Figures
Abstract
Biochar produced by pyrolysis of biomass can be used to counter nitrogen (N) pollution. The present study investigated the effects of feedstock and temperature on characteristics of biochars and their adsorption ability for ammonium N (NH4+-N) and nitrate N (NO3−-N). Twelve biochars were produced from wheat-straw (W-BC), corn-straw (C-BC) and peanut-shell (P-BC) at pyrolysis temperatures of 400, 500, 600 and 700°C. Biochar physical and chemical properties were determined and the biochars were used for N sorption experiments. The results showed that biochar yield and contents of N, hydrogen and oxygen decreased as pyrolysis temperature increased from 400°C to 700°C, whereas contents of ash, pH and carbon increased with greater pyrolysis temperature. All biochars could sorb substantial amounts of NH4+-N, and the sorption characteristics were well fitted to the Freundlich isotherm model. The ability of biochars to adsorb NH4+-N followed: C-BC>P-BC>W-BC, and the adsorption amount decreased with higher pyrolysis temperature. The ability of C-BC to sorb NH4+-N was the highest because it had the largest cation exchange capacity (CEC) among all biochars (e.g., C-BC400 with a CEC of 38.3 cmol kg−1 adsorbed 2.3 mg NH4+-N g−1 in solutions with 50 mg NH4+ L−1). Compared with NH4+-N, none of NO3−-N was adsorbed to biochars at different NO3− concentrations. Instead, some NO3−-N was even released from the biochar materials. We conclude that biochars can be used under conditions where NH4+-N (or NH3) pollution is a concern, but further research is needed in terms of applying biochars to reduce NO3−-N pollution.
Citation: Gai X, Wang H, Liu J, Zhai L, Liu S, Ren T, et al. (2014) Effects of Feedstock and Pyrolysis Temperature on Biochar Adsorption of Ammonium and Nitrate. PLoS ONE 9(12): e113888. https://doi.org/10.1371/journal.pone.0113888
Editor: Jonathan A. Coles, Glasgow University, United Kingdom
Received: August 23, 2014; Accepted: October 31, 2014; Published: December 3, 2014
Copyright: © 2014 Gai et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.
Data Availability: The authors confirm that all data underlying the findings are fully available without restriction. All relevant data are within the paper and its Supporting Information files.
Funding: This study was financially supported by the National Natural Science Foundation of China (41301311), the Special Fund for Agro-scientific Research in the Public Interest (201303095-10), and the National Natural Science Foundation of China (41203072). The funders had no role in study design, data collection and analysis, decision to publish, or preparation of the manuscript.
Competing interests: The authors have declared that no competing interests exist.
Introduction
Today, biochar is receiving great research attention due to its potential importance in agronomic and environmental applications. Biochar refers to a carbon (C)-rich and porous substance, which is produced by thermal decomposition of biomass under oxygen-limited conditions and at relatively low temperatures (<700°C) [1]. It has a high specific surface area, a high density of negative surface charges, and characteristic pores and surface functional groups [2]. Biochar has been reported to be able to improve soil fertility by sequestrating C and enhancing retention of nutrients [2]–[5] and to suppress greenhouse gas emissions to the air [6].
Leaching of nitrogen (N) from agricultural land caused by excessive application of N fertilizers may pose a great threat to the quality of surface- and groundwater, and results in eutrophication of water bodies [7]. This is a particular concern in China that is consuming about one third of the total N fertilizers in the world [8]. Biochar is considered as a potential applicable material to mitigate N leaching, since a few studies have indicated that it can affect availability and cycling of N in the soil [9]–[12]. However, confounding results have been reported with regard to the effect of biochar application on N leaching. For example, Ding et al. [10] observed a reduction of NH4+-N leaching at 0.2-m soil depth by 15% and Laird et al. [11] observed a reduction of total N leaching by 11% in typical US Midwestern agricultural soils after addition of biochar to the surface soil layer. Based on these findings, they concluded that biochar, mainly owing to a high N sorption capacity, can be used as an effective soil amendment to reduce N losses from soils. However, some studies oppositely showed a limited or no ability of biochar to adsorb NO3−-N. For instance, Hollister et al. [13] observed no adsorption of NO3− to biochar derived from corn (Zea mays L.) or oak (Quercus spp.). Yao et al. [14] found nine of thirteen biochars tested had little NO3− adsorption ability and some even released NO3− into water solution. These contradictory results are likely because of the differences in properties among the biochars, which poses an urgent need to disclose the relationship between biochar characteristics and their effects on adsorption of NH4+-N and NO3−-N.
Feedstock and temperature during pyrolysis can influence molecular structure and pores size distribution of biochar, and thus affect biochar sorption characteristics [15]–[16]. Sohi et al. [17] reported that different feedstocks resulted in different magnitudes of surface area, pores and functional groups in biochars, and all these variables affect sorption characteristics of biochars. Sun et al. [18] reported that poultry-litter biochar had a larger specific surface area and porosity than wheat-straw biochar, despite the two biochars were produced under the same temperature (400°C). In general, high pyrolysis temperature leads to greater specific surface area and aromaticity of biochar [15]. For example, charcoal made from wheat residue at 500–700°C is well carbonized and its specific surface area is relatively high (>300 m2 g−1), whereas chars formed at 300–400°C are partially carbonized and have a lower specific surface area (<200 m2 g−1) [19]. Moreover, low-temperature biochars (250–400°C) will probably be more suitable for improving soil fertility than high-temperature ones due to the relatively stable aromatic backbone from pyrolysis and more C = O and C-H functional groups which may serve as nutrient exchange sites after oxidation [20]. Addition of low-temperature biochars to soils was reported to improve soil fertility by raising soil cation exchange capacity (CEC) [2]. On the other hand, Gell et al. [21] reported that low temperature biochars were more phytotoxic due to accumulation of tars and other organic compounds. So temperature of pyrolysis plays a great role in biochar properties. Moreover, decrease of atomic ratios H/C and O/C resulted from removing H- and O-containing functional groups with increasing temperature will produce high aromaticity and low polarity biochars [22].
In recent years, development of new techniques has provided a great opportunity to better understand biochar components and structures. These new techniques include Fourier transform-infrared spectroscopy (FT-IR) and field emission-scanning electron microscopy (FE-SEM), which can be used to characterize the surface functional groups and micro-morphology of biochars. The main objectives of this study were to (i) investigate the effects of feedstock types and pyrolysis temperature on biochar characteristics related to N adsorption ability; and (ii) determine the main factors affecting the adsorption of NH4+-N and NO3−-N to biochars. These will help to gain insights in use of biochar to mitigate nonpoint source pollution from agricultural soils.
Materials and Methods
Preparation of biochars
Biochar samples were produced from three common agricultural by-products: wheat-straw, corn-straw and peanut-shell. Raw materials were cut into small pieces (2 cm) and oven-dried (70°C) for 2 days after washing with deionized (DI) water for five times. The materials were then ground and sieved to yield a uniform 1 mm size fraction, and converted to biochar under oxygen-limited conditions using a muffle furnace (SXZ-12-10). To minimize oxygen content at reaction, the container was filled with the feedstock materials and tightly sealed. The pyrolysis temperature was raised to the aimed values of 400°C, 500°C, 600°C and 700°C and held constant for 1.5 h [19]. Biochar yields were recorded and the resulting twelve biochar samples were hereafter referred as W-BC400, W-BC500, W-BC600, W-BC700, C-BC400, C-BC500, C-BC600, C-BC700, P-BC400, P-BC500, P-BC600 and P-BC700. The biochar production rate at each temperature was calculated as: Production rate (%) = (MBiochar/MFeedstock) ×100, where MBiochar is the mass of biochar and MFeedstock is the mass of feedstock, both on a basis of dry weight. Detailed information about the chemical and physical characteristics of biochars is listed in Table 1 and Table 2.
The crude product of biomass pyrolysis includes biochar and ash. To investigate the possible effects of ash on the sorption properties, samples of ash-free biochar were prepared. Crude biochar produced at 500°C was suspended in either 1 mol L−1 H2SO4 or DI water at 1.5 g in 30 mL and agitated for 2 h in an ultrasound bath [19]. Then the suspension was pumping filtrated until the pH of the filtrate stabilized between two consecutive extractions (±pH 0.02), and the filter cake was oven-dried (70°C) to obtain the treated biochars for further adsorption experiments. The acid-washed biochar is denoted as A-W-BC500, A-C-BC500, A-P-BC500, while the DI water-washed biochar as W-W-BC500, W-C-BC500, W-P-BC500. The biochar production rate and chemical compositions after washing are listed in Table 1.
Determination of physical and chemical properties of the biochars
The specific surface area and porous texture of biochar were determined from N2 adsorption isotherms at 77 K with a Surface Area and Porosity Analyzer (ASAP 2020 HD88, USA). Biochar samples were degassed under vacuum at 363 K for 1 h and at 623 K for another 3 h, before being filled with N2 gas at different vapor pressures. The N2 adsorbed per g biochar was plotted versus the relative vapor pressure (P/Po) of N2 ranging from 0.02 to 0.2, and the data was fitted to the Brunauer-Emmett-Teller equation (BET) by computer to calculate surface area [23]. Biochar shapes and surface physical morphology were examined using FE-SEM (SU8000, Hitachi, Tokyo, Japan) at 15 KeV. The X-ray powder diffraction (XRD) patterns were determined using a Macscience-M18XHF instrument (UK) with Cu-Ka radiation at 40 mA and 40 kV. The data was collected over a 2θ range of 10–90° using the Cu-Ka radiation at a scan rate of 2° min−1 [23]. The FT-IR spectra were recorded on Bruker Vertex 70 Fourier transform infrared spectrometer using the oven-dried KBr (at 105–110°C) pellet technique (1∶100). The total number of scans was 32 with the spectral resolution of 4 cm−1.
Elemental contents of C, N, hydrogen (H) and oxygen (O) were determined using the Elemental Analyzer (vario PYRO cube). Biochar pH was measured using a pH meter (Mettler Toledo Delta 320) and electrical conductivity (EC) was by an electrical conductivity meter (DDS-307A), both with biochar to DI water ratio of 1∶30 w/w, after stirring for 1.5 min and equilibration for 1 h. Ash was separated by placing biochar sample in a nickel crucible and it was heated at 700°C for 2 h under air [24]. The content of ash was calculated as: Ash content (%) = (MAsh/MBiochar) ×100, where MAsh was the mass of ash and MBiochar was the mass of biochar. The CEC of biochar was measured by a modified NH4+-acetate compulsory displacement method [25]. An amount of 0.2 g biochar was leached with 20 mL DI water for five times, and the contents of K+, Na+, Ca2+ and Mg2+ in the collective leachate were determined as the soluble base cations of the biochar. After this, the biochar sample was leached with 20 mL of 1 M Na+-acetate (pH 7) for five times to determine K+, Ca2+ and Mg2+ in the leachate as the exchangeable base cations. The biochar samples were then washed with 20 mL of ethanol for five times to remove the excessive Na+. Afterwards, the Na+ on the exchangeable sites of the biochar was displaced by 20 mL of 1 mol NH4+-acetate (pH 7) for five times, and CEC was calculated from the Na+ displaced by NH4+. The contents of K+ and Na+ in the leachate were determined by flame photometry, and Ca2+ and Mg2+ by atomic absorption spectrometry.
Sorption experiments
To investigate the ability of biochars to adsorb NH4+-N and NO3−-N, adsorption experiments were conducted by adding biochar samples to water solutions with different concentrations of NH4+-N and NO3−-N. The same experimental procedure was used for each type of biochar (excluding those treated with acid and DI water) and N solution. Specifically, 0.2 g biochar was added to 50 mL NH4Cl (or KNO3) solutions with concentrations of 10, 30, 50, 70, 100, 150, 300 and 500 mg NH4+ (or NO3−) L−1, respectively. The mixture was then shaken in a thermostatic shaker at 25°C and 200 rpm for 24 h to achieve equilibrium. The supernatant was filtered and analyzed for concentrations of NH4+-N (or NO3−-N) by a Flow Injector Auto analyzer (Auto Analyzer 3, High Resolution Digital Colorimeter). For the biochar samples treated with acid and DI water, the adsorption experiments were conducted only in NH4Cl (or KNO3) solution with 50 mg NH4+ (or NO3−) L−1, while the other experimental procedures were the same as for the non-washed biochar samples. The experiment for each sample was run in triplicate. The amount of NH4+-N (or NO3−-N) adsorbed on biochar was calculated as the difference between the original NH4+-N (or NO3−-N) concentration and the remaining aqueous concentration at equilibrium. The amount of NH4+-N (or NO3−-N) adsorbed per unit mass of biochar was calculated as Eq.1 [26].(1)where, Qe is the amount of N adsorbed by biochars (mg g−1) at equilibrium; C0 and Ce are the NH4+-N (or NO3−-N) concentration in the initial and equilibrium solution (mg L−1), respectively; V is the volume of the aqueous solution (L) and M is the mass of biochar (g).
Statistical analysis
The NH4+-N and NO3−-N sorption data were fitted to linear Freundlich and Langmuir models, which are the most frequently used models for describing sorption isotherms. The Freundlich adsorption model is as Eq. 2 [13]:(2)where, Qe is mass of NH4+-N or NO3−-N adsorbed per mass of biochar (mg g−1) at equilibrium; Ce is equilibrium concentration (mg L−1) of NH4+-N or NO3−-N in solution; KF and 1/n are experimentally derived constants.
The Langmuir isotherm model, which assumes homogeneous monolayer surface sorption, can be written as Eq.3 [10]: (3)where, Qm is the maximum sorption capacity of biochar (mg g−1), and KL refers to the Langmuir constants related to adsorption capacity and adsorption rate. When Ce/Qe is plotted against Ce, a straight line with a slope of 1/Qm and an intercept of 1/(Qm KL) is obtained.
The results were expressed as means and standard deviations. Figures were plotted with the Origin 8.1 software. Statistical analysis was performed using Statistical Analysis System (SAS, version 9.1). Significant differences were tested using Duncan's multiple range test (P = 0.05) and the correlation was analyzed with the Pearson test (two-tailed) at P = 0.05. Any differences between the mean values at P<0.05 were considered statistically significant.
Results and Discussion
Yields and element contents of different biochars
The yields and element contents of biochars from wheat-straw, corn-straw and peanut-shell at four different pyrolysis temperatures of 400, 500, 600 and 700°C are given in Table 1. The yields of W-BC, C-BC and P-BC samples were reduced from 32.4%–36.8% to 22.8%–25.8% as pyrolysis temperature increased from 400 to 700°C. This is due to greater losses of volatile components at the higher pyrolysis temperatures [20].
Content of C, which is the major constituent of the biochars, increased with higher pyrolysis temperature for W-BC, C-BC and P-BC (Table 1). This was due to highly carbonization at high temperature (600°C and 700°C), with a high degree of C in aromatic structures [20]. However, contents of H and O decreased by approximately 60% and 30%, respectively, as pyrolysis temperature increased from 400°C to 700°C (Table 1). This was attributed to the removal of water, hydrocarbons, tarry vapors, H2, CO and CO2 during the carbonization process [26]. Some of these H and O contents are likely presented in organic functional groups on biochar surface [19]. Decrease of their contents is likely to result in a reduction in N sorption capacity. The biochar samples contained small amount of N (W-BC, 1.2–1.5%; C-BC, 1.6–2.4%; P-BC, 1.4–1.8%) and the N content remained relatively stable, which was consistent with the findings by Zheng et al. [23]. However, content of N in C-BC was always higher than that in W-BC and P-BC at a given temperature. This is most likely because corn straws had a much higher content of total N (17.2 g kg−1) than wheat straws (10.5 g kg−1) and peanut shells (12.4 g kg−1). Atomic ratios of elements, which estimates the aromaticity (H/C) and polarity (O/C, (O+N)/C) of the biochars, were significantly affected by pyrolysis temperature (Table 1). A higher H/C ratio shows a lower degree of carbonization and aromaticity of the biochar [19]. The atomic O/C ratios were also lower in W-BC700 (0.30), C-BC700 (0.42) and P-BC700 (0.29) than those in W-BC400 (0.56), C-BC400 (0.59) and P-BC400 (0.54), indicating the less hydrophilic surface of biochars at higher temperature [19].
Acid washing effectively removed most of the inorganic fractions from the three biochars (63.3–89.6%). Both acid and DI water washing affected the relative contents of the remaining elements in the biochars. Specifically, washing caused the proportion of C to increase, but not the proportions of H, N and O. Moreover, washing decreased the H/C and O/C atomic ratios in the biochars (Table 1).
Characteristics of different biochars
1. pH and EC values of biochars.
All biochars produced in this study were alkaline, with a pH between 8.2 and 10.4 (Table 2). This range of pH is common for thermally produced biochars [1], [27]. In terms of different feedstocks, the pH values of W-BC (8.2–9.2) and P-BC (9.3–9.9) were lower than C-BC (10.2–10.4). The biochar pH significantly increased with higher pyrolysis temperature (P<0.05) (Table 2). For example, C-BC had a pH of 10.2 at 400°C and 10.4 at 700°C, which was consistent with the finding by Hossain et al. [28].
The biochars from the three feedstocks had a similar trend of EC values, that is, the values increased significantly with the higher pyrolysis temperature (Table 2). This apparent effect of pyrolysis temperature on EC values was consistent with the results of Cantrell et al. [29] and Quilliam et al. [30]. The EC estimates the amount of total dissolved salts or the total amount of dissolved ions in samples [10]. Its increase with pyrolysis temperature was likely due to loss of volatile materials at high temperatures, which promoted the relative concentrations of salts in the ash fraction.
2. Ash contents and CEC of biochars.
Ash contents in different biochars ranged from 11% to 18%, which were low compared with those in their feedstocks (wheat-straw 28%, corn-straw 31% and peanut-shell 27%). Apparently, ash content increased with rise in temperature due to increased concentrations of minerals and organic combustion residues [31]. Change of ash content in the biochars with temperature had a trend similar to that of biochars originated from other organic wastes such as pine needle and animal manure [32].
Biochar CEC values significantly differed with both feedstock and pyrolysis temperature. The CEC of C-BC (19.0–68.6 cmol kg−1) was much higher than that of P-BC (0.3–8.5 cmol kg−1) and W-BC (0.5–5.1 cmol kg−1), despite the fact that they had similar CEC in feedstocks (9.8–14 cmol kg−1). The trend of CEC changing with pyrolysis temperature was similar for the biochars from all feedstocks. All biochars pyrolysed at 400°C and 500°C had higher CEC than that at 600°C and 700°C. Whereas in the findings of Yuan et al. [24], CEC of biochar prepared from corn at 500°C was higher than that at 300°C and 700°C; and CEC of biochar prepared from peanut at 700°C was higher than that at 300°C and 500°C.
3. Specific surface area and morphology structures of biochars.
Specific surface area, pore volume and pore size of the biochars obtained from different feedstocks are summarized in Table 2. Biochar SBET ranged from 3 to 185 m2 g−1, which was significantly affected by biochar feedstock and pyrolysis temperature [33]. In general, the SBET of C-BC was much lower than that of W-BC and P-BC. Ahmad et al. [22] attributed this difference to the compositional compounds (lignin, cellulose and hemicellulose) in the original feedstocks, but the mechanisms behind were not clear. The SBET of C-BC, W-BC and P-BC showed the same trend as affected by temperature, that is, SBET increased as the temperature increased from 400 to 600°C, but substantially decreased at 700°C (Table 2). This is likely because of the removal of H- and O-carrying functional groups, including aliphatic alkyl-CH2, ester C = O, aromatic -CO and phenolic -OH groups, in biochars produced at 600°C, greatly enlarged their surface areas [32].
Pore structures of biochars as described by FE-SEM provide information about the structural change in biochar particles after thermal treatment. After pyrolysis, the biochars obtained rough surface and multiple sizes of pores, which resulted in a large specific surface area, a very important property for being sorbent materials [1]. FE-SEM micrographs of the morphological changes in the pore structure of the biochars at different temperatures and with different washing treatments implied that the clear and well-developed pore structure of the biochar consisted of cylinder-like tubes. The FE-SEM micrographs of C-BC as an example are shown in Figure S1a–f. The biochars contained microparticles and micropores, and the unregular fold structure changed into regular layer with the increasing temperature. But at 700°C, the biochars showed laminated texture. FE-SEM micrographs also demonstrated a homogeneous pore size distribution with a pore arrangement, and the pores in the inner portion of the biochars were obvious and well arranged in an array of cylinder-like structures. The above features of the FE-SEM micrographs, such as well-developed pore structure and pore size distribution, implied an excellent possibility for NH4+-N to be adsorbed by the biochars according to Sun et al. [34]. Compared with the non-washed C-BC500, biochar treated with diluted H2SO4 and DI water had some convexity structures (Figure S1e–f), and the pores increased after washing with acid.
4. Crystal structure of biochars.
Spectra for biochar crystal structure determined by XRD are shown in Figure S2a–c. Sharp peaks in all samples indicated presence of miscellaneous inorganic components, which suggested that there were quartz and sylvite in the biochar [24]. The XRD patterns for C-BC revealed sharp peaks, which showed a high degree of crystallinity with characteristic peaks at 26.6° (Figure S2b). The values matched the characteristic peaks of silicate carbonaceous (SiCO32−) material, according to the database of the Joint Committee on Powder Diffraction Standards [34]. The XRD spectra analysis revealed that W-BCs (Figure S2a) and P-BCs (Figure S2c) had similar crystal substances as in C-BCs. Moreover, peak intensities decreased with higher temperature, indicating that inorganic components were well crystallized during low-temperature pyrolysis process [23]. However, the XRD spectra of different feedstocks at the same pyrolysis temperature showed no significant difference among the three types of biochars.
5. Surface functional groups of biochars.
The FT-IR spectra of the twelve biochars are illustrated in Figure 1a–c. Different spectra reflected changes in the surface functional groups of biochars produced at different temperatures. The peak assignments in the spectra represented methyl C-H stretching compounds (∼2930 cm−1), methylene C-H stretching (∼2860 cm−1), aromatic carbonyl/carboxyl C = O (∼1700 cm−1), aromatic C = C and C = O (∼1600 cm−1), aliphatic C-O-C and alcohol-OH (1160–1030 cm−1), and aromatic C-H (∼815 cm−1) [18]. All these bands experienced different changes with increasing pyrolytic temperature, which is consistent with the study of Chen et al. [32]. At low pyrolysis temperatures (400–500°C) for W-BC, the band intensities were at 3438 cm−1 (-OH), which dramatically decreased and almost diminished at 600–700°C, whereas other bands (e.g., -CH2-, C = C and ester C = O) were preserved. The polar groups (-OH and C-O) exhibited the lower magnitude of peaks upon heating at high temperature (600°C and 700°C), suggesting a decrease in the polar functional groups with an increase in pyrolysis temperature. The maximum loss occurred in -OH, CH2- and C-O functional groups in biochars produced at 700°C, which was also apparent from their elemental compositions and element atomic ratio (Table 1). Thermal destruction of cellulose and lignin in the feedstocks might result in the exposure of aliphatic alkyl CH2-, hydroxyl -OH, ester C = O and aromatic C = O functional groups in biochars [32]. The changes in the peaks and their intensities and consequently functional groups of C-BC and P-BC were similar to those of W-BC. This is a result of strong dependence of the extent of carbonization on production temperature [31].
The comparisons of the functional groups between washed and non-washed biochars, as determined by FT-IR spectra, are presented in Figure 1d–f. After different treatments, the bands of W-BC, C-BC and P-BC changed considerably. FT-IR spectra confirmed that acid and DI water washing effectively removed most of the inorganic fractions of biochars. As seen from the FT-IR spectra in W-BC (Figure 1d), surface functional groups did not change by washing, which was supported by other studies [19], [32]. Compared with C-BC500 (Figure 1e), there were some differences in the FT-IR spectrum of A-C-BC500 and W-C-BC500. The strong peak at 1446 cm−1 (aromatic C = C) and 1600 cm−1 (-OH) decreased due to C condensation for A-C-BC500 and W-C-BC500 [35]. There was no peak at 1109 cm−1 (C-O-C) in C-BC500 and the new aromatic structure formed in A-C-BC500. But for P-BC (Figure 1f), the FT-IR spectra showed great difference. Compared with the non-washed samples, acid-washing decreased the intensities of surface functional groups at 3438 cm−1 (-OH) and 1600 cm−1 (aromatic C = C and C = O), but they were increased by DI water-washing. In addition, CH2- (1438 cm−1) diminished with acid- and DI water-washing.
Ammonium nitrogen sorption on different types of biochars
The equilibrium adsorption isotherms of NH4+-N, which are essential to understand the mechanism controlling biochar adsorption process, are presented in Figure 2a–c. The twelve tested biochars had considerable NH4+-N sorption capacity, e.g. 0.5–2.4 mg NH4+-N g−1 at an initial NH4+ concentration of 50 mg L−1. Biochars usually carry negative surface charges, which enhances the ability of soil to adsorb and retain cations (e.g. NH4+) and thus inhibit cation loss by leaching from acid soils [17], [20]. In general, C-BC had a greater NH4+-N sorption ability than W-BC and P-BC at a given pyrolysis temperature. For example, C-BC500 had a much higher Qe value than W-BC500 and P-BC500, when the initial NH4+ concentration was 50 mg L−1 (Table 3). More NH4+-N was adsorbed by the low-temperature biochars (400–500°C) than by the high-temperature biochars (600–700°C) for each feedstock at a given NH4+-N concentration. Taking an initial concentration of 100 mg NH4+ L−1 as an example, C-BC400 (Qe 3.6 mg g−1) and C-BC500 (Qe 3.0 mg g−1) had relatively higher Qe values than C-BC600 (2.8 mg g−1) and C-BC700 (2.4 mg g−1). Table 4 shows the Freundlich and Langmuir isotherm constants and NH4+-N adsorption correlation coefficients for different biochars. Sorption of NH4+-N to different biochars was better fitted to Freundlich isotherm model, with higher r values than that of Langmuir model. Despite both constants KF and n in Freundlich model affect NH4+-N adsorption isotherms, it seems KF plays a main role in reflecting differences of NH4+-N adsorption ability between biochars from different feedstocks. C-BC with a greater KF value in the isotherm had a relatively high NH4+-N sorption ability compared with W-BC and P-BC. Compared with the non-washed biochars, washing with acid and DI water reduced adsorption of NH4+-N, especially for C-BC500 (Table 3). This decrease in NH4+-N sorption ability is probably because ash was washed off from the biochar and some functional groups were removed from the biochar surface, Zheng et al. [36] stated that ash could substantially improve theNH4+-N adsorption capacity of biochars.
Bars indicate standard deviation of three replicates.
To investigate the main factors influencing biochar ability to adsorb NH4+-N, correlations between Qe and contents of elements and CEC of biochars were analyzed. The correlations for C-BCs as examples are shown in Figure 3a–f. The Qe values were negatively correlated with C contents (r = −0.9046) (Figure 3a). C-BC700 that had the highest C content among the C-BCs as a result of a high degree of carbonization at a high pyrolysis temperature [22], had the lowest adsorption amount of NH4+-N. In contrast, Qe was positively correlated with content of O in the biochar (r = 0.9104) (Figure 3b). This indicated that removal of the O-carrying functional groups with increasing pyrolysis temperature induced the increase in the hydrophobicity of the BC600 and the BC700. As mentioned above, the biochars produced at high pyrolysis temperatures had low polarity (i.e. low O/C ratio) and thus low ability to adsorb NH4+. Positive correlations between Qe and O/C (r = 0.9264), H/C (r = 0.8633) and (O+N)/C (r = 0.9275) were respectively observed (Figure 3c–e). All these implied a decrease in NH4+-N adsorption ability with decreasing polarity of biochars. In the present study, C-BCs had distinctly higher NH4+-N adsorption than W-BCs and P-BCs (Figure 2), despite the facts that C-BCs had obviously low specific surface area compared with the other biochars (Table 2). In addition, there was no clear trend of pore volume and pore size that could reflect the difference between biochars from different feedstocks, which was consistent with the finding by Yao et al. [14] in a test of thirteen biochars. These suggest that specific surface area and pore structures were not dominant factors affecting NH4+-N adsorption to biochars.
The symbols ▪, , ▴ and ▾ represented pyrolysis temperatures at 400°C, 500°C, 600°C and 700°C, respectively.
CEC seems to be the dominating factor influencing NH4+-N adsorption ability of biochars. The Qe values were positively correlated with CEC (r = 0.4633) (Figure 3f). That is to say, the biochars with higher CEC values had larger NH4+-N sorption capacity. In the present study, C-BC had a higher adsorption capacity compared with W-BC and P-BC (Figure 2), which is most likely to be a result of the higher CEC values. For example, at 50 mg NH4+ L−1 solutions, the C-BC with CEC of 19.0–68.6 cmol kg−1 presented obviously higher NH4+-N sorption capacity (1.6–2.3 mg g−1) than the W-BC (0.6–0.9 mg g−1) and P-BC (0.6–1.2 mg g−1) with CEC of 0.3–8.5 cmol kg−1. In addition, biochars derived from each feedstock at pyrolysis temperatures of 600–700°C had relatively low CEC, compared with those at 400–500°C (Table 2). For instance, the CEC values of C-BCs decreased by 72% when the pyrolysis temperatures increased from 500 to 700°C. Correspondingly, NH4+-N adsorption ability of the biochars decreased with increasing pyrolysis temperatures. The decrease in CEC with increasing temperature can be attributed to the loss of carboxyl functional groups during pyrolysis [2].
Nitrate nitrogen sorption on different types of biochars
In contrast to NH4+, no NO3−-N could be sorbed by W-BC400-700, C-BC400-700 and P-BC400-700 at series of NO3− concentrations (10–300 mg NO3− L−1). On contrary, these biochars even released NO3−-N into the solutions (Figure 4a–c). Disability of biochars to adsorb NO3−-N was in agreement with the previous sorption experiments with the biochar made from sugarcane (Saccharum officinarum L.) bagasse (particle sizes 250–500 mm) at a temperature range of 400 to 600°C [37]. In the present study, the six-biochars made at a lower temperature (400–500°C) released 0.25–0.40 mg NO3−-N g−1 to the solution with an initial NO3− concentration of 50 mg L−1 (Figure 4a–c). The other six biochars pyrolysed at higher temperatures released slightly less NO3−-N, at 0.16–0.32 mg g−1. Release of N in proportion of total N in biochar' ash was demonstrated with the following example. At an initial concentration of 10 mg NO3− L−1, the N content in the ash of C-BC400 was 2.4% and an amount of 17 mg NO3− was added with biochars to the 25 mL solution (Table 2). At equilibrium, the concentration of NO3− in the solution was 18.95 mg L−1. That is to say, the N released accounted for 2.1% of the total N in the C-BC400. However, these results were opposite with the findings of previous studies, which reported that NO3−-N could be sorbed by biochars. For example, Mizuta et al. [38] reported that bamboo biochar powder (−80 mm) made at 900°C had NO3−-N adsorption capacity of 20.2 mg g−1 as estimated by the Langmuir model. A recent study by Hollister et al. [13] demonstrated that approximately 1.6 mg NO3−-N g−1 was adsorbed by the 800°C treated bagasse-biochar in the solution with an initial concentration of 20 mg NO3−-N L−1. Meanwhile, one study on NO3−-N sorption to bamboo-biochar (300–500 µm) gave a maximum sorption capacity of 7.1 mg NO3−-N g−1 predicted with the Langmuir adsorption model [39]. The weak ability of biochar to adsorb NO3−-N at different NO3− concentrations in Mizuta et al. [38] and Hollister et al. [13] may be because their biochars were produced at a higher pyrolysis temperature (>800°C) than in the present study. Moreover, there may be other mechanisms involved to affect NO3−-N leaching in soil than direct adsorption of NO3−-N by biochars. Knowles et al. [40] found that biochar application reduced nitrate leaching from biosolid amended soils to levels at or below that in the control treatments in lysimeter experiments. Since we did not investigate the pyrolysis temperature higher than 700°C or N behavior in soil, further studies are needed in this regard to fully understand the mechanisms governing NO3−-N retention to biochars.
Bars indicate standard deviation of three replicates.
Washing with acid and DI water had a significant effect on biochar adsorption of NO3−-N (Table 3). In contrast to releasing of NO3−-N from the non-washed C-BC to solutions, small quantities of NO3−-N were adsorbed by A-C-BC (0.14 mg g−1) and W-C-BC (0.12 mg g−1) from 50 mg NO3− L−1 solutions. This trend was similar for W-BC and for P-BC (Table 3). First of all, washing with acid and DI water removed ash from biochars, and thus no NO3−-N was added with the biochar ash to the solution. In addition, removal of the ash from biochars might have created additional sorption sites on biochar surface and facilitated more sorption of NO3−-N [41]. Afkhami et al. [42] suggested that treatment of biochars with acid tends to produce positive sites on the biochars, by protonation of surface -OH groups that would cause an increase in electrostatic adsorption of anions.
Conclusions
Feedstock types and pyrolysis temperature greatly influenced the biochar chemical and physical characteristics, which further influenced N adsorption ability of the biochars. Adsorption of NH4+-N was predominantly affected by the CEC of biochars. The corn-straw biochar had the largest adsorption capacity for NH4+-N, in particular at a pyrolysis temperature of 400°C. In contrast, biochars released NO3−-N to the solutions rather than adsorb NO3−-N. However, retention of NO3−-N by biochar may be enhanced by promoting pyrolysis temperature or other mechanisms in soils. Therefore, we conclude that biochars, in particular corn-straw biochar (400°C), can be used under conditions where NH4+-N (or NH3) pollution is a concern, but further research is needed in terms of applying biochars to reduce NO3−-N pollution.
Supporting Information
Figure S1.
Field emission-scanning electron microscopy (FE-SEM) images of biochars derived from corn straw pyrolytic at different temperatures and with different treatments (a: 400°C, b: 500°C, c: 600°C, d: 700°C, e: 500°C and treated with diluted H2SO4, f: 500°C and treated with DI water).
https://doi.org/10.1371/journal.pone.0113888.s001
(DOCX)
Figure S2.
The X-ray diffraction (XRD) spectrum of wheat-straw biochar (W-BC), corn-straw biochar (C-BC) and peanut-shell biochar (P-BC) at different pyrolytic temperatures.
https://doi.org/10.1371/journal.pone.0113888.s002
(DOCX)
Acknowledgments
This work was conducted in the test station of Fluvo-aquic soil in Changping County, Beijing, China. Thanks for the assistance of BoYang, Qian Zhang and Bozhong Li.
Author Contributions
Conceived and designed the experiments: HBL HYW TZR. Performed the experiments: XPG SL. Analyzed the data: XPG HBL HYW JL LMZ TZR. Contributed reagents/materials/analysis tools: XPG HYW SL. Wrote the paper: XPG HYW JL.
References
- 1.
Lehmann J, Joseph S (2009) Biochar for environmental management: an introduction. in:Lehmann, JandJoseph, S. (Eds.)Biochar for environmental management–science and technology. Earthscan Publisher, UK and USA, p1–9.
- 2. Liang B, Lehmann J, Solomon D, Kinyangi J, Grossman J, et al. (2006) Black carbon increases cation exchange capacity in soils. Soil Sci Soc Am J 70:1719–1730.
- 3. Zhang AF, Bian RJ, Hussain Q, Li LQ, Pan GX, et al. (2013) Change in net global warming potential of a rice–wheat cropping system with biochar soil amendment in a rice paddy from China. Agric Ecosyst Environ 173:37–45.
- 4. Bruun EW, Hauggaard–Nielsen H, Ibrahim N, Egsgaard H, Ambus P, et al. (2011) Influence of fast pyrolysis temperature on biochar labile fraction and short–term carbon loss in a loamy soil. Biomass Bioenerg 35:1184–1189.
- 5.
Zhai LM, CaiJi Z, Liu J, Wang HY, Liu HB, et al. (2014). Short-term effects of maize residue biochar on phosphorus availability in two soils with different phosphorus sorption capacities. Biol Fertil Soils. (Published online).
- 6. Cayuela ML, van Zwieten L, Singh BP, Jeffery S, Roig A, et al. (2014) Biochar's role in mitigating soil nitrous oxide emissions: A review andmeta-analysis. Agric Ecosyst Environ 191:5–16.
- 7. Zhu AN, Zhang JB, Zhao BZ, Cheng ZH, Li LP (2005) Water balance and nitrate leaching losses under intensive crop production with Ochric Aquic Cambosols in North China Plain. Environ Int 31:904–912.
- 8.
IFA/IFDC/IPI/PPI/FAO. Fertilizer Use by Crop. 2009.
- 9. Galvez A, Sinicco T, Cayuela ML, Mingorance MD, Fornasier F, et al. (2012) Short term effects of bioenergy by–products on soil C and N dynamics, nutrient availability and biochemical properties. Agric Ecosyst Environ 160:3–14.
- 10. Ding Y, Liu YX, Wu WX, Shi DZ, Yang M, et al. (2010) Evaluation of biochar effects on nitrogen retention and leaching in multi–layered soil columns. Water Air Soil Poll 213:47–55.
- 11. Laird D, Fleming P, Wang B, Horton R, Karlen D (2010) Biochar impact on nutrient leaching from a Midwestern agricultural soil. Geoderma 158:436–442.
- 12. Lehmann J, Pereira da Silva J, Steiner C, Nehls T, Zech W, et al. (2003) Nutrient availability and leaching in an archaeological anthrosol and a ferralsol of the central amazon basin: fertilizer, manure and charcoal amendments. Plant Soil 249:343–357.
- 13. Hollister CC, Bisogni JJ, Lehmann J (2013) Ammonium, nitrate, and phosphate sorption to and solute leaching from biochars prepared from corn stover (Zea mays L.) and oak wood (Quercus spp.). J Environ Qual 42:137–144.
- 14. Yao Y, Gao B, Zhang M, Inyang M, Zimmerman AR (2012) Effect of biochar amendment on sorption and leaching of nitrate, ammonium, and phosphate in a sandy soil. Chemosphere 89:1467–1471.
- 15. Ahmad M, Lee SS, Dou XM, Mohan D, Sung JK, et al. (2012) Effects of pyrolysis temperature on soybean stover– and peanut shell–derived biochar properties and TCE adsorption in water. Bioresour Technol 118:536–544.
- 16. Keiluweit M, Nico PS, Johnson MG, Kleber M (2010) Dynamic molecular structure of plant biomass–derived black carbon (biochar). Environ Sci Technol 44:1247–1253.
- 17. Sohi SP, Krull E, Lopez-Capel E, Bol R (2010) A review of biochar and its use and function in soil. Adv Agron 105:47–82.
- 18. Sun K, Ro K, Guo MX, Novak J, Mashayekhi H, et al. (2011) Sorption of bisphenol A, 17a–ethinyl estradiol and phenanthrene on thermally and hydrothermally produced biochars. Bioresour Technol 102:5757–5763.
- 19. Chun Y, Sheng G, Chiou CT, Xing B (2004) Compositions and sorptive properties of crop residue–derived chars. Environ Sci Technol 38:4649–4655.
- 20. Novak JM, Lima I, Xing B, Gaskin JW, Steiner C, et al. (2009) Characterization of designer biochar produced at different temperatures and their effects on a loamy sand. Ann Environ Sci 3:2.
- 21. Gell K, van Groenigen JW, Cayuela ML (2011) Residues of bioenergy production chains as soil amendments: Immediate and temporal phytotoxicity. J Hazard Mater 186:2017–2025.
- 22. Ahmad M, Lee SS, Dou XM, Mohan D, Sung JK, et al. (2013) Trichloroethylene adsorption by pine needle biochars produced at various pyrolysis temperatures. Bioresour Technol 143:615–622.
- 23. Zheng H, Wang ZY, Deng X, Zhao J, Luo Y, et al. (2013) Characteristics and nutrient values of biochars produced from giant reed at different temperatures. Bioresour Technol 130:463–471.
- 24. Yuan JH, Xu RK, Zhang H (2011) The forms of alkalis in the biochar produced from crop residues at different temperatures. Bioresour Technol 102:3488–3497.
- 25. Gaskin JW, Steiner C, Harris K, Das KC, Bibens B (2008) Effect of low temperature pyrolysis conditions on biochar for agricultural use. Trans ASABE 51:2061–2069.
- 26. Ok YS, Yang JE, Zhang YS, Kim SJ, Chung DY, et al. (2007) Heavy metal adsorption by a formulated zeolite–Portl and cement mixture. J Hazard Mater 147:91–96.
- 27. Wu W, Yang M, Feng Q, McGrouther K, Wang H, et al. (2012) Chemical characterization of rice straw–derived biochar for soil amendment. Biomass Bioenerg 47:268–276.
- 28. Hossain MK, Strezov V, Chan KY, Ziolkowski A, Nelson PF (2011) Influence of pyrolysis temperature on production and nutrient properties of wastewater sludge biochar. J Environ Manage 92:223–228.
- 29. Cantrell KB, Hunt PG, Uchimiya M, Novak JM, Ro KS (2012) Impact of pyrolysis temperature and manure source on physicochemical characteristics of biochar. Bioresour Technol 107:419–428.
- 30. Quilliam RS, Marsden KA, Gertler C, Rousk J, DeLuca TH, et al. (2012) Nutrient dynamics, microbial growth and weed emergence in biochar amended soil are influenced by time since application and reapplication rate. Agric Ecosyst Environ 158:192–199.
- 31. Cao X, Harris W (2010) Properties of dairy–manure–derived biochar pertinent to its potential use in remediation. Bioresour Technol 101:5222–5228.
- 32. Chen B, Zhou D, Zhu L (2008) Transitional adsorption and partition of nonpolar and polar aromaric contaminants by biochars of pine needles with different pyrolytic temperatures. Environ Sci Technol 42:5137–5143.
- 33. Mimmo T, Panzacchi P, Baratieri M, Davies CA, Tonon G (2014) Effect of pyrolysis temperature on miscanthus (Miscanthus×giganteus) biochar physical, chemical and functional properties. Biomass Bioenerg 62:149–157.
- 34. Sun L, Wan SG, Luo WS (2013) Biochars prepared from anaerobic digestion residue, palm bark, and eucalyptus for adsorption of cationic methylene blue dye: Characterization, equilibrium, and kinetic studies. Bioresour Technol 140:406–413.
- 35. Zhao XC, Ouyang W, Hao FH, Lin CY, Wang FL, et al. (2013) Properties comparison of biochars from corn straw with different pretreatment and sorption behaviour of atrazine. Bioresour Technol 147:338–344.
- 36. Zheng H, Wang ZY, Zhao J, Herbert S, Xing BS (2013) Sorption of antibiotic sulfamethoxazole varies with biochars produced at different temperatures. Environ Pollut 181:60–67.
- 37. Kameyama K, Miyamoto T, Shiono T, Shinogi Y (2011) Influence of sugarcane bagasse–derived biochar application on nitrate leaching in calcaric dark red soil. J Environ Qual 41:1131–1137.
- 38. Mizuta K, Matsumoto T, Hatate Y, Nishihara K, Nakanishi T (2004) Removal of nitrate–nitrogen from drinking water using bamboo powder charcoal. Bioresour Technol 95:255–257.
- 39. Ohe K, Nagae Y, Nakamura S, Baba Y (2003) Removal of nitrate anion by carbonaceous materials prepared by bamboo and coconut shell. Chem Eng J 36:511–515.
- 40. Knowles OA, Robinson BH, Contangelo A, Clucas L (2011) Biochar for the mitigation of nitrate leaching from soil amended with biosolids. Sci Total Environ 409:3206–3210.
- 41. Ji L, Wan Y, Zheng S, Zhu D (2011) Adsorption of tetracycline and sulfamethoxazole on crop residue–derived ashes: implication for the relative importance of black carbon to soil sorption. Environ Sci Technol 45:5580–5586.
- 42. Afkhami A, Madrakian T, Karimi Z (2007) The effect of acid treatment of carbon cloth on the adsorption of nitrite and nitrate ions. J Hazard Mater 144:427–431.