The Glass-Transition Temperature of Supported PMMA Thin Films with Hydrogen Bond/Plasmonic Interface
Next Article in Special Issue
Unprecedentedly High Activity and/or High Regio-/Stereoselectivity of Fluorenyl-Based CGC Allyl-Type η31-tert-Butyl(dimethylfluorenylsilyl)amido Ligated Rare Earth Metal Monoalkyl Complexes in Olefin Polymerization
Previous Article in Journal
A New Strategy for the Synthesis of Hydroxyl Terminated Polystyrene-b-Polybutadiene-b-Polystyrene Triblock Copolymer with High Cis-1, 4 Content
Previous Article in Special Issue
Characteristics and Mechanism of Vinyl Ether Cationic Polymerization in Aqueous Media Initiated by Alcohol/B(C6F5)3/Et2O
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Synthesis and Photoinduced Anisotropy of Polymers Containing Nunchaku-Like Unit with an Azobenzene and a Mesogen

1
Research Branch of Advanced Functional Materials, School of Materials and Energy, University of Electronic Science and Technology of China, Chengdu 611731, China
2
School of Automotive Studies, Tongji University, Shanghai 201804, China
3
Department of Chemical Engineering, Laboratory of Advanced Materials (MOE), Tsinghua University, Beijing 100084, China
*
Author to whom correspondence should be addressed.
These authors contributed equally to this work.
Polymers 2019, 11(4), 600; https://doi.org/10.3390/polym11040600
Submission received: 14 March 2019 / Revised: 25 March 2019 / Accepted: 25 March 2019 / Published: 2 April 2019
(This article belongs to the Collection Design and Synthesis of Polymers)

Abstract

:
A series of polymers containing nunchaku-like unit with an azo chromophore and a mesogen group was successfully prepared and photoinduced anisotropy of the obtained polymers was minutely investigated. Firstly, monomers containing nunchaku-like unit with an azo chromophore and a mesogen group linked by flexible group were synthesized. The structure of the monomers was confirmed via NMR COSY spectra. Subsequently, the obtained monomers were polymerized into corresponding polymers through RAFT polymerization. The prepared polymer samples were characterized through NMR, FTIR, gel permeation chromatography (GPC), and UV-vis testing while the thermal properties of the samples were investigated through differential scanning calorimeter (DSC) and thermogravimetric analysis (TGA) measurements. The photoinduced isomerization of the polymers, which was researched in situ via measuring UV-vis spectra of the polymer solutions and spin-coated films under irradiation with 450 nm light or putting in darkness, demonstrated the rapid trans-cis-trans isomerization of the polymers. When irradiated with a linearly polarized light, significant photoinduced birefringence and dichroism were observed, suggesting photoinduced isomerization of azobenzene can drive orientation of mesogen in the system. This study blazes a way to design the optical materials with light-controllable birefringence and dichroism.

Graphical Abstract

1. Introduction

Azobenzene, which can perform trans-cis isomerization upon irradiating with suitable light, has been intensively investigated as photoresponsive materials [1,2,3,4]. Up to now, the materials containing azobenzene have exhibited a variety of photoresponsive properties such as photoinduced colloidal deformation, [5] bending, [6,7] spontaneous surface pattern, [8] phase transition, [9] surface-relief-gratings, [10,11] birefringence, [12] dichroism, [12,13], etc. [14,15,16]. The photoinduced dichroism and birefringence, also known as photoinduced anisotropy resulting from the repeating photoisomerization of azobenzene upon irradiation with light, are two of the most important properties attracting extensive attention [12,13,17,18]. The azobenzene materials will display a highest photoinduced anisotropy when all of the azobenzene chromophores move to the oriented direction at which no more light can be absorbed (the orientation perpendicular to polarization direction of irradiating ray). Hence, photoinduced anisotropy also results from the rod-like nature of azobenzene chromophores [12]. Furthermore, liquid crystals which usually contain rod-like mesogens can also exhibit giant dichroism and birefringence when oriented [19,20]. Consequently, the photoinduced anisotropy of the azobenzene materials will be theoretically improved through incorporating mesogens and other rod-like molecules.
Azobenzene can be divided as the aminoazobenzene, azobenzene branch, and pseudo-stilbene branch based on their isomerization behavior and spectral feature [21,22]. Due to the mesogenic property of azobenzene, the azobenzene branch usually displays liquid crystalline features [23,24,25,26]. As a consequence, such kind of azobenzene tends to exhibit higher photoinduced anisotropy when exposed to polarized light. However, the absorption of the abovementioned azobenzene is usually in the range of UV which greatly limits its further application. The pseudo-stilbene azobenzenes which have electron-withdrawing/donating groups on their 4 and 4′ sites are also known as push-pull azobenzenes [27]. Intense absorptions of the azobenzenes are observed in visible light benefiting from the π→π* transition. Unfortunately, liquid crystalline phase from pseudo-stilbene azobenzene is seldom observed on account of its nonlinear structure together with intense dipole [28]. To further improve the photoinduced anisotropy of the pseudo-stilbene azobenzenes, liquid crystalline mesogens are designed to be linked with the azobenzene chromophores. In accordance with the above standpoint, nunchaku-like molecules have been designed and synthesized [29,30]. The obtained molecules exhibiting the properties of azo molecular glasses display significant photoinduced birefringence and dichroism. In addition, compared with the azopolymers whose photoinduced birefringence is apt to decline when irradiated light is shut off, birefringence reduction is not observed for some of the aforementioned nunchaku-like molecules under the same condition. Nevertheless, the nunchaku-like molecules are much worse processable compared with the azo polymers on account of their relatively low molecular weight. Furthermore, few reports about azo polymer containing a nunchaku-like molecule with an azobenzene and a mesogen have been published.
In this paper, a series of polymers containing nunchaku-like unit with an azobenzene and a mesogen are reasonably designed and successfully synthesized. In the first step, monomers containing nunchaku-like unit with an azobenzene and a mesogen group linked by flexible group are synthesized. Then, the obtained monomers are polymerized into corresponding polymers through reversible-addition fragmentation-chain transfer polymerization. Finally, the photoinduced dichroism and birefringence of these polymers are studied minutely.

2. Experimentals

2.1. Materials

N-phenyldiethanolamine (97%), 4-cyanoaniline (98%), 4-aminobenzoic acid (99%), phosphorus oxychloride (98%), dichloromethane (99%), and hydrochloric acid (37%) were purchased from TCI. 4-Cyano-4-(phenylcarbonothioylthio) pentanoic acid (CPPA, 97%) was supplied by Sigma Aldrich. N,N-dimethylformamide (99%), potassium carbonate (99%), potassium iodide (99%), and magnesium sulphate (99%) were obtained from Tianjin Bodi (Tianjin, China). AIBN was recrystallized in methanol. Other reagents were commercially products.

2.2. Synthesis of the Polymers

4-(Acryloyloxyhexyloxycarbonyl)phenyl 4′-(2″-(N-ethyl(N-(4‴-(4′′′′-cyanophenylazo))phenyl)amino)ethyloxy)benzoate (7B). 1.2 g (10 mmol) 4-cyanoaniline was homogeneously dissolved in 30 mL acetic acid in the environment of ice bath. The diazonium salt was obtained by addition of 2 mL sulfuric acid and 0.8 g (12 mmol) sodium nitrite with conspicuous stirring. By adding diazonium salt sluggishly into 6.5 g (10 mmol) compound 6 in 100 mL DMF with conspicuous stirring in ice bath, continually reacting for another 12 h below 5 °C and precipitating with numerous deionized water, and the production was prepared via flitting and drying in vacuum for 12 h. Yield: 90%. 1 H NMR (600 MHz, CDCl3) δ (ppm): 8.13 (m, 4H), 7.89 (m, 4H), 7.74 (d, 2H), 7.26 (d, 2H), 6.97 (d, 2H), 6.81 (d, 2H), 6.36, 6.11, 5.79 (3m, 3H), 4.33 (t, 2H), 4.27 (t, 2H), 4.16 (t, 2H), 3.90 (t, 2H), 3.61 (m, 2H), 1.78 (m, 2H), 1.70 (m, 2H), 1.47 (m, 4H), 1.28 (t, 3H). IR (KBr, cm−1): 3062, 2937, 2868, 2222, 1741, 1709, 1633, 1605, 1512, 1257, 1167. MS (ESI): calcd.: m/z = 689.30; found: 689.29. UV-Vis: λmax = 448 nm.
4-(Acryloyloxyhexyloxycarbonyl)phenyl 4′-(2″-(N-ethyl(N-(4‴-(4′′′′-carboxylphenylazo))phenyl)amino)ethyloxy)benzoate (7A). 7A was similarly synthesized as 7B. Yield: 85%. 1 H NMR (600 MHz, d6-DMSO) δ (ppm): 13.00 (b, 1H), 8.02 (m, 6H), 7.79 (m, 4H), 7.39 (d, 2H), 7.11 (d, 2H), 6.91 (d, 2H), 6.28, 6.12, 5.87 (3m, 3H), 4.30 (t, 2H), 4.25 (t, 2H), 4.08 (t, 2H), 3.87 (t, 2H), 3.57 (m, 2H), 1.69 (m, 2H), 1.60 (m, 2H), 1.37 (m, 4H), 1.17 (t, 3H). IR (KBr, cm−1): 3063, 2933, 2858, 1716, 1682, 1633, 1595, 1508, 1255, 1161. MS (ESI): calcd.: m/z = 708.29; found: 708.29. UV-Vis: λmax = 433 nm.
4-(Acryloyloxyhexyloxycarbonyl)phenyl 4′-(2″-(N-ethyl(N-(4‴-(4′′′′-nitrophenylazo))phenyl)amino)ethyloxy)benzoate (7C). 7C was similarly synthesized as 7B. Yield: 90%. 1 H NMR (600 MHz, CDCl3) δ (ppm): 8.29 (d, 2H), 8.13 (m, 4H), 7.90 (m, 4H), 7.27 (d, 2H), 6.97 (d, 2H), 6.81 (d, 2H), 6.37, 6.11, 5.80 (3m, 3H), 4.32 (t, 2H), 4.27 (t, 2H), 4.16 (t, 2H), 3.89 (t, 2H), 3.63 (m, 2H), 1.79 (m, 2H), 1.70 (m, 2H), 1.47 (m, 4H), 1.29 (t, 3H). IR (KBr, cm−1): 3060, 2937, 1732, 1709, 1631, 1603, 1514, 1254, 1157. MS (ESI): calcd.: m/z = 709.29; found: 709.29. UV-Vis: λmax = 476 nm.
Poly 4-(acryloyloxyhexyloxycarbonyl)phenyl 4′-(2″-(N-ethyl(N-(4‴-(4′′′′-cyanophenylazo))phenyl)amino)ethyloxy)benzoate (8B). 7B (1.72 g, 2.5 mmol), AIBN (0.5 mL, 1.64 mg/mL in anisole), 1.5 mL of anisole and CPPA (14 mg, 50 µmol) were added into Schlenk flask. The system was degassed and placed at 80 °C for 24 h. Crude product was purified by washing with hot ethanol yielding red product (80%). GPC: Mn = 1.5 × 104, Mw/Mn = 1.26. 1 H NMR (300 MHz, CDCl3) δ (ppm): 8.04, 7.89, 7.72, 7.27, 6.95, 6.83, 4.24, 4.02, 3.87, 3.60, 2.30, 1.73, 1.62, 1.43, 1.28. IR (KBr, cm−1): 2931, 2847, 2223, 1790, 1591, 1507, 1386, 1256, 1156, 1065. UV-vis: λmax = 449 nm.
Poly 4-(acryloyloxyhexyloxycarbonyl)phenyl 4′-(2″-(N-ethyl(N-(4‴-(4′′′′-carboxylphenylazo))phenyl)amino)ethyloxy)benzoate (8A). 8A was similarly polymerized as 8B (60%). GPC: Mn = 1.3 × 104, Mw/Mn = 1.22. 1 H NMR (300 MHz, d6-DMSO) δ (ppm): 8.01, 7.86, 7.72, 7.19, 6.89, 4.09, 2.14, 1.43, 1.20. IR (KBr, cm−1): 3349, 2931, 2847, 1790, 1728, 1591, 1507, 1386, 1256, 1156, 1065. UV-vis: λmax = 435 nm.
Poly 4-(acryloyloxyhexyloxycarbonyl)phenyl 4′-(2″-(N-ethyl(N-(4‴-(4′′′′-nitrophenylazo))phenyl)amino)ethyloxy)benzoate (8C). 8C was similarly polymerized as 8B (85%). GPC: Mn = 1.6 × 104, Mw/Mn = 1.28. 1 H NMR (300 MHz, CDCl3) δ (ppm): 8.21, 8.01, 7.87, 7.19, 6.91, 6.76, 4.23, 4.00, 3.85, 3.56, 2.28, 1.67, 1.62, 1.37, 1.24. IR (KBr, cm−1): 2931, 2847, 1790, 1591, 1507, 1386, 1332, 1256, 1156, 1065. UV-vis: λmax = 478 nm.

2.3. Photo-Responsive Properties of the Polymers

Photoinduced isomerization of the polymers. The trans-cis photoinduced isomerization of 8A, 8B, and 8C was investigated with ultraviolet spectrometer and a LED (450 nm, 0.8 mW/cm2). 0.02 mg/mL THF solutions and spin-coated films with a thickness of about 0.2 µm of these polymers were prepared for the photo-isomerization study. When the photo-stationary states of the sample were reached, the LED lamp was shut off (at night) to study cis-trans isomerization of the polymer solutions until azobenzene molecules got back to the trans state.
Photoinduced birefringence of the polymers. Spin-coated polymer film of 8A, 8B, and 8C on the glass slide was utilized for such study. The film thickness was controlled in the range of 0.2–0.5 μm. The films were dried at 50 °C under vacuum for 18 h before use. One laser beam (532 nm, 50 mW/cm2) was used as the light source irradiating on the polymer film homogenously. Another laser beam (633 nm, 1.8 mW/cm2) was utilized as probe beam transmitting two crossed polarizers before being recorded by a photodiode [31].
Photoinduced dichroism of the polymers. Spin-coated polymer film of 8A, 8B, and 8C on CaF2 were utilized for such study. The film thickness was about 100 nm. The films were dried at 50 °C under vacuum for 18 h before use. According to the results of the photoinduced birefringence, the irradiation time was controlled to ensure saturation of the samples. Then, the polarized FT-IR spectra of the polymers were measured. A polarizer was inserted ahead of the sample. The polarized FT-IR was recorded at every 10° during rotating the samples [31].

2.4. Characterization

The polymers 8A, 8B, and 8C and the intermediates were characterized through 1 H and 13 C NMR spectra (JEOL JNM-ECA300 and JEOL JNM-ECA600, Tokyo, Japan, solvent: d6-DMSO or CDCl3), Fourier-transform infrared spectroscopic spectrum (FT-IR, Nicolet 560, Madison, WI, USA, in KBr disk), UV-Vis spectrum (UV-vis, Agilent 8453, Santa Clara, CA, USA, THF solution or spin-coated film), mass spectrum (MS, Thermofisher LTQ, Waltham, MA, USA, dissolved in chloroform), differential scanning calorimeter (DSC, TA Q100, New Castle, DE, USA, 10 °C/min in a nitrogen), Thermogravimetric analysis (TGA, TA Q50, New Castle, DE, USA, 20 °C/min in a nitrogen), polarizing microscopy (POM, Nikon LV 1000 POL, Tokyo, Japan) observations, and gel permeation chromatography (GPC, PLgel 5 μm mixed-D column and Wyatt Optilab rEX detector, Santa Barbara, CA, USA, 35 °C, THF as the eluent, PS as standard). The photoresponsive properties were characterized via UV-Vis spectrum, photoinduced birefringence, and photoinduced dichroism measurements.

3. Results and Discussion

The polymers (8A, 8B, and 8C) are prepared according to the synthetic route as shown in Figure 1. The products and intermediates are named from compound 1 to compound 8 as shown in Figure 1. In the first five steps, 4-acryloyloxyhexyloxycarbonyl)phenyl 4′-(2′’-(N-ethyl(N-phenyl)amino)ethyloxy)benzoate (compound 6) containing a mesogen group and a terminal aniline functionality that is suitable for azo coupling are synthesized. Then, diazonium salts from p-aminobenzoic acid, p-cyanoaniline, and p-nitroaniline react with compound 6 generating the corresponding monomers 7A, 7B, and 7C. Finally, the obtained monomers are polymerized into corresponding polymers (8A, 8B, and 8C) through RAFT polymerization.
Synthetic details of intermediates are descripted in the supporting information (Figures S1–S6). The NMR COSY spectrum of the monomer 7B with resonance signal assignments is displayed in Figure 2 [32]. The signals at 6.36, 6.11, and 5.79 ppm root in the protons (a, b, and c) at the acrylate. Signals at 8.13, 7.26, 6.97 ppm attribute to hydrogens on aromatic rings from the mesogen group. In contrast, the other aromatic resonances in the low fields result from the protons on the aromatic rings from the azobenzene. The triplet from 1.28 ppm hails from methyl group proton p, and the only quartet at 3.61 ppm derives from the methylene q next to the methyl group. The multiple resonances at 1.78, 1.70, and 1.47 ppm come from the protons at the four middle methylene groups connecting the acrylate and the mesogen. According to the coupling, the triplets at 4.32 and 4.16 ppm originate in the protons from the other two methylene groups (i and d) connecting the acrylate and the mesogen. The other two triplets at 4.27 and 3.90 ppm showing mutual coupling stem from the protons from the methylene groups (n and o) connecting the mesogen and the azobenzene. All of the resonances and couplings can be perfectly assigned according to the structure of 7B, indicating the successful preparation of monomer 7B. Similarly, the NMR COSY spectra of the monomer 7A and 7C with resonance signal assignments are shown in Figures S7 and S8.
The polymers 8A, 8B, and 8C are prepared through RAFT polymerization [31]. Figure 3a depicts 1 H NMR spectrum of 8A, 8B, and 8C. Compared with 1 H NMR spectra of 7A, 7B, and 7C, resonances from acrylate disappear while the other resonances transform into broad peaks, indicating the successful polymerization of the monomers. It needs to be pointed out that proton NMR spectrum of 8A shows low resolution due to its insoluble in chloroform and relatively poor solubility in DMSO. However, the abovementioned polymers can be totally dissolved in DMF which is a necessary for the fabrication of the corresponding films for the later study. Figure 3b exhibits the FTIR spectra of polymers 8A, 8B, and 8C. All of the polymers display absorption features at 2931, 2847, 1790, 1591, 1507, 1386, 1256, 1156, and 1065 cm−1. In addition, 8A demonstrates absorption features at 3349 and 1728 cm−1 attributing to carboxyl group, 8B shows the absorption feature at 2223 cm−1 coming from cyano group and 8C exhibits the absorption feature at 1332 cm−1 resulting from nitro group [29,33]. Mn is determined to be 13,000, 15,000, and 16,000, and PDI is 1.22, 1.26, and 1.28 respectively for 8A, 8B, and 8C according to GPC results (Figure S9a) [34]. Figure S9b exhibits UV-vis spectra of 8A, 8B, and 8C in THF. The λmax of 8A, 8B, and 8C is 435, 449, and 478 nm, respectively [35,36].
The thermal performance of the polymers 8A, 8B, and 8C is further studied after the synthesis of them. According to the literature, polymers containing the mesogen which is used in this study can form liquid crystalline phase when cooled from their melt [37]. However, the pseudo-stilbene azobenzene cannot form liquid crystalline phase due to the nonlinear structure together with intense dipole [28]. Figure S10 is the DSC curves of the monomers 7A, 7B, and 7C during the second heating and cooling scan from −5 °C to 180 °C and back to −5 °C. All of the three monomers show only one endothermic and exothermic peak during the heating and cooling scans corresponding to the melting and crystallizing point of the monomers, suggesting that the monomers cannot form liquid crystal phase. Figure S11a depicts the DSC curves of 8A, 8B, and 8C cooling from 180 °C. As shown from the figure, all of the polymers exhibit only one Tg and no liquid crystalline phase transition is observed upon cooling from high temperature. The Tg is 83, 75, and 70 °C for 8A, 8B, and 8C, respectively [38]. POM observations also suggest that 8A, 8B, and 8C are isotropic without preferential molecular orientation. This would be deriving from the nunchaku-like structure of the side chain in the polymers which impedes the formation of ordered structure. TGA curves of the polymers 8A, 8B, and 8C are illustrated in Figure S11b from which decomposition temperature (T10%) is determined to be 272, 282, and 286 °C for 8A, 8B, and 8C, respectively.
Figure 4a displays UV-vis spectral variation of 8B solution as a typical example for studying photo-isomerization of the polymers. Upon irradiation with 450 nm light, absorbance peak at 449 nm decreases while a new absorbance peak (382 nm) is observed simultaneously evidencing trans-cis isomerization of the azobenzenes. After irradiating for 60 s, λmax keeps constant due to the attainment of photo-stationary state [39]. Figure 4b indicates the changing of λmax of 8A, 8B, and 8C irradiated with the LED light for different time. This UV-vis result as depicted by Figure 4b could be best fitted by Equation (1):
At/A0 = O + P exp(−t/Q)
where A0 is intensity at λmax before irradiating, while At reflects intensity at λmax after irradiating t seconds, O, P, and Q are constants [39]. According to this equation, results depicted in Figure 4b can be best fitted by curves given in the same figure. Another result obtained from the figure is that the isomerization degree (A0At)/A0 decreases from 0.57 for 8A to 0.39 and 0.04 for 8B and 8C, respectively. Furthermore, the time consumed to reach the photo-stationary state decreases from 8A to 8C gradually. The differences of the isomerization degree and the time consumed to reach the photo-stationary state are attributed to electron-withdrawing groups at 4′ position of azobenzene. According to the literature, the highest isomerization degree of 8A would be resulting from the hydrogen-bonding formed from the carboxyl groups [31]. In addition, the stronger electron-withdrawing ability of nitro group which can be confirmed by the red-shifted λmax of 8C (Figure S9b) results in faster cis-trans isomerization of 8C at the same condition [40]. The faster cis-trans isomerization of the sample will lead to lower isomerization degree and shorter time reaching the photo-stationary state. When photo-stationary stated 8B solution is put in darkness, the metastable cis-azobenzene will return to the trans-azobenzene. Under such situation, absorbance peak of trans isomer (λmax = 449 nm) gradually increases while absorbance peak of the cis isomer (λmax = 382 nm) gradually decreases (Figure 4c). After about 10 min, all of the azobenzene relaxes back to the trans conformation [39]. The similar results about the variation of the azobenzene isomerization are also observed for the other polymer solutions (Figure 4d). Furthermore, the cis-trans isomerization of 8A, 8B, and 8C can also be best fitted by Equation (1) (Figure 4d).
Photoinduced isomerization of the spin-coated film of 8A, 8B, and 8C is further investigated as the photoinduced anisotropy is carried out on the film state. As shown in Figure 5a, a similar UV-vis absorption peak as that of 8B solution is observed for the spin-coated film of 8B. However, the λmax of spin-coated film of 8B blue-shifts to 446 nm due to the aggregation of azo chromophores. The λmax of spin-coated film of 8A and 8C also blue-shifts to 432 and 475 nm, respectively. Upon irradiation with 450 nm light, photoinduced isomerization is also observed from the 8B film. On the other hand, the isomerization degree of 8B film (0.102) is much lower than that of 8B solution, indicating that the photoinduced isomerization of 8B film is restricted to some extent. This is due to the much worse mobility of azo chromophore on the film state. The changing of λmax of 8B film during the photoinduced isomerization can also be best fitted by Equation (1) (Figure 5b). Putting photo-stationary stated 8B film in darkness, cis-trans isomerization of the azobenzene in the sample is observed, as shown in Figure 5c. Similarly, resulting from the poorer mobility of azo chromophore on the film state, it takes longer time for the cis sample of 8B to relax back to the trans state. Nevertheless, the photoinduced trans-cis and the thermal cis-trans isomerization can be observed in the spin-coated film of 8B. As for spin-coated film of 8A and 8C, similar results as that of 8B film are also observed (Figure 5b,d).
Photoinduced birefringence of 8A, 8B, and 8C is studied according to the literature [31]. Birefringence (Δn) is obtained based on the probe beam using Equation (2):
I = I0 sin 2 (πΔnd/λ)
In which d represents film thickness, λ means 633 nm, and I and I0 correspond to intensity of probe beam with and without through the 8A, 8B, and 8C films. Figure 6 represents Δn changing of 8A, 8B, and 8C. Δn is zero for all polymers before irradiating with light due to the un-orientation of the spin-coated film. Δn raises abruptly once the light source is turned on and then saturates in 40 s [29]. The saturated birefringence of the polymers is 0.066, 0.036, and 0.018 for 8A, 8B, and 8C, respectively. Table 1 listed the photoinduced Δn of some typical azo materials. The azobenzene type azopolymers demonstrate high saturated Δn due to the orientation of liquid crystalline domain induced by the photoisomerization of the azo chromophore. Pseudo-stilbene azo molecular glasses also exhibit high saturated Δn on account of their smaller molecular weight. The high saturated Δn of azo molecular glasses also benefits from higher density of azo chromophores in the system, which can be confirmed by the biazo-containing polymers. In comparison, pseudo-stilbene azobenzene polymers show much lower saturated Δn. However, the photoinduced Δn of 8A and 8B is higher than that of similar azopolymers reported in the literatures, which would be derived from the fact that the photoinduced movement of the azo chromophore tend to drive the orientation of the mesogen. Upon switching off the irradiation, Δn decreases simultaneously, as shown in Figure 6 [31]. For azo containing materials, the higher the saturated Δn is, the higher the retention value of Δn is. The retention value of Δn is 0.055, 0.028, and 0.014 for 8A, 8B, and 8C, respectively. As the photoinduced Δn is derived from the photo-isomerization of the azobenzene, saturated Δn and retention value of Δn of 8A, 8B, and 8C exhibit similar result as that of isomerization degree of the samples. This could be used to explain the low saturated value of Δn and retention value of Δn of 8C. While, as for the time needed to reach the saturated Δn, it is determined by the structures of the samples as well as the irradiation light. One can adjust the time easily through controlling the state of irradiation light.
Polarized FTIR spectrometer is utilized for the study of photoinduced dichroisms. [29] 8A, 8B, and 8C films are firstly irradiated by polarized light (532 nm, 50 mW/cm2) and then tested through polarized FT-IR spectrometer at different angles. Figure 7 exhibits polarized plot of infrared absorption from ν (benzene ring) at 1507 cm−1 for 8A, 8B, and 8C. The orientation order parameter (S) which can be used to show the dichroism is obtained through Equation (3):
S = (AA||) / (A + 2A||)
where A and A|| correspond to intensity of the infrared absorption perpendicular as well as parallel to incident light polarization direction [29]. According to the polarized FTIR result, S is 0.179, 0.105, and 0.011 for 8A, 8B, and 8C. The value of S of 8A and 8B is also higher than that of similar azopolymers without mesogen group, indicating the photoinduced isomerization of azobenzene tend to drive the orientation of the mesogen groups in the system [31]. The low S of 8C is also a result of the low isomerization degree of the samples. In consequence, the obtained polymers blaze a way to design optical materials with light controllable birefringence and dichroism.

4. Conclusions

A series of polymers (8A, 8B, and 8C) containing nunchaku-like unit with an azobenzene and a mesogen was polymerized from monomers (7A, 7B, and 7C) containing nunchaku-like unit with an azobenzene and a mesogen linked by flexible group which were synthesized through a seven-step procedure. The structure of the obtained monomers was confirmed via NMR COSY spectrum while the synthesis of these polymers was verified by proton NMR and FTIR spectra. According to the GPC results, the number average molecular weight is 13,000, 15,000, 16,000, and PDI is 1.22, 1.26, and 1.28 respectively for 8A, 8B, and 8C. UV-vis spectra indicate that λmax of 8A, 8B, and 8C are 435, 449, and 478 nm respectively. DSC and POM demonstrate that 8A, 8B, and 8C are amorphous polymers whose Tg is 83, 75, and 70 °C respectively. Photoinduced trans-cis isomerization kinetics reveal the rapid photo-isomerization of the polymers. Under polarized light irradiation, photoinduced birefringence of the polymers reach saturation quickly which is 0.066, 0.036, and 0.018 for 8A, 8B, and 8C, respectively. The orientation order parameter calculated by polarized FTIR is 0.179, 0.105, as well as 0.011 for 8A, 8B, and 8C which is higher than that of the azo polymers without mesogen group, indicating the photoinduced isomerization will drive the orientation of the mesogen groups in the system. The obtained polymers blaze a way to design the optical materials with light-controllable birefringence and dichroism.

Supplementary Materials

The Supplementary Materials are available online at https://www.mdpi.com/2073-4360/11/4/600/s1.

Author Contributions

Conceptualization, L.W., Y.Z., and R.W.; validation, L.W., C.Z., and Y.Y.; formal analysis, L.W., H.Z., and J.M.; investigation, L.W. and Z.X.; writing—original draft preparation, L.W., Y.Z., and R.W.; writing—review and editing, R.W.; visualization, R.W.; supervision, X.L.; funding acquisition, R.W. and X.L.

Funding

The work was funded by National Natural Science Foundation of China (No. 51603029 and 51773028), China Postdoctoral Science Foundation (2017M623001) and National Postdoctoral Program for Innovative Talents (BX201700044).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Han, G.D.; Park, S.S.; Liu, Y.; Zhitomirsky, D.; Cho, E.; Dincă, M.; Grossman, J.C. Photon energy storage materials with high energy densities based on diacetylene–azobenzene derivatives. J. Mater. Chem. A 2016, 4, 16157–16165. [Google Scholar] [CrossRef] [Green Version]
  2. Zhou, H.; Xue, C.; Weis, P.; Suzuki, Y.; Huang, S.; Koynov, K.; Auernhammer, G.K.; Berger, R.; Butt, H.J.; Wu, S. Photoswitching of glass transition temperatures of azobenzene-containing polymers induces reversible solid-to-liquid transitions. Nat. Chem. 2017, 9, 145–151. [Google Scholar] [CrossRef] [PubMed]
  3. Chi, X.; Ji, X.; Xia, D.; Huang, F. A dual-responsive supra-amphiphilic polypseudorotaxane constructed from a water-soluble pillar[7]arene and an azobenzene-containing random copolymer. J. Am. Chem. Soc. 2015, 137, 1440–1443. [Google Scholar] [CrossRef] [PubMed]
  4. Ahn, S.K.; Ware, T.H.; Lee, K.M.; Tondiglia, V.P.; White, T.J. Photoinduced topographical feature development in blueprinted azobenzene-functionalized liquid crystalline elastomers. Adv. Funct. Mater. 2016, 26, 5819–5826. [Google Scholar] [CrossRef]
  5. Wang, J.; Wang, S.; Zhou, Y.; Wang, X.; He, Y. Fast photoinduced large deformation of colloidal spheres from a novel 4-arm azobenzene compound. ACS Appl. Mater. Interfaces 2015, 7, 16889–16895. [Google Scholar] [CrossRef]
  6. Guo, S.; Matsukawa, K.; Miyata, T.; Okubo, T.; Kuroda, K.; Shimojima, A. Photoinduced bending of self-assembled azobenzene-siloxane hybrid. J. Am. Chem. Soc. 2015, 137, 15434–15440. [Google Scholar] [CrossRef] [PubMed]
  7. Liu, Z.; Tang, R.; Xu, D.; Liu, J.; Yu, H. Precise actuation of bilayer photomechanical films coated with molecular azobenzene chromophores. Macromol. Rapid Commun. 2015, 36, 1171–1176. [Google Scholar] [CrossRef]
  8. Wang, X.; Yin, J.; Wang, X. Self-structured surface patterns on epoxy-based azo polymer films induced by laser light irradiation. Macromolecules 2011, 44, 6856–6867. [Google Scholar] [CrossRef]
  9. Bisoyi, H.K.; Li, Q. Light-driven liquid crystalline materials: From photo-induced phase transitions and property modulations to applications. Chem. Rev. 2016, 116, 15089–15166. [Google Scholar] [CrossRef]
  10. Wang, D.; Ye, G.; Wang, X.; Wang, X. Graphene functionalized with azo polymer brushes: Surface-initiated polymerization and photoresponsive properties. Adv. Mater. 2011, 23, 1122–1125. [Google Scholar] [CrossRef]
  11. Xiong, Z.; Liao, C.; Wang, X. Reduced graphene oxide diffraction gratings from duplication of photoinduced azo polymer surface-relief-gratings through soft-lithography. J. Mater. Chem. C 2015, 3, 6224–6231. [Google Scholar] [CrossRef]
  12. Wang, Y.; Ye, G.; Wang, X. Photoinduced orientation in nunchaku-like azo molecular glass studied by birefringence characterization and FT-IR spectroscopy. J. Mater. Chem. 2012, 22, 7614–7621. [Google Scholar] [CrossRef]
  13. Kharintsev, S.S.; Fishman, A.I.; Saikin, S.K.; Kazarian, S.G. Near-field Raman dichroism of azo-polymers exposed to nanoscale dc electrical and optical poling. Nanoscale 2016, 8, 19867–19875. [Google Scholar] [CrossRef] [Green Version]
  14. Yang, L.; Tang, H.L.; Sun, H. Progress in Photo-responsive polypeptide derived nano-assemblies. Micromachines 2018, 9, 296. [Google Scholar] [CrossRef]
  15. Hu, J.; Li, X.; Ni, Y.; Ma, S.D.; Yu, H.F. A programmable and biomimetic photo-actuator: A composite of a photo-liquefiable azobenzene derivative and commercial plastic film. J. Mater. Chem. C 2018, 6, 10815–10821. [Google Scholar] [CrossRef]
  16. Ma, S.D.; Li, X.; Huang, S.; Hu, J.; Yu, H.F. A Light-activated polymer composite enables on-demand photocontrolled mMotion: Transportation at the liquid/air interface. Angew. Chem. 2019, 131, 2681–2685. [Google Scholar] [CrossRef]
  17. Hernández-Ainsa, S.; Alcalá, R.; Barberá, J.; Marcos, M.; Sánchez, C.; Serrano, J.L. Ionic photoresponsive azo-codendrimer with room temperature mesomorphism and high photoinduced optical anisotropy. Macromolecules 2010, 43, 2660–2663. [Google Scholar] [CrossRef]
  18. Fernández, R.; Etxeberria, H.; Eceiza, A.; Tercjak, A. Enhanced stability of photo-induced anisotropy due to intermolecular interactions in an azo-prepolymer confined in block copolymer. Eur. Polym. J. 2013, 49, 984–990. [Google Scholar] [CrossRef]
  19. Dąbrowski, R.; Kula, P.; Herman, J. High birefringence liquid crystals. Crystals 2013, 3, 443–482. [Google Scholar] [CrossRef]
  20. Li, X.; Tan, N.; Pivnenko, M.; Sibik, J.; Zeitler, J.A.; Chu, D. High-birefringence nematic liquid crystal for broadband THz applications. Liq. Cryst. 2016, 43, 955–962. [Google Scholar] [CrossRef]
  21. Ho, M.S.; Natansohn, A.; Barrett, C.; Rochon, P. Azo polymers for reversible optical storage. 8. The effect of polarity of the azobenzene groups. Can. J. Chem. 1995, 73, 1773–1778. [Google Scholar] [CrossRef] [Green Version]
  22. Rau, H. Photoisomerization of Azobenzenes; CRC Press: Boca Raton, FL, USA, 1990. [Google Scholar]
  23. Wei, R.; Wang, X.; He, Y. Synthesis, self-assembly and photo-responsive behavior of AB2 shaped amphiphilic azo block copolymer. Chin. Chem. Lett. 2015, 26, 857–861. [Google Scholar] [CrossRef]
  24. Beppu, K.; Nagashima, Y.; Hara, M.; Nagano, S.; Seki, T. Photoalignment of vertically oriented microphase separated lamellae in LC–LC diblock copolymer thin film. Macromol. Rapid Commun. 2017, 38, 1600659. [Google Scholar] [CrossRef] [PubMed]
  25. Huang, S.; Chen, Y.X.; Ma, S.D.; Yu, H.F. Hierarchical self-assembly in liquid-crystalline block copolymers enabled by chirality transfer. Angew. Chem. Int. Ed. 2018, 57, 12524–12528. [Google Scholar] [CrossRef]
  26. Li, X.; Ma, S.D.; Hu, J.; Ni, Y.; Lin, Z.Q.; Yu, H.F. Photo-activated bimorph composites of Kapton and liquid-crystalline polymer towards biomimetic circadian rhythms of Albizia julibrissin leaves. J. Mater. Chem. C 2019, 7, 622–629. [Google Scholar] [CrossRef]
  27. Wei, R.; Ma, J.; Zhang, H.; He, Y. Synthesis, characterization, and photo-responsive properties of Y-shaped amphiphilic azo triblock copolymer. J. Appl. Polym. Sci. 2016, 133, 43695. [Google Scholar] [CrossRef]
  28. Zhu, Y.; Wang, X. Photoresponsive diblock copolymers bearing strong push-pull azo chromophores and mesogenic biphenyl groups. Dyes Pigment. 2013, 97, 222–229. [Google Scholar] [CrossRef]
  29. Wei, R.; Xu, Z.; Liu, X.; He, Y.; Wang, X. Liquid-crystalline compounds containing both a strong push-pull azo chromophore and a cholesteryl unit as photoresponsive molecular glass materials. J. Mater. Chem. C 2015, 3, 10925–10933. [Google Scholar] [CrossRef]
  30. Ye, G.; Wang, D.; He, Y.; Wang, X. Nunchaku-like molecules containing both an azo chromophore and a biphenylene unit as a new type of high-sensitivity photo-storage material. J. Mater. Chem. 2010, 20, 10680–10687. [Google Scholar] [CrossRef]
  31. Zhu, Y.; Zhou, Y.; Wang, X. Photoresponsive behavior of two well-defined azo polymers with different electron-withdrawing groups on push-pull azo chromophores. Dyes Pigment. 2013, 99, 209–219. [Google Scholar] [CrossRef]
  32. Wei, R.; Wang, Z.; Zhang, H.; Liu, X. Photo-responsive liquid crystalline elastomer with reduced chemically modified graphene oxide. Liq. Cryst. 2016, 43, 1009–1016. [Google Scholar] [CrossRef]
  33. Wei, R.; Tu, L.; You, Y.; Zhan, C.; Wang, Y.; Liu, X. Fabrication of crosslinked single-component polyarylene ether nitrile composite with enhanced dielectric properties. Polymer 2019, 161, 162–169. [Google Scholar] [CrossRef]
  34. Wei, R.; Wang, X.; He, Y. Synthesis of side-on liquid crystalline diblock copolymers through macromolecular azo coupling reaction. Eur. Polym. J. 2015, 69, 584–591. [Google Scholar] [CrossRef]
  35. Yang, Y.; Hughes, R.; Aprahamian, I. Visible light switching of a BF2-coordinated azo compound. J. Am. Chem. Soc. 2012, 134, 15221–15224. [Google Scholar] [CrossRef]
  36. Wang, J.; Wu, B.; Li, S.; Sinawang, G.; Wang, X.; He, Y. Synthesis and characterization of photoprocessable lignin-based azo polymer. ACS Sustain. Chem. Eng. 2016, 4, 4036–4042. [Google Scholar] [CrossRef]
  37. Bobrovsky, A.; Boiko, N.; Shibaev, V. Unusual electro-optical behaviour of the nematic polyacrylate. Liq. Cryst. 2017, 44, 1870–1876. [Google Scholar] [CrossRef]
  38. Wei, R.; Wang, J.; Zhang, H.; Han, W.; Liu, X. Crosslinked polyarylene ether nitrile interpenetrating with zinc ion bridged graphene sheet and carbon nanotube network. Polymers 2017, 9, 342. [Google Scholar] [CrossRef]
  39. Wei, R.; He, Y.; Wang, X. Diblock copolymers composed of a liquid crystalline azo block and a poly (dimethylsiloxane) block: Synthesis, morphology and photoresponsive properties. RSC Adv. 2014, 4, 58386–58396. [Google Scholar] [CrossRef]
  40. Zhang, X.; Wen, Z.; Zhang, H.; Han, W.; Ma, J.; Wei, R.; Hua, X. Dielectric properties of azo polymers: Effect of the push-pull azo chromophores. Int. J. Polym. Sci. 2018, 2018, 4541937. [Google Scholar] [CrossRef]
  41. Zhu, Y.; Wang, X. Synthesis and photoresponsive properties of two liquid crystalline polymers bearing branched azobenzene-containing side chains. Polym. Chem. 2013, 4, 5108–5118. [Google Scholar] [CrossRef]
  42. Okano, K.; Shishido, A.; Ikeda, T. Synthesis and photoresponsive behavior of a liquid-crystalline polymer with a 4-ring azotolane moiety with huge birefringence. Mol. Cryst. Liq. Cryst. 2007, 478, 259–1015. [Google Scholar] [CrossRef]
  43. Lachut, B.L.; Maier, S.A.; Atwater, H.A.; de Dood, M.J.; Polman, A.; Hagen, R.; Kostromine, S. Large spectral birefringence in photoaddressable polymer films. Adv. Mater. 2004, 16, 1746–1750. [Google Scholar] [CrossRef]
  44. Zhu, Y.; Zhou, Y.; Chen, Z.; Lin, R.; Wang, X. Photoresponsive diblock copolymers bearing strong push–pull azo chromophores and cholesteryl groups. Polymer 2012, 53, 3566–3576. [Google Scholar] [CrossRef]
Figure 1. Synthetic route for the polymers 8A, 8B, and 8C.
Figure 1. Synthetic route for the polymers 8A, 8B, and 8C.
Polymers 11 00600 g001
Figure 2. NMR COSY spectrum of 7B.
Figure 2. NMR COSY spectrum of 7B.
Polymers 11 00600 g002
Figure 3. Proton NMR spectra (a) and FTIR spectra (b) of 8A, 8B, and 8C.
Figure 3. Proton NMR spectra (a) and FTIR spectra (b) of 8A, 8B, and 8C.
Polymers 11 00600 g003
Figure 4. UV-vis spectra of solution of 8B irradiated with 450 nm light (a) and in the dark after reaching photo-stationary state (c); relative absorbance at λmax and the corresponding fitted curves for solutions of 8A, 8B, and 8C during the trans-cis (b) and cis-trans (d) isomerization.
Figure 4. UV-vis spectra of solution of 8B irradiated with 450 nm light (a) and in the dark after reaching photo-stationary state (c); relative absorbance at λmax and the corresponding fitted curves for solutions of 8A, 8B, and 8C during the trans-cis (b) and cis-trans (d) isomerization.
Polymers 11 00600 g004
Figure 5. UV-vis spectra of spin-coated film of 8B irradiated with 450 nm light (a) and in the dark after reaching photo-stationary state (c); relative absorbance at λmax and the corresponding fitted curves for spin-coated film of 8A, 8B, and 8C during the trans-cis (b) and cis-trans (d) isomerization.
Figure 5. UV-vis spectra of spin-coated film of 8B irradiated with 450 nm light (a) and in the dark after reaching photo-stationary state (c); relative absorbance at λmax and the corresponding fitted curves for spin-coated film of 8A, 8B, and 8C during the trans-cis (b) and cis-trans (d) isomerization.
Polymers 11 00600 g005
Figure 6. Change of birefringence of 8A, 8B, and 8C at different irradiation time and relaxation time.
Figure 6. Change of birefringence of 8A, 8B, and 8C at different irradiation time and relaxation time.
Polymers 11 00600 g006
Figure 7. Polar plots of IR absorption intensities from ν (benzene ring) at 1507 cm−1 for 8A, 8B, and 8C.
Figure 7. Polar plots of IR absorption intensities from ν (benzene ring) at 1507 cm−1 for 8A, 8B, and 8C.
Polymers 11 00600 g007
Table 1. Saturated Δn and retention value of Δn of some typical azo materials.
Table 1. Saturated Δn and retention value of Δn of some typical azo materials.
SampleType of AzobenzeneType of MaterialsGroup at 4′ PositionSaturated ΔnRetention Value of ΔnReference
P3ABMAazobenzenePolymer-C4H90.014--[41]
P4ATTazobenzenePolymerTolane0.690--[42]
PAPpseudo-stilbene/biazoPolymer-CN0.590--[43]
CN-Cholpseudo-stilbeneMolecular glass-CN0.0950.110[24]
AZBP-CNpseudo-stilbeneMolecular glass-CN0.0930.107[25]
PAzoCNpseudo-stilbenePolymer-CN0.0350.024[26]
PBiPMA50-PAzoCN43pseudo-stilbeneCopolymer-CN0.0340.030[23]
PChEMA50-PAzoCN50pseudo-stilbeneCopolymer-CN0.0250.017[44]
PAzoCApseudo-stilbenePolymer-COOH0.0370.034[26]
8Apseudo-stilbenePolymer-COOH0.0660.055This work
8Bpseudo-stilbenePolymer-CN0.0360.028This work

Share and Cite

MDPI and ACS Style

Wang, L.; Zhang, Y.; Zhan, C.; You, Y.; Zhang, H.; Ma, J.; Xiong, Z.; Liu, X.; Wei, R. Synthesis and Photoinduced Anisotropy of Polymers Containing Nunchaku-Like Unit with an Azobenzene and a Mesogen. Polymers 2019, 11, 600. https://doi.org/10.3390/polym11040600

AMA Style

Wang L, Zhang Y, Zhan C, You Y, Zhang H, Ma J, Xiong Z, Liu X, Wei R. Synthesis and Photoinduced Anisotropy of Polymers Containing Nunchaku-Like Unit with an Azobenzene and a Mesogen. Polymers. 2019; 11(4):600. https://doi.org/10.3390/polym11040600

Chicago/Turabian Style

Wang, Lingling, Yingchuan Zhang, Chenhao Zhan, Yong You, Hongxing Zhang, Jinyi Ma, Zhiyuan Xiong, Xiaobo Liu, and Renbo Wei. 2019. "Synthesis and Photoinduced Anisotropy of Polymers Containing Nunchaku-Like Unit with an Azobenzene and a Mesogen" Polymers 11, no. 4: 600. https://doi.org/10.3390/polym11040600

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.