Abstract
The antimonide laser heterostructures growth technology using MBE epitaxy is currently well-developed, while MOVPE method is still being improved. It is known that the principal problem for MOVPE is the oxygen and carbon contamination of aluminium containing waveguides and claddings. The solution would be to apply a proper aluminium precursor. In this study we present the results of metal-organic epitaxy of In- and Al-containing layers and quantum well structures composing antimonide lasers devices. Special emphasis was put on the aluminium precursor and its relation to AlGaSb and AlGaAsSb materials properties. The crystalline quality of the layers grown with two different Al precursors was compared, very good structural quality films were obtained. The results suggested a substantial influence of precursors pre-reactions on the epitaxial process. The oxygen contamination was measured by SIMS, which confirmed its dependence on the precursor choice. We also optimised the GaSb substrate thermal treatment to deposit high quality GaSb homoepitaxial layers. Quaternary InGaAsSb layers were obtained even within the predicted miscibility gap, when arsenic content reached high above 10% values. InGa(As)Sb/AlGa(As)Sb quantum wells were grown and their optical properties were characterised by photoluminescence and photoreflectance spectroscopy. Type-I quantum wells showed a fundamental optical transition in the 1.9–2.1 μm range at room temperature. The epitaxial technology of the structures was subjected to an optimisation procedure. The investigated layers and heterostructures can be considered for application in laser devices.
[1] J.G. Kim, L. Shterengas, R.U. Martinelli, and G.L. Belenky, “High-power room-temperature continuous wave operation of 2.7 and 2.8 μm In(Al)GaAsSb/GaSb diode lasers”, Appl. Phys. Lett. 83, 1926–1928 (2003). http://dx.doi.org/10.1063/1.160524510.1063/1.1605245Search in Google Scholar
[2] M. Rattunde, J. Schmitz, G. Kaufel, M. Kelemen, J. Weber, and J. Wagner, “GaSb-based 2.X μm quantum-well diode lasers with low beam divergence and high output power”, Appl. Phys. Lett. 88, 081115–081117 (2006). http://dx.doi.org/10.1063/1.217850610.1063/1.2178506Search in Google Scholar
[3] A. Joullie and P. Christol, “GaSb-based mid-infrared 2-5-μm laser diodes”, CR Phys. 4, 621–637 (2003). http://dx.doi.org/10.1016/S1631-0705(03)00098-710.1016/S1631-0705(03)00098-7Search in Google Scholar
[4] C.A. Wang and H.K. Choi, “GaInAsSb/AlGaAsSb multiple-quantum-well diode lasers grown by organometallic vapour phase epitaxy”, Appl. Phys. Lett. 70, 802–804 (1997). http://dx.doi.org/10.1063/1.11822710.1063/1.118227Search in Google Scholar
[5] C.A. Wang, “Organometallic vapour phase epitaxial growth of AlSb-based alloys”, J. Cryst. Growth 170, 725–731 (1997). http://dx.doi.org/10.1016/S0022-0248(96)00579-910.1016/S0022-0248(96)00579-9Search in Google Scholar
[6] C.A. Wang, K.F. Jensen, A.C. Jones, and H.K. Choi, “n-AlGaSb and GaSb/AlGaSb double-heterostructure lasers grown by organometallic vapour phase epitaxy”, Appl. Phys. Lett. 68, 400–402 (1996). http://dx.doi.org/10.1063/1.11669810.1063/1.116698Search in Google Scholar
[7] C.A. Wang and H.K. Choi, “OMVPE growth of GaInAsSb/AlGaAsSb for quantum-well diode lasers”, J. Electron. Mater. 26, 1231–1236 (1997). http://dx.doi.org/10.1007/s11664-997-0025-810.1007/s11664-997-0025-8Search in Google Scholar
[8] Z. Yin and X. Tang, “A review of energy bandgap engineering in III–V semiconductor alloys for mid-infrared laser applications”, Solid-State Electron. 51, 6–15 (2007). http://dx.doi.org/10.1016/j.sse.2006.12.00510.1016/j.sse.2006.12.005Search in Google Scholar
[9] C.A. Wang, “Progress and continuing challenges in GaSb-based III–V alloys and heterostructures grown by organometallic vapour-phase epitaxy”, J. Cryst. Growth 272, 664–681 (2004). http://dx.doi.org/10.1016/j.jcrysgro.2004.09.01910.1016/j.jcrysgro.2004.09.019Search in Google Scholar
[10] P.S. Dutta and H.L. Bhat, “The physics and technology of gallium antimonide: An emerging optoelectronic material”, J. Appl. Phys. 81, 5821–5870 (1997). http://dx.doi.org/10.1063/1.36535610.1063/1.365356Search in Google Scholar
[11] B.R. Bennett, R. Magno, J.B. Boos, W. Kruppa, and M.G. Ancona, “Antimonide-based compound semiconductor electronics: A review”, Solid-State Electron. 49, 1875–1895 (2005). http://dx.doi.org/10.1016/j.sse.2005.09.00810.1016/j.sse.2005.09.008Search in Google Scholar
[12] E. Plis, J.B. Rodriguez, H.S. Kim, G. Bishop, Y.D. Sharma, L.R. Dawson, S. Krishn, S.J. Lee, C.E. Jones, and V. Gopal, “Type II InAs/GaSb strain layer superlattice detectors with p-on-n polarity”, Appl. Phys. Lett. 91, 133512–133514 (2007). http://dx.doi.org/10.1063/1.279007810.1063/1.2790078Search in Google Scholar
[13] J.G. Cederberg, M.J. Hafich, R.M. Biefeld, and M. Palmisiano, “The preparation of InGa(As)Sb and Al(Ga)AsSb films and diodes on GaSb for thermophotovoltaic applications using metal-organic chemical vapour deposition”, J. Cryst. Growth 248, 289–295 (2003). http://dx.doi.org/10.1016/S0022-0248(02)01927-910.1016/S0022-0248(02)01927-9Search in Google Scholar
[14] M.G. Mauk and V.M. Andreev, “GaSb-related materials for TPV cells”, Semicond. Sci. Tech. 18, 191–201 (2003). http://dx.doi.org/10.1088/0268-1242/18/5/30810.1088/0268-1242/18/5/308Search in Google Scholar
[15] A. Aardvark, N.J. Mason, and P.J. Walker, “The growth of antimonides by MOVPE”, Prog. Cryst. Growth Ch. 35, 207–241 (1997). http://dx.doi.org/10.1016/S0960-8974(98)00004-710.1016/S0960-8974(98)00004-7Search in Google Scholar
[16] F. Dimroth, C. Agert, and A.W. Bett, “Growth of Sb-based materials by MOVPE”, J. Cryst. Growth 248, 265–273 (2003). http://dx.doi.org/10.1016/S0022-0248(02)01818-310.1016/S0022-0248(02)01818-3Search in Google Scholar
[17] Ch. Giesen, A. Szymakowski, S. Rushworth, M. Heuken, and K. Heime, “MOVPE of AlGaAsSb using TTBAl as an alternative aluminium precursor”, J. Cryst. Growth 221, 450–455 (2000). http://dx.doi.org/10.1016/S0022-0248(00)00739-910.1016/S0022-0248(00)00739-9Search in Google Scholar
[18] R.M. Biefeld, “The metal-organic chemical vapour deposition and properties of III–V antimony-based semiconductor materials”, Mater. Sci. Eng. 36, 105–142 (2002). http://dx.doi.org/10.1016/S0927-796X(02)00002-510.1016/S0927-796X(02)00002-5Search in Google Scholar
[19] J.J. Hill, A.A. Aquino, C.P.A. Mulcahy, N. Harwood, A.C. Jones, and T.S. Jones, “The adsorption and thermal decomposition of trimethylaluminium and dimethylaluminium hydride on GaAs(100)”, Surf. Sci. 340, 49–56 (1995). http://dx.doi.org/10.1016/0039-6028(95)00683-410.1016/0039-6028(95)00683-4Search in Google Scholar
© 2011 SEP, Warsaw
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.