Next Article in Journal
Electrospun Silica-Polyacrylonitrile Nanohybrids for Water Treatments
Next Article in Special Issue
Engineering Metal-Organic-Framework (MOF)-Based Membranes for Gas and Liquid Separation
Previous Article in Journal
Concepts and Misconceptions Concerning the Influence of Divalent Ions on the Performance of Reverse Electrodialysis Using Natural Waters
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Double-Layered Pebax® 3533/ZIF-8 Membranes with Single-Walled Carbon Nanotube Buckypapers as Support for Gas Separation

1
Instituto de Nanociencia y Materiales de Aragón (INMA), CSIC-Universidad de Zaragoza, 50018 Zaragoza, Spain
2
Chemical and Environmental Engineering Department, Universidad de Zaragoza, 50018 Zaragoza, Spain
*
Author to whom correspondence should be addressed.
Membranes 2023, 13(1), 71; https://doi.org/10.3390/membranes13010071
Submission received: 16 December 2022 / Revised: 29 December 2022 / Accepted: 3 January 2023 / Published: 6 January 2023
(This article belongs to the Special Issue Research Progress of Metal-Organic-Framework (MOF) Membranes)

Abstract

:
Single-walled carbon nanotube buckypapers (SWCNT-bps) coated with a metal–organic framework ZIF-8 layer were used as supports for the preparation of Pebax® 3533 TFC membranes by both phase inversion and spin coating techniques. Upon proper characterization of the materials by X-ray diffraction, IR spectroscopy, thermogravimetry and electron microscopy, the obtained membranes were tested in gas separation experiments with a 15:85 CO2/N2 mixture. These experiments proved that the ZIF-8 layer prevented from the penetration of the polymer selective film into the SWCNT-bp support, giving rise to a highly permeable selective membrane. The optimum membrane was achieved by the spin-coating method, with better permeation results than that prepared by the phase inversion method, obtaining a CO2 permeance of 566 GPU together with a CO2/N2 selectivity of 20.9.

Graphical Abstract

1. Introduction

In recent times, climate change and its effects on the planet are more prominent (an increase in temperatures, the retreat of glaciers and extreme weather conditions) [1], which is mainly caused by greenhouse gases. Carbon dioxide (CO2) is the most common of these gases, considered the main cause of the increase in global temperature. For that reason, technologies for its capture and sequestration are in high demand [2]. Post-combustion CO2 capture is the simplest approach to this problem and could be easily adapted to industrial facilities. Gas separation with membranes is drawing more interest over traditional techniques (absorption with amines, cryogenic distillation and adsorption) [3] due to the relevant properties of membranes such as their mechanical simplicity, lower energy consumption and the low-cost of fabrication and maintenance [4].
Polymer membranes exhibit excellent properties and transport parameters for the separation of the CO2/N2 post-combustion mixture, where the CO2 concentration varies between 15% (from the exhaust of a typical combustion process) to 30% (in the case of cement and steel industries). Among the quasi-infinite variety of polymers, poly(ether-block-amide) copolymers (Pebax®) are very promising due to the characteristics that their variable composition, based on different proportions of polyamide (PA) and polyether (PE) blocks, confer them [5,6].
An ideal membrane for gas separation should be composed of a selective skin layer exceeding the Robeson trade-off relation between selectivity and permeability [7], as thin as possible with the objective of achieving high permeance (permeability divided by membrane thickness) but mechanically robust [8,9].
A thin-film composite (TFC) membrane consists of a selective layer with very thin thickness, since the mechanical stability relies on the support, which has to be robust, chemically and thermally stable and very permeable. In these conditions, the objective is to achieve a highly permeable TFC membrane with the same separation selectivity observed when the selective membrane polymer material is available as a dense membrane. The selective layer in the TFC membrane can be further improved with the addition of nanoparticles acting as nanofillers, giving rise to the so-called thin-film nanocomposite (TFN) membrane. Among the variety of nanofillers, MOFs (metal–organic frameworks) and special ZIFs (zeolitic imidazolate frameworks), with a generally narrower porosity than typical carboxylate-type MOFs, are widely studied due to their affinity with the polymer matrix [10,11]. ZIF-8 is probably the most applied MOF as a membrane material. In addition, ZIFs are a subfamily of MOFs firstly reported and named by Park et al. [12] that have crystalline topologies similar to those of zeolites. In particular, ZIF-8, under a different name, was first synthesized by Huang et al. [13] consisting of Zn2+ ions coordinated to four nitrogen atoms present in the positions 1 and 3 of the 2-methylimidazolate ligand, forming a SOD-type topology present in several other ZIFs with slightly different composition [14].
Another strategy that has been used to improve gas separation in TFC membranes is to incorporate an intermediate layer between the selective layer and the support; this layer sometimes performs the function of a gutter layer [15]. For this function, several nanostructured materials have been used: MOF nanosheets for Polyactive® [16] or polyamide [17] selective layers and COF for Pebax® 1657 selective layers [18], among others.
Carbon nanotubes are promising materials for gas and water filtration based on membranes due to their high specific porosity and surface area, hydrophobicity, mechanical strength and potential functionalization [9,19,20,21]. In addition, they are commercially available. In this work, we report the preparation of Pebax® 3533 TFC membranes with single-walled carbon nanotubes conforming to a buckypaper (SWCNT-bp) as support, which provides a highly permeable and mechanically robust base for obtaining a high-performance membrane. Pebax® 3533 is a suitable polymer for CO2 separation due to its composition comprising 75 wt % poly(tetramethylene oxide, PTMO) and 25 wt % aliphatic polyamide (PA12). In addition, a ZIF-8 layer was grown on the SWCNT-bp to avoid the penetration of the Pebax® 3533 into the support porosity, having a gutter layer effect [22,23]. All this configures a unique membrane architecture exhibiting high gas separation performance and stability.

2. Experimental Procedure

2.1. Materials

Polyether-block-amide Pebax® 3533 SA 01 MED (75 wt % poly(tetramethylene oxide) (PTMO), 25 wt % aliphatic polyamide (PA12)) in the form of pellets was kindly provided by Arkema, France. Single-walled carbon nanotubes (SWCNT, 1.2–2 nm) ≥93% carbon content and non-ionic surfactant Triton™ X-100 were purchased from Sigma-Aldrich. SWCNTs were used as received; additional characterization of them can be found in our previous publication [9]. 2-propanol (IPA, HPLC grade, ≥99.9%) and methanol (HPLC grade, ≥99.9%) were obtained at Panreac Applichem. 1-propanol, 1-butanol and zinc nitrate hexahydrate (reagent grade) were purchased from Scharlab, while 2-methylimidazole (mIm) (99%) was acquired from Acros Organics. Finally, Nylon™ filter with a diameter of 47 mm and 0.22 µm pore size was purchased from Labbox.

2.2. Single-Walled Carbon Nanotube Buckypaper (SWCNT-bp) Preparation

By adapting a previously published technique, free-standing SWCNT films were prepared using a vacuum filtering process [9,24,25,26]. Typically, 10 mg of SWCNT was dispersed in 60 mL of distilled water with 1 wt % of Triton X-100 surfactant using an ultrasound probe sonicator (Sonics Materials VC-750–220, 750 W, 20 kHz) for 1 h. The sonicated suspension was then filtered through a porous Nylon™ filter housed in a glass filtration funnel with a diameter of 47 mm and washed with a 1:1 (v/v) acetone:2-propanol solution [24]. After allowing it to dry at room temperature overnight, it could be peeled off from the filter, obtaining a 15 µm thick, self-standing SWCNT buckypaper, thick enough as to ensure the needed mechanical strength for the gas phase separation characterization.

2.3. ZIF-8 Synthesis on SWCNT-bp

The synthesis of ZIF-8 was performed by adapting a technique that was already published [26,27]. In order to keep one of their sides away from the solutions, the free-standing SWCNT-bp was positioned in between a ring and a disc of stainless steel (Figure S1) vertically in 100 mL of a 10 mM zinc nitrate hexahydrate methanolic solution for 30 min. After being rinsed in fresh methanol for 1 min, the SWCNT-bp was then immersed vertically in 100 mL of a 20 mM 2-methylimidazole methanolic solution for 24 h. Then, it was washed again in pure methanol for 1 min. This treatment was repeated twice. The membrane was then detached from the metal rig, cleaned in pure methanol for 10 min and allowed to dry at room temperature overnight. The entire synthesis process was carried out at ambient temperature.

2.4. Preparation of Pebax® 3533 Dense Membranes

The membranes were prepared using a modified reported method [28]. Concisely, 0.3 g of the polymer was dissolved in 6.7 g of 3:1 (v/v) of 1-propanol:1-butanol mixture under reflux for 1 h at 80 °C. Afterwards, the solution at room temperature was cast into a glass Petri dish and dried at 40 °C for 24 h.

2.5. Preparation of Pebax® 3533 Supported Membranes by Phase Inversion (PI)

A polymer solution was prepared dissolving the required amount of Pebax® 3533 pellets in a 3:1 (v/v) of 1-propanol:1-butanol mixture stirred under reflux at 80 °C for 1 h, obtaining a 1 wt % Pebax® 3533 solution. The method used for the membrane preparation was based on a previous report [29]. First, the support was fixed horizontally with a vacuum pump. Secondly, the support was put in contact with the Pebax® 3533 solution, previously poured in a Petri dish, for about 2 to 3 s. Then, the support was soaked in distilled water (provoking the phase inversion) in another Petri dish for 2 min. After this, the membrane was gently dried with compressed air. This procedure was repeated three times, after which the membrane was dried at 40 °C for 24 h.

2.6. Preparation of Pebax® 3533 Supported Membranes by Spin Coating (SC)

First, a 3 wt % Pebax® 3533 solution was obtained following the previous method. Then, the membrane was prepared following a previously reported protocol [30]. Briefly, the support was introduced in a Laurell WS-650MZ-23NPP/A1/AR1 spin coater and fixed with vacuum. Then, 500 µL of the polymer solution was poured on the support, which was spun at 2500 rpm for 20 s. The membrane was posteriorly dried at 40 °C for 24 h.

2.7. Membrane Characterization

Fourier transform infrared spectroscopy (FTIR) was performed with a Bruker Vertex 70 FTIR spectrometer equipped with a DTGS detector and a Golden Gate diamond ATR accessory. The spectra were recorded by averaging 40 scans in the wavenumber range of 4000–600 cm−1 at a resolution of 4 cm−1. Thermogravimetric analyses (TGA) were carried out using a Mettler Toledo TGA/STDA 851e. Small pieces of membranes (~3 mg) placed in 70 µL alumina pans were heated under an airflow (40 cm3(STP) min−1) from 35 to 700 °C at a heating rate of 10 °C min−1. Scanning electron microscopy (SEM) images were collected with a FEI-Inspect F50 microscope at a voltage of 10 kV. The samples were previously coated with Au/Pd under vacuum conditions, and transversal images were obtained by cutting the cooled samples with liquid nitrogen. X-ray diffraction (XRD) measurements were performed with an Empyrean PANalytical diffractometer with a Cu-Kα source (λ = 1.5406 Å). Data were collected in the 2θ range from 5 to 40° at a scanning rate of 0.01°·s−1.

2.8. Mixed Gas Permeation

Membranes were cut and placed in a module consisting of two stainless steel pieces and a 316LSS macro-porous disk support (Mott Co., Farmington, CT, USA) with a 20 µm nominal pore size. Membranes, 2.12 cm2 in area, were sealed inside the module by means of Viton O-rings. To control the temperature of the experiment (in this work, in the 25–50 °C range), the permeation module was placed in a UNE 200 Memmert oven. The gas separation measurements were carried out by feeding the post-combustion gaseous mixture of CO2/N2 (15/85 cm3(STP) min−1) to the feed side at an operating pressure of 3 bar to favor CO2 permeation. Two mass flow controllers (Alicat Scientific, Tucson, AZ, USA, MC-100CCM-D) controlled the gas flows. The permeate side of the membrane was swept with 50 cm3(STP) min−1 of He at atmospheric pressure (~1 bar) (Alicat Scientific, MC-100CCM-D). Concentrations of N2 and CO2 in the permeate stream were analyzed online by an Agilent 990 micro-chromatograph. Permeances were calculated in GPU (Equation (1)) once steady state at the exit stream was reached (after at least 2 h). The separation selectivity (α) (Equation (2)) was calculated as the ratio of the corresponding permeances (P).
1 GPU = 10−6 cm3(STP) cm−2 s−1 cm Hg−1
α = Pa/Pb

3. Results and Discussion

3.1. Membrane Characterization

Figure 1 shows the surface of the SWCNT-bp support before (Figure 1A) and after ZIF-8 synthesis (ZIF-8/SWCNT-bp, Figure 1B). It can be seen the open structure of the interweaved SWCNT-bp, as has been observed previously [26], and that the ZIF-8 layer provides a continuous coating of intergrowth MOF crystals on top of the support with a thickness of ca. 90–100 nm.
On top of the ZIF-8 layer, a selective Pebax® 3533 coating was added via two different methods. Pebax® 3533 was chosen for this purpose for its hydrophobic nature (as compared to other Pebax® codes with a lower content of the PE segment) [29], which is compatible with both SWCNT and ZIF-8. This, along with the solvent used in the polymer solution (1-propanol/1-butanol mixture), make Pebax® 3533 an ideal choice for the membrane preparation.
The first Pebax® 3533 coating method was phase inversion (PI), carried out by the previously mentioned protocol forming the Pebax®/SWCNT-bp-PI (Figure 2A) and Pebax®/ZIF-8/SWCNT-bp-PI (Figure 2C) membranes. In addition, a spin-coating (SC) method was applied following the previously mentioned conditions, producing the Pebax®/SWCNT-bp-SC (Figure 2B) and Pebax®/ZIF-8/SWCNT-bp-SC (Figure 2D) membranes. These two pairs of Pebax® coatings on both bare SWCNT-bp and ZIF-8/SWCNT-bp allow one to infer the importance of the MOF layer. In fact, the SEM images in Figure 2A,B depict that the SWCNT-bp surface is continuously covered with the polymer in the case of the Pebax®/SWCNT-bp. However, none of the two applied methods can avoid, as seen in the cross-section images, the penetration of the polymer inside the SWCNT-bp support.
Membranes with the ZIF-8 layer also show a good coating with the polymer without observing the SWCNT-bp support on the surface (insets in Figure 2C,D). In addition, their cross-section images indicate that Pebax® penetration into the support was avoided thanks to the ZIF layer. In these two cases, the thicknesses of the layers can be deduced from Figure 2C,D. The ZIF-8 layer is around 90–100 nm thick. In addition, although this ZIF layer may not be well intergrown, it should be known that the selective layer is going to be, as will be verified in the separation measurements, the polymer layer. The main difference between membranes Pebax®/SWCNT-bp-SC and Pebax®/ZIF-8/SWCNT-bp-SC resides in the Pebax® thickness achieved with each method. The phase inversion method formed a denser polymer layer with a thickness in the ca. 300–350 nm range, whilst the spin coating method provided a thinner and more regular layer ca. 100–120 nm thick. This will be of paramount importance when evaluating the separation properties of the two membranes.
The thermal stability of the membranes was studied by thermogravimetric analysis (TGA). The TGA results are visualized in Figure 3A. It can be seen that ZIF-8 is stable up to 425 °C, which is in agreement with the literature [31]. Nevertheless, the degradation of the ZIF-8 layer begins above 300 °C, which is due to the greater accessibility of oxygen to the thin layer of ZIF-8. Regarding Pebax®, it can be observed that its main degradation begins above 350 °C, which is also in agreement with the literature [29]. In multilayer membranes, the degradation of Pebax®, given its smaller thickness, is more difficult to discern, but it would take place coupled with that of the ZIF, which would also be related to the good integration of these two materials. However, a greater loss of solvents (weight loss below 200 °C) was observed in the membranes with Pebax®. Regarding the TGA of the SWCNTs, their degradation does not start until 550 °C having at 700 °C a remaining weight; this thermal stability has already been observed previously [9]. In the membrane, it can also be seen that an incomplete degradation was observed at 700 °C due to the presence of SWCNTs and ZnO formation from ZIF decomposition.
The XRD diffractogram shown in Figure 3B confirms the correct synthesis of the ZIF-8 layer (with some shielding from the polymer coating) with the presence of the most intense and characteristic peaks of ZIF-8 (7.4, 10.4 and 12.7°) in agreement with the simulated pattern [32]. It can also be seen the characteristic peaks of Pebax® 3533 at 5.8, 11.3 and 22.4° [29,33,34]. In addition, the more defined ZIF-8 peaks in the Pebax®/ZIF-8/SWCNT-bp-SC correlate with the lower thickness of the polymer layer obtained by the spin-coating technique and observed by SEM (Figure 2C,D).
Figure 3C,D show the characteristic bands in FTIR-ATR corresponding to ZIF-8 at 1583 cm−1 for the C=N bond and at 1149 and 995 cm−1 for the C-N bond [35]. Regarding Pebax® 3533, it has characteristic bands at 1639 cm−1 (the vibration of the H-N-C=O group), 2935 cm−1 (the bending of the C-H aliphatic chain) and 1101 cm−1 (the C-O-C ether group) [36,37,38]. In the membrane in which ZIF-8 was synthesized, some of the characteristic peaks of ZIF-8 can be observed, which were mostly preserved when the Pebax layer was deposited. Some of the characteristic peaks of Pebax® 3533 were detectable on the TFC membranes.

3.2. Mixture Gas Permeation Tests

The gas separation performance of the membranes was tested for the 15:85 CO2/N2 mixture at 35 °C and 3 bar feed pressure. Three different membrane samples of each type were evaluated at the same conditions to demonstrate the reliability of the membranes and their preparation procedures, allowing, in turn, the calculation of the error bars shown along this section. The results of the experiments are depicted in Figure 4, where the parameters corresponding to a Pebax® 3533 dense membrane are also shown for comparison.
All the data shown in Figure 4 are also collected in Table S2. Concerning the separation results for the Pebax®/SWCNT-bp membranes, a slight improvement in permeance in relation to the dense membrane but with a decline in the selectivity, less accused in the SC membrane, was obtained. This correlates with the fact that the polymer would have penetrated into the porosity of the SWCNT support. Compared to the membrane containing the ZIF-8 interlayer, as discussed below, this penetration would simultaneously increase the membrane resistance (giving rise to a lower CO2 permeance) and decrease its separation selectivity due to the difficulty of obtaining, in such conditions, a defect-free membrane. What is evident is the increase in permeance with respect to the dense membrane, given its lesser thickness, which would give it, despite the slight decrease in selectivity, a certain advantage.
When a ZIF-8 layer was placed on top of the SWCNT support and then the polymer was coated on the ZIF, a clear improvement in the CO2 permeance was accomplished as compared to the dense Pebax® and to the Pebax® directly prepared on the SWCNTs. In the case of the Pebax®/ZIF-8/SWCNT-bp-PI (phase inversion) membrane, the improvement in CO2 permeance was not as significant as Pebax®/ZIF-8/SWCNT-bp-SC (spin-coating), in line with the fact that the phase inversion method generated a thickness three times larger than the spin-coating method. In these conditions, the membrane Pebax®/ZIF-8/SWCNT-bp-SC presents the best results in terms of both CO2 permeance (566 ± 22 GPU) and CO2/N2 selectivity (20.9 ± 4.2). In fact, this selectivity value is practically the same as that achieved with the dense bare polymer (21.0), supporting the idea that the polymer skin layer was defect-free. However, CO2 permeance increased from 2.4 GPU to 566 GPU, i.e., by a factor of 235. In conclusion, no apparent effect on the selectivity occurs when ZIF-8 is present as an intermediate layer between the SWCNT support and the Pebax® 3533 skin, which is related to a gutter layer effect achieved from the ZIF-8 coating [39,40].
In addition, to study permeance and selectivity dependence with temperature, gas permeation tests for the best performing membrane (Pebax®/ZIF-8/SWCNT-bp-SC) were carried out between 25 and 50 °C at a 3 bar feed pressure (Figure 5). The Arrhenius model was applied in Figure S2 with Equation (3) [4,41]:
P = P 0 · exp E p R T
where P is the gas permeance in GPU, P0 is the pre-exponential factor in GPU, Ep is the permeation apparent activation energy in J·mol−1, R is the ideal gas constant (8.314 J·mol−1·K−1) and T is the temperature in K.
On the basis of this model, the apparent activation energies for the permeation of CO2 and N2 are 13.8 kJ·mol−1 and 35.1 kJ·mol−1, respectively. These results are in concordance with the reported values for Pebax® 3533 membranes, prepared on polymeric supports, of 14.2 kJ·mol−1 for CO2 and 29.6 kJ·mol−1 for N2 [29] and justify the reduction in selectivity with the temperature due to the higher activation energy for N2 with respect to CO2 [42]. It must be taken into account that permeance is proportional to diffusion and solubility, and these two factors affect the defined apparent activation energy. On the one hand, diffusivity, which increases with temperature due to the mobility of molecules and polymer chains, has positive activation energy. On the other, the solubility (adsorption), being an exothermic process, has a negative heat of adsorption. The low value of CO2 Ep is due to the fact that adsorption is a predominant factor for this gas, and therefore, the decrease in selectivity is due to the decrease in CO2 adsorption. Moreover, these values, together with the fact that the best CO2/N2 selectivity corresponded to that of the dense membrane, suggest that, beyond the ancillary role of ZIF-8 to properly coat with a thin layer of polymer Pebax® 3533, the contribution of the MOF to the gas transport is not significant, which is in agreement with the fact that the SEM observation did not reveal a perfectly intergrown layer strictly necessary for gas separation.
One of the Pebax®/ZIF-8/SWCNT-bp-SC membranes was tested again, after 3 months of room temperature storage with preservation from light, to study the stability of the membrane with time. As collected in Table 1, no appreciable decrease in its separation properties was observed, confirming its stability in terms of CO2/N2 separation.
Finally, Figure 6 shows the Robeson-type upper bound for CO2/N2 with permeance calculated in GPU instead of typical permeability in Barrer. This permits the comparison of the best membranes in this work with other Pebax® TFC membranes observed in the literature, always based on Pebax® 3533. It can be concluded that the membranes developed in this work are amongst the most permeable with high values of CO2/N2 selectivity.

4. Conclusions

It can be concluded that single-walled carbon nanotube buckypapers (SWCNT-bps) can be used as supports for Pebax® 3533 membranes if an intermediate (gutter) layer of MOF ZIF-8 is placed by crystal intergrowth between both materials. Two different methods can be applied for the purpose of preparing the Pebax® thin layer: phase inversion and spin coating. When no ZIF-8 was used and the Pebax® was directly placed on the SWCNT-bp surface, the obtained membranes presented a small increase in CO2 permeance values and a decrease in CO2/N2 selectivity due to the polymer penetration in the support. The ZIF-8 layer placed on top of the SWCNT-bp allowed solving the problem of Pebax® penetration with either of the two polymer coating procedures applied (phase inversion and spin coating). However, the membranes prepared with the spin-coating method, which had less thickness and higher quality, presented the best separation results of this work, with a CO2 permeance of 566 ± 22 GPU and a CO2/N2 selectivity of 20.9 ± 4.2. The permeation testing at different temperatures in the 25–50 °C range allowed estimating the apparent activation energies for both permeating gases. This explains the permeation behavior with the temperature related to the CO2 sorption, which is in line with the reported literature, further suggesting that, together with the fact that the best CO2/N2 selectivity corresponds to that of the dense membrane, the contribution of the MOF to gas transport is not significant.
Finally, as this current gas separation performance is among the best in the literature for the polymer used, the methodology applied here opens the door for an intermediate ZIF layer, with a function similar to that of a gutter layer, to be used for the development of ultra-thin, high-quality membranes that retain the separation selectivity properties of the dense polymer.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/membranes13010071/s1, Figure S1. Photographs of the experimental rig for the synthesis of the ZIF-8 layer on the SWCNT buckypaper (A). The buckypaper placed between the disc and the ring (B). ZIF-8 layer being synthesized on the buckypaper (C) at room temperature; Figure S2. Arrhenius model linear fit for the calculation of the apparent activation energy of permeance in the Pebax®/ZIF-8/SWCNT-bp-SC for CO2 (A) and N2 (B). R2 fitting parameter is 0.97 and 0.94, respectively for CO2 and N2; Figure S3. CO2/N2 bound defined in GPU at 35 °C, adapted from the data published in Robeson [7]; Table S1. Gas permeation and selectivity results at 35 °C and 3 bar feed pressure.

Author Contributions

Methodology, V.B.-S., C.T. and J.C.; Validation, V.B.-S., C.T. and J.C.; Formal analysis, V.B.-S., C.T. and J.C.; Investigation, V.B.-S., C.T. and J.C.; Resources, C.T. and J.C.; Data curation, V.B.-S., C.T. and J.C.; Writing – original draft, V.B.-S., C.T. and J.C.; Writing – review & editing, V.B.-S., C.T. and J.C.; Visualization, C.T. and J.C.; Supervision, C.T. and J.C.; Project administration, C.T. and J.C.; Funding acquisition, C.T. and J.C. All authors have read and agreed to the published version of the manuscript.

Funding

Grant PID2019-104009RB-I00 funded by MCIN/AEI/10.13039/501100011033 is gratefully acknowledged (Agencia Estatal de Investigación (AEI) and Ministerio de Ciencia e Innovación (MCIN), Spain). Financial support from the Aragón Government is also gratefully acknowledged (T43_20R). V.B.-S. thanks the Grant BES-2017-080209 funded by MCIN/AEI/10.13039/501100011033 and by “ESF Investing in your future”. The authors would like to acknowledge the use of the Servicio General de Apoyo a la Investigación-SAI and the use of instrumentation, as well as the technical advice provided by the National Facility ELECMI ICTS, node “Laboratorio de Microscopias Avanzadas” at the University of Zaragoza.

Data Availability Statement

Complementary data available as supporting information and upon request to the authors.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Solomon, S.; Plattner, G.K.; Knutti, R.; Friedlingstein, P. Irreversible climate change due to carbon dioxide emissions. Proc. Natl. Acad. Sci. USA 2009, 106, 1704–1709. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  2. Kárászová, M.; Zach, B.; Petrusová, Z.; Červenka, V.; Bobák, M.; Šyc, M.; Izák, P. Post-combustion carbon capture by membrane separation, Review. Sep. Purif. Technol. 2020, 238, 116448. [Google Scholar] [CrossRef]
  3. Chao, C.; Deng, Y.; Dewil, R.; Baeyens, J.; Fan, X. Post-combustion carbon capture. Renew. Sustain. Energy Rev. 2021, 138, 110490. [Google Scholar] [CrossRef]
  4. Martínez-Izquierdo, L.; Malankowska, M.; Sánchez-Laínez, J.; Téllez, C.; Coronas, J. Poly (ether-block-amide) copolymer membrane for CO2/N2 separation: The influence of the casting solution concentration on its morphology, thermal properties and gas separation performance. R. Soc. Open Sci. 2022, 6, 190866. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  5. Pazani, F.; Aroujalian, A. Enhanced CO2-selective behavior of Pebax-1657: A comparative study between the influence of graphene-based fillers. Polym. Test. 2020, 81, 106264. [Google Scholar] [CrossRef]
  6. Reijerkerk, S.R.; Knoef, M.H.; Nijmeijer, K.; Wessling, M. Poly (ethylene glycol) and poly (dimethyl siloxane): Combining their advantages into efficient CO2 gas separation membranes. J. Memb. Sci. 2010, 352, 126–135. [Google Scholar] [CrossRef]
  7. Robeson, L.M. The upper bound revisited. J. Memb. Sci. 2008, 320, 390–400. [Google Scholar] [CrossRef]
  8. Benito, J.; Sánchez-Laínez, J.; Zornoza, B.; Martín, S.; Carta, M.; Malpass-Evans, R.; Téllez, C.; McKeown, N.B.; Coronas, J.; Gascón, I. Ultrathin Composite Polymeric Membranes for CO2/N2 Separation with Minimum Thickness and High CO2 Permeance. ChemSusChem 2017, 10, 4014–4017. [Google Scholar] [CrossRef] [Green Version]
  9. Berned-Samatán, V.; Jiménez, S.; Rubio, C.; Téllez, C.; Coronas, J. Self-supported single-wall carbon nanotube buckypaper membranes applied to air and water fi ltration. J. Chem. Technol. Biotechnol. 2022, 98, 159–167. [Google Scholar] [CrossRef]
  10. Sánchez-Laínez, J.; Paseta, L.; Navarro, M.; Zornoza, B.; Téllez, C.; Coronas, J. Ultrapermeable Thin Film ZIF-8/Polyamide Membrane for H2/CO2 Separation at High Temperature without Using Sweep Gas. Adv. Mater. Interfaces 2018, 5, 1800647. [Google Scholar] [CrossRef]
  11. Tang, P.-H.H.; So, P.B.; Li, W.-H.H.; Hui, Z.-Y.Y.; Hu, C.-C.C.; Lin, C.-H.H. Carbon Dioxide Enrichment PEBAX/MOF Composite Membrane for CO2 Separation. Membranes 2021, 11, 404. [Google Scholar] [CrossRef] [PubMed]
  12. Park, K.S.; Ni, Z.; Côté, A.P.; Choi, J.Y.; Huang, R.; Uribe-Romo, F.J.; Chae, H.K.; O’Keeffe, M.; Yaghi, O.M. Exceptional chemical and thermal stability of zeolitic imidazolate frameworks. Proc. Natl. Acad. Sci. USA 2006, 103, 10186–10191. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  13. Huang, X.C.; Lin, Y.Y.; Zhang, J.P.; Chen, X.M. Ligand-directed strategy for zeolite-type metal-organic frameworks: Zinc(II) imidazolates with unusual zeolitic topologies. Angew. Chem. Int. Ed. 2006, 45, 1557–1559. [Google Scholar] [CrossRef] [PubMed]
  14. Guan, W.X.; Dai, Y.; Dong, C.Y.; Yang, X.C.; Xi, Y. Zeolite imidazolate framework (ZIF)-based mixed matrix membranes for CO2 separation: A review. J. Appl. Polym. Sci. 2020, 137, 48968. [Google Scholar] [CrossRef]
  15. Kattula, M.; Ponnuru, K.; Zhu, L.; Jia, W.; Lin, H.; Furlani, E.P. Designing ultrathin film composite membranes: The impact of a gutter layer. Sci. Rep. 2015, 5, 1–9. [Google Scholar] [CrossRef] [Green Version]
  16. Liu, M.; Xie, K.; Nothling, M.D.; Gurr, P.A.; Tan, S.S.L.; Fu, Q.; Webley, P.A.; Qiao, G.G. Ultrathin Metal–Organic Framework Nanosheets as a Gutter Layer for Flexible Composite Gas Separation Membranes. ACS Nano 2018, 12, 11591–11599. [Google Scholar] [CrossRef]
  17. Ma, Y.; Zhang, W.; Li, H.; Zhang, C.; Pan, H.; Zhang, Y.; Feng, X.; Tang, K.; Meng, J. A microporous polymer TFC membrane with 2-D MOF nanosheets gutter layer for efficient H2 separation. Sep. Purif. Technol. 2021, 261, 118283. [Google Scholar] [CrossRef]
  18. Ying, Y.; Yang, Z.; Shi, D.; Peh, S.B.; Wang, Y.; Yu, X.; Yang, H.; Chai, K.; Zhao, D. Ultrathin covalent organic framework film as membrane gutter layer for high-permeance CO2 capture. J. Memb. Sci. 2021, 632, 119384. [Google Scholar] [CrossRef]
  19. Gibson, P.; Schreuder-Gibson, H.; Rivin, D. Transport properties of porous membranes based on electrospun nanofibers. Colloids Surf. A Physicochem. Eng. Asp. 2001, 187, 469–481. [Google Scholar] [CrossRef]
  20. Balamurugan, R.; Sundarrajan, S.; Ramakrishna, S. Recent trends in nanofibrous membranes and their suitability for air and water filtrations. Membranes 2011, 1, 232–248. [Google Scholar] [CrossRef]
  21. Rashid, M.H.-O.O.; Ralph, S.F. Carbon Nanotube Membranes: Synthesis, Properties and Future Filtration Applications. Nanomaterials 2017, 7, 99. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  22. Sutrisna, P.D.; Hou, J.; Li, H.; Zhang, Y.; Chen, V. Improved operational stability of Pebax-based gas separation membranes with ZIF-8: A comparative study of flat sheet and composite hollow fibre membranes. J. Memb. Sci. 2017, 524, 266–279. [Google Scholar] [CrossRef]
  23. Chen, F.; Dong, S.; Wang, Z.; Xu, J.; Xu, R.; Wang, J. Preparation of mixed matrix composite membrane for hydrogen purification by incorporating ZIF-8 nanoparticles modified with tannic acid. Int. J. Hydrogen Energy 2020, 45, 7444–7454. [Google Scholar] [CrossRef]
  24. Rojas, J.A.; Ardila-Rodríguez, L.A.; Diniz, M.F.; Gonçalves, M.; Ribeiro, B.; Rezende, M.C. Optimization of Triton X-100 removal and ultrasound probe parameters in the preparation of multiwalled carbon nanotube buckypaper. Mater. Des. 2019, 166, 107612. [Google Scholar] [CrossRef]
  25. Chew, S.Y.; Ng, S.H.; Wang, J.; Novák, P.; Krumeich, F.; Chou, S.L.; Chen, J.; Liu, H.K. Flexible free-standing carbon nanotube films for model lithium-ion batteries. Carbon 2009, 47, 2976–2983. [Google Scholar] [CrossRef]
  26. Berned-Samatán, V.; Rubio, C.; Galán-González, A.; Muñoz, E.; Benito, A.M.; Maser, W.K.; Coronas, J.; Téllez, C. Single-walled carbon nanotube buckypaper as support for highly permeable double layer polyamide/zeolitic imidazolate framework in nanofiltration processes. J. Memb. Sci. 2022, 652, 120490. [Google Scholar] [CrossRef]
  27. Valadez Sánchez, E.P.; Gliemann, H.; Haas-Santo, K.; Wöll, C.; Dittmeyer, R. ZIF-8 SURMOF Membranes Synthesized by Au-Assisted Liquid Phase Epitaxy for Application in Gas Separation. Chem. Ing. Tech. 2016, 88, 1798–1805. [Google Scholar] [CrossRef]
  28. Sabetghadam, A.; Liu, X.; Benzaqui, M.; Gkaniatsou, E.; Orsi, A.; Lozinska, M.M.; Sicard, C.; Johnson, T.; Steunou, N.; Wright, P.A.; et al. Influence of Filler Pore Structure and Polymer on the Performance of MOF-Based Mixed-Matrix Membranes for CO2 Capture. Chem.—A Eur. J. 2018, 24, 7949–7956. [Google Scholar] [CrossRef] [Green Version]
  29. Martínez-Izquierdo, L.; Malankowska, M.; Téllez, C.; Coronas, J. Phase inversion method for the preparation of Pebax® 3533 thin film membranes for CO2/N2 separation. J. Environ. Chem. Eng. 2021, 9, 105624. [Google Scholar] [CrossRef]
  30. Martínez-Izquierdo, L.; Téllez, C.; Coronas, J. Highly stable Pebax® Renew® thin-film nanocomposite membranes with metal organic framework ZIF-94 and ionic liquid [Bmim][BF4] for CO2 capture. J. Mater. Chem. A 2022, 10, 18822–18833. [Google Scholar] [CrossRef]
  31. James, J.B.; Lin, Y.S. Kinetics of ZIF-8 Thermal Decomposition in Inert, Oxidizing and Reducing Environments. J. Phys. Chem. C 2016, 120, 14015–14026. [Google Scholar] [CrossRef]
  32. Zhang, Y.; Jia, Y.; Hou, L. Synthesis of zeolitic imidazolate framework-8 on polyester fiber for PM2.5 removal. RSC Adv. 2018, 8, 31471–31477. [Google Scholar] [CrossRef] [Green Version]
  33. Sánchez-Laínez, J.; Ballester-Catalán, M.; Javierre-Ortín, E.; Téllez, C.; Coronas, J. Pebax® 1041 supported membranes with carbon nanotubes prepared: Via phase inversion for CO2/N2 separation. Dalt. Trans. 2020, 49, 2905–2913. [Google Scholar] [CrossRef]
  34. Martínez-Izquierdo, L.; Perea-Cachero, A.; Malankowska, M.; Téllez, C.; Coronas, J. A comparative study between single gas and mixed gas permeation of polyether-block-amide type copolymer membranes. J. Environ. Chem. Eng. 2022, 10, 108324. [Google Scholar] [CrossRef]
  35. Hu, Y.; Kazemian, H.; Rohani, S.; Huang, Y.; Song, Y. In situ high pressure study of ZIF-8 by FTIR spectroscopy. Chem. Commun. 2011, 47, 12694–12696. [Google Scholar] [CrossRef]
  36. Elyasi Kojabad, M.; Momeni, M.; Babaluo, A.A.; Vaezi, M.J. PEBA/PSf Multilayer Composite Membranes for CO2 Separation: Influence of Dip Coating Parameters. Chem. Eng. Technol. 2020, 43, 1451–1460. [Google Scholar] [CrossRef]
  37. Sanaeepur, H.; Mashhadikhan, S.; Mardassi, G.; Ebadi Amooghin, A.; Van der Bruggen, B.; Moghadassi, A. Aminosilane cross-linked poly ether-block-amide PEBAX 2533: Characterization and CO2 separation properties. Korean J. Chem. Eng. 2019, 36, 1339–1349. [Google Scholar] [CrossRef]
  38. Fu, Q.; Halim, A.; Kim, J.; Scofield, J.M.P.; Gurr, P.A.; Kentish, S.E.; Qiao, G.G. Highly permeable membrane materials for CO2 capture. J. Mater. Chem. A 2013, 1, 13769–13778. [Google Scholar] [CrossRef]
  39. Liu, M.; Xie, K.; Nothling, M.D.; Zu, L.; Zhao, S.; Harvie, D.J.E.; Fu, Q.; Webley, P.A.; Qiao, G.G. Ultrapermeable Composite Membranes Enhanced via Doping with Amorphous MOF Nanosheets. ACS Cent. Sci. 2021, 7, 671–680. [Google Scholar] [CrossRef]
  40. Ashtiani, S.; Sofer, Z.; Průša, F.; Friess, K. Molecular-level fabrication of highly selective composite ZIF-8-CNT-PDMS membranes for effective CO2/N2, CO2/H2 and olefin/paraffin separations. Sep. Purif. Technol. 2021, 274, 119003. [Google Scholar] [CrossRef]
  41. Feng, S.; Ren, J.; Zhao, D.; Li, H.; Hua, K.; Li, X.; Deng, M. Effect of poly (ethylene glycol) molecular weight on CO2/N2 separation performance of poly (amide-12-b-ethylene oxide)/poly (ethylene glycol) blend membranes. J. Energy Chem. 2019, 28, 39–45. [Google Scholar] [CrossRef] [Green Version]
  42. Zhu, T.; Yang, X.; Zheng, Y.; He, X.; Chen, F.; Luo, J. Preparation of poly (ether-block-amide)/poly (amide-co-poly (propylene glycol)) random copolymer blend membranes for CO2/N2 separation. Polym. Eng. Sci. 2019, 59, E14–E23. [Google Scholar] [CrossRef]
Figure 1. SEM images of the surface of the SWCNT-bp (A) and the ZIF-8/SWCNT-bp (B).
Figure 1. SEM images of the surface of the SWCNT-bp (A) and the ZIF-8/SWCNT-bp (B).
Membranes 13 00071 g001
Figure 2. SEM images of the surfaces of Pebax®/SWCNT-bp-PI (A) and Pebax®/SWCNT-bp-SC (B). Cross-section images of Pebax®/ZIF-8/SWCNT-bp-PI (C) and Pebax®/ZIF-8/SWCNT-bp-SC (D). The insets correspond to the cross-sections of the membranes (A,B) and their surfaces (C,D). Cross-section images were obtained by cutting the samples under liquid nitrogen, which causes the apparent gap between the Pebax® and ZIF-8 layers.
Figure 2. SEM images of the surfaces of Pebax®/SWCNT-bp-PI (A) and Pebax®/SWCNT-bp-SC (B). Cross-section images of Pebax®/ZIF-8/SWCNT-bp-PI (C) and Pebax®/ZIF-8/SWCNT-bp-SC (D). The insets correspond to the cross-sections of the membranes (A,B) and their surfaces (C,D). Cross-section images were obtained by cutting the samples under liquid nitrogen, which causes the apparent gap between the Pebax® and ZIF-8 layers.
Membranes 13 00071 g002
Figure 3. TGA curves (A), XRD diffractograms (B) and FTIR-ATR spectra (C,D) of the membranes.
Figure 3. TGA curves (A), XRD diffractograms (B) and FTIR-ATR spectra (C,D) of the membranes.
Membranes 13 00071 g003
Figure 4. Gas permeance (bars) and selectivity (squares) for the CO2/N2 (15:85) gas mixture at 35 °C and 3 bar feed pressure for the membranes prepared in this work.
Figure 4. Gas permeance (bars) and selectivity (squares) for the CO2/N2 (15:85) gas mixture at 35 °C and 3 bar feed pressure for the membranes prepared in this work.
Membranes 13 00071 g004
Figure 5. Permeance (A) and selectivity (B) results for the gas separation experiments carried out at 25, 35 and 50 °C with the Pebax®/ZIF-8/SWCNT-bp-SC membrane for CO2/N2 (15:85) at 3 bar.
Figure 5. Permeance (A) and selectivity (B) results for the gas separation experiments carried out at 25, 35 and 50 °C with the Pebax®/ZIF-8/SWCNT-bp-SC membrane for CO2/N2 (15:85) at 3 bar.
Membranes 13 00071 g005
Figure 6. CO2/N2 selectivity-CO2 permeance upper bound defined in GPU at 35 °C (red line). Comparison between TFC membranes based on Pebax® 3533 [29,38] with the membranes obtained in this work, including the dense membrane.
Figure 6. CO2/N2 selectivity-CO2 permeance upper bound defined in GPU at 35 °C (red line). Comparison between TFC membranes based on Pebax® 3533 [29,38] with the membranes obtained in this work, including the dense membrane.
Membranes 13 00071 g006
Table 1. Permeance and selectivity values of a Pebax®/ZIF-8/SWCNT-bp-SC membrane after 90 and 100 cumulative days of storage at room temperature.
Table 1. Permeance and selectivity values of a Pebax®/ZIF-8/SWCNT-bp-SC membrane after 90 and 100 cumulative days of storage at room temperature.
Time
(days)
CO2 Permeance
(GPU)
CO2/N2 Selectivity
056520.5
9056620.1
10056420.1
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Berned-Samatán, V.; Téllez, C.; Coronas, J. Double-Layered Pebax® 3533/ZIF-8 Membranes with Single-Walled Carbon Nanotube Buckypapers as Support for Gas Separation. Membranes 2023, 13, 71. https://doi.org/10.3390/membranes13010071

AMA Style

Berned-Samatán V, Téllez C, Coronas J. Double-Layered Pebax® 3533/ZIF-8 Membranes with Single-Walled Carbon Nanotube Buckypapers as Support for Gas Separation. Membranes. 2023; 13(1):71. https://doi.org/10.3390/membranes13010071

Chicago/Turabian Style

Berned-Samatán, Víctor, Carlos Téllez, and Joaquín Coronas. 2023. "Double-Layered Pebax® 3533/ZIF-8 Membranes with Single-Walled Carbon Nanotube Buckypapers as Support for Gas Separation" Membranes 13, no. 1: 71. https://doi.org/10.3390/membranes13010071

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop