Abstract
Artificial heterostructures composed of dissimilar transition metal oxides provide unprecedented opportunities to create remarkable physical phenomena. Here, we report a means to deliberately control the orbital polarization in LaNiO3 (LNO) through interfacing with SrCuO2 (SCO), which has an infinite-layer structure for CuO2. Dimensional control of SCO results in a planar-type (P–SCO) to chain-type (C–SCO) structure transition depending on the SCO thickness. This transition is exploited to induce either a NiO5 pyramidal or a NiO6 octahedral structure at the SCO/LNO interface. Consequently, a large change in the Ni d orbital occupation up to ~30% is achieved in P–SCO/LNO superlattices, whereas the Ni eg orbital splitting is negligible in C–SCO/LNO superlattices. The engineered oxygen coordination triggers a metal-to-insulator transition in SCO/LNO superlattices. Our results demonstrate that interfacial oxygen coordination engineering provides an effective means to manipulate the orbital configuration and associated physical properties, paving a pathway towards the advancement of oxide electronics.
Similar content being viewed by others
Introduction
The correlated d-orbital plays a central role in creating collective phenomena in transition metal oxides, since the s-electrons of transition metals are transferred to oxygen ions, and the remaining d-electrons determine the delicate interplay between spin, charge, and orbital degrees of freedom1. For example, superexchange can induce either antiferromagnetic or ferromagnetic coupling of spins depending on the orbital filling and ordering, yielding a vast array of magnetic ground states2,3,4,5. In high transition temperature (TC) cuprate superconductors, the x2 − y2 orbital character is crucial for Cooper pairing6. The remarkable Mott metal-insulator transition often found in correlated oxides can be engineered by tailoring the orbital occupancy7. Thus, identifying ways to deliberately control the orbital degree of freedom in correlated oxides is highly desirable to discover electronic and magnetic phenomena that are useful for developing oxide electronic and spintronic devices. Interface engineering is a powerful method to manipulate such orbital degrees of freedom7,8,9,10,11,12,13 and has revealed many intriguing phenomena not possible in bulk material counterparts, such as interfacial charge transfer, orbital covalency, and broken inversion symmetry at nanometer scale12,13,14,15,16,17,18,19.
Rare-earth nickelate (RNiO3) heterostructures provide good experimental and theoretical frameworks to investigate influence of orbital occupation on the physical properties17,18,19,20,21,22,23,24. The d7 ionic configuration of Ni3+ in nickelates contains a full t2g shell and a single electron occupying the eg orbital. This orbital configuration generally favors a Jahn–Teller distortion as observed in LaMnO325. However, the eg orbitals in nickelates are doubly degenerate. A recent theoretical study proposed that the planar x2-y2 orbital order could be realized by spatially confining LaNiO3 into a ultrathin layer between two insulators, leading to a cuprate-like Fermi surface and, subsequently, high TC superconductivity23,24. This idea triggered enormous experimental efforts to study the RNiO3 systems. However the orbital polarization caused by spatial confinement and strain was much smaller than the predicted one17,26,27,28. Resonant inelastic X-ray scattering indicated a very minor eg splitting energy \(( {\Delta E_{e_{\mathrm{g}}}} )\) induced by heterostructural engineering29. It has also been suggested that nickelate thin films prefer to retain their preferred electronic and structural configurations determined by the bulk phase, which limits the control of the orbital parameters through heterostructural engineering30.
Here, we report that one can largely manipulate the occupancy of Ni 3d orbitals in LNO-SrCuO2 (SCO) heterostructures by dimensional control of the SCO layers. The SCO which in the bulk phase is orthorhombic (Cmcm) with a double-chain structure formed in a perovskite like framework with missing apical oxygen in thin films31,32. Upon reducing the thickness when grown in thin films, the planar-type structure of SCO (P–SCO) is transformed to a chain-type structure (C–SCO)33,34,35. The CuO2 planes of P–SCO and C–SCO are parallel and perpendicular with respect to the film plane, respectively. This difference effectively yields two different heterostructures (see Fig. 1a, b). In the case of a P–SCO/LNO heterostructure grown on a B-site terminated ABO3 perovskite substrate, the interfacial atomic stacking sequence is hypothesized to be (CuO2/Sr)/(NiO2/LaO), leading to a truncated NiO5 pyramid structure (see Fig. 1a). On the other hand, the stacking sequence for the C–SCO/LNO interface would become (CuO/SrO)/(NiO2/LaO), which yields an octahedrally coordinated Ni and thus no modification of the LNO structure (see Fig. 1b). Our results demonstrate how the unique infinite-layer structure offered in SCO can be utilized to induce a very large Ni 3d orbital polarization in P–SCO/LNO superlattices or to create degenerate (i.e., little or no polarization) Ni eg orbitals in C–SCO/LNO superlattices as sketched in Fig. 1a, b. The observed changes in the electronic and orbital states may have a profound impact on transport properties of SCO/LNO superlattices.
Results
Dimensional control of the sub-lattice structure of SrCuO2
LNO and SCO films and their superlattices were grown on TiO2 terminated (001) SrTiO3 (STO) substrates by pulsed laser epitaxy. The growth condition was optimized to achieve high-quality SCO films in the bulk planar structure (see Supplementary Fig. 1), and all films were atomically flat with step-terrace features on their surfaces (See Supplementary Fig. 2). As shown in Fig. 1c, X-ray diffraction (XRD) θ–2θ scans of an 80 unit-cell (u.c.) SCO film revealed clearly the SCO 002 peak near 2θ = 53o, confirming the bulk-like infinite-layer structure33,34. Using the same growth conditions, high-quality LNO films were obtained as well. When growing (SCON/LNO1)M superlattices (noted as SN/L1), a systematic change in XRD spectra was observed with increasing the SCO layer thickness. Since the P–SCO and C–SCO have quite different out-of-plane lattice constants of ~3.45 Å (2θ = 53o) and ~3.8 Å (2θ = 47.8o), respectively33,35, the position of the main superlattice peak SL(0) can be used to identify the SCO structure type. For relatively thick SCO layers (e.g., N = 7 u.c.), SL(0) was located between the SCO 002 and the LNO 002 XRD peaks, suggesting the formation of the planar-type SCO structure within the superlattice. When the SCO layer thickness is reduced to 2 u.c., the SL(0) peak shifts close to the LNO 002 peak, indicating that 2 u.c.-thick SCO has a similar out-of-plane lattice constant with that of LNO. This result suggests that a chain-type SCO structure was formed in the S2/L1 superlattice. With increasing the SCO film thickness to 5 u.c., a sudden large shift of the superlattice peaks occurred. This shift suggests the critical thickness of the phase conversion from P–SCO to C–SCO to be at 5 u.c.. This thickness-driven transition of the SCO structure in SCO/LNO superlattices was also observed for other LNO sublayer thicknesses (see Supplementary Fig. 3).
Further evidence of the structural transition triggered by reducing the SCO thickness was observed from XRD reciprocal space mapping (RSM). The RSM shown in Fig. 2a indicates that all the superlattices and reference SCO and LNO films were coherently grown on STO substrates. The reciprocal lattice vector (qz) of thick SCO superlattices (e.g., N = 7 and 16 in SN/L1) was very close to that of a P–SCO film, confirming that the SCO layers in the superlattices possess the bulk-like planar-type structure. On the other hand, the qz of thin SCO superlattices (N = 2–4) was similar to that of a LNO film. Interestingly, as shown in Fig. 2b, the SCO thickness dependent change in the out-of-plane lattice constant (cSL) calculated from the RSMs around the 103 peak (cSL = 3/qz) clearly reveals a sudden transition at around 5 u.c. of the SCO sublayer thickness. If the bulk-like P–SCO is maintained when the SCO thickness is reduced, one can only expect a gradual increase in cSL. Therefore, our observation of the step-like transition shown in Fig. 2a, b unambiguously demonstrates that the planar-type lattice structure of SCO can be converted into the chain-type structure by reducing the SCO thickness below 5 u.c. Detailed XRD and transport analyses further suggest the formation of a twin domain structure within the chain-type SCO (see supplementary Fig. 4), originating from the two-fold symmetry of C–SCO on the four-fold (001) STO substrate.
Such a change in the orientation of the oxygen plane can be confirmed as a change in the orbital occupancy measured from linearly polarized X-ray absorption spectroscopy (XAS) acquired in fluorescence yield (FY) mode. The orbital occupancy of Cu x2-y2 and 3z2-r2 orbitals was probed by the XAS measured with in-plane (σ) and out-of-plane (π) polarized x-rays, respectively. As shown in Fig. 2c, the large I(σ) versus I(π) XAS of the Cu L2,3-edge of the S7/L1 superlattice indicates exclusive \(3d_{x^2 - y^2}\) character, consistent with orbital configuration in layer-structured cuprates (see supplementary Fig. 5). By contrast, I(σ) and I(π) share a similar intensity and shape for the S3/L1 superlattice, suggesting the chain-type SCO structure and \(3d_{y^2 - z^2}\)orbital character36. Additionally, the change in the SCO microstructure and oxygen coordination of Ni were confirmed by scanning transmission electron microscopy (STEM) (see Supplementary Fig. 6), consistent with XRD and XAS data.
Engineered Ni orbital polarization in SrCuO2-LaNiO3 superlattices
Now we turn to investigate the reconstruction of the Ni eg orbital. Figure 3a shows the XAS of the Ni L2-edge of an S7/L1 superlattice. Since the Ni L3-edge largely overlaps with the La M-edge, and FY of the La3+ (4f0) M-edge deviates from the true XAS for the conventional detection geometry used, the Ni L2-edge is more suitable to illustrate the orbital reconstruction (see supplementary Fig. 7)17. The I(σ) exhibits a higher intensity than I(π), indicating that holes prefer to occupy the \(3d_{x^2 - y^2}\)orbital. For the S3/L1 superlattice, the I(σ) and I(π) intensities are similar to each other. Therefore, the Ni eg orbital is degenerate (Fig. 3b). The different orbital configuration between the S7/L1 superlattice and the S3/L1 superlattice is also observed in total electron yield mode (see supplementary Fig. 7), indicating that the observed polarization dependence of the FY XAS originates from the intrinsic orbital polarization. The orbital configuration in the S3/L1 superlattice confirms the chain-type SCO structure within the S3/L1 superlattice, which recovers the octahedral coordination. Using the difference between in-plane polarized absorption I(ab) and out-of-plane polarized absorption I(c), the ratio of unoccupied states, r, can be quantified using the following sum rule17,37
Here, a, b, and c are the Cartesian coordination axis of the substrates with c along out-of-plane direction and h is the hole occupancy. The π-polarized absorption I(π) was corrected for the angle θ = 20o between the incident X-rays and sample plane in our experimental setup using I(c) = [I(π) − I(ab)sin2θ]/cos2θ, while the orientation of the incident beam with respect to the sample did not affect I(σ) and I(ab) = I(σ). The linear dichroism (LD) [LD = I(c) − I(ab)] shown in Fig. 3a, b further emphasizes the orbital polarization of the S7/L1 superlattice. Using the integrated intensity of I(ab) and I(c) from background-subtracted XAS, the hole ratio r can be quantified (see supplementary Fig. 8). The r values for S7/L1 and S3/L1 superlattices are 0.7 and 1.0, respectively, suggesting a predominant x2 − y2 hole character in S7/L1 and degenerate orbital in S3/L1. Previously, the r value of the largest orbital polarization \([ {P = ( {n_{x^2 - y^2} - n_{3z^2 - r^2}} )/( {n_{x^2 - y^2} + n_{3z^2 - r^2}} )} ]\) achieved by inducing tensile strain was ~1.1926. The spatial confinement in LAO/LNO superlattices has been reported to result in a value of r ~ 1.0517,27. The hole ratio that we observed cannot be compared directly to these previous values since our experiments had a flipping orbital configuration in which the \(3d_{3z^2 - r^2}\)orbital has more hole occupancy. The relative change of occupancy (≡|1 − r|) is instead used here for a quantitative comparison. In comparison to ~19% by strain26 and ~5% by spatial confinement17,27, the observed 30% change of Ni orbital occupancy in P–SCO/LNO superlattice confirms the significant impact of oxygen coordination on orbital reconstruction.
The prevailing \(3d_{x^2 - y^2}\) character cannot be explained by spatial confinement, which favors the \(3d_{3z^2 - r^2}\) hole occupancy due to the confinement of the \(3d_{3z^2 - r^2}\) orbital in the z direction17,23,24,38. We attribute the observed large orbital polarization in the S7/L1 superlattice to the NiO5 pyramid structure, which is expected to lower the \(3d_{3z^2 - r^2}\) with respect to \(3d_{x^2 - y^2}\)39. In fact, our polarization dependent XAS revealed quite similar features to the square-planar La4Ni3O8 and YBa2Cu3O7 (YBCO) single crystals36,40. The La4Ni3O8 is comprised of NiO2 planar structures while the main building block of YBCO is a CuO5 pyramid40,41. These two materials possess similar eg band structures with the \(3d_{3z^2 - r^2}\) lying lower than \(3d_{x^2 - y^2}\). In sharp contrast, there is a negligible orbital polarization when the apical oxygen is retained in the S3/L1 superlattice. Although there is still tensile strain on LNO within the S3/L1 superlattice, the observed degenerate eg orbital indicates that the octahedrally coordinated Ni prefers to retain a bulk-like electronic configuration. This retainment of bulk orbital configuration was reported previously30 and is also observed in our LNO films (see Supplementary Fig. 9). The corresponding eg orbital energy diagrams for the NiO5 pyramid and the NiO6 octahedron are schematically plotted in Fig. 3c (S7/L1) and Fig. 3d (S3/L1). Using the outermost filled orbital, a sketch of the orbital configuration in SCO/LNO superlattice is plotted Fig. 1a, b, demonstrating the designed orbital configuration through heterostructural engineering.
The charge states of Cu and Ni at interfaces
The charge states of Cu and Ni are further investigated using XAS. As shown in Fig. 4a, the Cu L-edge spectrum of a S7/L1 superlattice shows a characteristic Cu2+ feature as observed in SCO films36,42. Meanwhile, the S3/L1 superlattice shows a strong shoulder at ~933.28 eV, which is positioned ~1 eV higher than that of the Cu2+ peak and is consistent with the d9L state36,42. Here L represents the ligand hole. The doped holes are unlikely from interfacial charge transfer, since the Ni in S3/L1 maintains Ni3+ as demonstrated by the lack of Ni L-edge shift (see Fig. 4b). Further, La interdiffusion should favor Cu1+. It is more likely that the hole arises from oxygen excess SrCuO2+x. For the S7/L1 superlattice, the Ni L-edge shifts by about −0.3 eV relative to that of the LNO film. Since a 1 eV shift corresponds to roughly one electron valence change43,44, the energy shift suggests an averaged Ni2.7+ valence state in S7/L1. It has been reported that doped electrons at a LNO/La2CuO4 interface are predominantly accommodated by change of Ni valence45. A similar situation may occur for a SCO/LNO interface where a possible formation of oxygen vacancies may dope the interface state with electrons.
Controlled metal-to-insulator transition
Functionally, we see that these observed changes to electronic and orbital states have a profound impact on transport properties of SCO/LNO superlattices. Figure 5a shows the transport properties of SN/L1 superlattices with different SCO thicknesses. The SN/L1 superlattices exhibit a metallic behavior (dR/dT > 0) to insulating behavior (dR/dT < 0) transition (MIT) with increasing the SCO layer thickness. The critical thickness for MIT is 5 u.c., which coincides with the critical thickness for a structural transition (see Fig. 2). This fact suggests that the P–SCON/LNO1 and C–SCON/LNO1 superlattices are insulating and metallic, respectively. Since LNO will undergo a MIT with reducing thickness across ~3–5 u.c.46,47,48,49, the single unit-cell LNO should be insulating and thus the metallic behavior arises from the C–SCO layer, which can be explained by the hole doping as observed by XAS (see Fig. 4a).
Figure 5b, c show the LNO layer thickness dependent transport properties in P–SCO7/LN and C–SCO3/LN superlattices, respectively. With reducing thickness of LNO layers, the P–SCO7/LN superlattices gradually evolve from a metallic state to an insulating state. Such behavior is similar to MIT in single LNO films, which is associated with dimensional crossover46,49. What is more, the 3 u.c. critical thickness for MIT in P–SCO7/LN is also similar to bare LNO films46,47,48,49. These results strongly suggest that the MIT in P–SCO7/LN is driven by LNO sub-layers. Since the C–SCO is metallic, all C–SCO3/LN superlattices exhibit good metallic behavior regardless of the thickness of LNO (see Fig. 5c). However, there is still a sharp decrease of the resistance when the LNO thickness is reduced from N = 3 to 2 u.c., while the C–SCO3/L1 and C–SCO3/L2 showed similar resistance values. This result implies a MIT in the LNO layers when reducing LNO thickness from 3 to 2 u.c. The different critical thickness (tc) for MIT of LNO in P–SCO7/LN (tc = 3) and in C–SCO3/LN (tc = 2) indicates that a MIT in 3 u.c. LNO sublayer occurs when the top surface of the LNO layer is transformed from the octahedral coordination to the pyramidal coordination (Fig. 5d, e). This result is further emphasized by comparing the resistance of P–SCO7/L3 with C–SCO7/L3 superlattices in Fig. 5f. Although the metallic C–SCO layer also contributes to the transport, the transport behavior of C–SCO3/L3 is dominated by the LNO layer since the resistance of C–SCO3/L1 is ~2 times larger than that of C–SCO3/L3. To further confirm the effect of oxygen coordination on transport, we measured the transport properties of STO7/LN superlattices where the LNO interface has the same octahedral coordination as that in C–SCO3/L3. The critical thickness for MIT in STO7/LN is 2 u.c. (see Supplementary Fig. 10), which is the same with C–SCO3/LN superlattices and thinner than P–SCO7/LN superlattices. This indicates that recovering the top pyramid NiO5 in P–SCO7/L3 to a full octahedral structure in STO7/L3 or C–SCO3/L3 will drive the LNO layer to be metallic. As shown in Fig. 5f, the STO7/L3 is metallic and has a similar resistance with C–SCO3/L3. The relative small change of resistance from P–SCO7/L3 to STO7/L3 is due to the crossover MIT in LNO and also the fact that P–SCO is not a good insulator and contributes to the transport as well. Higher LNO resistance in P–SCO/LNO superlattices could be due to the reduced oxygen coordination, as observed in bare LNO films50,51. The smaller Ni eg bandwidth in pyramidal coordination and reduced in-plane electron hopping strength due to preferential 3z2-r2 orbital occupation would increase the resistance. Further, the appearance of Ni2+ may also play a role by opening a charge excitation gap38,43.
Discussion
In conclusion, we have demonstrated that the orbital polarization and transport properties of SCO/LNO superlattices can be manipulated by templating the infinite structure of SCO into LNO through dimensionally controlling the oxygen coordination. Reducing the SCO thickness below 5 u.c. resulted in a structural transition from a planar-type to a chain-type structure. At SCO/LNO interfaces, the planar-type SCO structure induced a NiO5 pyramidal structure in LNO, whereas the chain-type SCO structure yielded a NiO6 octahedron in LNO, allowing us to selectively control the out-of-plane and in-plane orbital occupancies. This type of oxygen coordination manipulation could enhance the Ni orbital polarization up to ~30%. This enhancement is larger than that achieved from other means, including by strain (~19%) or spatial confinement (~5%). Our findings unambiguously demonstrate how the interfacial oxygen coordination engineering can effectively manipulate the orbital configuration and electronic properties, providing a possible new approach to realizing superconducting nickelates with high Tc. The oxygen coordination control using SCO as a template could also be applied to other perovskites to explore previously inaccessible orbital-driven phenomena.
Methods
Sample growth
All superlattices and thin films were grown on TiO2 terminated (001) SrTiO3 substrates by pulsed laser epitaxy using a KrF excimer laser (λ = 248 nm). The single TiO2 terminated and atomically flat SrTiO3 substrates were obtained by the etching with standard buffered-HF and subsequent annealing at 950 oC for 1.5 h. The laser fluence and repetition rate were fixed at 2 J cm−2 and 5 Hz, respectively. The oxygen partial pressure and substrate temperature were maintained at 100–150 mTorr and 650 oC, respectively.
Sample characterization
The surface morphology was characterized by atomic force microscopy. The lattice structure was characterized by a high-resolution four-circle X-ray diffractometer. Transport measurements were performed in a van-der-Pauw geometry using a Physical Property Measurement System. The TEY and FY XAS measurements of the Cu and Ni edges were performed at the beamline 4–ID–C of the Advanced Photon Source. XAS was measured at 300 K, with the X-rays at a grazing (20°) angle to the films surface, and the TFY detector at 90° from the incoming X-rays.
Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
References
Tokura, Y. & Nagaosa, N. Orbital physics in transition-metal oxides. Science 288, 462–468 (2000).
Goodenough, J. B. Theory of the role of covalence in the perovskite-type manganites [La,M(II)]MnO3. Phys. Rev. 100, 564–573 (1955).
Goodenough, J. B. An interpretation of the magnetic properties of the perovskite-type mixed crystals La1−xSrxCoO3−λ. J. Phys. Chem. Solids 6, 287–297 (1958).
Kanamori, J. Superexchange interaction and symmetry properties of electron orbitals. J. Phys. Chem. Solids 10, 87–98 (1959).
Tokura, Y. & Tomioka, Y. Colossal magnetoresistive manganites. J. Magn. Magn. Mater. 200, 1–23 (1999).
Keimer, B., Kivelson, S. A., Norman, M. R., Uchida, S. & Zaanen, J. From quantum matter to high-temperature superconductivity in copper oxides. Nature 518, 179–186 (2015).
Aetukuri, N. B. et al. Control of the metal–insulator transition in vanadium dioxide by modifying orbital occupancy. Nat. Phys. 9, 661–666 (2013).
Hwang, H. Y. et al. Emergent phenomena at oxide interfaces. Nat. Mater. 11, 103–113 (2012).
Ohshima, R. et al. Strong evidence for d-electron spin transport at room temperature at a LaAlO3/SrTiO3 interface. Nat. Mater. 16, 609–614 (2017).
Matsuno, J. et al. Interface-driven topological Hall effect in SrRuO3-SrIrO3 bilayer. Sci. Adv. 2, e1600304 (2017).
Chakhalian, J. et al. Orbital reconstruction and covalent bonding at an oxide interface. Science 318, 1114–1117 (2007).
Chakhalian, J. et al. Magnetism at the interface between ferromagnetic and superconducting oxides. Nat. Phys. 2, 244–248 (2006).
Okamoto, S. et al. Charge Transfer in Iridate-Manganite Superlattices. Nano. Lett. 17, 2126–2130 (2017).
Nichols, J. et al. Emerging magnetism and anomalous Hall effect in iridate–manganite heterostructures. Nat. Commun. 7, 12721 (2016).
Lee, H. N., Christen, H. M., Chisholm, M. F., Rouleau, C. M. & Lowndes, D. H. Strong polarization enhancement in asymmetric three-component ferroelectric superlattices. Nature 433, 395–399 (2005).
Petrie, J. R. et al. Enhanced bifunctional oxygen catalysis in strained LaNiO3 perovskites. J. Am. Chem. Soc. 138, 2488–2491 (2016).
Benckiser, E. et al. Orbital reflectometry of oxide heterostructures. Nat. Mater. 10, 189–193 (2011).
Frano, A. et al. Orbital control of noncollinear magnetic order in nickel oxide heterostructures. Phys. Rev. Lett. 111, 106804 (2013).
Disa, A. S. et al. Orbital engineering in symmetry-breaking polar heterostructures. Phys. Rev. Lett. 114, 026801 (2015).
Gibert, M., Zubko, P., Scherwitzl, R., Íñiguez, J. & Triscone, J.-M. Exchange bias in LaNiO3-LaMnO3 superlattices. Nat. Mater. 11, 195–198 (2012).
Grisolia, M. N. et al. Hybridization-controlled charge transfer and induced magnetism at correlated oxide interfaces. Nat. Phys. 12, 484–492 (2016).
van Veenendaal, M. Anomalous ground states at the interface between two transition-metal compounds. Phys. Rev. B 78, 165415 (2008).
Chaloupka, J. & Khaliullin, G. Orbital order and possible superconductivity in LaNiO3/LaMO3 superlattices. Phys. Rev. Lett. 100, 016404 (2008).
Hansmann, P. et al. Turning a nickelate fermi surface into a cupratelike one through heterostructuring. Phys. Rev. Lett. 103, 016401 (2009).
Sawada, H., Morikawa, Y., Terakura, K. & Hamada, N. Jahn-Teller distortion and magnetic structures in LaMnO3. Phys. Rev. B 56, 12154 (1997).
Wu, M. et al. Strain and composition dependence of orbital polarization in nickel oxide superlattices. Phys. Rev. B 88, 125124 (2013).
Freeland, J. W. et al. Orbital control in strained ultra-thin LaNiO3/LaAlO3 superlattices. Europhys. Lett. 96, 57004 (2011).
Disa, A. S., Walker, F. J., Ismail-Beigi, S. & Ahn, C. H. Research update: orbital polarization in LaNiO3-based heterostructures. APL Mater. 3, 062303 (2015).
Fabbris, G. et al. Orbital engineering in nickelate heterostructures driven by anisotropic oxygen hybridization rather than orbital energy levels. Phys. Rev. Lett. 117, 147401 (2016).
Tung, I. C. et al. Connecting bulk symmetry and orbital polarization in strained RNiO3 ultrathin films. Phys. Rev. B 88, 205112 (2013).
Teske, C. L. & Mueller-Buschbaum, H. Über Erdalkalimetall‐Oxocuprate, V. Zur Kenntnis von Ca2CuO3 und SrCuO2. Z. Anorg. Allg. Chem. 379, 234–241 (1970).
Norton, D. P. et al. Superconductivity in SrCuO2-BaCuO2 superlattices: formation of artificially layered superconducting materials. Science 265, 2074–2077 (1994).
Zhong, Z. C., Koster, G. & Kelly, P. J. Prediction of thickness limits of ideal polar ultrathin films. Phys. Rev. B 85, 121411(R) (2012).
Harter, J. W. et al. Doping evolution and polar surface reconstruction of the infinite-layer cuprate Sr1−xLaxCuO2. Phys. Rev. B 92, 035149 (2015).
Samal, D. et al. Experimental evidence for oxygen sublattice control in polar infinite layer SrCuO2. Phys. Rev. Lett. 111, 096102 (2013).
Hawthorn, D. G. et al. Resonant elastic soft x-ray scattering in oxygen-ordered YBa2Cu3O6+δ. Phys. Rev. B 84, 075125 (2011).
van der Laan, G. Sum rules and fundamental spectra of magnetic X-Ray dichroism in crystal field symmetry. J. Phys. Soc. Jpn. 63, 2393–2400 (1994).
Cao, Y. W. et al. Engineered Mott ground state in a LaTiO3/LaNiO3 heterostructure. Nat. Commun. 7, 10418 (2015).
Chancey, C. C. & O’Brien, M. C. M. The Jahn-Teller effect: An introduction and current review. Am. J. Phys. 61, 688–697 (1993).
Zhang, J. J. et al. Large orbital polarization in a metallic square-planar nickelate. Nat. Phys. 13, 864–869 (2017).
Izumi, F. et al. Crystal structure of the orthorhombic form of Ba2YCu3O7-x at 42 K. Jpn. J. Appl. Phys. 26, L1193–L1196 (1987).
Chen, C. T. et al. Out-of-plane orbital characters of intrinsic and doped holes in La2-xSrxCuO4. Phys. Rev. Lett. 68, 2543 (1992).
Guo, E. J. et al. Oxygen diode formed in nickelate heterostructures by chemical potential mismatch. Adv. Mater. 30, 1705904 (2018).
Liu, J. et al. Effect of polar discontinuity on the growth of superlattices. Appl. Phys. Lett. 96, 133111 (2010).
Wrobel, F. et al. Digital modulation of the nickel valence state in a cuprate-nickelate heterostructure. Phys. Rev. Mater. 2, 035001 (2018).
Scherwitzl, R. et al. Metal-insulator transition in ultrathin LaNiO3 Films. Phys. Rev. Lett. 106, 246403 (2011).
Boris, A. V. et al. Dimensionality control of electronic phase transitions in nickel-oxide superlattices. Science 332, 937–940 (2011).
King, P. D. C. et al. Atomic-scale control of competing electronic phases in ultrathin LaNiO3. Nat. Nanotechnol. 9, 443–447 (2014).
Sakai, E. et al. Gradual localization of Ni 3d states in LaNiO3 ultrathin films induced by dimensional crossover. Phys. Rev. B 87, 075132 (2013).
Kumah, D. P. et al. Effect of surface termination on the electronic properties of LaNiO3 films. Phys. Rev. Appl. 2, 054004 (2014).
Kumah, D. P. et al. Tuning the structure of nickelates to achieve two-dimensional electron conduction. Adv. Mater. 26, 1935 (2014).
Acknowledgements
This work was supported by the U.S. Department of Energy (DOE), Office of Science, Basic Energy Sciences (BES), Materials Sciences and Engineering Division. Use of the Advanced Photon Source, an Office of Science User Facility operated for the U.S. DOE, Office of Science by Argonne National Laboratory, was supported by the U.S. DOE under Grant No. DEAC02-06CH11357. Part of XAS measurements and experimental assistance for thin film synthesis by E.G., R.D., T.Z., T.C. and M.R.F. were supported by the DOE, BES, Scientific User Facilities Division.
Author information
Authors and Affiliations
Contributions
Z.L. performed the sample synthesis with help of T.Z. Z.L. conducted the structural and basic physical property characterization with help of C.S., A.R. and T.Z.W.. E.S., E.G., R.D., C.S., A.R., Z.L. and J.F. performed XAS measurements. X.G. performed STEM characterization. Z.L., E.S., E.G., T.Z.W., T.C., M.R.F. and H.N.L. discussed the results. Z.L. and H.N.L. designed the experiment and wrote the manuscript with inputs from all authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Journal peer review information: Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Liao, Z., Skoropata, E., Freeland, J.W. et al. Large orbital polarization in nickelate-cuprate heterostructures by dimensional control of oxygen coordination. Nat Commun 10, 589 (2019). https://doi.org/10.1038/s41467-019-08472-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-08472-y
This article is cited by
-
Dimensional control of interface coupling-induced ferromagnetism in CaRuO3/SrCuO2 superlattices
NPG Asia Materials (2024)
-
Tuning orbital-selective phase transitions in a two-dimensional Hund’s correlated system
Nature Communications (2023)
-
Overview of magnetic anisotropy evolution in La2/3Sr1/3MnO3-based heterostructures
Science China Materials (2023)
-
Atomic and electronic structures of correlated SrRuO3/SrTiO3 superlattices
Journal of the Korean Physical Society (2023)
-
Interfacial engineering manipulation of magnetic anisotropy evolution via orbital reconstruction in low-dimensional manganite superlattices
Science China Materials (2022)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.