Abstract
This paper examines the effect of graphite and silicon carbide reinforcements on the pitting behavior of graphite/aluminum (Gr/Al) and silicon carbide/aluminum 
metal matrix composites. Electrochemical corrosion tests were performed on both Gr/Al and 
composite specimens. Identical tests were completed on powder metallurgy processed aluminum and wrought aluminum of the same composition. The electrochemical behavior of the 
composites was essentially identical to that of the powder processed and wrought aluminum alloys; however, the pitting attack on the 
composites was distributed more uniformly across the surface, and the pits penetrated to significantly less depths. The presence of graphite in the Gr/Al composites did not cause an electropositive shift in corrosion potential as anticipated, but caused a substantial decrease in resistance to passive film breakdown. This effect is the predominant reason for the poor performance of Gr/Al composites in marine environments.