Next Article in Journal
Synergistic Piezo-Photocatalysis of BiOCl/NaNbO3 Heterojunction Piezoelectric Composite for High-Efficient Organic Pollutant Degradation
Previous Article in Journal
Recent Advances in the Surface Functionalization of PLGA-Based Nanomedicines
Previous Article in Special Issue
Biogenic Ferrihydrite Nanoparticles Produced by Klebsiella oxytoca: Characterization, Physicochemical Properties and Bovine Serum Albumin Interactions
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Performance of Graphene/Polydimethylsiloxane Surfaces against S. aureus and P. aeruginosa Single- and Dual-Species Biofilms

by
Isabel M. Oliveira
1,†,
Marisa Gomes
1,†,
Luciana C. Gomes
1,
Manuel F. R. Pereira
2,
Olívia S. G. P. Soares
2,* and
Filipe J. Mergulhão
1,*
1
LEPABE—Laboratory for Process Engineering, Environment, Biotechnology and Energy, Faculty of Engineering, University of Porto, Rua Dr. Roberto Frias, 4200-465 Porto, Portugal
2
LSRE–LCM—Laboratory of Separation and Reaction Engineering–Laboratory of Catalysis and Materials, Faculty of Engineering, University of Porto, Rua Dr. Roberto Frias, 4200-465 Porto, Portugal
*
Authors to whom correspondence should be addressed.
These authors contributed equally to this work.
Nanomaterials 2022, 12(3), 355; https://doi.org/10.3390/nano12030355
Submission received: 30 December 2021 / Revised: 16 January 2022 / Accepted: 19 January 2022 / Published: 22 January 2022
(This article belongs to the Special Issue Nanocomposites for Biomedical Engineering Applications)

Abstract

:
The increasing incidence of implant-associated infections has prompted the development of effective strategies to prevent biofilm formation on these devices. In this work, pristine graphene nanoplatelet/polydimethylsiloxane (GNP/PDMS) surfaces containing different GNP loadings (1, 2, 3, 4, and 5 wt%) were produced and evaluated on their ability to mitigate biofilm development. After GNP loading optimization, the most promising surface was tested against single- and dual-species biofilms of Staphylococcus aureus and Pseudomonas aeruginosa. The antibiofilm activity of GNP/PDMS surfaces was determined by the quantification of total, viable, culturable, and viable but nonculturable (VBNC) cells, as well as by confocal laser scanning microscopy (CLSM). Results showed that 5 wt% GNP loading reduced the number of total (57%), viable (69%), culturable (55%), and VBNC cells (85%) of S. aureus biofilms compared to PDMS. A decrease of 25% in total cells and about 52% in viable, culturable, and VBNC cells was observed for P. aeruginosa biofilms. Dual-species biofilms demonstrated higher resistance to the antimicrobial activity of GNP surfaces, with lower biofilm cell reductions (of up to 29% when compared to single-species biofilms). Still, the effectiveness of these surfaces in suppressing single- and dual-species biofilm formation was confirmed by CLSM analysis, where a decrease in biofilm biovolume (83% for S. aureus biofilms and 42% for P. aeruginosa and dual-species biofilms) and thickness (on average 72%) was obtained. Overall, these results showed that pristine GNPs dispersed into the PDMS matrix were able to inhibit biofilm growth, being a starting point for the fabrication of novel surface coatings based on functionalized GNP/PDMS composites.

1. Introduction

Implantable medical devices (IMDs) play an active role in the therapy of different medical conditions, enhancing the quality of life [1,2]. Although they are extremely successful in supporting or even replacing damaged body organs, IMDs (e.g., cardiac implantable devices, hemodialyzers, urinary or central venous catheters, contact lenses, artificial breasts, and orthodontal and orthopedic prosthetics) carry the risk of inducing future infections, seriously affecting the patients’ health and even endangering their lives [3,4,5]. Implant-associated infections (IAIs) present a high incidence, corresponding to 60–70% of the nosocomial infections reported each year in the United States [6], and are responsible for a severe burden on healthcare systems and high economic costs [7,8].
IMDs are prone to bacterial adhesion and, consequently, biofilm formation, contributing to the persistence and spread of infection [9]. The implants act as foreign materials in the human body, enabling the colonization of several microbial species that are not eliminated by the host’s innate immune system. The predominant microorganisms identified as colonizers of IMDs include Staphylococcus epidermidis and Staphylococcus aureus, which account for 50–60% of IAIs [10]. However, depending on the type and location of the implant, other species can be found, namely Escherichia coli, Pseudomonas aeruginosa, Enterococcus spp., Candida spp., and Klebsiella pneumoniae [11,12]. Once adhered to the implant surface, the microorganisms form either single- or multi-species biofilms, which are typically less susceptible to antimicrobial treatment [13,14].
To overcome the limitations noted above, it is crucial to develop new strategies that specifically reduce the adhesion and growth of microorganisms [15]. Currently, one of the most promising antimicrobial strategies is the development of antifouling polymeric nanomaterials. These systems include the release of antimicrobial agents (e.g., metals and biocides), contact-killing materials (e.g., antimicrobial peptides), matrix disruptive agents (e.g., enzymes and cationic chelators), or a combination of these approaches [5,16,17]. Although there are promising strategies to mitigate IAIs, their application as a coating in IMDs is still limited by the low biocompatibility, the resistance phenomena, the toxicity that originates from the coatings, and the loss of antimicrobial properties over time [5,18].
Due to its remarkable chemical and physical properties, graphene has emerged as a novel material with relevant applications in the biomedical field [19]. This nanomaterial, in its pure form, is characterized by a single-layer sheet of sp2-hybridized carbon atoms with a honeycomb structure [20], and provides multiple advantages: it is easily renewable, easy to prepare and functionalize, and possesses a large surface area, high stability in the physiological environment, and unique mechanical strength [21]. Due to their outstanding antimicrobial activity, graphene-based materials (e.g., graphene nanoplatelets, graphene nanosheets, graphene oxide, and reduced graphene oxide) have been extensively studied for application as coatings/surfaces for biomedical devices [22,23]. However, it is worth noting the use of functionalized graphene-based materials for other applications, including biosensing and bioimaging, gene therapy, tissue engineering, and drug delivery [23,24]. For instance, the use of graphene-based composites as a support to release antimicrobial agents for wound dressing applications has been described [25,26]. The good biocompatibility of graphene, which has been improved through functionalization, clearly contributes to its high demand in the biomedical field [22,27].
The antibacterial activity of graphene-based materials involves physical and chemical mechanisms. The most usual antibacterial activity occurs upon direct contact to the bacterial membrane by the sharp edges of graphene sheets, or wrapping and trapping bacterial membranes by the nanosheets [28]. The chemical damage is associated with the oxidative stress originated by the production of molecules known as reactive oxygen species (ROS) [29].
The antimicrobial and anti-adhesive activity of graphene and its derivatives against implant-associated pathogens have been widely addressed, with significant inhibition of biofilm formation or even reduction of mature biofilms [23,30,31,32]. Despite the interesting results using graphene-based surfaces to prevent bacterial biofilm formation, the use of non-functionalized graphene as a coating for IMDs is still poorly explored and documented [22,23,29]. In addition, most of the studies reporting the use of pristine graphene tend to combine it with other materials with expected synergetic effects, such as silver nanoparticles [33,34], cadmium sulfide [35], titanium [36], magnetite [37], or chitosan [32], hindering the in-depth understanding of the effective antibiofilm performance of graphene alone. At the same time, there are a scarce number of studies reporting the employment of graphene to enhance the antibacterial properties of polydimethylsiloxane (PDMS) [38,39,40,41], a polymer belonging to the group of silicone elastomers with high applicability in IMDs [42,43].
Taking this evidence into account, the primary objective of this study was to optimize the graphene nanoplatelets (GNPs) loading of PDMS surfaces and evaluate the performance of these composites in the mitigation of single- and dual-species biofilms of S. aureus and P. aeruginosa—two common colonizers of IMDs. As far as we know, this is the first work reporting the antimicrobial activity of pristine GNPs against multi-species biofilms. Furthermore, there are no previous studies addressing the activity of pristine GNPs while incorporated into a polymeric surface against biofilms of the two specific bacterial species under study—S. aureus and P. aeruginosa.

2. Materials and Methods

Figure 1 presents the flowchart of the experimental work fully described in the upcoming sections.

2.1. Production of GNP/PDMS Composites

To prepare GNP/PDMS surfaces, commercially available GNPs aggregates (Alfa Aesar, Thermo Fisher Scientific, Erlenbachweg, Germany), PDMS elastomer (Sylgard 184 Part A, Dow Corning, Midland, MI, USA), and curing agent (Sylgard 184 Part B, Dow Corning) were used.
The GNP/PDMS composites were produced through a bulk mixing process by incorporation of GNPs into the PDMS base elastomer (Part A) as detailed by Vagos et al. [44]. The GNPs were first incorporated at different loadings (1, 2, 3, 4, and 5 wt%) to determine the most efficient GNP load to decrease bacterial biofilm formation. To improve the GNP dispersion, the mixture was stirred for 30 min at 500 rpm and then sonicated (Hielscher UP400S, at 200 W and 12 kHz) for 60 min. After that, the composites were kept in an ultrasound bath (Selecta Ultrasons, Lisbon, Tecnilab, Portugal) for 30 min to remove the remaining air bubbles. At that point, the curing agent (Part B) was added to the elastomer/GNP mixture (in an A:B ratio of 10:1) and gently shaken. The GNP composites were placed as a thin layer on top of glass slides (1 x 1 cm, Vidraria Lousada, Lda, Lousada, Portugal) through spin coating (Spin150 PolosTM, Caribbean, The Netherlands) for 1 min with a 500 rpm ramp to 6000 rpm. Likewise, PDMS surfaces were produced as control [45].

2.2. Surface Characterization

2.2.1. GNP Textural Properties

Nitrogen adsorption-desorption isotherms were obtained using a Quantachrome NOVA 4200e multi-station equipment (Quantachrome Instruments, Boynton Beach, FL, USA) at −196 °C. These isotherms were used to assess the textural properties of the GNP sample after degasification at 120 °C for 3 h under vacuum. The surface area of the GNP sample was obtained according to the Brunauer–Emmett–Teller method (SBET), and the total pore volume (Vp) was obtained from the amount of N2 adsorption at a relative pressure p/p0 of 0.99 [46]. The external surface area (Smeso) and micropore volume (Vmicro) were also acquired applying the t-method.

2.2.2. GNP/PMDS and PDMS Hydrophobicity

The contact angles of PDMS and GNP/PDMS surfaces at 1, 2, 3, 4, and 5 wt% GNP were obtained through the sessile drop method (OCA 15 Plus, Dataphysics, Germany). Contact angles with three pure liquids—water, formaldehyde, and α-bromonaphthalene—were estimated to determine the surface tension elements of the target surfaces. The surface tension components of the noted liquids ( I ) were collected from the literature [47]. Surface hydrophobicity was then assessed by the method of van Oss et al. [48,49,50]. In this method, the hydrophobicity level of a surface (i) is defined as the free energy of interaction between two elements of that surface immersed in water (w)-∆Giwi. If the interaction between the two elements is greater than the interaction of each element with water (∆Giwi < 0 mJ m−2), the surface is hydrophobic. Contrarily, if ∆Giwi > 0 mJ m−2, the material is considered hydrophilic. The value of ∆Giwi was obtained from the surface tension components of the interacting elements in conformity with Equation (1):
Δ G i w i = 2 ( γ i L W γ w L W ) 2 + 4 ( γ i + γ w + γ i γ w + γ i + γ i γ w + γ w ) ,
where γ LW corresponds to Lifshitz–van der Waals element of the surface free energy, and γ + and γ  are the electron acceptor and electron donor parameters, respectively, of the Lewis acid-base component (γ AB), with γ AB =   2   γ +   γ .
The surface tension components were determined by the simultaneous solving of three equations similar to Equation (2):
( 1 + cos θ ) γ i T O T = 2 ( γ i L W γ I L W + γ i + γ I + γ i γ I + ) ,
where θ is the contact angle and γ TOT = γ LW + γ AB.

2.2.3. GNP/PMDS and PDMS Morphology

The surface morphology and the distribution of GNPs into the PDMS matrix were evaluated by scanning electron microscopy (FEI Quanta 400 FEG ESEM/EDAX Genesis X4M microscope; FEI Europe, Eindhoven, The Netherlands).

2.3. Antibiofilm Studies

2.3.1. Bacterial Strain and Culture Conditions

The antimicrobial/anti-adhesive activity of GNP/PDMS coatings was assessed using a Staphylococcus aureus reference strain (ATCC 25923) and a mCherry-Pseudomonas aeruginosa PAO1 strain because these two bacteria are frequently found in implantable medical devices [51]. The mCherry-expressing strain enabled P. aeruginosa detection in dual-species biofilms. Bacteria were stored at −80 °C in Luria-Bertani Broth (LB) medium (Thermo Fisher Scientific, Waltham, MA, USA). Before each experiment, both bacteria were spread on Plate Count Agar (PCA; Merck KGaA, Darmstadt, Germany) petri dishes and incubated overnight at 37 °C.
LB broth was then inoculated with individual colonies harvested from PCA plates and incubated overnight at 37 °C, 160 rpm. In the specific case of P. aeruginosa cultures, tetracycline antibiotic (1.25 mg L−1) was applied to select the transformed bacteria [52]. After centrifugation at 3772× g, 18 °C for 10 min (Eppendorf Centrifuge 5810R, Eppendorf, Hamburg, Germany), the pellet was resuspended in fresh LB medium, and a final cell suspension with an optical density at 610 nm of 0.1 (corresponding to 1 × 108 colony-forming units per mL, CFU mL−1) was prepared. To form dual-species biofilms, the bacterial suspensions of S. aureus and P. aeruginosa were mixed in a ratio of 1:1, maintaining the final cell concentration of 1 × 108 CFU mL−1.

2.3.2. Antibiofilm Assays

To assess biofilm formation on GNP/PDMS composites, the composites were first sterilized through UV radiation for 1 h. Sterilized surfaces of PDMS, and 1, 2, 3, 4, and 5 wt% GNP/PDMS were placed on the microplate wells (12-well plate, VWR International, Carnaxide, Portugal) and inoculated with 3 mL of the bacterial suspension. Plates were incubated at 37 °C for 24 h under static conditions.

Biofilm Quantification

After 24 h of biofilm formation, GNP/PDMS surfaces were detached from the microplate wells, immersed in 2 mL of saline solution, and vigorously agitated for 3 min to obtain biofilm cell suspensions. The number of culturable cells was evaluated by spreading the biofilm suspensions on PCA (after proper dilution in saline solution) followed by CFU counts. The biofilm total and viable cells were assessed by staining biofilm suspensions with the Live/Dead kit (Invitrogen Life Technologies, Alfagene, Portugal) [53] and subsequent analysis in an epifluorescence microscope (Leica DM LB2, Wetzlar, Germany). The number of viable but nonculturable (VBNC) cells was also calculated as the difference between the number of viable and culturable cells [54].

Visualization of the Biofilms Using Confocal Laser Scanning Microscopy (CLSM)

The spatial structure of single- and dual-species biofilms of P. aeruginosa and S. aureus on PDMS and GNP/PDMS surfaces was assessed by CSLM as described by Lima et al. [7]. S. aureus and P. aeruginosa + S. aureus biofilms were first counterstained with 6 µM SYTO®9 (Invitrogen Life Technologies, Alfagene, Portugal). All biofilm samples were then observed using a 40× water immersion objective lens (Leica Microsystems, Wetzlar, Germany) in an inverted microscope Leica DMI6000-CS with 488 nm argon and 633 nm helium-neon lasers. Image stacking was acquired with a 1 μm thickness for each sample at a minimum of five random fields. Image processing was performed using the IMARIS 9.1 software package (Bitplane, Zurich, Switzerland) for modelling in two and three dimensions [55]. The CLSM acquisitions were analyzed by the plug-in COMSTAT2 associated with the ImageJ software to determine biofilm structural parameters such as biovolume (µm3 µm−2) and average thickness (µm) [56].

2.4. Statistical Analysis

Statistical analysis was conducted in GraphPad Prism 8 version. After assessing data normality with the Shapiro–Wilk test, the most appropriate tests for mean comparison were applied. The Kruskal–Wallis test was used to evaluate the differences between the contact angles of PDMS, and 1, 2, 3, 4, and 5 wt% GNP/PDMS surfaces, as this variable was not normally distributed. Differences in the number of culturable cells obtained for PDMS, and 1, 2, 3, 4, and 5 wt% GNP/PDMS surfaces were evaluated using one-way analysis of variance (ANOVA). The Mann–Whitney test was applied to evaluate the differences in the number of total, viable, culturable, and VBNC cells between PDMS and 5 wt% GNP/PDMS surfaces, as the variables were normally distributed. Quantitative parameters obtained from confocal microscopy, namely biovolume and thickness, were compared using ANOVA. Statistical significance was indicated as * for p < 0.05, ** for p < 0.01, *** for p < 0.001, and **** for p < 0.0001. All experiments were performed in triplicate, and the results presented as mean ± standard deviation (SD) or error (SE).

3. Results and Discussion

3.1. Graphene Characterization

As particle morphology affects the microstructure and porosity of nanocomposites, the characterization of the graphene sample is of extreme importance [57]. Therefore, the textural properties of GNP powders were first assessed by the N2 adsorption-desorption isotherms.
The isotherms of the GNP sample fit the Type-II isotherm profile, characteristic of carbon materials with slit-shaped mesoporosity, according to IUPAC classification [58]. The physisorption isotherms obtained are in accordance with those described in previous reports on pristine GNPs [59,60]. The presence of an H3 type hysteresis loop indicates capillary condensation phenomena and mesoporous materials that comprise aggregates of plate-like particles [61]. The sharp rise of N2 uptake at low relative pressure is quite characteristic of microporous materials [62].
The results of N2 adsorption-desorption isotherms are reflected in the specific surface area (SBET), external surface area (Smeso), micropore volume (Vmicro), and total pore volume (Vp) of GNPs, textural parameters that are summarized in Table 1.
As one might expect, the results of N2 adsorption-desorption isotherms proved that GNPs present, along with the microporous character (Vmicro of about 0.05 cm3 g−1), an extended mesoporosity, and a high specific surface area, which is in good agreement with that provided by the manufacturer. The obtained surface area is still significantly lower than the theoretical surface area of individual graphene sheets (2630 m2 g−1) [63]. However, these results are consistent with the GNP structure, which is characterized by overlapped graphene layers that limit nitrogen adsorption, as previously noted by Srinivas et al. [64]. As it is well known that high surface area potentiates the interaction with bacterial cells and, consequently, cell death [65], the use of these GNPs for antimicrobial applications is a promising approach. Furthermore, several studies reported the potential of microporous materials in the biomedical field for antibacterial applications [66].

3.2. Physicochemical Characterization of GNP/PDMS Surfaces

Because the surface properties, such as hydrophobicity and charge, are known to affect the extent of cell adhesion and biofilm formation [67], the GNP/PDMS surfaces were first characterized by contact angle measurements and the calculation of the respective free energy of interaction (ΔGiwi) among the two entities of a specific surface (i) when immersed in water (w) (Table 2).
The results showed that tested surfaces presented a hydrophobic behaviour. This evidence is in accordance with previously published studies using graphene-based materials [68,69,70], including pristine GNPs embedded in a PDMS matrix [38]. Although it is not possible to observe a linear trend in the evolution of hydrophobicity with the incorporation of increasing GNP loadings, the enhancement of surface hydrophobicity with the incorporation of 5 wt% is quite remarkable. Indeed, it was possible to verify that 5 wt% GNP/PDMS surfaces showed a higher value for the water contact angle (p < 0.0001) compared to PDMS.
Considering that the topography of nanocomposite films may significantly influence the cell adhesion behaviour [71], the characterization of 5 wt% GNP/PDMS surfaces was supplemented by SEM analysis (Figure 2).
From the SEM images, it was possible to draw some conclusions regarding the overall incorporation and distribution of GNPs into the PDMS matrix. Although some bigger conglomerates still exist, reflecting the layer-stacked compact structure of GNPs (which results from the strong π-π interactions between graphene nanoplatelets) [72], in general, GNPs were uniformly dispersed into the PDMS network (Figure 2b,c). This dispersion uniformity guarantees a larger exposure of the surface of GNPs to bacterial cells and, potentially, higher antimicrobial activity [28,73]. The typical flake-like structure of GNPs is perfectly evidenced at higher magnifications (Figure 2d).

3.3. Biological Characterization

The antibiofilm activity of PDMS surfaces containing different GNP loadings was first assessed against S. aureus ATCC 25923. After 24 h of incubation with 1, 2, 3, 4, and 5 wt% GNP/PDMS composites, the culturable cells were quantified (Figure 3). The addition of GNPs to the PDMS matrix resulted in a decrease in cell culturability. A total reduction of up to 55% was achieved for the 5 wt% GNP/PDMS surface, which was chosen for further assays, although there were no statistically significant differences between GNP loadings. These results are in line with those found in the literature, where higher concentrations of graphene derivatives have demonstrated a higher bactericidal or bacteriostatic activity [74,75,76].
The results of S. aureus culturability were supported by the contact angle measurements, which showed higher hydrophobicity levels for 5 wt% GNP/PDMS composite materials compared to the other tested surfaces. Some studies reported the efficient use of hydrophobic and superhydrophobic surfaces to reduce bacterial adhesion (including of S. aureus and P. aeruginosa) and, consequently, biofilm formation [77,78]. The limited antibacterial activity shown by pristine GNP/PDMS composites (reductions of on average 26%; Figure 3), especially those of lower loads, may be explained by the existence of vigorous inter-plane interactions that, by inducing the formation of stronger agglomerates, can reduce the available surface area and, therefore, hinder the GNP mode of action [29].
The 5 wt% GNP/PDMS surface was evaluated in subsequent assays with single- and dual-species biofilms of S. aureus and P. aeruginosa, where its antibiofilm activity was assessed by means of total, viable, culturable, and VBNC cells quantification, and confocal microscopy. By choosing these specific microorganisms, a better understanding of the GNP antibiofilm performance against Gram-positive (S. aureus) and Gram-negative (P. aeruginosa) bacteria can be achieved.
The antibiofilm activity of 5 wt% GNP/PDMS surfaces against single-species biofilms of S. aureus and P. aeruginosa is shown in Figure 4. The analysis of biofilm cells indicated that S. aureus biofilm (Figure 4a) grown on 5 wt% GNP/PDMS surfaces presented significant reductions in the number of total (51%), viable (69%), and VBNC cells (85%) compared to PDMS (p < 0.0001). However, the reduction achieved for the culturable cells (55% compared to PDMS) was not statistically significant (p > 0.05, Figure 3 and Figure 4a).
Regarding P. aeruginosa (Figure 4b), biofilms formed on 5 wt% GNP/PDMS surfaces presented lower reduction percentages of total (25%, p < 0.001), viable (52%, p < 0.0001), and VBNC cells (53%, p > 0.05) compared to PDMS. When compared with S. aureus biofilms, the same extent of reduction of cell culturability was observed (51% compared to PDMS, p < 0.0001).
The antimicrobial and antibiofilm activity of graphene-based nanocomposites against S. aureus and P. aeruginosa was previously reported in other studies. However, those were studies performed with functionalized graphene-based materials, including graphene oxide [79,80,81,82] or reduced graphene oxide [83,84]. Additionally, although some studies report the antimicrobial use of GNP against common causative microorganisms of IAIs [38,73,85,86,87], to the best of our knowledge, only two publications refer to the antimicrobial activity of GNPs against S. aureus and P. aeruginosa, and none of these makes use of pristine GNPs incorporated into a surface [88,89]. Concerning the greater efficacy of GNPs against S. aureus in comparison to P. aeruginosa [81], earlier publications also reported that Gram-positive bacteria are more susceptible to graphene-based materials than Gram-negative bacteria [90,91]. This is mainly due to differences in the cell wall structure [91]. The outer membrane layer in Gram-negative bacteria can act as a protective barrier against graphene exposure compared to Gram-positive bacteria [90].
Overall, these results suggest that loading PDMS with 5 wt% GNPs presents anti-adhesive and antimicrobial properties against both strains, also exerting an effective role in reducing the percentage of VBNC cells, particularly for S. aureus (85%). Given the involvement of these cells in the recurrence of infections [54], our results indicate that 5 wt% GNP/PDMS surfaces may be advantageous for application in IMDs. At the same time, as non-oxidized nanoplatelets induce lower ROS production, they can be considered safer materials for use as antimicrobial agents compared with their functionalized derivatives [92].
Considering that in the natural environment biofilms are characterized by multi-species communities, and that the investigations carried out so far failed to predict the antibiofilm performance of GNP composites on this scenario, 5 wt% GNP/PDMS surfaces were tested against dual-species biofilms of S. aureus and P. aeruginosa (Figure 5). It was possible to observe lower reduction percentages of total (24%), viable (23%), culturable (20%), and VBNC cells (29%) compared to PDMS. Therefore, the antibiofilm activity of 5 wt% GNP/PDMS surfaces was higher in single- than in dual-species biofilms. However, there was still a significant reduction in the number of total and viable cells (p < 0.0001), hence these GNPs constitute promising materials in this field.
The cell culturability of dual-species biofilms also showed that the dominant strain in co-culture biofilms was undoubtedly the Gram-negative P. aeruginosa, with a percentage of 93% and 88% on PDMS and 5 wt% GNP/PDMS composites, respectively (Figure S2a in Supplementary Material). These outcomes are in agreement with previously reported studies, which demonstrated that P. aeruginosa inhibits the growth of S. aureus in dual-species biofilms [7,93,94]. The higher percentage of P. aeruginosa in the co-culture may justify the similarity of behaviours between the single-species biofilms of this Gram-negative bacteria and the mixed ones, which showed higher overall resistance to GNP/PDMS composites.
Representative CLSM images of single-species biofilms of P. aeruginosa and S. aureus and dual-species biofilms on PDMS (control surface) and GNP/PDMS composites are shown in Figure 6.
Concerning single-species biofilms, marked variability in the three-dimensional (3D) structure of biofilms could be observed between the bacterial strains after 24 h of biofilm growth, regardless of the surface material tested (Figure 6a–d). P. aeruginosa completely covered the surface, developing dense and thick biofilms (Figure 6a,b), whereas the S. aureus strain formed highly heterogeneous biofilms consisting of cell aggregates dispersed on the surface (Figure 6c,d). This visual information was supported through the calculated structural parameters of biofilm biovolume and thickness (Figure 7a,b).
Indeed, P. aeruginosa formed biofilms which had on average 74% more biovolume and were 47% thicker than staphylococcal biofilms. Looking at the surface effect, the PDMS surfaces showed the highest biofilm amount and thickness (shadow projection on the right of Figure 6a,c) when compared to the graphene-based surface (Figure 6b,d). In fact, the GNP/PDMS composite was able to reduce the P. aeruginosa and S. aureus biovolume and biofilm thickness compared to the PDMS surface (p < 0.01, Figure 7a,b). However, whereas the decrease in biofilm thickness was similar for both strains (approximately 71%), the biovolume reduction on the surface containing graphene was higher for S. aureus than for P. aeruginosa (83% versus 42% reduction). This result is in agreement with that obtained by epifluorescence microscopy (Figure 4), in which the reduction in the total cell number between the PDMS and 5 wt% GNP/PDMS surface was 57% for S. aureus biofilms and only 25% for Pseudomonas biofilm.
Figure 6e,f shows the architecture of dual-species biofilms of P. aeruginosa and S. aureus grown on PDMS and 5 wt% GNP/PDMS surfaces, respectively. Dual-species biofilms were quite dense and thick as those formed by P. aeruginosa alone (Figure 6a,b). Nevertheless, as for the single-species biofilms (Figure 6a–d), less biofilm amount was observed on the graphene composite compared to PDMS. The quantitative results confirmed the similarity of biovolume and thickness values between dual-species biofilms and P. aeruginosa biofilms (Figure 7), regardless of the tested surface. Additionally, biofilms developed on GNP/PDMS had 42% less biovolume and 74% less thickness than on PDMS coating, reinforcing the anti-adhesive and antimicrobial activities of this surface in typically more adverse conditions such as the presence of different microbial species.
The CLSM study also revealed that the dominant strain in co-culture biofilms was clearly the Gram-negative bacterium P. aeruginosa (Figure 6e,f, and Figures S1 and S2b in Supplementary Material). A small number of S. aureus cells were heterogeneously distributed across surfaces (Figure 6e,f and Figure S1 in Supplementary Material), and the percentage of S. aureus population in biofilms was approximately 11% (Figure S2 in Supplementary Material). This suggests a strong antagonistic behavior by P. aeruginosa towards the Gram-positive bacterium S. aureus. In terms of vertical distribution within biofilms, S. aureus was relatively more abundant at the top, whereas the bottom layers of the biofilm consisted predominantly of Pseudomonas cells (Figure S2 in Supplementary Material).
This work demonstrates the antimicrobial activity of GNP/PDMS surfaces against single- and dual-species biofilms of S. aureus and P. aeruginosa. Although the studied pristine GNP-based materials combined good performance with the simplicity of preparation compared to functionalized composites, graphene functionalization with bioactive molecules and/or polymers may improve its antimicrobial performance. This will be explored in the future, as the percentages of biofilm reduction achieved here were lower than those reported in the literature for these particular bacteria in other coating systems for implantable medical devices [95]. For example, using nanocoatings based on magnetite, polyethyleneglycol, and a biologically active molecule (polymyxin B-PM), Caciandone and colleagues [95] were able to reduce S. aureus and P. aeruginosa culturable cells of up to four and five orders of magnitude, respectively.
Considering the ultimate goal of the produced GNP/PMDS coatings, cytotoxicity assays will be performed in the near future. However, it is known that, although graphene-based materials are not devoid of risks for the human body, they possess lower toxicity and higher biocompatibility than other carbon allotropes, including carbon nanotubes [96]. Furthermore, the vast majority of the studies in this field have shown that conjugating graphene with other biocompatible materials can help to create graphene materials with reduced bioaccumulation impact [97].

4. Conclusions

In this work, GNP/PDMS surfaces were produced and tested for the prevention of single- and dual-species biofilms of S. aureus and P. aeruginosa. It was shown that GNP/PDMS surfaces present high hydrophobicity and a good dispersion level, which are promising characteristics for the application of this carbon compound as an antibacterial agent.
Furthermore, biological assays showed that 5 wt% GNP loading was able to reduce the total and viable cell numbers of S. aureus and P. aeruginosa biofilms compared to PDMS. Although dual-species biofilms demonstrated higher resistance to the antimicrobial activity of 5 wt% GNP/PDMS surfaces, the performance of these coatings in inhibiting single- and dual-species biofilm cells was supported by confocal microscopy analysis, with a significant decrease in the two measured quantitative parameters—biofilm biovolume and thickness. Overall, the results obtained present enough potential to envisage a possible application of 5 wt% graphene/PDMS as an antimicrobial coating in biomedical devices. Future investigations are needed to evaluate the biocompatibility of these specific graphene derivatives, due to the lack of studies in the field.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/nano12030355/s1, Figure S1: Spatial heterogeneity of dual-species biofilms of P. aeruginosa (labeled by the red fluorescent protein mCherry) and S. aureus (countermarked in green with Syto9) formed on 5 wt% GNP/PDMS: section views of the CLSM image presented in Figure 6f. Dotted white lines indicate vertical sections. Scale bar is 100 μm; Figure S2: Proportion of S. aureus (in blue) and P. aeruginosa (in orange) (a) culturable cells and (b) biovolume in dual-species biofilms formed on GNP/PDMS surfaces.

Author Contributions

Conceptualization, M.F.R.P., O.S.G.P.S. and F.J.M.; methodology, I.M.O., M.G., L.C.G. and O.S.G.P.S.; investigation, I.M.O., M.G., L.C.G. and O.S.G.P.S.; resources, M.F.R.P. and F.J.M.; data curation, I.M.O., M.G., L.C.G. and O.S.G.P.S.; writing—original draft preparation, I.M.O., M.G. and L.C.G.; supervision, M.F.R.P., O.S.G.P.S. and F.J.M.; funding acquisition, M.F.R.P. and F.J.M. All authors have read and agreed to the published version of the manuscript.

Funding

This work was financially supported by: Base-UIDB/50020/2020 and Programmatic-UIDP/50020/2020 Funding of LSRE-LCM, funded by national funds through FCT/MCTES (PIDDAC). Base Funding—UIDB/00511/2020 of the Laboratory for Process Engineering, Environment, Biotechnology and Energy—LEPABE—funded by national funds through the FCT/MCTES (PIDDAC); and by Projects PTDC/CTM-COM/4844/2020 (NanoCAT) supported by national funds through the FCT/MCTES (PIDDAC) and NORTE-01-0145-FEDER-000054 (2SMART), supported by Norte Portugal Regional Operational Programme (NORTE 2020), under the PORTUGAL 2020 Partnership Agreement, through the European Regional Development Fund (ERDF). M.G. acknowledges the receipt of a PhD grant from FCT (2021.07149.BD). L.C.G. thanks FCT for the financial support of her work contract through the Scientific Employment Stimulus—Individual Call—[CEECIND/01700/2017]. O.S.G.P.S. acknowledges FCT funding under the Scientific Employment Stimulus—Institutional Call CEECINST/00049/2018.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding authors. The data are not publicly available yet as some datasets are being used for additional publications.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Joung, Y.-H. Development of implantable medical devices: From an engineering perspective. Int. Neurourol. J. 2013, 17, 98–106. [Google Scholar] [CrossRef] [PubMed]
  2. Ellouze, N.; Allouche, M.; Ahmed, H.B.; Rekhis, S.; Boudriga, N. Security of implantable medical devices: Limits, requirements, and proposals. Secur. Commun. Netw. 2014, 7, 2475–2491. [Google Scholar] [CrossRef]
  3. Khatoon, Z.; McTiernan, C.D.; Suuronen, E.J.; Mah, T.-F.; Alarcon, E.I. Bacterial biofilm formation on implantable devices and approaches to its treatment and prevention. Heliyon 2018, 4, e01067. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  4. Weinstein, R.A.; Darouiche, R.O. Device-associated infections: A macroproblem that starts with microadherence. Clin. Infect. Dis. 2001, 33, 1567–1572. [Google Scholar] [CrossRef]
  5. Li, X.; Sun, L.; Zhang, P.; Wang, Y. Novel Approaches to Combat Medical Device-Associated BioFilms. Coatings 2021, 11, 294. [Google Scholar] [CrossRef]
  6. VanEpps, J.S.; Younger, J.G. Implantable device-related infection. Shock 2016, 46, 597–608. [Google Scholar] [CrossRef] [Green Version]
  7. Lima, M.; Teixeira-Santos, R.; Gomes, L.C.; Faria, S.I.; Valcarcel, J.; Vázquez, J.A.; Cerqueira, M.A.; Pastrana, L.; Bourbon, A.I.; Mergulhão, F.J. Development of chitosan-based surfaces to prevent single- and dual-species biofilms of Staphylococcus aureus and Pseudomonas aeruginosa. Molecules 2021, 26, 4378. [Google Scholar] [CrossRef]
  8. Oliva, A.; Miele, M.C.; Al Ismail, D.; Di Timoteo, F.; De Angelis, M.; Rosa, L.; Cutone, A.; Venditti, M.; Mascellino, M.T.; Valenti, P.; et al. Challenges in the microbiological diagnosis of implant-associated infections: A summary of the current knowledge. Front. Microbiol. 2021, 12, 750460. [Google Scholar] [CrossRef]
  9. Jacobsen, S.M.; Stickler, D.J.; Mobley, H.L.T.; Shirtliff, M.E. Complicated catheter-associated urinary tract infections due to Escherichia coli and Proteus mirabilis. Clin. Microbiol. Rev. 2008, 21, 26–59. [Google Scholar] [CrossRef] [Green Version]
  10. Tande, A.J.; Patel, R. Prosthetic joint infection. Clin. Microbiol. Rev. 2014, 27, 302–345. [Google Scholar] [CrossRef] [Green Version]
  11. Haque, M.; Sartelli, M.; McKimm, J.; Abu Bakar, M. Health care-associated infections—An overview. Infect. Drug Resist. 2018, 11, 2321–2333. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  12. Folliero, V.; Franci, G.; Dell’Annunziata, F.; Giugliano, R.; Foglia, F.; Sperlongano, R.; De Filippis, A.; Finamore, E.; Galdiero, M. Evaluation of antibiotic resistance and biofilm production among clinical strain isolated from medical devices. Int. J. Microbiol. 2021, 2021, 9033278–9033288. [Google Scholar] [CrossRef] [PubMed]
  13. Kandi, V.; Vadakedath, S. Implant-associated infections: A review of the safety of cardiac implants. Cureus 2020, 12, e12267. [Google Scholar] [CrossRef]
  14. Seebach, E.; Kubatzky, K.F. Chronic implant-related bone infections-can immune modulation be a therapeutic strategy? Front. Immunol. 2019, 10, 1724. [Google Scholar] [CrossRef] [Green Version]
  15. Tiller, J.C. Chapter 18—Coatings for Prevention or Deactivation of Biological Contaminants. In Developments in Surface Contamination and Cleaning, 2nd ed.; Kohli, R., Mittal, K.L., Eds.; William Andrew Publishing: Oxford, UK, 2008; pp. 751–794. [Google Scholar]
  16. Adlhart, C.; Verran, J.; Azevedo, N.F.; Olmez, H.; Keinänen-Toivola, M.M.; Gouveia, I.; Melo, L.F.; Crijns, F. Surface modifications for antimicrobial effects in the healthcare setting: A critical overview. J. Hosp. Infect. 2018, 99, 239–249. [Google Scholar] [CrossRef] [Green Version]
  17. Tran, H.M.; Tran, H.; Booth, M.A.; Fox, K.E.; Nguyen, T.H.; Tran, N.; Tran, P.A. Nanomaterials for treating bacterial biofilms on implantable medical devices. Nanomaterials 2020, 10, 2253. [Google Scholar] [CrossRef]
  18. Gomes, M.; Gomes, L.; Teixeira-Santos, R.; Mergulhão, F. PDMS in urinary tract devices: Applications, problems and potential solutions. In Polydimethylsiloxane: Structure and Applications, 1st ed.; Carlsen, P.N., Ed.; Nova Science Publishers: Hauppauge, NY, USA, 2020; pp. 95–144. [Google Scholar]
  19. Tiwari, S.K.; Sahoo, S.; Wang, N.; Huczko, A. Graphene research and their outputs: Status and prospect. J. Sci.-Adv. Mater. Devices 2020, 5, 10–29. [Google Scholar] [CrossRef]
  20. Teixeira-Santos, R.; Gomes, M.; Gomes, L.C.; Mergulhão, F.J. Antimicrobial and anti-adhesive properties of carbon nanotube-based surfaces for medical applications: A systematic review. Iscience 2020, 24, 102001. [Google Scholar] [CrossRef] [PubMed]
  21. Mohan, V.B.; Lau, K.-t.; Hui, D.; Bhattacharyya, D. Graphene-based materials and their composites: A review on production, applications and product limitations. Compos. Part B Eng. 2018, 142, 200–220. [Google Scholar] [CrossRef]
  22. Pandit, S.; Gaska, K.; Kádár, R.; Mijakovic, I. Graphene-based antimicrobial biomedical surfaces. ChemPhysChem 2021, 22, 250–263. [Google Scholar] [CrossRef]
  23. Staneva, A.D.; Dimitrov, D.K.; Gospodinova, D.N.; Vladkova, T.G. Antibiofouling activity of graphene materials and graphene-based antimicrobial coatings. Microorganisms 2021, 9, 1839. [Google Scholar] [CrossRef]
  24. Syama, S.; Mohanan, P.V. Comprehensive application of graphene: Emphasis on biomedical concerns. Nanomicro Lett. 2019, 11, 6. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  25. Croitoru, A.-M.; Karaçelebi, Y.; Saatcioglu, E.; Altan, E.; Ulag, S.; Aydoğan, H.K.; Sahin, A.; Motelica, L.; Oprea, O.; Tihauan, B.-M.; et al. Electrically triggered drug delivery from novel electrospun poly(lactic acid)/graphene oxide/quercetin fibrous scaffolds for wound dressing applications. Pharmaceutics 2021, 13, 957. [Google Scholar] [CrossRef] [PubMed]
  26. Yaragalla, S.; Bhavitha, K.B.; Athanassiou, A. A review on graphene based materials and their antimicrobial properties. Coatings 2021, 11, 1197. [Google Scholar] [CrossRef]
  27. Szunerits, S.; Boukherroub, R. Antibacterial activity of graphene-based materials. J. Mater. Chem. B 2016, 4, 6892–6912. [Google Scholar] [CrossRef] [Green Version]
  28. Mohammed, H.; Kumar, A.; Bekyarova, E.; Al-Hadeethi, Y.; Zhang, X.; Chen, M.; Ansari, M.S.; Cochis, A.; Rimondini, L. Antimicrobial mechanisms and effectiveness of graphene and graphene-functionalized biomaterials. a scope review. Front. Bioeng. Biotechnol. 2020, 8, 465–486. [Google Scholar] [CrossRef] [PubMed]
  29. Kumar, P.; Huo, P.; Zhang, R.; Liu, B. Antibacterial properties of graphene-based nanomaterials. Nanomaterials 2019, 9, 737. [Google Scholar] [CrossRef] [Green Version]
  30. Seifi, T.; Kamali, A.R. Anti-pathogenic activity of graphene nanomaterials: A review. Colloids Surf. B Biointerfaces 2021, 199, 111509. [Google Scholar] [CrossRef] [PubMed]
  31. Zhao, M.; Shan, T.; Wu, Q.; Gu, L. The antibacterial effect of graphene oxide on Streptococcus mutans. J. Nanosci. Nanotechnol. 2020, 20, 2095–2103. [Google Scholar] [CrossRef]
  32. Muthuchamy, M.; Govindan, R.; Shine, K.; Thangasamy, V.; Alharbi, N.S.; Thillaichidambaram, M.; Khaled, J.M.; Wen, J.L.; Alanzi, K.F. Anti-biofilm investigation of graphene/chitosan nanocomposites against biofilm producing P. aeruginosa and K. pneumoniae. Carbohydr. Polym. 2020, 230, 115646. [Google Scholar] [CrossRef]
  33. Tian, T.; Shi, X.; Cheng, L.; Luo, Y.; Dong, Z.; Gong, H.; Xu, L.; Zhong, Z.; Peng, R.; Liu, Z. Graphene-based nanocomposite as an effective, multifunctional, and recyclable antibacterial agent. ACS Appl. Mater. Interfaces 2014, 6, 8542–8548. [Google Scholar] [CrossRef] [PubMed]
  34. Dybowska-Sarapuk, Ł.; Kotela, A.; Krzemiński, J.; Wróblewska, M.; Marchel, H.; Romaniec, M.; Łęgosz, P.; Jakubowska, M. Graphene nanolayers as a new method for bacterial biofilm prevention: Preliminary results. J. AOAC Int. 2017, 100, 900–904. [Google Scholar] [CrossRef] [PubMed]
  35. Deng, C.-H.; Gong, J.-L.; Zeng, G.-M.; Jiang, Y.; Zhang, C.; Liu, H.-Y.; Huan, S.-Y. Graphene–CdS nanocomposite inactivation performance toward Escherichia coli in the presence of humic acid under visible light irradiation. Chem. Eng. J. 2016, 284, 41–53. [Google Scholar] [CrossRef]
  36. Dubey, N.; Ellepola, K.; Decroix, F.E.D.; Morin, J.L.P.; Castro Neto, A.H.; Seneviratne, C.J.; Rosa, V. Graphene onto medical grade titanium: An atom-thick multimodal coating that promotes osteoblast maturation and inhibits biofilm formation from distinct species. Nanotoxicology 2018, 12, 274–289. [Google Scholar] [CrossRef] [PubMed]
  37. Arshad, A.; Iqbal, J.; Mansoor, Q. Graphene/Fe3O4 nanocomposite: Solar light driven fenton like reaction for decontamination of water and inhibition of bacterial growth. Appl. Surf. Sci. 2019, 474, 57–65. [Google Scholar] [CrossRef]
  38. Gomes, R.N.; Borges, I.; Pereira, A.T.; Maia, A.F.; Pestana, M.; Magalhães, F.D.; Pinto, A.M.; Gonçalves, I.C. Antimicrobial graphene nanoplatelets coatings for silicone catheters. Carbon 2018, 139, 635–647. [Google Scholar] [CrossRef]
  39. Hu, X.; Qian, W.; Li, X.; Fei, G.; Luo, G.; Wang, Z.; Xia, H. A novel method to prepare homogeneous biocompatible graphene-based PDMS composites with enhanced mechanical, thermal and antibacterial properties. Polym. Compos. 2018, 40, E1397–E1406. [Google Scholar] [CrossRef]
  40. Tu, Q.; Zhang, Q.; Wang, Y.; Jiao, Y.; Xiao, J.; Peng, T.; Wang, J. Antibacterial properties of poly(dimethylsiloxane) surfaces modified with graphene oxide-catechol composite. Prog. Org. Coat. 2019, 129, 247–253. [Google Scholar] [CrossRef]
  41. Qian, W.; Hu, X.; He, W.; Zhan, R.; Liu, M.; Zhou, D.; Huang, Y.; Hu, X.; Wang, Z.; Fei, G.; et al. Polydimethylsiloxane incorporated with reduced graphene oxide (rGO) sheets for wound dressing application: Preparation and characterization. Colloids Surf. B 2018, 166, 61–71. [Google Scholar] [CrossRef] [PubMed]
  42. Sardar, V.B.; Rajhans, N.; Pathak, A.; Prabhu, T. Developments in silicone material for biomedical applications-A review. In Proceedings of the 14th International Conference on Humanizing Work and Work Environment, Punjab, India, 8–11 December 2016; p. 14. [Google Scholar]
  43. Victor, A.; Ribeiro, J.; Araújo, F.F. Study of PDMS characterization and its applications in biomedicine: A review. J. Mech. Eng. Biomech. 2019, 4, 1–9. [Google Scholar] [CrossRef]
  44. Vagos, M.R.; Moreira, J.M.; Soares, O.S.; Pereira, M.F.; Mergulhão, F.J. Incorporation of carbon nanotubes in polydimethylsiloxane to control Escherichia coli adhesion. Polym. Compos. 2019, 40, E1697–E1704. [Google Scholar] [CrossRef]
  45. Gomes, M.; Gomes, L.C.; Teixeira-Santos, R.; Pereira, M.F.R.; Soares, O.S.G.P.; Mergulhão, F.J. Optimizing CNT loading in antimicrobial composites for urinary tract application. Appl. Sci. 2021, 11, 4038. [Google Scholar] [CrossRef]
  46. Rocha, R.P.; Silva, A.M.T.; Romero, S.M.M.; Pereira, M.F.R.; Figueiredo, J.L. The role of O- and S-containing surface groups on carbon nanotubes for the elimination of organic pollutants by catalytic wet air oxidation. Appl. Catal. B 2014, 147, 314–321. [Google Scholar] [CrossRef]
  47. Janczuk, B.; Chibowski, E.; Bruque, J.M.; Kerkeb, M.L.; Caballero, F.G. On the consistency of surface free energy components as calculated from contact angles of different liquids: An application to the cholesterol surface. J. Colloid Interface Sci. 1993, 159, 421–428. [Google Scholar] [CrossRef]
  48. van Oss, C.J.; Chaudhury, M.K.; Good, R.J. Monopolar surfaces. Adv. Colloid Interface Sci. 1987, 28, 35–64. [Google Scholar] [CrossRef]
  49. van Oss, C.; Good, R.; Chaudhury, M. Additive and nonadditive surface tension components and the interpretation of contact angles. Langmuir 1988, 4, 884–891. [Google Scholar] [CrossRef]
  50. van Oss, C.J.; Ju, L.; Chaudhury, M.; Good, R. Estimation of the polar parameters of the surface tension of liquids by contact angle measurements on gels. J. Colloid Interface Sci. 1989, 128, 313–319. [Google Scholar] [CrossRef]
  51. Kétyi, I. A model for testing drug susceptibility of Pseudomonas aeruginosa and Staphylococcus aureus grown in biofilms on medical devices. Acta Microbiol. Immunol. Hung. 1995, 42, 215–219. [Google Scholar] [PubMed]
  52. El Mohtadi, M. Effect of Estrogen on Host-Pathogen Interactions in Ex Vivo and In Vitro Models of the Inflammatory Phase of Age-Related Impaired Healing. Ph.D. Thesis, Manchester Metropolitan University, Manchester, UK, 2019. [Google Scholar]
  53. Gomes, L.; Silva, L.; Simões, M.; Melo, L.; Mergulhão, F. Escherichia coli adhesion, biofilm development and antibiotic susceptibility on biomedical materials. J. Biomed. Mater. Res. Part A 2015, 103, 1414–1423. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  54. Li, L.; Mendis, N.; Trigui, H.; Oliver, J.D.; Faucher, S.P. The importance of the viable but non-culturable state in human bacterial pathogens. Front. Microbiol. 2014, 5, 258. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  55. Gomes, L.C.; Deschamps, J.; Briandet, R.; Mergulhão, F.J. Impact of modified diamond-like carbon coatings on the spatial organization and disinfection of mixed-biofilms composed of Escherichia coli and Pantoea agglomerans industrial isolates. Int. J. Food Microbiol. 2018, 277, 74–82. [Google Scholar] [CrossRef] [PubMed]
  56. Heydorn, A.; Nielsen, A.T.; Hentzer, M.; Sternberg, C.; Givskov, M.; Ersbøll, B.K.; Molin, S. Quantification of biofilm structures by the novel computer program COMSTAT. Microbiology 2000, 146, 2395–2407. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  57. Anovitz, L.M.; Cole, D.R. Characterization and analysis of porosity and pore structures. Rev. Mineral. Geochem. 2015, 80, 61–164. [Google Scholar] [CrossRef] [Green Version]
  58. Sing, K.S.W. Reporting physisorption data for gas/solid systems with special reference to the determination of surface area and porosity (Provisional). Pure Appl. Chem. 1982, 54, 2201–2218. [Google Scholar] [CrossRef]
  59. Solís, R.R.; Mena, I.F.; Nadagouda, M.N.; Dionysiou, D.D. Adsorptive interaction of peroxymonosulfate with graphene and catalytic assessment via non-radical pathway for the removal of aqueous pharmaceuticals. J. Hazard. Mater. 2020, 384, 121340. [Google Scholar] [CrossRef]
  60. Daş, E.; Kaplan, B.Y.; Gürsel, S.A.; Yurtcan, A.B. Graphene nanoplatelets-carbon black hybrids as an efficient catalyst support for Pt nanoparticles for polymer electrolyte membrane fuel cells. Renew. Energy 2019, 139, 1099–1110. [Google Scholar] [CrossRef]
  61. Lee, G.-J.; Rhee, C.K. Enhanced thermal conductivity of nanofluids containing graphene nanoplatelets prepared by ultrasound irradiation. J. Mater. Sci. 2014, 49, 1506–1511. [Google Scholar] [CrossRef]
  62. Wang, Z.; Zhang, X.; Liu, X.; Lv, M.; Yang, K.; Meng, J. Co-gelation synthesis of porous graphitic carbons with high surface area and their applications. Carbon 2011, 49, 161–169. [Google Scholar] [CrossRef]
  63. Zhang, S.; Wang, H.; Liu, J.; Bao, C. Measuring the specific surface area of monolayer graphene oxide in water. Mater. Lett. 2020, 261, 127098. [Google Scholar] [CrossRef]
  64. Srinivas, G.; Zhu, Y.; Piner, R.; Skipper, N.; Ellerby, M.; Ruoff, R. Synthesis of graphene-like nanosheets and their hydrogen adsorption capacity. Carbon 2010, 48, 630–635. [Google Scholar] [CrossRef]
  65. Zawadzka, K.; Kądzioła, K.; Felczak, A.; Wrońska, N.; Piwoński, I.; Kisielewska, A.; Lisowska, K. Surface area or diameter–which factor really determines the antibacterial activity of silver nanoparticles grown on TiO2 coatings? New J. Chem. 2014, 38, 3275–3281. [Google Scholar] [CrossRef] [Green Version]
  66. Morris, R.E. Microporous Materials in Antibacterial Applications. In Antimicrobial Coatings and Modifications on Medical Devices; Zhang, Z., Wagner, V.E., Eds.; Springer: Cham, Switzerland, 2017; pp. 171–188. [Google Scholar]
  67. Renner, L.D.; Weibel, D.B. Physicochemical regulation of biofilm formation. MRS Bull. 2011, 36, 347–355. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  68. Wang, J.-N.; Zhang, Y.-L.; Liu, Y.; Zheng, W.; Lee, L.P.; Sun, H.-B. Recent developments in superhydrophobic graphene and graphene-related materials: From preparation to potential applications. Nanoscale 2015, 7, 7101–7114. [Google Scholar] [CrossRef]
  69. McCallion, C.; Burthem, J.; Rees-Unwin, K.; Golovanov, A.; Pluen, A. Graphene in therapeutics delivery: Problems, solutions and future opportunities. Eur. J. Pharm. Biopharm. 2016, 104, 235–250. [Google Scholar] [CrossRef]
  70. Wang, P.; Yao, T.; Sun, B.; Fan, X.; Dong, S.; Bai, Y.; Shi, Y. A cost-effective method for preparing mechanically stable anti-corrosive superhydrophobic coating based on electrochemically exfoliated graphene. Colloid Surf. A Physicochem. Eng. Asp. 2017, 513, 396–401. [Google Scholar] [CrossRef]
  71. Wu, S.; Zuber, F.; Maniura-Weber, K.; Brugger, J.; Ren, Q. Nanostructured surface topographies have an effect on bactericidal activity. J. Nanobiotechnol. 2018, 16, 20. [Google Scholar] [CrossRef]
  72. Gong, J.; Zhou, Z.; Sumathy, K.; Yang, H.; Qiao, Q. Activated graphene nanoplatelets as a counter electrode for dye-sensitized solar cells. J. Appl. Phys. 2016, 119, 135501. [Google Scholar] [CrossRef]
  73. Borges, I.; Henriques, P.C.; Gomes, R.N.; Pinto, A.M.; Pestana, M.; Magalhães, F.D.; Gonçalves, I.C. Exposure of smaller and oxidized graphene on polyurethane surface improves its antimicrobial performance. Nanomaterials 2020, 10, 349. [Google Scholar] [CrossRef] [Green Version]
  74. Radhi, A.; Mohamad, D.; Rahman, F.S.A.; Abdullah, A.M.; Hasan, H. Mechanism and factors influence of graphene-based nanomaterials antimicrobial activities and application in dentistry. J. Mater. Res. Technol. 2021, 11, 1290–1307. [Google Scholar] [CrossRef]
  75. Liu, S.; Zeng, T.H.; Hofmann, M.; Burcombe, E.; Wei, J.; Jiang, R.; Kong, J.; Chen, Y. Antibacterial activity of graphite, graphite oxide, graphene oxide, and reduced graphene oxide: Membrane and oxidative stress. ACS Nano 2011, 5, 6971–6980. [Google Scholar] [CrossRef] [PubMed]
  76. Sun, W.; Wu, F.G. Two-dimensional materials for antimicrobial applications: Graphene materials and beyond. Chem. Asian J 2018, 13, 3378–3410. [Google Scholar] [CrossRef] [PubMed]
  77. Zhang, X.; Wang, L.; Levänen, E. Superhydrophobic surfaces for the reduction of bacterial adhesion. Rsc Adv. 2013, 3, 12003–12020. [Google Scholar] [CrossRef]
  78. Yuan, Y.; Hays, M.P.; Hardwidge, P.R.; Kim, J. Surface characteristics influencing bacterial adhesion to polymeric substrates. RSC Adv. 2017, 7, 14254–14261. [Google Scholar] [CrossRef] [Green Version]
  79. Liu, S.; Cao, S.; Guo, J.; Luo, L.; Zhou, Y.; Lin, C.; Shi, J.; Fan, C.; Lv, M.; Wang, L. Graphene oxide–silver nanocomposites modulate biofilm formation and extracellular polymeric substance (EPS) production. Nanoscale 2018, 10, 19603–19611. [Google Scholar] [CrossRef]
  80. Wu, X.; Tan, S.; Xing, Y.; Pu, Q.; Wu, M.; Zhao, J.X. Graphene oxide as an efficient antimicrobial nanomaterial for eradicating multi-drug resistant bacteria in vitro and in vivo. Colloids Surf. B Biointerfaces 2017, 157, 1–9. [Google Scholar] [CrossRef]
  81. Di Giulio, M.; Zappacosta, R.; Di Lodovico, S.; Di Campli, E.; Siani, G.; Fontana, A.; Cellini, L. Antimicrobial and antibiofilm efficacy of graphene oxide against chronic wound microorganisms. Antimicrob. Agents Chemother. 2018, 62, e00547-18. [Google Scholar] [CrossRef] [Green Version]
  82. Khan, A.; Ameen, F.; Khan, F.; Al-Arfaj, A.; Ahmed, B. Fabrication and antibacterial activity of nanoenhanced conjugate of silver (I) oxide with graphene oxide. Mater. Today Commun. 2020, 25, 101667–101675. [Google Scholar] [CrossRef]
  83. Dat, N.M.; Long, P.N.B.; Nhi, D.C.U.; Minh, N.N.; Duy, L.M.; Quan, L.N.; Nam, H.M.; Phong, M.T.; Hieu, N.H. Synthesis of silver/reduced graphene oxide for antibacterial activity and catalytic reduction of organic dyes. Synth. Met. 2020, 260, 116260. [Google Scholar] [CrossRef]
  84. Wang, H.; Zhang, Y.; Xu, X.; Yang, F.; Li, K.; Wei, D.; Liu, Z. Efficient loading of silver nanoparticles on graphene oxide and its antibacterial properties. Nano Express 2020, 1, 010041. [Google Scholar] [CrossRef]
  85. Rago, I.; Bregnocchi, A.; Zanni, E.; D’Aloia, A.G.; De Angelis, F.; Bossu, M.; De Bellis, G.; Polimeni, A.; Uccelletti, D.; Sarto, M.S. Antimicrobial activity of graphene nanoplatelets against Streptococcus mutans. In Proceedings of the IEEE International Conference on Nanotechnology, Rome, Italy, 27–30 July 2015; pp. 9–12. [Google Scholar]
  86. Bregnocchi, A.; Zanni, E.; Uccelletti, D.; Marra, F.; Cavallini, D.; De Angelis, F.; De Bellis, G.; Bossu, M.; Ierardo, G.; Polimeni, A.; et al. Graphene-based dental adhesive with anti-biofilm activity. J. Nanobiotechnology 2017, 15, 89. [Google Scholar] [CrossRef]
  87. Scaffaro, R.; Botta, L.; Maio, A.; Gallo, G. PLA graphene nanoplatelets nanocomposites: Physical properties and release kinetics of an antimicrobial agent. Compos. Part B Eng. 2017, 109, 138–146. [Google Scholar] [CrossRef]
  88. Bregnocchi, A.; Zanni, E.; Rago, I.; Paliotta, L.; Bellis, G.D.; Uccelletti, D.; Sarto, M.S. Antimicrobial activity of graphene nanoplatelets against Staphylococcus aureus. In Proceedings of the GraphIta 2015, Bologna, Italy, 14–18 September 2015. [Google Scholar]
  89. Zanni, E.; Bruni, E.; Chandraiahgari, C.; De Bellis, G.; Santangelo, M.; Leone, M.; Bregnocchi, A.; Mancini, P.; Sarto, M.; Uccelletti, D. Evaluation of the antibacterial power and biocompatibility of zinc oxide nanorods decorated graphene nanoplatelets: New perspectives for antibiodeteriorative approaches. J. Nanobiotechnology 2017, 15, 57. [Google Scholar] [CrossRef]
  90. Pulingam, T.; Thong, K.L.; Ali, M.E.; Appaturi, J.N.; Dinshaw, I.J.; Ong, Z.Y.; Leo, B.F. Graphene oxide exhibits differential mechanistic action towards Gram-positive and Gram-negative bacteria. Colloids Surf. B Biointerfaces 2019, 181, 6–15. [Google Scholar] [CrossRef] [PubMed]
  91. Akhavan, O.; Ghaderi, E. Toxicity of graphene and graphene oxide nanowalls against bacteria. ACS Nano 2010, 4, 5731–5736. [Google Scholar] [CrossRef]
  92. McIntyre, J.; Verma, N.; Smith, R.; Rezvani, E.; Duesberg, G.; Coleman, J.; Volkov, Y. Biocompatibility of pristine graphene monolayers, nanosheets and thin films. arXiv 2014, arXiv:1406.2497. [Google Scholar]
  93. Dehbashi, S.; Alikhani, M.Y.; Tahmasebi, H.; Arabestani, M.R. The inhibitory effects of Staphylococcus aureus on the antibiotic susceptibility and virulence factors of Pseudomonas aeruginosa: A549 cell line model. AMB Express 2021, 11, 50. [Google Scholar] [CrossRef] [PubMed]
  94. Kim, S.; Yoon, Y.; Choi, K.H. Pseudomonas aeruginosa DesB promotes Staphylococcus aureus growth inhibition in coculture by controlling the synthesis of HAQs. PLoS ONE 2015, 10, e0134624. [Google Scholar] [CrossRef] [Green Version]
  95. Caciandone, M.; Niculescu, A.-G.; Roșu, A.R.; Grumezescu, V.; Negut, I.; Holban, A.M.; Oprea, O.; Vasile, B.Ș.; Bîrcă, A.C.; Grumezescu, A.M.; et al. PEG-functionalized magnetite nanoparticles for modulation of microbial biofilms on voice prosthesis. Antibiotics 2022, 11, 39. [Google Scholar] [CrossRef]
  96. Mendes, R.G.; Bachmatiuk, A.; Büchner, B.; Cuniberti, G.; Rümmeli, M.H. Carbon nanostructures as multi-functional drug delivery platforms. J. Mater. Chem. B 2013, 1, 401–428. [Google Scholar] [CrossRef] [PubMed]
  97. Zhang, Q.; Wu, Z.; Li, N.; Pu, Y.; Wang, B.; Zhang, T.; Tao, J. Advanced review of graphene-based nanomaterials in drug delivery systems: Synthesis, modification, toxicity and application. Mater. Sci. Eng. C 2017, 77, 1363–1375. [Google Scholar] [CrossRef]
Figure 1. Representative scheme of the experimental tasks performed within the scope of this work.
Figure 1. Representative scheme of the experimental tasks performed within the scope of this work.
Nanomaterials 12 00355 g001
Figure 2. Scanning electron microscopy (SEM) images of (a) PDMS (magnification of 100×) and 5 wt% GNP/PDMS surfaces with a magnification of (b) 100×, (c) 500×, and (d) 10,000×.
Figure 2. Scanning electron microscopy (SEM) images of (a) PDMS (magnification of 100×) and 5 wt% GNP/PDMS surfaces with a magnification of (b) 100×, (c) 500×, and (d) 10,000×.
Nanomaterials 12 00355 g002
Figure 3. Percentage of S. aureus culturable cells after 24 h of biofilm formation on PDMS (control), and 1, 2, 3, 4, and 5 wt% GNP/PDMS composites. The means ± standard error (SE) are presented.
Figure 3. Percentage of S. aureus culturable cells after 24 h of biofilm formation on PDMS (control), and 1, 2, 3, 4, and 5 wt% GNP/PDMS composites. The means ± standard error (SE) are presented.
Nanomaterials 12 00355 g003
Figure 4. Percentage of S. aureus (a) and P. aeruginosa (b) single-species biofilm cells on PDMS (control) and 5 wt% GNP/PDMS composites. The means ± SE are presented. Significant differences compared with PDMS are represented for p < 0.001 by *** and p < 0.0001 by ****.
Figure 4. Percentage of S. aureus (a) and P. aeruginosa (b) single-species biofilm cells on PDMS (control) and 5 wt% GNP/PDMS composites. The means ± SE are presented. Significant differences compared with PDMS are represented for p < 0.001 by *** and p < 0.0001 by ****.
Nanomaterials 12 00355 g004
Figure 5. Percentage of S. aureus + P. aeruginosa biofilm cells on PDMS (control) and 5 wt% GNP/PDMS composites. The means ± SE are presented. Significant differences compared with PDMS are represented for p < 0.0001 by ****.
Figure 5. Percentage of S. aureus + P. aeruginosa biofilm cells on PDMS (control) and 5 wt% GNP/PDMS composites. The means ± SE are presented. Significant differences compared with PDMS are represented for p < 0.0001 by ****.
Nanomaterials 12 00355 g005
Figure 6. Single-species biofilms of (a,b) P. aeruginosa and (c,d) S. aureus, and (e,f) mixed biofilms of P. aeruginosa (in red) and S. aureus (in green) formed on PDMS (left images) and 5 wt% GNP/PDMS (right images). These pictures were extracted from confocal files by IMARIS software and present an aerial view of biofilm structures. The shadow projection on the right represents the biofilm thickness. Scale bars are 50 μm.
Figure 6. Single-species biofilms of (a,b) P. aeruginosa and (c,d) S. aureus, and (e,f) mixed biofilms of P. aeruginosa (in red) and S. aureus (in green) formed on PDMS (left images) and 5 wt% GNP/PDMS (right images). These pictures were extracted from confocal files by IMARIS software and present an aerial view of biofilm structures. The shadow projection on the right represents the biofilm thickness. Scale bars are 50 μm.
Nanomaterials 12 00355 g006
Figure 7. (a) Biovolumes and (b) thickness of P. aeruginosa and S. aureus single-species biofilms, and mixed biofilms (P. aeruginosa + S. aureus) on PDMS and 5 wt% GNP/PDMS surfaces. Both parameters were extracted from confocal files with the ImageJ software. The means ± standard deviation are presented. Significant differences are represented for p < 0.01 by ** and <0.001 by *** when compared with PDMS.
Figure 7. (a) Biovolumes and (b) thickness of P. aeruginosa and S. aureus single-species biofilms, and mixed biofilms (P. aeruginosa + S. aureus) on PDMS and 5 wt% GNP/PDMS surfaces. Both parameters were extracted from confocal files with the ImageJ software. The means ± standard deviation are presented. Significant differences are represented for p < 0.01 by ** and <0.001 by *** when compared with PDMS.
Nanomaterials 12 00355 g007
Table 1. Textural properties of graphene nanoplatelets (GNPs).
Table 1. Textural properties of graphene nanoplatelets (GNPs).
Sample SBET
(m2 g−1)
Smeso
(m2 g−1)
Vmicro
(cm3 g−1)
Vp p/p0 = 0.99
(cm3 g−1)
GNPs4643630.0450.535
Table 2. Contact angles with water (θw), formamide (θF), and α-bromonaphthalene (θB) for bare polydimethylsiloxane (PDMS) and GNP/PDMS surfaces. The respective free energy of interaction (ΔGiwi) is also included.
Table 2. Contact angles with water (θw), formamide (θF), and α-bromonaphthalene (θB) for bare polydimethylsiloxane (PDMS) and GNP/PDMS surfaces. The respective free energy of interaction (ΔGiwi) is also included.
SurfaceContact Angle (°)Hydrophobicity
(mJ m−2)
θwθFθBΔGiwi
PDMS110.2 ± 3.6112.4 ± 3.190.5 ± 4.9−50.2
1 wt% GNP/PDMS108.6 ± 2.2104.1 ± 3.382.5 ± 3.5−58.9
2 wt% GNP/PDMS110.4 ± 1.9105.7 ± 4.588.2 ± 3.6−63.1
3 wt% GNP/PDMS110.3 ± 1.6105.5 ± 2.788.6 ± 3.1−57.2
4 wt% GNP/PDMS111.9 ± 2.3107.9 ± 5.792.8 ± 2.8−65.5
5 wt% GNP/PDMS121.8 ± 3.3113.9 ± 3.6102.4 ± 4.1−87.7
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Oliveira, I.M.; Gomes, M.; Gomes, L.C.; Pereira, M.F.R.; Soares, O.S.G.P.; Mergulhão, F.J. Performance of Graphene/Polydimethylsiloxane Surfaces against S. aureus and P. aeruginosa Single- and Dual-Species Biofilms. Nanomaterials 2022, 12, 355. https://doi.org/10.3390/nano12030355

AMA Style

Oliveira IM, Gomes M, Gomes LC, Pereira MFR, Soares OSGP, Mergulhão FJ. Performance of Graphene/Polydimethylsiloxane Surfaces against S. aureus and P. aeruginosa Single- and Dual-Species Biofilms. Nanomaterials. 2022; 12(3):355. https://doi.org/10.3390/nano12030355

Chicago/Turabian Style

Oliveira, Isabel M., Marisa Gomes, Luciana C. Gomes, Manuel F. R. Pereira, Olívia S. G. P. Soares, and Filipe J. Mergulhão. 2022. "Performance of Graphene/Polydimethylsiloxane Surfaces against S. aureus and P. aeruginosa Single- and Dual-Species Biofilms" Nanomaterials 12, no. 3: 355. https://doi.org/10.3390/nano12030355

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.