In this study, severe plastic deformation through high-pressure sliding (HPS) was applied for in situ high-energy X-ray diffraction analysis at SPring-8 in JASRI (Japan Synchrotron Radiation Research Institute). Allotropic transformation of pure Ti was examined in terms of temperatures, pressures and imposed strain using a miniaturized HPS facility. The true pressure applied on the sample was estimated from the peak shift. Peak broadening due to local variation of pressure was reduced using white X-ray. The phase transformation from α phase to ω phase occurred at a pressure of ∼4.5 GPa. Straining by the HPS processing was effective to promote the transformation to the ω phase and to maintain the ω phase even at ambient pressure. The reverse transformation from ω phase to α phase occurred at a temperature of ∼110℃ under ambient pressure, while under higher pressure as ∼4 GPa, the ω phase remained stable even at ∼170℃ covered in this study. It was suggested that the reverse transformation from the ω phase to the α phase is controlled by thermal energy.

Mater. Trans. 62 (2021) 167-176に掲載