Abstract
We present a model which accounts for the dramatic evolution in the microstructure of electroplated copper thin films near room temperature. Microstructure evolution occurs during a transient period of hours following deposition, and includes an increase in grain size, changes in preferred crystallographic texture, and decreases in resistivity, hardness and compressive stress. As the grain size increases from the as-deposited value of 0.05-0.1 μm up to several μm, the decreasing grain boundary contribution to electron scattering lowers the resistivity by tens of percent to near-bulk values. Concurrently, as the volume of grain boundaries decreases, the stress is shown to change in the tensile direction by tens of MPa. The as-deposited grain size is also shown to be consistent with grain boundary pinning.
Similar content being viewed by others
References
P.C. Andricacos, C. Uzoh, J. Dukovic, J. Horkans and H. Deligianni, IBM J. Res. Develop. 42 (5), 567 (1998).
C. Cabral Jr., P.C. Andricacos, L. Gignac, I.C. Noyan, K.P. Rodbell, T.M. Shaw, R. Rosenberg, J.M.E. Harper, P.W. DeHaven, P.S. Locke, S. Malhotra, C. Uzoh and S.J. Kiepeis, Proc. Adv. Metall. Conf. (1998), in press.
T. Ritzdorf, L. Graham, S. Jin, C. Mu and D.B. Fraser, Proc. Int’l. Interconnect Technol. Conf., p. 166 (IEEE, 1998).
M.E. Gross, C. Lingk, T. Siegrist, E. Coleman, W.L. Brown, K. Ueno, Y. Tsuchiya, N. Itoh, T. Ritzdorf, J. Turner, K. Gibbons, E. Klawuhn, M. Biberger, W.Y.C. Lai, J.F. Miner, G. Wu and F. Zhang, Mater. Res. Soc. Symp. Proc. 514, 293 (1998).
V.M. Dubin, G. Morales, C. Ryu and S.S. Wong, Mat. Res. Soc. Symp. 505, 137 (1998).
C. Lingk and M.E. Gross, J. Appl. Phys. 84, 5547 (1998
Q.-T. Jiang, R. Mikkola, B. Carpenter and M.E. Thomas, Proc. Adv. Metall. Conf. (1998)
Q.-T. Jiang and K. Smekalin, Proc. Adv. Metall. Conf. (1998).
L.M. Gignac, K.P. Rodbell, C. Cabral Jr., P.C. Andricacos, P.S. Locke, S.J. Klepeis, R.B. Beyers and P.M. Rice, Proc. Mat. Res. Soc. Spring 1999, Symposium N “Advanced Interconnects and Contacts”, San Francisco, CA, to be published.
C.V. Thompson, J. Appl. Phys. 58, 763 (1985).
J.M.E. Harper, E.G. Colgan, C.K. Hu, J. Hummel, L.P. Buchwalter and C.E. Uzoh, MRS Bulletin, 19, 23 (1994).
R.G. Chambers, Proc. Royal Soc. London, A202 378 (1950).
Handbook of Electrical Resistivities of Binary Metallic Alloys (CRC Press, 1983).
P.J. Schultz and K.G. Lynn, Rev. Mod. Phys. 60, 701 (1988); K.P. Rodbell, M. Weber and K.G. Lynn, unpublished results (1998).
A.F. Mayadas and M. Shatzkes, Phys. Rev. B 1 (4), 1382 (1970).
P. Chaudhari, J. Vac. Sci. Technol. 9 (1), 520 (1972).
Metallization Theory and Practice for VLSI and ULSI, S. Murarka (Butterworth-Heinemann, Boston, 1993), p. 19.
B.M. Hogan, Proc. Surf.-Finish 84, Amer. Electroplaters and Surface Finishers Soc., Orlando (1984)
H.J. Wiesner and W.J. Frey, Plating and Surf. Finishing 66, 51 (1979).
C. Zener, quoted by C.S. Smith, Trans. AIME 175, 15 (1948).
Phase Transformations in Metals and Alloys, D.A. Porter and K.E. Easterling (Van Nostrand Reinhold, UK, 1984), p. 141.
G. Bai, C. Chiang, J.N. Cox, S. Fang, D.S. Gardner, A. Mack, T. Marieb, X.-C. Mu, V. Ochoa, R. Villasol and J. Yu, p. 48, 1996 IEEE Symp. on VLSI Technol. Digest (1996).
Recrystallization and Related Annealing Phenomena, F.J. Humphreys and M. Hatherly (Elsevier Science Ltd., Oxford, U.K. 1996), p. 314.
J.M.E. Harper, C. Cabral Jr., P.C. Andricacos, L. Gignac, I.C. Noyan, K.P. Rodbell and C.K. Hu, to be published.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Harper, J.M.E., Cabral, C., Andricacos, P.C. et al. Mechanisms for Microstructure Evolution in Electroplated Copper Thin Films. MRS Online Proceedings Library 564, 387–392 (1999). https://doi.org/10.1557/PROC-564-387
Published:
Issue Date:
DOI: https://doi.org/10.1557/PROC-564-387