Abstract
In-situ tensile tests have been performed in a dual beam focused ion beam and scanning electron microscope on as-grown and prestrained single-crystal molybdenum-alloy (Mo-alloy) fibers. The fibers had approximately square cross sections with submicron edge lengths and gauge lengths in the range of 9-41 μm. In contrast to previously observed yield strengths near the theoretical strength of 10 GPa in compression tests of ~1-3-μm long pillars made from similar Mo-alloy single crystals, a wide scatter of yield strengths between 1 and 10 GPa was observed in the as-grown fibers tested in tension. Deformation was dominated by inhomogeneous plastic events, sometimes including the formation of Lüders bands. In contrast, highly prestrained fibers exhibited stable plastic flow, significantly lower yield strengths of ~1 GPa, and stress-strain behavior very similar to that in compression. A simple, statistical model incorporating the measured dislocation densities is developed to explain why the tension and compression results for the as-grown fibers are different.
Similar content being viewed by others
References
M.D. Uchic and D.M. Dimiduk: A methodology to investigate size scale effects in crystalline plasticity using uniaxial compression testing Mater. Sci. Eng, A 400-401, 268 (2005).
J.R. Greer, W.C. Oliver, and W.D. Nix: Size dependence of mechanical properties of gold at the micron scale in the absence of strain gradients Acta Mater. 53, 1821 (2005).
D. Kiener, C. Motz, T. Schöberl, M. Jenko, and G. Dehm: Determination of mechanical properties of copper at the micron scale Adv. Eng. Mater. 8, 1119 (2006).
C.A. Volkert and E.T. Lilleodden: Size effects in the deformation of sub-micron Au columns Philos. Mag. 86, 5567 (2006).
K.J. Hemker and W.N. Sharpe: Microscale characterization of mechanical properties Annu. Rev. Mater. Res. 37, 93 (2007).
D. Kiener, W. Grosinger, G. Dehm, and R. Pippan: A further step towards an understanding of size-dependent crystal plasticity: In situ tension experiments of miniaturized single-crystal copper samples Acta Mater. 56, 580 (2008).
M.D. Uchic, P.A. Shade, and D.M. Dimiduk: Plasticity of micrometer-scale single crystals in compression Annu. Rev. Mater. Res. 39, 361 (2009).
A.S. Schneider, B.G. Clark, C.P. Frick, P.A. Gruber, and E. Arzt: Effect of orientation and loading rate on compression behavior of small-scale Mo pillars Mater. Sci. Eng, A 508, 241 (2009).
O. Kraft, P.A. Gruber, R. Mönig, and D. Weygand: Plasticity in confined dimensions Annu. Rev. Mater. Res. 40, 293 (2010).
G.M. Pharr, E.G. Herbert, and Y. Gao: The indentation size effect: A critical examination of experimental observations and mechanistic interpretations Annu. Rev. Mater. Res. 40, 271 (2010).
D. Gianola and C. Eberl: Micro- and nanoscale tensile testing of materials JOM 61, 24 (2009).
H. Bei, S. Shim, E.P. George, M.K. Miller, E.G. Herbert, and G.M. Pharr: Compressive strengths of molybdenum alloy micro-pillars prepared using a new technique Scr. Mater. 57, 397 (2007).
H. Bei, S. Shim, G.M. Pharr, and E.P. George: Effects of pre-strain on the compressive stress-strain response of Mo-alloy single-crystal micropillars Acta Mater. 56, 4762 (2008).
S. Ogata, J. Li, N. Hirosaki, Y. Shibutani, and S. Yip: Ideal shear strain of metals and ceramics Phys. Rev. B 70, 104104 (2004).
P.S. Phani, K.E. Johanns, G. Duscher, A. Gali, E.P. George, and G.M. Pharr: Scanning transmission electron microscope observations of defects in as-grown and pre-strained Mo alloy fibers Acta Mater. 59, 2172 (2011).
M.B. Lowry, D. Kiener, M.M. LeBlanc, C. Chisholm, J.N. Florando, J.W. Morris Jr., and A.M. Minor: Achieving the ideal strength in annealed molybdenum nanopillars Acta Mater. 58, 5160 (2010).
R. Maaβ, Van S. Petegem, C.N. Borca, and Van H. Swygenhoven: In situ Laue diffraction of metallic micropillars Mater. Sci. Eng, A 524, 40 (2009).
D. Kiener, C. Motz, M. Rester, M. Jenko, and G. Dehm: FIB damage of Cu and possible consequences for miniaturized mechanical tests Mater. Sci. Eng, A 459, 262 (2007).
J.R. Greer and W.D. Nix: Size dependence of mechanical properties of gold at the sub-micron scale Appl. Phys, A Mater. Sci. Process. 80, 1625 (2005).
H. Bei and E.P. George: Microstructures and mechanical properties of a directionally solidified NiAl-Mo eutectic alloy Acta Mater. 53, 69 (2005).
J.M. Dickinson and P.E. Armstrong: Temperature dependence of the elastic constants of molybdenum J. Appl. Phys. 38, 602 (1967).
D.S. Gianola, A. Sedlmayr, R. Monig, C.A. Volkert, R.C. Major, E. Cyrankowski, S.A.S. Asif, O.L. Warren, and O. Kraft: In situ nanomechanical testing in focused ion beam and scanning electron microscopes Rev. Sci. Instrum. 82, 063901 (2011).
C. Eberl, D. Gianola, and K. Hemker: Mechanical characterization of coatings using microbeam bending and digital image correlation techniques Exp. Mech. 50, 85 (2010).
J.-Y. Kim and J.R. Greer: Tensile and compressive behavior of gold and molybdenum single crystals at the nano-scale Acta Mater. 57, 5245 (2009).
J.-Y. Kim, D. Jang, and J.R. Greer: Tensile and compressive behavior of tungsten, molybdenum, tantalum and niobium at the nanoscale Acta Mater. 58, 2355 (2010).
D. Frankel, S. Milenkovic, A.J. Smith, and A.W. Hassel: Nanostructuring of NiAl-Mo eutectic alloys by selective phase dissolution Electrochim. Acta 54, 6015 (2009).
P. Roediger, H.D. Wanzenboeck, G. Hochleitner, and E. Bertagnolli: Evaluation of chamber contamination in a scanning electron microscope J. Vac. Sci. Technol. B 27, 2711 (2009).
van W.F. Dorp and C.W. Hagen: A critical literature review of focused electron beam induced deposition J. Appl. Phys. 104, 081301 (2008).
S. Shim, H. Bei, M.K. Miller, G.M. Pharr, and E.P. George: Effects of focused-ion-beam milling on the compressive behavior of directionally solidified micropillars and the nanoindentation response of an electropolished surface Acta Mater. 57, 503 (2009).
H. Bei, S. Shim, M.K. Miller, G.M. Pharr, and E.P. George: Effects of focused-ion-beam milling on the nanomechanical behavior of a molybdenum-alloy single crystal Appl. Phys. Lett. 91, 111915 (2007).
S.S. Brenner: Tensile strength of whiskers J. Appl. Phys. 27, 1484 (1956).
S.S. Brenner: Plastic deformation of copper and silver whiskers J. Appl. Phys. 28, 1023 (1957).
T.A. Parthasarathy, S.I. Rao, D.M. Dimiduk, M.D. Uchic, and D.R. Trinkle: Contribution to size effect of yield strength from the stochastics of dislocation source lengths in finite samples Scr. Mater. 56, 313 (2007).
Acknowledgments
This work was supported by the U.S. Department of Energy, Basic Energy Sciences, Materials Sciences and Engineering Division (materials synthesis and modeling) and the Center for Defect Physics, an Energy Frontier Research Center supported by the Office of Basic Energy Sciences, U.S. Department of Energy (materials characterization and testing). GMP gratefully acknowledges the Alexander von Humboldt Foundation for fellowship support during the period in which the work was performed.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Johanns, K.E., Sedlmayr, A., Phani, P.S. et al. In-situ tensile testing of single-crystal molybdenum-alloy fibers with various dislocation densities in a scanning electron microscope. Journal of Materials Research 27, 508–520 (2012). https://doi.org/10.1557/jmr.2011.298
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/jmr.2011.298