Abstract
High Tc superconducting powders and thin films on silicon have been fabricated by the sol-gel process. Both powder and film preparation involved the synthesis of metal alkoxides, followed by the complexation of yttrium, barium, and copper alkoxides in a common solvent. Bulk gels were then vacuum dried and fired at 700 and 950 °C in flowing oxygen. Thin films on (100) silicon were fired at 700 °C in flowing oxygen. Susceptibility vs temperature measurements showed that the thin films on silicon had a Tc of 40 K while the bulk gels fired under the same conditions had a Tc of 75 K. The sample fired at 950 °C was superconducting at 90 K.
Similar content being viewed by others
References
J. G. Bednorz and K. A. Muller, Z. Phys. B. 64, 189 (1986).
C. W. Chu, P. H. Hor, R. L. Meng, L. Gao, Z. J. Haang and Y. Q. Wang, Phys. Rev. Lett. 58, 405 (1987).
S. Sakka, Treatise on Material Science and Technology, Eds. M. Tomocawa and R. H. Doremus, Vol. 22 Glass III, p. 129.
S. Kramer, K. Wu, and G. Kordas, J. Elct. Met, in press.
C. Webb, S. L. Weng, J. N. Eckstein, N. Missert, K. Char, D. G. Schlom, E. S. Hellman, and M. R. Beasley, Appl. Phys. Lett. 51, 1191 (1987).
B. Y. Tsaur and G. M. Metze, Appl. Phy. Lett. 45, 535 (1984).
H. B. Kroemer, Proc. Mater. Res. Soc. 67, 3 (1986).
J. W. Lee, H. Schichijo, H. L. Tsai, and R. J. Matyi, Appl. Phys. Lett. 50, 31, (1987).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kramer, S., Wu, K. & Kordás, G. Preparation of thin Film YBa2CU3O6+X Ceramic Superconductors by the Sol-Gel Process. MRS Online Proceedings Library 99, 323–326 (1987). https://doi.org/10.1557/PROC-99-323
Published:
Issue Date:
DOI: https://doi.org/10.1557/PROC-99-323