Selective Laser Melting of Prealloyed High Alloy Steel Powder Beds

Article Preview

Abstract:

This paper presents the results of a recent comprehensive investigation of selective laser melting (slm) of prealloyed gas and water atomised M2 and H13 tool steel powders. The objective of the study was to establish the parameters that control the densification of single and multiple layers with the aim of producing high density parts without the need for infiltration. Powders were processed using continuous wave (CW) CO2 and Nd:YAG lasers. Relationships between alloy composition, powder particle size and shape, flowability, microstructure (phases present, their size, morphology and distribution), track morphology, post scanned density, surface finish and scan conditions (Laser power, spot size and scan speed) are discussed for single track, single layer and multi-layer (up to 25 layers) constructions. Processing with a Nd:YAG laser with powders placed on substrates rather than on a loose powder bed gave more stable builds than with the CO2 laser. Using the Nd:YAG laser densities up to ~90% relative were possible with H13 powder compared with a maximum of ~70% for M2 in multi-layer builds. Maximum density achieved with CW CO2 processing was only ~60%, irrespective of powder composition. The paper compares the processibility of these materials with stainless steel powders processed to higher densities (up to 99% relative) under similar conditions. The results of the work show that a crucial factor for high density processing is melt pool wettability and this is controlled largely by carbon content; low carbon contents producing better wettability, flatter tracks and higher densities. The significance of this observation for the processing high alloy steels by slm will be discussed.

You might also be interested in these eBooks

Info:

Periodical:

Materials Science Forum (Volumes 514-516)

Pages:

516-523

Citation:

Online since:

May 2006

Export:

Price:

[1] G. N. Levy, R Schindel and J. P. Kruth: Annals of the CIRP Vol. 52/2 (2003), p.589.

Google Scholar

[2] K.W. Dalgarno and C.S. Wright: Approaches to Processing Metal and Ceramics through the Laser Scanning of Powder Beds, Powder Metallurgy Progress, Vol. 1(1) (2001), p.70.

Google Scholar

[3] K.W. DALGARNO and T. Stewart: Production Tooling for Polymer Moulding using the RapidSteel Process, Rapid Prototyping Journal Vol. 3(2) (2001), p.70.

DOI: 10.1108/13552540110395600

Google Scholar

[4] J. Kotila, J-E Lind, T. Syvänen, O. Nyrhilä and J. Hänninen: Direct Metal Laser Sintering in Rapid Manufacturing, Proceedings of EuroPM2003 Vol. 3 (2003) p.385.

DOI: 10.2351/1.5059286

Google Scholar

[5] R. Morgan, C. J. Sutcliffe and W. O'Neill: Density Analysis of Direct Laser Re-melted 316L Stainless Steel Cube Primitives, Journal of Materials Science, Vol. 39 (2004), p.1195.

DOI: 10.1023/b:jmsc.0000013875.62536.fa

Google Scholar

[6] A. Simchi, F. Petzodt and H. Pohl: Direct Metal Laser Sintering: Material Considerations and Mechanisms of Particle Bonding, Int. J. Powder Metallurgy Vol 37 (2001) p.51.

Google Scholar

[7] C. Hauser: Selective Laser Sintering of Stainless Steel Powder, PhD Thesis, (University of Leeds 2003).

Google Scholar

[8] M. Dewidar, K.W. Dalgarno, and C.S. Wright: Processing Conditions and Mechanical Properties of High Speed Steel Parts Fabricated Using Direct Selective Laser Sintering, Proc. IMechE Part B, Vol. 217 (2003), p.1651.

DOI: 10.1243/095440503772680587

Google Scholar

[9] N.K. Tolochko et. al. : Absorptance of Powder Materials Suitable for Laser Sintering, Rapid Prototyping Journal, Vol. 6(3) (2001), p.1355.

Google Scholar

[10] C Hauser et. al.: Effects of Laser Beam Width and Scan Strategy during Direct Selective Laser Sintering of Tool Steel Powders to High Density: Part A, Proceedings of 13th Solid FreeForm Fabrication Symposium 2003 (University of Texas at Austin, 2003).

Google Scholar

[11] S.P. Akhtar et. al: Direct Selective Laser Sintering of Tool Steel Powders to High Density, Proceedings of EuroPM2003 (EPMA, Shrewsbury, UK) Vol. 3 (2003) p.379.

Google Scholar

[12] G. Hoyle: Modification of the Cast Structure of High Speed Steel, J. Iron Steel Institute (1959), p.254.

Google Scholar

[13] C.S. Wright et. al.: Supersolidus Liquid Phase Sintering of High Speed Steels - Part 3 the Computer Aided Design of Sinterable Alloys, Powder Metallurgy, Vol. 42(2) (1999), p.131.

DOI: 10.1179/003258999665486

Google Scholar

[14] M.A. Gomes, A.S. Wronski and C.S. Wright, Fracture Behaviour of a Highly Alloyed High Speed Steel, Fracture and Fatigue of Engineering Materials and Structures, Vol. 18(1) (995), p.1.

DOI: 10.1111/j.1460-2695.1995.tb00137.x

Google Scholar

[15] G. Hoyle: High Speed Steels (Butterworths, London, UK, 1988).

Google Scholar

[16] N. J. Niu and I.T.H. Chang: Selective Laser Sintering of Gas and Water Atomised High Speed Steel Powders, Scripta Materialia Vol. 42 (1999), p.25.

DOI: 10.1016/s1359-6462(99)00089-5

Google Scholar

[17] N. J. Niu and I. T. H. Chang: Instability of Scan Tracks of Selective Laser Sintering of High Speed Steel Powder, Scripta Materialia¸, Vol. 42 (1999), p.1229.

DOI: 10.1016/s1359-6462(99)00276-6

Google Scholar

[18] J. W. Xie et. al.: Direct Laser Re-melting of Tool Steels, Proceedings of EuroPM2003 (EPMA, Shrewsbury, UK) Vol 3 (2003) p.473.

Google Scholar