Poly(dimethylsiloxane) Surface Modification by Plasma Treatment for DNA Hybridization Applications
In this work, the surface modification of poly(dimethylsiloxane) (PDMS) was carried out by using a 2-step plasma modification with Ar followed by acrylic acid (AAc). The optimal conditions were found to be 0.5 min with Ar at 0.7 mbar; and 5 min with AAc at 0.2 mbar. The water contact angle (WCA) of the native PDMS decreased from 110° to 30° after modification, then stabilized to values between 50° to 60° after 1 day exposure to air. The stability of the modified PDMS was further improved by Soxhlet-extracting the PDMS with hexane prior to plasma treatment. Atomic force microscopy (AFM) showed significant changes in surface morphology after the 2-step plasma modification. X-ray photoelectron (XPS) spectroscopy further confirmed the successful modification of the PDMS surface with PAAc, by exhibiting C1s peaks at 285.9 eV, 287.4 eV and 289.9 eV, originating from C–O, C=O and O–C=O moieties, respectively. Fourier transform infrared-attenuated total reflection (FTIR-ATR) spectroscopy of the poly(acrylic acid) (PAAc) modified PDMS surface showed a distinctive peak at 1715 cm−1, attributed to the presence of COOH groups from the PAAc. The carboxyl peak on the spectra of the PAAc modified PDMS was quite stable even after storage at room temperature in phosphate buffer saline (PBS) and N-2-hydroxyethylpiperazine-N′-2-ethanesulfonic acid (HEPES) buffer for 17 h.5′-amino-terminated oligonucleotides were covalently attached to the PAAc modified PDMS surface via carbodiimide coupling. Subsequently, fluorescently tagged complementary oligonucleotides were successfully hybridized to this surface, as determined by fluorescence microscopy.
Keywords: DNA HYBRIDIZATION; MICROFLUIDICS; PLASMA; POLY(DIMETHYLSILOXANE) (PDMS); SURFACE MODIFICATION
Document Type: Research Article
Publication date: 01 November 2010
- Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
- Editorial Board
- Information for Authors
- Subscribe to this Title
- Terms & Conditions
- Ingenta Connect is not responsible for the content or availability of external websites
- Access Key
- Free content
- Partial Free content
- New content
- Open access content
- Partial Open access content
- Subscribed content
- Partial Subscribed content
- Free trial content