Temperature-induced phase-transitions of methoxyoligo(oxyethylene) styrene-based block copolymers in aqueous solution

Fengjun Hua,a   Weizhong Yuan,abc   Phillip F. Britt,d   Jimmy W. Maysde  and  Kunlun Hong*a  

* Corresponding authors

a Center for Nanophase Materials Sciences, Oak Ridge National Laboratory, Oak Ridge, TN 37831, USA
E-mail: hongkq@ornl.gov
Fax: +1-865-574-4974
Tel: +1-865-574-1753

b Institute of Nano and Bio-polymeric Materials, School of Materials Science and Engineering, Tongji University, Shanghai 201804, China
E-mail: yuanwz@tongji.edu.cn
Fax: +86 21 69584723
Tel: +86 21 69580234

c Department of Materials Sciences and Engineering, The University of Tennessee, Knoxville, TN 37996, USA

d Chemical Sciences Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831, USA

e Department of Chemistry, The University of Tennessee, Knoxville, TN 37996, USA

Abstract

Novel well-defined diblock copolymers based upon styrene substituted with pendant methoxyoligo(oxyethylene) groups (4-CH3O(EO)4St, TrEGS) were prepared by sequential atom transfer radical polymerization. Polystyrene (PS) was synthesized as the first block in the copolymer using (1-bromoethyl)benzene as the initiator. This was followed by growth of a second block composed of PTrEGS. Each copolymer exhibits a lower critical solution temperature (LCST) in aqueous solution, and the LCST depends on the length of the PTrEGS block and the copolymer composition. Longer PTrEGS chains result in higher LCST values in aqueous solutions. The cloud points (Tcs) of PS-b-PTrEGS copolymers are lower than that of PTrEGS homopolymer as determined by UV-visible spectroscopy. Variable-temperature NMR spectra show that the intensity of proton signals from oxyethylene groups dramatically decreases at temperatures above the cloud point, indicating phase transition due to hydrogen bonding changes. Dynamic light scattering (DLS) measurements indicate that micelles are formed, where the PS backbone serves as the core at 25 °C. Each of these block copolymer solutions transformed from transparent bluish solutions to white gels above certain concentrations (≥10 wt%) and temperatures (lower critical gelation temperature, LCGT). The gelation process is thermally reversible, implying physical crosslinking through hydrophobic interactions.

Graphical abstract: Temperature-induced phase-transitions of methoxyoligo(oxyethylene) styrene-based block copolymers in aqueous solution

About
Cited by
Related
Download options Please wait...

Article information

DOI
https://doi.org/10.1039/C3SM51208H
Article type
Paper
Submitted
30 Apr 2013
Accepted
08 Aug 2013
First published
09 Aug 2013

Soft Matter, 2013,9, 8897-8903

Permissions

Request permissions

Temperature-induced phase-transitions of methoxyoligo(oxyethylene) styrene-based block copolymers in aqueous solution

F. Hua, W. Yuan, P. F. Britt, J. W. Mays and K. Hong, Soft Matter, 2013, 9, 8897 DOI: 10.1039/C3SM51208H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements