Abstract
A new butt joining method for ceramics by microwave heating was developed. Ceramics were heated in a rectangular cavity, and a klystron of maximum 3 kW at 6 GHz was used as the power amplifier. The heating system can control an iris, a plunger, and the microwave power to maintain the power efficiency up to 90% and the accuracy within ±10°C at 1800 °C. This system was applied to alumina-alumina direct joining. The average strength of alumina rods (92% purity) joined for 3 min was 420 MPa, which was equal to the original strength. The joined boundary line at the interface was not observed, and there was little difference in microstructure between before and after joining. This suggests that sintering aids in the grain boundary phase were preferentially heated and melted, resulting in the sound joining of ceramics. Next, silicon nitride ceramics containing yttrium were indirectly joined with an intermediate, which was a sintered ceramic sheet having lower purity and larger dielectric loss factor than the base material. The microwave energy was concentrated on the ceramic sheet, so that only the joining area was locally heated. The strength of the joined rods was in excess of 70% of the base material, but a deficient layer of yttrium occurred in the area of the joined boundary.
Similar content being viewed by others
References
D. L. Johnson and M. E. Brodwin, U. S. Army Research Office, Grant No. DAAG 29-80-K-0031, 1984.
T. T. Meek and R. D. Blake, J. Mater. Sci. Lett. 5, 270 (1986).
D. Palaith, R. Silberglitt, and E. Libelo, Ceram. Mater. Conpor. Engines, 459 (1986).
F. Okada, S. Tashiro, and M. Suzuki, Adv. Ceram. 201 (1985).
H. Fukushima, T. Yamanaka, H. Azuma, and M. Matsui, J. Japan Soc. of Prec. Eng. 54, 305 (1988).
H. Fukushima, T. Yamanaka, and M. Matsui, J. Japan Soc. of Prec. Eng. 53, 743 (1987).
Phase Diagrams for Ceramics, Am. Ceram. Soc., 185 (1964).
A. Kohno, S. Hioki, T. Yamada, and N. Nakae, Brit. Ceram. Proc. 37, 125 (1986).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Fukushima, H., Yamanaka, T. & Matsui, M. Microwave heating of ceramics and its application to joining. Journal of Materials Research 5, 397–405 (1990). https://doi.org/10.1557/JMR.1990.0397
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1990.0397