Abstract
The outdoor service life of common plastic materials is limited by their susceptibility to solar ultraviolet radiation. Of the solar wavelengths the UV-B component is particularly efficient in bringing about photodamage in synthetic and naturally occurring materials. This is particularly true of plastics, rubber and wood used in the building and agricultural industries. Any depletion in the stratospheric ozone layer and resulting increase in the UV-B component of terrestrial sunlight will therefore tend to decrease the service life of these materials. The extent to which the service life is reduced is, however, difficult to estimate as it depends on several factors. These include the chemical nature of the material, the additives it contains, the type and the amount of light-stabilizers (or protective coatings) used, and the amount of solar exposure it receives. Concomitant climate change is likely to increase the ambient temperature and humidity in some of the same regions likely to receive increased UV-B radiation. These factors, particularly higher temperatures, are also well known to accelerate the rate of photodegradation of materials, and may therefore further limit the service life of materials in these regions. To reliably assess the damage to materials as a consequence of ozone layer depletion, the wavelength sensitivity of the degradation process, dose-response relationships for the material and the effectiveness of available stabilizers need to be quantified. The data needed for the purpose are not readily available at this time for most of the commonly used plastics or wood materials. Wavelength sensitivity of a number of common plastic materials and natural biopolymers are available and generally show the damage (per photon) to decrease exponentially with the wavelength. Despite the relatively higher fraction of UV-A in sunlight, the UV-B content is responsible for a significant part of light-induced damage of materials.
The primary approach to mitigation relies on the effectiveness of the existing light stabilizers (such as hindered amine light stabilizers, HALS) used in plastics exposed to harsh solar UV conditions coupled with climate change factors. In developing advanced light-stabilizer technologies, more light-resistant grades of common plastics, or surface protection technologies for wood, the harsh weathering environment created by the simultaneous action of increased UV-B levels due to ozone depletion as well as the relevant climate change factors need to be taken into consideration. Recent literature includes several studies on synergism of HALS-based stabilizers, stabilizer effectiveness in the new m-polyolefins and elucidation of the mechanism of stabilization afforded by titania pigment in vinyl plastics.
Similar content being viewed by others
Reference
A. Torikai, Wavelength sensitivity of the photodegradation of polymers, in Handbook of Polymer Degradation, Second Edition, ed. S.H. Hamid, Marcel Dekker, New York, 2000, pp. 573–604.
J. F. Rabek, Polymer Photodegradation, Chapman and Hall, New York,1995.
M. Johansson, G. Gellerstedt, Chromophoric content in wood and mechanical pulps Nord. Pulp. Pap. Res. J., 2000, 15, 282–286.
F. G. Lennox, M. G. King, I. H. Leaver, G. C. Ramsey, W. E. Savige, Mechanism of prevention and correction of wool photoyellowing Applied Polymer Symposium., 1971, 18353–18369.
A. Sionkowska, Modification of collagen films by ultraviolet irradiation Polym. Degrad. Stab., 2000, 68, 147–151.
M. S. Jahan, T. R. Drouuin, R. M. Sayre, Effect of humidity on photoinduced ESR signal from human hair Photochem. Photobiol., 1987, 45.
F. H. Winslow, W. Matreyek, A. M. Trozzolo, Weathering of polymers Soc. Plast. Eng. Tech. Pap., 1972, 18, 766–772.
IPCC, Climate Change, 2001: The Scientific Basis, IPPC Report No 3.
E. B. Rabonavitch, J. G. Queensberry, J. W. Summers, Predicting heat building up due to sun’s energy J. Vinyl Technol., 1983, 5, 110–115.
J. Fuwape and S. Adedunter, Performance of UV absorbers in plastics and coatings, in Handbook of Polymer Degradation, Second Edition, ed. S.H. Hamid, Marcel Dekker Inc., New York, 2000, pp. 163–190.
R. Gardner, J. Martin, Humid aging of plastics. Effect of molecular weight on the mechanical properties and fracture morphology of polycarbonate J. Appl. Polymer Sci., 1979, 24, 1269.
Y. Nagai, T. Ogawa, Y. Nishimoto, F. Ohishi, Analysis of weathering of a thermoplastic polyester Elastomer II. Factors affecting weathering of a polyether-polyester elastomer Polym. Degrad. Stab., 1999, 65, 217–224.
V. Godard, M. Triboulet, A. Merlin, M. Andre, Photostabilization of natural and weathered wood Pint. Acadbados Ind., 2001, 42, 36–46.
C. Hill, C. Nihat, An investigation of the potential for chemical modification and subsequent polymeric grafting as a means of protecting wood against photodegradation Polym. Degrad. Stab., 2001, 72, 133–139.
A. L. Andrady, Effect of increased solar ultraviolet radiation on materials J. Photochem. Photobiol., 1998, 46, 96–103.
A. L. Andrady, Wavelength sensitivity in polymer photodegradation Adv. Polymer Sci., 1997, 128, 49–94.
A. L. Andrady, A. Torikai, Photoyellowing of mechanical pulps III Polym. Degrad. Stab., 1998, 66, 317–322.
A. Torikai, Wavelength sensitivity in the photodegradation of polymethylmethcrylate: Accelerated degradation and gel formation, in Science and Technology of Polymers and Advanced Materials, ed. P.N. Prasad, Plenum Press, New York, 1999, pp. 581–586.
A. Torikai, H. Shibata, Effect of ultraviolet radiation on photodeegradation of collagen J. Appl. Polymer Sci., 1999, 73, 1259–1265.
F. Gugumus, Possibilities and limits of synergism with light stabilizers in polyolefins 1. HALS in polyolefins Polym. Degrad. Stab., 2002, 75, 295–309.
J. Pan, S. Cui, Study of the photolysis of a commercial hindered amine light stabilizer Polym. Degrad. Stab., 1993, 40, 375–378.
F. Gugumus, Possibilities and limits of synergism with light stabilizers in polyolefins 2. UV absorbers in polyolefins Polym. Degrad. Stab., 2002, 75, 309–320.
S. Chmela, P. Hrdlovic, J. Lacoste, Combined oligometric light and heat stabilizers Polym. Degrad. Stab., 2001, 71, 171–177.
L. Bucsiova, S. Chmela, P. Krdlovic, Preparation, photochemical stability and photostabilising efficiency of adducts of pyrene and hindered amine stabilisers in iPP matrix Polym. Degrad. Stab., 2001, 71, 135–145.
S. Jipa, R. Setnescu, T. Setnescu, T. Zaharescu, Efficiency assessment of additives in thermal degradation of i-PP by chemiluminescence I, Triazines Polym. Degrad. Stab., 2000, 68, 159–164.
S. Jipa, R. Setnescu, T. Setnescu, T. Zaharescu, Efficiency assessment of additives in thermal degradation of i-PP by chemiluminescence II, Selenium Polym. Degrad. Stab., 2000, 68, 165–169.
U. Gesenhues, Influence of titanium dioxide pigments on the photodegradation of poly(vinyl chloride) Polym. Degrad. Stab., 2000, 68, 185–196.
F. Gugumus, N. Lelli, Light stabilization of metallocene polyolefins Polym. Degrad. Stab., 2001, 72, 407–421.
S. H. Hamid, I. Hussain and K. Alam, Loss of additives from films exposed to harsh outdoor climate of Saudi Arabia, in 4th Chemistry in Industry Conference and Exhibition, Saudi Arabian Section–American Chemical Society (SAS–ACS), Bahrain, 2001.
H. G. Jellinek, Aspects of degradation and stabilization of polymers, Elsevier Publishing, Amsterdam, 1978.
A. Davis and D. Sims, Weathering of Polymers, Applied Science Publishers, New York, 1983.
S. H. Hamid, Role of thermal degradation of polyethylene under natural weathering conditions, in Proceedings of ANTEC 2000, Society of Plastic Engineers Meeting, Orlando, FL, USA, May 7–11, 2000, Marcel Dekker, New York, 2000, pp. 3768–3769.
D. Hon, Degradative effect of ultraviolet light and acid rain on wood surface quality Wood Fiber Sci., 1994, 26, 185–191.
B. Lindeberg, Improving the outdoor durability of wood by surface treatment FATIPEC, 1986, 2/B, 589–608.
Author information
Authors and Affiliations
Additional information
This article is published as part of the United Nations Environmental Programme: Environmental effects of ozone depletion and its interactions with climate change: 2002 assessment.
Rights and permissions
About this article
Cite this article
Andrady, A.L., Hamid, H.S. & Torikai, A. Effects of climate change and UV-B on materials. Photochem Photobiol Sci 2, 68–72 (2003). https://doi.org/10.1039/b211085g
Published:
Issue Date:
DOI: https://doi.org/10.1039/b211085g