Synthesis and Properties of New Poly( Amide-Imide)s Based on Imide Dicarboxylic Acid
Abstract:
Two kinds of imide dicarboxylic acid monomers, 4,4'-bis(trimellitimido) diphenyl ether Ⅰ and p-trimellitimido-benzoic acid Ⅱ were successfully synthesized from 4,4'-diaminodiphenyl ether and p-aminobenzoic acid with trimellitic anhydride respectively.and used to synthesize a series of new aromatic poly(amide-imide)s (PAIs) by the tri-phenyl phosphite-activated polycondensation method. The preparation of PAIs was carried out using triphenyl phosphate and pyridine symtem. The PAIs had inherent viscosities of 0.55–1.46 dL g-1. PAI films were obtained by casting their N-Methyl-2-pyrrolidone (NMP) solution. Their cast films had tensile strengths ranging from 37.4 to 83.9 MPa. The glass-transition temperatures (measured by differential scanning calorimetry) were in the range of 265-310°C. According to thermogravimetric analysis, the polymers were fairly stable up to temperature around 420°C, and 10% weight losses in the temperature range of 474-550°C in nitrogen, that showed good thermal stabilities of these polymers.
Info:
Periodical:
Pages:
1722-1726
Citation:
Online since:
September 2011
Authors:
Price:
Permissions: