistry, performed the AFM and Raman spectroscopy measurements and analysis, and prepared the manuscript. J.D.W. performed XPS measurements and analysis and contributed to the analysis of AFM and Raman spectroscopy data. S.A.W. fabricated BP FETs and analysed the device data. Y.Y. conducted DFT calculations and their analysis with the guidance of G.C.S. D.J. assisted with BP FET measurements and analysis. T.J.M. and M.C.H. oversaw the development and execution of the research. All the authors contributed to the revision of the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary information
Supplementary information (PDF 7067 kb)
Rights and permissions
About this article
Cite this article
Ryder, C., Wood, J., Wells, S. et al. Covalent functionalization and passivation of exfoliated black phosphorus via aryl diazonium chemistry. Nature Chem 8, 597–602 (2016). https://doi.org/10.1038/nchem.2505
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/nchem.2505
This article is cited by
-
Chemomechanical modification of quantum emission in monolayer WSe2
Nature Communications (2023)
-
Insight into the growth mechanism of black phosphorus
Frontiers of Physics (2023)
-
Emerging low-dimensional black phosphorus: from physical-optical properties to biomedical applications
Science China Chemistry (2023)
-
Black-phosphorus-based junctions and their optoelectronic device applications
Nano Research (2023)
-
Gas Sensing Properties of Black Phosphorene-Like InP3 Monolayer: A First-Principles Study
Journal of Electronic Materials (2023)