18%Niマルエージング鋼におけるNi3Mo析出物の電子顕微鏡による研究
清水 謙一岡本 尚機
著者情報
ジャーナル フリー

1971 年 35 巻 3 号 p. 204-210

詳細
抄録

Transmission electron microscopy and electron diffraction studies were carried out in order to make clear the crystallographic property of strengthening precipitates in an 18%Ni maraging steel. The primary precipitate observed in the maximum hardness state was rod in shape, the size being about 25 Å in width and 500 Å in length. The length direction was parallel to the ⟨111⟩ of the matrix, and the crystal structure was identified as the orthorhombic Ni3Mo intermetallic compound. The orientation relationship between the Ni3Mo precipitate and the matrix was proposed to be (010)Ni3Mo\varparallel(011)α′, [100]Ni3Mo\varparallel[1\bar11]α′; that is, the closest packed plane and the direction of precipitates were parallel to those of the matrix, as observed in many other precipitation phenomena. When the ordering of atoms in the Ni3Mo crystal is disregarded, the relationship can be represented by Burgers relationship which is well known in the bcc to hcp phase transformation. The length direction ⟨111⟩ of the Ni3Mo precipitate was verified to be the [1\bar11]α′ involved in the above orientation relationship.
The interfacial coherency between the Ni3Mo precipitate and the matrix was examined referring to the orientation relationship and the length direction. The hexagonal Ni3Ti phase was also detected as the secondary precipitate.

著者関連情報
© 社団法人 日本金属学会
前の記事 次の記事
feedback
Top