Abstract
The impression creep behavior of lead was investigated using a 100 μm diameter punch at ambient and elevated temperatures (433 K-563 K) under punching stresses of 6–70 MPa. The results were compared with the data obtained from conventional creep tests reported in the literature. Unlike the indentation creep test, the impression creep test showed a steady-state velocity after a short transient period when the flat-end cylindrical punch was pushed against the lead surface by a constant load. Both the temperature and stress dependences were comparable to those of the constant stress tensile creep tests under similar conditions. A master curve for lead was established by collecting data from the impression creep tests and the constant stress tensile creep tests. The indentation creep measurements for lead were included also. However, the indentation data depend on the load applied.
Similar content being viewed by others
References
S.N.G. Chu and J.C.M. Li, Mater. Sci. Eng. 39, 1–10 (1979).
P. S. Godavarti and K. L. Murty, J. Mater. Sci. Lett. 6, 456–458 (1987).
A. Jurhasz, P. Tasnadi, P. Szaszvari, and I. Kovacs, J. Mater. Sci. 21, 3287–3289 (1986).
E.C. Yu and J.C.M. Li, Philos. Mag. 36 4, 811–825 (1977).
H. Y. Yu and J. C. M. Li, J. Mater. Sci. 12, 2214–2222 (1977).
S. N. G. Chu and J. C. M. Li, J. Mater. Sci. 12, 2200–2208 (1977).
Fuqian Yang and J.C.M. Li, J. Appl. Phys. 74, 4382–4397 (1993).
A. D. L. Torre, P. Adeva, and M. Aballe, J. Mater. Sci. 26, 4351–4354 (1991).
V. Raman and R. Berriche, J. Mater. Res. 7, 627–638 (1992).
J. Weertman, Trans. AIME 218, 207–218 (1960).
P. Feltham, Proc. Phys. Soc. 12–B, 1173–1188 (1956).
A.K. Mukherjee, J.E. Bird, and J.E. Dorn, Trans. ASM 62, 155–178 (1969).
R. A. Laudise, The Growth of Single Crystals, edited by N. Holonyak, Jr. (Prentice-Hall, Englewood Cliffs, NJ, 1970), pp. 164–168.
E. C. Yu, Ph.D. dissertation, University of Rochester (1977).
G.S. Murthy and D.H. Sastry, Phys. Status Solidi A 70, 63–71 (1982).
N.H. Nachtrieb and G.S. Handler, J. Chem. Phys. 23 9, 1569–1570 (1955).
B. Okkerse, Acta Metall. 2, 551–553 (1954).
J.B. Hudson and R.E. Hoffman, Trans. AIME 221, 761–770 (1961).
F. A. Mohamed, K. L. Murty, and J. W. Morris, Jr., Metall. Trans. 4, 935–940 (1973).
M. A. Meyers and K. K. Chawla, Mechanical Metallurgy Principles and Applications (Prentice-Hall, Englewood Cliffs, NJ, 1984), p. 612.
D. Tabor, in The Hardness of Metals, Chap. 3 (Clarendon Press, Oxford, 1951).
J.C.M. Li, Trans. Metall. Soc. AIME 233, 219–224 (1965).
N. Balasubramanian and J. C. M. Li, J. Mater. Sci. 5, 434–444 (1970).
E. N. da C. Andrade, Viscosity and Plasticity (Chemical Publishing Co., 1951), pp. 68–69.
H. J. Kestenbach, W. Krause, and T. L. da Silverira, Acta Metall. 26, 661–670 (1978).
G. E. Lucas and C. Pendleton, J. Nucl. Mater. 103&104, 1539–1544 (1981).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chiang, D., Li, J.C.M. Impression creep of lead. Journal of Materials Research 9, 903–908 (1994). https://doi.org/10.1557/JMR.1994.0903
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1994.0903