Comparative and Equilibrium Studies on Anionic and Cationic Dyes Removal by Nano-Alumina-Doped Catechol Formaldehyde Composite

Karthik, V.; Selvakumar, P.; Sivarajasekar, N.; Megavarshini, P.; Brinda, N.; Kiruthika, J.; Balasubramani, K.; Ahamad, Tansir; Naushad, Mu.

doi:https://doi.org/10.1155/2020/7617989

Journal of Chemistry

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusion Data Availability Conflicts of Interest Authors’ Contributions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2020 | Article ID 7617989 | https://doi.org/10.1155/2020/7617989

Comparative and Equilibrium Studies on Anionic and Cationic Dyes Removal by Nano-Alumina-Doped Catechol Formaldehyde Composite

V. Karthik,¹P. Selvakumar,²N. Sivarajasekar,³P. Megavarshini,¹N. Brinda,¹J. Kiruthika,¹K. Balasubramani,⁴Tansir Ahamad,⁵and Mu. Naushad⁵

Academic Editor: Khaled Mostafa

Received07 May 2020

Revised06 Sept 2020

Accepted12 Sept 2020

Published26 Sept 2020

Abstract

Nano-alumina-doped catechol formaldehyde polymeric composite was prepared, characterized, and applied as an adsorbent for the removal of an anionic dye Congo red (CR) and a cationic dye SafraninO (SF), by adsorption process especially from aqueous solutions. Characterizations such as particle size distribution, zeta potential, BET, FTIR, and FESEM-EDAX were carried out for the adsorbent prepared. All experiments were conducted at the batch condition to study the effects of initial dye concentration (CR: 30–90 mg/L and SF: 10–50 mg/L), pH (2–11), temperature (25–55°C), and adsorbent dosage (0.05–0.3 g) on dye removal. The isotherm models (Langmuir, Freundlich, and Temkin) were analyzed for this adsorption work. The kinetic data obtained were analyzed by the pseudo-first-order, pseudo-second-order, Bangham, and Chien–Clayton equations. Dyes adsorption data were well fitted with the Freundlich isotherm equilibrium model and the pseudo-second-order kinetic model. Study results suggested that the nano-alumina-polymeric composite could be an effective adsorbent for anionic dye rather than cationic dye.

1. Introduction

Dyes are color-forming complex compounds and naturally get adsorbed over the surface of the substrate. Because of this property, it has majorly been used for various industrial applications such as textiles, cosmetics, pulp, and paper, and so on [1–4]. Generally, the dyes are classified into two main groups, namely natural dyes and synthetic dyes. Anionic and cationic dyes come under the category of synthetic dyes, and cationic dyes are significantly more harmful than the other one [5, 6]. It is estimated that the amount of dyes used all over the world to be in the range of 10,000 tons per year [7]. Owing to the increase in population, the usage of dyes in the industries has also been elevated.

Even though industries have many advanced eco-friendly technologies and recycling techniques for treating wastewater, the entire dyes present in the sewer could not entirely be eliminated. It is well documented that CR is a highly water-soluble dye and a significant pollutant in the wastewater draining from the textile, pulp and paper, printing, and dyeing industries [8]. SF is a basic azo dye and water-soluble synthetic dye. It has majorly been used in the dyeing of leather, fibers, cotton, wool, paper, and silk. Because of its over usage as a colorant in many industries, it acts as a model compound for dyes. These widely used dyes are major hazardous to the environment and also cause severe illnesses such as skin allergies, tumor, and mutation to humans [9, 10].

These dyes are nonbiodegradable, and thus, typical conventional practices are not sufficient to eliminate them. As a result, various physicochemical approaches were developed for taking them away from wastewater. But neither of the techniques was fruitful in providing complete removal of dyes in wastewater [11, 12]. As the adsorption technique has high-quality treatment processes, it was favored for the expulsion of toxins, for example, dyes. Also, this technique is most desirable for dye removal because of its smooth operation, simpler design setup [13–19].

This procedure, for the most part, comprises two principle segments viz., adsorbent and adsorbate. Adsorbates are referred to as dyes in the fluid, while adsorbents are the substances added to the dye solution to capture the coloring complexes [20, 21]. Some of the research outcomes revealed that the production of adsorbents from different low-cost materials such as clays, agricultural waste (rice husk, maize cob, and coconut shell), siliceous materials (perlite, silica beads, and alunite), zeolites, metal oxides (iron and alumina), and others (chitosan, starch, and cotton as biosorbents) is making this process inexpensive [15, 22]. Among them, the polymer composites have majorly been preferred and considered as adsorbents to remove the synthetic dyes from the sewer [23–27]. Since it is more effective in the process, thereby, it could contribute to resolving water pollution problems [28].

Although several studies have been reported on the polymeric composite adsorbents for separating the dyes from the wastewater, doping of any of the adsorbent material in a polymeric matrix followed by carbonization and activation makes polymeric composite adsorbents [29–31]. At this stage, there is still a need of more investigations on polymeric composite adsorbents on dye removal to make this process more effective and commercial. So far, no study has been carried out to remove the commercial dyes, namely CR and SF, in the wastewater using Alumina Polymeric Composite (APC). Hence, the present study was aimed to prepare alumina nanoparticle adsorbent doped with catechol formaldehyde resin and used as an adsorbent to check its feasibility in the dye removal. This polymeric composite adsorbent was prepared by the suspension polymerization technique [32]. CR, an anionic dye and SF, a cationic dye, were selected to evaluate the adsorption efficiency of prepared alumina polymeric matrix composite in the aqueous solutions [33–36]. The equilibrium data obtained were examined using different kinetic and isotherm models to understand the adsorption mechanism.

2. Materials and Methods

2.1. APC Preparation

A sterile 250 mL beaker contains catechol (50 g) with few drops of water was heated at 150°C till the catechol switched over to the molten state. To that, 63 mL of formaldehyde solvent (37%), 1.5 mL of triethylamine and 3.5 g of hexamine were added and continuously stirred for 30 min for proper mixing. In this reaction, triethylamine acts as a catalyst, while hexamine acts as a cross-linking agent among the catechol and formaldehyde. Subsequently, the reaction mixture was heated at 31°C for 40 min until the solution turned into the whitish-yellow color emulsion. A 3 g of polyvinyl alcohol (PVA), a stabilizing agent, and 0.5 g of aluminum oxide were added to the whitish-yellow color emulsion within 15 min and continuously heated until it turns into a crystalline state. Then, the crystals were cooled by keeping them for 8 h at room temperature. The prepared crystal was washed twice with deionized water, acetone, and ethanol separately and placed in a hot air oven to remove moisture content. The dried crystals (i.e., APC) were made into powdered form with uniform particle size and utilized as an adsorbent for further experiments. The synthesized APC was characterized using particle size analyzer, zeta potential, BET (Brunauer–Emmett–Teller) analysis, FTIR (Fourier transform infrared spectroscopy), and FESEM-EDAX (field emission scanning electron microscopy with energy dispersive X-ray spectroscopy).

2.2. Batch Experiment

The pH of working dye solutions of CR and SF dyes were adjusted into pH 2 and pH 10, respectively, by adding 0.5 M HCL and 0.5 M NaOH. About 0.1 g of APC was added into 25 mL of each dye solution, the flask was covered with coil and kept in an orbital shaker at 200 rpm for different time intervals. After the desired time was attained, the mixture of dye solution with APC was filtered and the optical density of filtrate was examined by using UV-Spectrometer (Shimadzu UV–vis 2550, Japan) to determine the adsorption efficiency, i.e., the concentration of solution after adsorption. A similar procedure was continued to evaluate the effects of various experimental parameters such as initial dye concentration, pH of the dye solutions, process temperature, and contact time for the different regular intervals. The removal percentage of dyes calculated using the following equation:where C_i and C₀ (mg l⁻¹) are initial and final concentrations of the dyes in the aqueous solution. The dye adsorption capacity q_t (mg/g) at any time t, was determined as follows:where C_t (mg/L) is the concentration of dye at any time t, V (L) is the volume of dye solution, and M (g) is the amount of APC. The exhausted APC was rejuvenated using acetone, hot water, dilute HCl, dilute NaOH solution, and dilute NaCl solution in order to find a suitable regenerating solvent.

3. Results and Discussion

3.1. Characterization of the Adsorbent

The particle size of synthesized alumina doped polymeric composites was determined after the carbonization and activation for different systematic time intervals (60, 90, and 120 min) at 400°C. The measured particle size for 60, 90, and 120 min carbonized material was found to be 651.4, 525.5, and 503.7 nm, respectively. The results showed that 120 min carbonized material produced small-sized particles when compared to short-time heat exposed materials. The observed effects on the variation of particle sizes were similar to the study outcomes reported elsewhere [37]. The particle size distribution of APC after carbonization at 400°C for 120 min analyzed by a particle size analyzer is represented in Figure 1(a). Further experiments in this study were carried out with the materials carbonized at 400°C for 120 min exposure time.

(a)

(b)

Figure 1(b) impersonates the values of zeta potential, from which the surface charge of the APC is determined. Up to pH 6.5, the APC zeta potential value diminished precisely. Then the value continually decreased for the increase in pH and after the pH value reached 9.0, the zeta potential value decreased rapidly. From these results, it was decided that the isoelectric point of the APC is 6.0. This depicted that the layer of the adsorbent charged negatively and it expedited the positive (cationic) species. Similarly, the solution pH value exceeds 6.0, then the surface layer of the adsorbent positively charged and it expedited the negative (anionic) species. This explained the effective adsorption of anionic dye CR in a medium that has acidic nature, whereas the cationic dye SF showed efficient adsorption in a medium that has basic nature.

The BET analysis is mostly used to determine the definitive exterior area, from which the size of the pores can also be estimated. This data is also very useful to anticipate the dissolution rate since the definitive exterior area is proportional to the dissolution rate. From the BET analysis, the following information was obtained: the initial pore volume (0.947 cm³/g), average pore diameter (2.76 nm), BET surface area (2.781 m²/g), and monolayer volume (0.2434 cm³/g).

The FTIR analysis is an important technique that gives the information on functional groups of various compounds and helps to identify the chemical structural changes of polymeric, organic, and inorganic materials. The response of functional groups to IR rays may fluctuate over a wide range, depending on the interaction of atoms within the molecule. Hence, the infrared light range 400–4000 cm⁻¹ was utilized to examine the test samples and look out the chemical properties in the FTIR investigation. The observed FTIR spectra of the composite before and after the adsorption of two different dyes are illustrated in Figure 2. It can be seen from Figure 2(a) that adsorption bands between the range 3500 to 4000 cm⁻¹ for the APC before adsorption indicated the presence of many aromatic groups clustered to form the polymeric matrix. In the same image, it can be observed that the peak around the 500 cm⁻¹ region showed the presence of alumina in the APC. The broad FTIR peak at 3500 cm⁻¹ range represents O-H stretching; the peak at 3685 cm⁻¹ indicates the presence of phenolic O-H group in the composite before adsorption. The medium broad band observed at the range 600–800 cm⁻¹ of spectra of APC after adsorption was due to the frequency of azo group, amine group in CR dye and C-S stretching, and methyl group in SF dye. Similar results were observed on the adsorption study of cationic and anionic dyes on polymer-modified yeast adsorbents [38]. The adsorption peak at 1652 cm⁻¹ range is attributed to the stretching vibration of C=O.

The FESEM is used to characterize the surface morphology of APC before and after the adsorption dyes, and the observed results are shown in Figures 3(a)–3(c). The outcomes of FESEM analysis revealed that tested samples (APC) were cylindrical rod-shaped with a size range of 500–800 nm. As depicted in Figure 3(a), the FESEM image of APC illustrated that pores were formed well on the matrix with alumina incorporated polymeric materials. It also confirmed that alumina was well embedded with the polymeric matrix and homogeneously spread over the porous surface of the catechol and formaldehyde matrix cross-linked by hexamine. Similar observations were also documented in the analysis of magnetic oxide embedded bentonite clay for Cr (III) adsorption [39]. The well-impregnated and distributed small-sized alumina particles on the polymer matrix could make a considerable increase in the surface area of APC. It would be an indicative measure of a suitable adsorbent for adsorbing more dyes in the process. The adsorption of dyes created distinct changes in the physical structure of the materials taken. The FESEM images after dye adsorption indicated that the nonporous structure was due to the presence of dye constituents in the matrix of APC. It was evident that the chosen dyes adsorbed well on the porous surface of prepared APC.

The chemical elemental composition of APC was analyzed using Energy Dispersive Analysis X-Ray (EDAX). The EDAX spectra of composite confirmed the presence of Al, C, and O elements in the composite. It is also estimated that the composition of carbon (72%) was very high, and the oxygen (26%) and alumina (12%) were in the ratio of 2 : 1, respectively.

3.2. Effect of pH on Adsorption

Determination of the impact of pH is essential in the adsorption experiments. The adsorption of CR and SF dyes onto APC was investigated for different pH from 2 to 11. The observed results are illustrated in Figure 4(a). The removal percentage of CR dye solution was plotted against the pH at 25 mL of 30 mg/L initial dye solution, 0.1 g APC dose, and 55°C for prefixed process time. As represented in Figure 4(a), the removal percentage of CR solution reduced from 98 to 36.8% when the solution pH was changed from 2 to 4. At the acidic range, the percentage of dye removal for CR was higher initially and suddenly decreased with an increase in pH, mostly in the first region. From this study, the optimum pH was determined as 2 at which the maximum 98% removal of CR dye was observed. With decreasing pH, weak base groups were protonated and acquired a net positive charge on the APC surface. This brought out an electrostatic attraction between the surface of the APC and CR. As a result, a high removal percentage was observed.

(a)

(b)

(c)

(d)

(e)

SF has a pKa value of 6.4 and a pH 10. The SF removal percentage was witnessed in the basic pH range, whereas with a gradual decrease in pH, it showed an indicative reduction in the dye removal. The percentage removal of dye ranges from 35 to 64% removal when pH varied from 3 to 11. The maximum removal of color was attained at pH 10.0, and the removal percentage of SF at this optimum pH was 64%. At pH 10, further investigation was carried out with a low pka value at 55°C. As SF is a basic dye, a strong electrostatic repulsion exists between the positively charged ions present in the SF solution and the positively charged APC surface due to the protonation of the functional groups, which resulted in low removal percentage. Also, with an increase in pH of the SF solution, a significant rate of dye removal was noted, as represented in Figure 4(a). At high pH, consecutive deprotonation of the positively charged groups present on the surface of APC existed. It led to the strong electrostatic desirability between SF and APC.

3.3. Effect of Temperature on Adsorption

At four different temperatures (25, 35, 45, and 55°C), the experiments were carried out for adsorption of CR and SF onto the APC material. Figure 4(b) represents that increase in temperature resulted in the increased percentage of dye removal. It denoted that high temperature favored the CR and SF removal from aqueous solution. The solubility of dyes decreased when the temperature increased and hence, it led to a high adsorption rate—a similar result for the adsorption of dyes reported in the literature [5]. Due to the rise in the mobility of the dye molecules at high temperatures, there was an increase in dye adsorption. Therefore, the adsorptive uptake of CR and SF increased with an increase in temperature could partially be attributed to chemisorption.

3.4. Effect of Initial Dye Concentrations and Contact Time

The investigation about the influence of different initial dye concentrations of CR and SF by APC is represented in Figures 4(c) and 4(d). The active sites of the adsorbent were surrounded by much more CR and SF ions when the concentration of CR or SF solution was higher. The efficiency of the adsorption phenomenon was higher in CR than SF. The removal percentage was higher for low dye concentration of 30 ppm and 10 ppm for CR and SF, respectively. The value of q_e increased when the initial CR and SF dye concentrations were increased. The removal percentage was improved with contact time and became constant at a particular time. So the value of q_em was raised with the augmentation of initial CR and SF dye concentrations. Otherwise, it could be seen that initial dye concentration increased when the percentage removal of dye decreased. At the minimum dye concentrations, entire dye molecules present in the reaction mixture interacted well to the binding sites of APC, enabling about 98% for CR adsorption and 64% for SF. However, all adsorbents were saturated at an absolute concentration and had a limited number of binding sites. There were more dye molecules persisting unabsorbed in the solution at higher concentrations. It might be a reason that the saturation of binding sites resulted in decreased adsorption efficiency. A similar outcome was observed for adsorption of CR and SF on alumina-nickel composites [40].

3.5. Effect of Adsorbent Dosage

The adsorbent dose is an essential parameter for the examination of adsorption studies, which determined the percentage removal of given initial dye concentration. For analyzing the impact of adsorbent dosage on the adsorption of CR and SF dyes, the adsorbent dose was varied from 0.05 to 0.3 g/L at 55°C with optimized pH and time. The number of dye molecules adsorbed over APC by changing the dosage of APC is illustrated in Figure 4(e). It showed that the adsorption of CR and SF increased as the amount of adsorbent was increased from 0.2 to 0.3 g/L for CR and 0.25 to 0.3 g/L for SF and then maintained constant. This was due to the number of active sites increased on alumina polymer matrix with the increase in the adsorbent dosage to a certain level. Therefore, 0.2 g/L and 0.25 g/L of APC for CR and SF dye, respectively, were taken as the optimum adsorbent dose for further experiments.

4. Adsorption Isotherm Studies

Establishment of equilibrium correlation based on adsorption data is necessary for the optimization and design of adsorption process. To investigate the batch adsorption data Langmuir, Freudlich and Temkin isotherms were employed.

4.1. Langmuir Isotherm

Langmuir isotherm studies say that adsorption proceeds on monolayer surface and energy will be the same on the sites of adsorption. Adsorption isotherm provides valuable information such as equilibrium sorption capacity and certain constants whose values express the surface properties and affinity of the adsorbent. The linear equation of Langmuir isotherm is symbolized as in the following equation [41]:where q_m is the maximum monolayer capacity (mg/g); K_Lis the Langmuir isotherm constant (L/mg). The graph was plotted C_e/q_e against C_e at various temperatures (25, 35, 45, and 55°C) in Figures 5(a) and 5(b) from which q_m and K_L values were calculated. From Table 1 for CR dye, q_m and K_L values increased with an increase in temperature till 45°C and then an insignificant increment was noticed. The estimated correlation coefficients value (R²) ranges from 0.917 to 0.994. For SF dye, the q_m value decreased and K_L value increased with an increase in temperature, and the R² was determined in ranges from 0.890 to 0.932. It was confirmed from the value of R² that both adsorption data measured for CR and SF onto APC reasonably fitted with the Langmuir isotherm. A similar isotherm response was found for the adsorption of Pb(II), Zn(II), and Cd(II) on hyacinth weed [42].

(a)

(b)

(c)

(d)

4.2. Freundlich Isotherm

Freundlich isotherm studies reveal that the adsorption takes place on the heterogeneous surface and the energy of adsorption will be non-uniform [39]. The linear equation of Freundlich isotherm can be denoted as the following equation [43]:where K_f is the Freundlich isotherm constant (mg/g) and n is the adsorption intensity. The measured values of both CR and SF dyes for Freundlich isotherm are presented in Figures 5(c) and 5(d). The graph was plotted as log q_e against log C_e at different temperatures (25, 35, 45, and 55°C). From this graph, n and K_f values were calculated. For CR, n and K_f values decreased with an increase in temperature and R² values range from 0.971 to 0.994, as presented in Table 1. In the case of SF dye, these values increased with an increase in temperature and R² values range from 0.927 to 0.935. R² indicated that the attained adsorption data of CR dye onto APC fitted with the Freundlich isotherm rather than the Langmuir isotherm. The estimated adsorption data of SF onto APC was also fitting good with Freundlich isotherm. Similar isotherm results were also reported in reactive dyes removal using biomaterial-based polymer composites [44].

4.3. Temkin Isotherm

The Temkin equation reveals that the heat of adsorption weakens with the increase in the area of surface coverage. The linear equation for Temkin isotherm can be represented as the following equation:where A_T is the Temkin isotherm equilibrium binding constant (L/g), B_T is the Temkin isotherm constant, R is the universal gas constant (8.314 J/mol/K), T is the temperature at 298 K, and B is the constant related to the heat of adsorption (J/mol). The graph was plotted between q_e against ln C_e at different temperatures (25, 35, 45, and 55°C) in Figures 6(a) and 6(b) from which B_T and A_T values were calculated. From Table 1, for CR, B_T and A_T values decreased with an increase in temperature and R² values ranged from 0.735 to 0.923. In the case of SF, B_T and A_T values decreased with an increase in temperature and values ranged from 0.752 to 0.945. The values of R² indicated that the adsorption data of CR and SF dyes onto APC were not well fitted into Temkin isotherm like Freundlich isotherm. Similar isotherm results were also reported in adsorption of Congo red dye from aqueous solutions using the roots of Eichhornia crassipes [45].

(a)

(b)

5. Adsorption Kinetics

The uptake of CR and SF onto APC at temperatures extending from 25 to 55°C and its diffusion processes were studied at an initial CR concentration of 30 mg/L and SF concentration of 10 mg/L for the same range of temperature, pH 2 and 10 for CR and SF, respectively. The experimental data was investigated with five kinetic models: pseudo-first-order, pseudo-second-order, Bhangam kinetic model, intraparticle diffusion, and Elovich model.

5.1. Pseudo-First-Order Kinetic Model

The pseudo-first-order kinetic model is more suitable for lower concentrations of solute. The pseudo-first-order kinetic model equation is expressed by the following equation [46]:where is the rate constant of first-order adsorption (min⁻¹). The straight-line plot of log (q_e − q_t) against t is given in Figures 7(a) and 7(b) which indicates log (q_e) as slope and intercept equal to /2.303. The amount of solute adsorbed per g of APC at equilibrium (q_e) and the first-order rate constant () could be evaluated from the slope and the intercept and the values are tabulated in Table 2. From the graph, the dye adsorption by APC did not obey the pseudo-first-order kinetics for both CR and SF. Similar outcome was observed in iron-doped phenolic resin-based activated carbon of micro- and nanoparticles for arsenic removal [47].

(a)

(b)

(c)

(d)

5.2. Pseudo-Second-Order Kinetics

The pseudo-second-order model developed on the assumption of chemisorption which involves valence and electrostatic forces via sharing of electrons between the dye and the adsorbent. This is given by the following equation [48]:where is the rate constant. The plot of versus time gives the plot for the pseudo-second-order model. Table 2 presents the value of and for CR and SF dye adsorption at four different temperatures. From Table 2 and Figures 7(c) and 7(d), the pseudo-second-order equation fitted well with the experimental data, as the correlation coefficient was close to unity and extremely high was obtained for both CR and SF adsorption process compared with the first-order equation. As the experimental data fitted well with the pseudo-second-order model, the adsorption process was solely dependent on both APC and dyes concentration. This adsorption mechanism was chemically rate controlled. Similar kinetic results were obtained for basic dyes removal from aqueous solutions onto apricot stone activated carbon [49].

5.3. Bhangam Kinetic Model

Bhangam’s model is a pore distribution model that can determine the rate-controlling step in the adsorption process, which is given by the following equation:

The plot of log q_t versus log t represents the Bhangam kinetic model. The graph was plotted for an initial dye concentration of 30 mg/L and 10 mg/L for CR and SF, respectively, as shown in Figures 8(a) and 8(b). The correlation coefficients (R²) obtained ranged from 0.811 to 0.976 for CR and SF, respectively, as shown in Table 2. Nonlinear curve was obtained for CR but a linear curve resulted in the case of SF adsorption. This indicated that the rate-limiting step was the adsorbate diffusion into pore or matrix for CR. Similar kinetics observed for the adsorption of CR and SF onto kenaf core fiber [46].

(a)

(b)

(c)

(d)

5.4. Intraparticle Diffusion Model

Transport of dye molecules from the bulk of the solution into the adsorbent is normally via an intraparticle diffusion, which is regularly the rate-limiting step in the adsorption process. Intraparticle diffusion model, according to which the amount adsorbed at time t, q_t, reads as follows:where k_p is the intraparticle diffusion rate constant (mg g⁻¹min^0.5), C (mg g⁻¹) is a constant related to the thickness of the boundary layer. The graph plotted between versus t^0.5 provided a straight line, as presented in Figures 8(c) and 8(d). From the graph, k_p and C was determined from the slope and intercept. Values of C indicated the thickness of the boundary layer; i.e., the larger intercept, the greater the boundary layer effect. The small value of the intraparticle diffusion constant indicated that the boundary layer has a less significant effect on the diffusion and is shown in Table 2. A similar result was reported for basic dyes adsorption onto activated carbon [50].

5.5. Elovich Model

Elovich equation is also used to describe second-order kinetic assuming that the actual solid adsorbent surfaces are energetically heterogeneous. The Elovich equation is given as follows:

This simplified equation (11) is as follows:

Elovich constants α and β were calculated from the plot of q_e versus ln (t), as shown in Figures 9(a) and 9(b). The correlation coefficient (R²) ranged from 0.804 to 0.875 for CR and from 0.946 to 0.978 for SF as shown in Table 2. α value increased for both CR and SF as temperature increased. Similar kinetic results were reported for acid dye removal by dead fungal biomass of T. harzianum [51]. This model fitted well for SF adsorption than the CR. It was concluded that SF followed chemisorption as it fitted well with the Elovich model. A similar kinetic result of the adsorption process was reported in the adsorption of dye by chitosan systems [52].

(a)

(b)

5.6. Adsorption Thermodynamics

The process of spontaneity approval is based on the thermodynamic study of the adsorption process. The study of adsorption thermodynamics was used to interpret the adsorption mechanism, either physical or chemical. For the adsorption of CR and SF, the thermodynamic parameters (∆G°, ∆H°, ∆S°) were determined using the Van’t Hoff equation. The relationship between the parameters is given as follows:

Van’t Hoff equation is obtained as follows:where K_C is the equilibrium constant (dimensionless). The change in enthalpy (∆H°) and the change in entropy (∆S°) were determined from the slope and intercept of equation (11), respectively. Gibbs energy change was determined directly from equation (10). Table 3 lists the value of thermodynamic parameters for both CR and SF at four different temperatures, respectively. The negative value of ∆G at all experimented temperatures concluded that the adsorption process occurred spontaneously. In contrast, the positive value of ΔH° indicated that the adsorption had occurred in an endothermic manner. As well as the positive value of ΔS° suggested the arrangement of dye molecules onto APC very well with more randomness as temperature increased from 25 to 55°C. Here, as temperature increased, the equilibrium constant also increased. This proved that the rate of adsorption increased with an increase in temperature. The value of entropy and enthalpy for the adsorption of CR and SF indicated the endothermic nature of the adsorption process. An endothermic reaction is generally associated with chemisorption [53].

5.7. Regeneration and Comparison with Other Adsorbents

The comparison of desorption efficiency is presented in Figure 10. The physical adsorption was not a predominant factor, while sodium hydroxide, which conformed high desorption efficiency 93% for CR and 87% SF representing the chemical binding of dye adsorbent of interface route. Apart from the other solvent such as HCl and NaCl of H⁺ and Cl⁻ was obtained and neutralized in the distilled water, which was approved by the chemisorption of the dye molecules. APC was regenerated after CR and SF dyes adsorption several times and used for readsorption experiments. Regenerated APC was found good at least for 4 cycles (Figure 11).

The comparison of adsorption capabilities of various adsorbents for CR and SF dyes is presented in Table 4. It is clear from Table 4 that the prepared APC was moderately good compared with other adsorbents for CR and SF.

6. Conclusion

The adsorbent Alumina doped synthetic polymeric composite was synthesized by ball milling method. A yield of 81.5% was obtained by this method. Here, it was used to remove synthetic dyes such as CR and SF. Characterizations such as particle size distribution, zeta potential, BET, FTIR, and FESEM with EDAX were performed for the APC composite to study the nature of the synthesized particle. The particle size analysis of the synthetic polymeric composite estimated was about 503.7 nm. FTIR study revealed that the presence of functional groups in the composite before and after adsorption process. FE SEM and EDAX characterization was done, which gave the surface image and the composition of the composite. A comparison of anionic and cationic dye using APC was studied. The effect of parameters for the adsorption process such as the effect of pH, temperature, adsorbent dosage, initial dye concentration, and contact time for CR and SF adsorption were studied. A significant interaction was observed in CR and SF removal with the combination of parameters. The maximum adsorption of CR and SF dyes was obtained with pH 2 and 10, respectively, at the process temperature of 55°C. Several isotherm models were used to fit the experimental data point. The Langmuir isotherm, Freundlich isotherm, and Temkin isotherm were studied. Among them, observed experimental data were well fitted with Freundlich isotherm. It suggests that the mechanism can be a chemical adsorption process onto the surface binding sites of the adsorbent. The kinetic modeling of the CR and SF onto the composite indicates that the adsorption process fits into pseudo-second-order kinetics with a correlation coefficient higher than 0.9. The removal percentage and adsorption capacity of CR was higher than that of cationic dye SF over a wide range of aqueous concentrations by the APC. Thus, the results suggest that the APC could be a potential adsorbent for the removal of anionic dyes from aqueous solution.

Data Availability

No data were used to support this study.

Conflicts of Interest

The authors declare that there are no conflicts of interest regarding the publication of this paper.

Authors’ Contributions

V. Karthik and N. Sivarajasekar were responsible for methodology, project administration, and supervision. P. Selvakumar framed the conceptualization, investigation, and writing of the original draft. P. Megavarshini, N. Brinda, and J. Kiruthika performed the experiment and wrote the original draft. K. Balasubramani involved in methodology, supervision, reviewing, and editing. Tansir Ahamad and Mu. Naushad carried out reviewing and editing.

Acknowledgments

The authors are grateful to the Researchers Supporting Project number RSP-2020/6, King Saud University, Riyadh, Saudi Arabia, for the support.

References

K. O. Adebowale, B. I. Olu-owolabi, and E. C. Chigbundu, “Removal of safranin-O from aqueous solution by adsorption onto kaolinite clay,” Journal of Encapsulation and Adsorption Sciences, vol. 4, no. 3, pp. 89–104, 2014.
View at: Publisher Site | Google Scholar
A. B. Albadarin, M. N Collins, M. Naushad, S. Shirazian, and C. Mangwandi, “Activated lignin-chitosan extruded blends for efficient adsorption of methylene blue,” Chemical Engineering Journal, vol. 307, pp. 264–272, 2017.
View at: Publisher Site | Google Scholar
E. Bulut and İ. A. Şengil, “Adsorption of malachite green onto bentonite: equilibrium and kinetic studies and process design,” Microporous and Mesoporous Materials, vol. 115, no. 3, pp. 234–246, 2008.
View at: Publisher Site | Google Scholar
V. J. Sharavanan, M. Sivaramakrishnan, N. Sivarajasekar et al., “Pollutants inducing epigenetic changes and diseases,” Environmental Chemistry Letters, vol. 18, no. 2, pp. 325–343, 2020.
View at: Publisher Site | Google Scholar
Y.-F. Hao, L.-G. Yan, H.-Q. Yu et al., “Comparative study on adsorption of basic and acid dyes by hydroxy-aluminum pillared bentonite,” Journal of Molecular Liquids, vol. 199, pp. 202–207, 2014.
View at: Publisher Site | Google Scholar
M. El Haddad, R. Slimani, R. Mamouni, M. R. Laamari, S. Rafqah, and S. Lazar, “Evaluation of potential capability of calcined bones on the biosorption removal efficiency of safranin as cationic dye from aqueous solutions,” Journal of the Taiwan Institute of Chemical Engineers, vol. 44, no. 1, pp. 13–18, 2013.
View at: Publisher Site | Google Scholar
T. A. Saleh and V. K. Gupta, “Photo-catalyzed degradation of hazardous dye methyl orange by use of a composite catalyst consisting of multi-walled carbon nanotubes and titanium dioxide,” Journal of Colloid And Interface Science, vol. 371, no. 1, pp. 101–106, 2012.
View at: Publisher Site | Google Scholar
M. Sulak, E. Demirbas, and M. Kobya, “Removal of Astrazon Yellow 7GL from aqueous solutions by adsorption onto wheat bran,” Bioresource Technology, vol. 98, no. 13, pp. 2590–2598, 2007.
View at: Publisher Site | Google Scholar
V. K. Gupta, A. Mittal, R. Jain, M. Mathur, and S. Sikarwar, “Adsorption of Safranin-T from wastewater using waste materials- activated carbon and activated rice husks,” Journal of Colloid and Interface Science, vol. 303, no. 1, pp. 80–86, 2006.
View at: Publisher Site | Google Scholar
N. Sivarajasekar, K. Balasubramani, R. Baskar, S. Sivamani, and I. Ganesh Moorthy, “Eco-friendly acetaminophen sequestration using waste cotton seeds: equilibrium, optimization and validation studies,” Journal of Water Chemistry and Technology, vol. 40, no. 6, pp. 334–342, 2018.
View at: Publisher Site | Google Scholar
W. Bran, “Rice husk ash as a low cost adsorbent for the removal of methylene blue and congo red in aqueous phases,” Clean-Soil Air Water, vol. 37, no. 7, pp. 581–591, 2009.
View at: Google Scholar
M. T. Yagub, T. K. Sen, S. Afroze, and H. M. Ang, “Dye and its removal from aqueous solution by adsorption : a review,” Advances in Colloid and Interface Science, vol. 209, pp. 172–184, 2014.
View at: Publisher Site | Google Scholar
C. Namasivayam and D. Kavitha, “Removal of congo red from water by adsorption onto activated carbon prepared from coir pith, an agricultural solid waste,” Dyes and Pigments, vol. 54, no. 1, pp. 47–58, 2002.
View at: Publisher Site | Google Scholar
A. Regti, A. El Kassimi, M. R. Laamari, and M. El Haddad, “Competitive adsorption and optimization of binary mixture of textile dyes: a factorial design analysis,” Journal of the Association of Arab Universities for Basic and Applied Sciences, vol. 24, no. 1, pp. 1–9, 2017.
View at: Publisher Site | Google Scholar
A. Regti, M. R. Laamari, S.-E. Stiriba, and M. El Haddad, “Potential use of activated carbon derived from Persea species under alkaline conditions for removing cationic dye from wastewaters,” Journal of the Association of Arab Universities for Basic and Applied Sciences, vol. 24, no. 1, pp. 10–18, 2017.
View at: Publisher Site | Google Scholar
P. Asaithambi, R. Govindarajan, M. Busier Yesuf, P. Selvakumar, and E. Alemayehu, “Enhanced treatment of landfill leachate wastewater using sono (US)-ozone(O₃)-electrocoagulation(EC) process: role of process parameters on color, COD and electrical energy consumption,” Process Safety and Environmental Protection, vol. 142, pp. 212–218, 2020.
View at: Publisher Site | Google Scholar
A. Regti, M. R. Laamari, S.-E. Stiriba, and M. E. Haddad, “Removal of Basic Blue 41 dyes using Persea americana-activated carbon prepared by phosphoric acid action,” International Journal of Industrial Chemistry, vol. 8, no. 2, pp. 187–195, 2017.
View at: Publisher Site | Google Scholar
N. Sivarajasekar, K. Balasubramani, N. Mohanraj et al., “Fixed-bed adsorption of atrazine onto microwave irradiated Aegle marmelos Correa fruit shell: statistical optimization, process design and breakthrough modeling,” Journal of Molecular Liquids, vol. 241, pp. 823–830, 2017.
View at: Publisher Site | Google Scholar
N. Sivarajasekar, N. Mohanraj, K. Balasubramani et al., “Optimization, equilibrium and kinetic studies on ibuprofen removal onto microwave assisted-activated Aegle marmelos correa fruit shell,” Desalination and Water Treatment, vol. 84, pp. 48–58, 2017.
View at: Publisher Site | Google Scholar
D. N. Ahmed, L. A. Naji, A. A. H. Faisal, N. Al-Ansari, and M. Naushad, “Waste foundry sand/MgFe-layered double hydroxides composite material for efficient removal of Congo red dye from aqueous solution,” Scientific Reports, vol. 10, pp. 2042–2053, 2020.
View at: Publisher Site | Google Scholar
M. Naushad, A. A. Alqadami, Z. A. AlOthman, I. H. Alsohaimi, M. S. Algamdi, and A. M. Aldawsari, “Adsorption kinetics, isotherm and reusability studies for the removal of cationic dye from aqueous medium using arginine modified activated carbon,” Journal of Molecular Liquids, vol. 293, p. 111442, 2019.
View at: Publisher Site | Google Scholar
A. Mahapatra, B. G. Mishra, and G. Hota, “Adsorptive removal of congo red dye from wastewater by mixed iron oxide-alumina nanocomposites,” Ceramics International, vol. 39, no. 5, pp. 5443–5451, 2013.
View at: Publisher Site | Google Scholar
K. M. Mostafa, A. R. Samarkandy, and A. A. El-Sanabary, “Preparation of poly (DMAEM)-cross linked pregelled starch graft copolymer and its application in waste water treatments,” Carbohydrate Polymers, vol. 86, no. 2, pp. 491–498, 2011.
View at: Publisher Site | Google Scholar
K. M. Mostafa, A. R. Samarkandy, and A. A. El-Sanabary, “Removal of basic dyes from aqueous medium using novel poly (MAA)-cross linked pregelled starch graft copolymer,” Journal of Applied Polymer Science, vol. 118, no. 5, pp. 2728–2735, 2010.
View at: Publisher Site | Google Scholar
K. M. Mostafa and A. A. El-Sanabary, “Synthesis and characterization of novel smart flocculant based on poly (MAam)-pregelled starch graft copolymers and their degraded products,” Advances in Polymer Technology, vol. 32, no. 2, p. 21339, 2013.
View at: Publisher Site | Google Scholar
M. Naushad, G. Sharma, and Z. A. Alothman, “Photodegradation of toxic dye using Gum Arabic-crosslinked-poly(acrylamide)/Ni(OH)₂/FeOOH nanocomposites hydrogel,” Journal of Cleaner Production, vol. 241, p. 118263, 2019.
View at: Publisher Site | Google Scholar
J. Mohanraj, D. Durgalakshmi, S. Balakumar et al., “Low cost and quick time absorption of organic dye pollutants under ambient condition using partially exfoliated graphite,” Journal of Water Process Engineering, vol. 34, p. 101078, 2020.
View at: Publisher Site | Google Scholar
V. Ranjithkumar, S. Sangeetha, and S. Vairam, “Synthesis of magnetic activated carbon/α-Fe₂O₃ nanocomposite and its application in the removal of acid yellow 17 dye from water,” Journal of Hazardous Materials, vol. 273, pp. 127–135, 2014.
View at: Publisher Site | Google Scholar
S. Dawood and T. K. Sen, “Removal of anionic dye congo red from aqueous solution by raw pine and acid-treated pine cone powder as adsorbent: equilibrium, thermodynamic, kinetics, mechanism and process design,” Water Research, vol. 46, no. 6, pp. 1933–1946, 2012.
View at: Publisher Site | Google Scholar
R. F. Mehmood, F. Mehmood, J. Akhtar, S. S. Shah, and M. A. Khosa, “Adsorption of Cd(II) by sol-gel silica doped withN-(dipropylcarbamothioyl)thiophene-2-carboxamide,” Journal of Dispersion Science and Technology, vol. 34, no. 2, pp. 153–160, 2013.
View at: Publisher Site | Google Scholar
S. Alam, N. Rehman, A. Noor Ul, L. A. Shah, I. Mian, and H. Ullah, “Removal of basic green 5 by carbonaceous adsorbent: adsorption kinetics,” Bulletin of the Chemical Society of Ethiopia, vol. 31, no. 3, pp. 411–422, 2018.
View at: Publisher Site | Google Scholar
S. Preethi, A. Sivasamy, S. Sivanesan, V. Ramamurthi, and G. Swaminathan, “Removal of safranin basic dye from aqueous solutions by adsorption onto corncob activated carbon,” Industrial & Engineering Chemistry Research, vol. 45, no. 22, pp. 7627–7632, 2006.
View at: Publisher Site | Google Scholar
A. Navya, S. Nandhini, S. Sivamani, G. Vasu, N. Sivarajasekar, and A. Hosseini-Bandegharaei, “Preparation and characterization of cassava stem biochar for mixed reactive dyes removal from simulated effluent,” Desalination and Water Treatment, vol. 189, pp. 440–451, 2020.
View at: Publisher Site | Google Scholar
S. Muthusaravanan, S. V. Priyadharshini, N. Sivarajasekar et al., “Optimization and extraction of pharmaceutical micro-pollutant-norfloxacin using emulsion liquid membranes,” Desalination and Water Treatment, vol. 156, pp. 238–244, 2019.
View at: Publisher Site | Google Scholar
K. Balasubramani, N. Sivarajasekar, and M. Naushad, “Effective adsorption of antidiabetic pharmaceutical (metformin) from aqueous medium using graphene oxide nanoparticles: equilibrium and statistical modelling,” Journal of Molecular Liquids, vol. 301, Article ID 112426, 2020.
View at: Publisher Site | Google Scholar
S. Muthusaravanan, N. Sivarajasekar, J. S. Vivek et al., “Phytoremediation of heavy metals: mechanisms, methods and enhancements,” Environmental Chemistry Letters, vol. 16, no. 4, pp. 1339–1359, 2018.
View at: Publisher Site | Google Scholar
B. Hameed, A. Din, and A. Ahmad, “Adsorption of methylene blue onto bamboo-based activated carbon: kinetics and equilibrium studies,” Journal of Hazardous Materials, vol. 141, no. 3, pp. 819–825, 2007.
View at: Publisher Site | Google Scholar
J.-x. Yu, X.-l. Cai, L.-y. Feng et al., “Synergistic and competitive adsorption of cationic and anionic dyes on polymer modified yeast prepared at room temperature,” Journal of the Taiwan Institute of Chemical Engineers, vol. 57, pp. 98–103, 2015.
View at: Publisher Site | Google Scholar
Y. Zhang, D. Qian, D. Wu, and X. Ma, “Magnetic halloysite nanotubes/iron oxide composites for the adsorption of dyes,” Chemical Engineering Journal, vol. 168, no. 2, pp. 959–963, 2011.
View at: Publisher Site | Google Scholar
X. Yao, Z. Huang, L. Chen et al., “Alumina-nickel composites densified by spark plasma sintering,” Materials Letters, vol. 59, no. 18, pp. 2314–2318, 2005.
View at: Publisher Site | Google Scholar
C. E. H. Bawn, “The adsorption of gases and vapors on plane surfaces,” Journal of the American Chemical Society, vol. 54, no. 1, pp. 72–86, 1932.
View at: Publisher Site | Google Scholar
C. Mahamadi and T. Nharingo, “Utilization of water hyacinth weed (Eichhornia crassipes) for the removal of Pb(II), Cd(II) and Zn(II) from aquatic environments: an adsorption isotherm study,” Environmental Technology, vol. 31, no. 11, pp. 1221–1228, 2010.
View at: Publisher Site | Google Scholar
P. Taylor, M. Foroughi-dahr, and H. Abolghasemi, “Adsorption characteristics of congo red from aqueous solution onto tea waste,” Chemical Engineering Communications, vol. 202, no. 2, pp. 37–41, 2014.
View at: Google Scholar
P. N. Palanisamy, A. Agalya, and P. Sivakumar, “Polymer composite-a potential biomaterial for the removal of reactive dye,” E-journal of Chemistry, vol. 9, no. 4, pp. 1823–1834, 2012.
View at: Publisher Site | Google Scholar
W. C. Wanyonyi, J. M. Onyari, and P. M. Shiundu, “Adsorption of congo red dye from aqueous solutions using roots of Eichhornia crassipes: kinetic and equilibrium studies,” Energy Procedia, vol. 50, pp. 862–869, 2014.
View at: Publisher Site | Google Scholar
I. J. Idan and T. S. Y. Choong, “Equilibrium , kinetics and thermodynamic adsorption studies of acid dyes on adsorbent developed from kenaf core fiber,” Adsorption Science & Technology, vol. 36, no. 12, pp. 694–712, 2018.
View at: Publisher Site | Google Scholar
A. Sharma, N. Verma, A. Sharma, D. Deva, and N. Sankararamakrishnan, “Iron doped phenolic resin based activated carbon micro and nanoparticles by milling: synthesis, characterization and application in arsenic removal,” Chemical Engineering Science, vol. 65, no. 11, pp. 3591–3601, 2010.
View at: Publisher Site | Google Scholar
Y. S. Ho and G. McKay, “Pseudo-second order model for sorption processes,” Process Biochemistry, vol. 34, no. 5, pp. 451–465, 1999.
View at: Publisher Site | Google Scholar
E. Demirbas, M. Kobya, and M. T. Sulak, “Adsorption kinetics of a basic dye from aqueous solutions onto apricot stone activated carbon,” Bioresource Technology, vol. 99, no. 13, pp. 5368–5373, 2008.
View at: Publisher Site | Google Scholar
E. N. El Qada, S. J. Allen, and G. M. Walker, “Adsorption of basic dyes from aqueous solution onto activated carbons,” Chemical Engineering Journal, vol. 135, no. 3, pp. 174–184, 2008.
View at: Publisher Site | Google Scholar
V. Karthik, N. Sivarajasekar, V. C. Padmanaban, E. Nakkeeran, and N. Selvaraju, “Biosorption of xenobiotic reactive black B onto metabolically inactive T. harzianum biomass: optimization and equilibrium studies,” International Journal of Environmental Science and Technology, vol. 16, no. 7, pp. 3625–3636, 2019.
View at: Publisher Site | Google Scholar
G. Z. Kyzas, M. Kostoglou, and N. K. Lazaridis, “Relating interactions of dye molecules with chitosan to adsorption kinetic data,” Langmuir, vol. 26, no. 10, pp. 9617–9626, 2010.
View at: Publisher Site | Google Scholar
V. Karthik, K. Saravanan, C. Patra, B. Ushadevi, S. Vairam, and N. Selvaraju, “Biosorption of acid yellow 12 from simulated wastewater by non-viable T. harzianum: kinetics, isotherm and thermodynamic studies,” International Journal of Environmental Science and Technology, vol. 16, no. 11, pp. 6895–6906, 2019.
View at: Publisher Site | Google Scholar
P. Senthil Kumar, S. Ramalingam, C. Senthamarai, M. Niranjanaa, P. Vijayalakshmi, and S. Sivanesan, “Adsorption of dye from aqueous solution by cashew nut shell: studies on equilibrium isotherm, kinetics and thermodynamics of interactions,” Desalination, vol. 261, no. 1-2, pp. 52–60, 2010.
View at: Publisher Site | Google Scholar
V. Vimonses, S. Lei, B. Jin, C. W. K. Chow, and C. Saint, “Kinetic study and equilibrium isotherm analysis of congo red adsorption by clay materials,” Chemical Engineering Journal, vol. 148, no. 3, pp. 354–364, 2009.
View at: Publisher Site | Google Scholar
J. Mohammed, U. I. Noah, I. Jibrin, K. S. Madaki, and S. I. Audu, “Equilibrium, kinetics and thermodynamic studies on the removal of safranin-O from waste water using activated carbons derived from coconut shell and pineapple peel,” American Journal of Physical Chemistry, vol. 8, no. 1, pp. 1–10, 2019.
View at: Publisher Site | Google Scholar
N. Laskar and UpendraKumar, “Adsorption of safranin (cationic) dye from water by Bambusa tulda : characterization and ANN modeling,” Environmental Engineering Science, vol. 35, no. 12, pp. 1–15, 2018.
View at: Publisher Site | Google Scholar
S. Chowdhury, R. Mishra, P. Kushwaha, and P. Saha, “Removal of safranin from aqueous solutions by NaOH-treated rice husk: thermodynamics, kinetics and isosteric heat of adsorption,” Asia-Pacific Journal of Chemical Engineering, vol. 7, no. 2, pp. 236–249, 2010.
View at: Publisher Site | Google Scholar
A. Tyagi, S. Das, and V. C. Srivastava, “Removal of toxic hydroquinone : comparative studies on use of iron impregnated granular activated carbon as an adsorbent and catalyst,” Environmental Engineering Research, vol. 24, no. 3, pp. 474–483, 2018.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2020 V. Karthik et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1589

Downloads

954

Citations